CN103483952B - A kind of Acrylic transparent powder paint - Google Patents
A kind of Acrylic transparent powder paint Download PDFInfo
- Publication number
- CN103483952B CN103483952B CN201310393228.7A CN201310393228A CN103483952B CN 103483952 B CN103483952 B CN 103483952B CN 201310393228 A CN201310393228 A CN 201310393228A CN 103483952 B CN103483952 B CN 103483952B
- Authority
- CN
- China
- Prior art keywords
- powder paint
- acrylic transparent
- powder
- transparent powder
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of Acrylic transparent powder paint, it is made up of the raw material of following weight parts: epoxide number is the acrylic resin 70-80 of 320-525, tetradecane binary acid 6-10, polyisobutylene 2-3, Benzoinum 0.1-0.3, N-phenyl-3-TSL 8330 2.1-3.2, Fluorspar Powder 10-13, hydration zinc borate 2-4, Colophonium 3-4, sodium tripolyphosphate 1-2, tartaric acid 1-2, mannitol 2-3, compounded mix 16-20;Acrylic transparent powder paint of the present invention has heigh clarity and excellent levelability, anti-thread splendid with crazing, and can solidify under cryogenic, is particularly suitable for aluminum wheels of automobiles and car surface spraying。
Description
Technical field
The invention mainly relates to a kind of coating, particularly relate to a kind of Acrylic transparent powder paint。
Background technology
Heat curable powder coating refers to using thermosetting resin as film forming matter, added the firming agent of cross-linking reaction heated after can form insoluble not molten quality hard coat。Temperature this coating high again softens without as thermoplastic coating, and can only decompose。The resin adopted due to thermosetting powder coating is the prepolymer that the degree of polymerization is relatively low, molecular weight is relatively low, so the levelability of coating is better, there is good dicoration, and low-molecular-weight prepolymer cured after, the macromole of cross-linked network can be formed, thus coating has better anti-corrosive properties and mechanical performance。Therefore thermosetting powder coating development is particularly rapid, and in order to improve the overall performance of conventional powder, by adding new compounded mix etc., to improve its performance be necessary。
Summary of the invention
The object of the invention is contemplated to provide a kind of Acrylic transparent powder paint。
The present invention is achieved by the following technical solutions:
A kind of Acrylic transparent powder paint, it is characterised in that it is made up of the raw material of following weight parts:
Epoxide number is the acrylic resin 70-80 of 320-525, tetradecane binary acid 6-10, polyisobutylene 2-3, Benzoinum 0.1-0.3, N-phenyl-3-TSL 8330 2.1-3.2, Fluorspar Powder 10-13, hydration zinc borate 2-4, Colophonium 3-4, sodium tripolyphosphate 1-2, tartaric acid 1-2, mannitol 2-3, compounded mix 16-20;
Described compounded mix is made up of the raw material of following weight parts:
Laterite 50-60, bone meal 4-6, iron mine ground-slag 10-13, wollastonite in powder 5-7, sodium tripolyphosphate 1-2, Dodecyl trimethyl ammonium chloride 2-3, Eucalyptus oil 1-2;
By above-mentioned laterite, iron mine ground-slag, wollastonite in powder mixing, calcine 3-4 hour at 600-800 DEG C, cooling discharging, add Eucalyptus oil, mix homogeneously, obtains premix material, is joined by sodium tripolyphosphate in 15-20 times of water, it is stirring evenly and then adding into Dodecyl trimethyl ammonium chloride, raise temperature and be 60-80 DEG C, with above-mentioned premix material mixed grinding, drying, cross 80-100 mesh sieve, obtain described compounded mix。
The preparation method of a kind of Acrylic transparent powder paint, comprises the following steps:
Above-mentioned N-phenyl-3-TSL 8330 is mixed with Fluorspar Powder, hydration zinc borate, it is heated to 55-60 DEG C, 400-600 rev/min dispersed with stirring 2-3 minute, mix with remaining each raw material, put into mixing in high-speed mixer abundant, then gained compound is put into mixing extrusion in high-speed extruder, after then tabletting crushes, pulverize then through atomizer, sieve, obtain described Acrylic transparent powder paint。
