CN103483952A - Acrylic transparent powder paint - Google Patents
Acrylic transparent powder paint Download PDFInfo
- Publication number
- CN103483952A CN103483952A CN201310393228.7A CN201310393228A CN103483952A CN 103483952 A CN103483952 A CN 103483952A CN 201310393228 A CN201310393228 A CN 201310393228A CN 103483952 A CN103483952 A CN 103483952A
- Authority
- CN
- China
- Prior art keywords
- parts
- mix
- powder paint
- transparent powder
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses acrylic transparent powder paint which is composed of the following raw materials in parts by weight: 70-80 parts of acrylic resin having an epoxide number of 320-525, 6-10 parts of tetradecanedioic acid, 2-3 parts of polyisobutylene, 