The invention have the advantage that
Acrylic transparent powder paint of the present invention has heigh clarity and excellent levelability, anti-thread splendid with crazing, and can solidify under cryogenic, is particularly suitable for aluminum wheels of automobiles and car surface spraying。
Detailed description of the invention
Embodiment 1,
A kind of Acrylic transparent powder paint, it is made up of the raw material of following weight parts (kilogram):
Epoxide number is the acrylic resin 80 of 320-525, tetradecane binary acid 10, polyisobutylene 3, Benzoinum 0.3, N-phenyl-3-TSL 8330 3.2, Fluorspar Powder 13, hydration zinc borate 2, Colophonium 4, sodium tripolyphosphate 1-2, tartaric acid 1, mannitol 2, compounded mix 20;
Described compounded mix is made up of the raw material of following weight parts:
Laterite 60, bone meal 6, iron mine ground-slag 13, wollastonite in powder 7, sodium tripolyphosphate 1, Dodecyl trimethyl ammonium chloride 2, Eucalyptus oil 2;
By above-mentioned laterite, iron mine ground-slag, wollastonite in powder mixing, calcine 4 hours at 800 DEG C, cooling discharging, add Eucalyptus oil, mix homogeneously, obtains premix material, is joined by sodium tripolyphosphate in 20 times of water, it is stirring evenly and then adding into Dodecyl trimethyl ammonium chloride, raising temperature is 80 DEG C, with above-mentioned premix material mixed grinding, drying, cross 80-100 mesh sieve, obtain described compounded mix。
The preparation method of a kind of Acrylic transparent powder paint, comprises the following steps:
Above-mentioned N-phenyl-3-TSL 8330 is mixed with Fluorspar Powder, hydration zinc borate, it is heated to 60 DEG C, 600 revs/min of dispersed with stirring 3 minutes, mix with remaining each raw material, put into mixing in high-speed mixer abundant, then gained compound is put into mixing extrusion in high-speed extruder, after then tabletting crushes, pulverize then through atomizer, sieve, obtain described Acrylic transparent powder paint。
Performance test:
Impact resistance: >=50kg/cm;
Hardness: 2H。
Claims (2)
1. an Acrylic transparent powder paint, it is characterised in that it is made up of the raw material of following weight parts:
Epoxide number is the acrylic resin 70-80 of 320-525, tetradecane binary acid 6-10, polyisobutylene 2-3, Benzoinum 0.1-0.3, N-phenyl-3-TSL 8330 2.1-3.2, Fluorspar Powder 10-13, hydration zinc borate 2-4, Colophonium 3-4, sodium tripolyphosphate 1-2, tartaric acid 1-2, mannitol 2-3, compounded mix 16-20;
Described compounded mix is made up of the raw material of following weight parts:
Laterite 50-60, bone meal 4-6, iron mine ground-slag 10-13, wollastonite in powder 5-7, sodium tripolyphosphate 1-2, Dodecyl trimethyl ammonium chloride 2-3, Eucalyptus oil 1-2;
By above-mentioned laterite, iron mine ground-slag, wollastonite in powder mixing, calcine 3-4 hour at 600-800 DEG C, cooling discharging, add Eucalyptus oil, mix homogeneously, obtains premix material, is joined by sodium tripolyphosphate in 15-20 times of water, it is stirring evenly and then adding into Dodecyl trimethyl ammonium chloride, raise temperature and be 60-80 DEG C, with above-mentioned premix material mixed grinding, drying, cross 80-100 mesh sieve, obtain described compounded mix。
2. the preparation method of an Acrylic transparent powder paint as claimed in claim 1, it is characterised in that comprise the following steps:
Above-mentioned N-phenyl-3-TSL 8330 is mixed with Fluorspar Powder, hydration zinc borate, it is heated to 55-60 DEG C, 400-600 rev/min dispersed with stirring 2-3 minute, mix with remaining each raw material, put into mixing in high-speed mixer abundant, then gained compound is put into mixing extrusion in high-speed extruder, after then tabletting crushes, pulverize then through atomizer, sieve, obtain described Acrylic transparent powder paint。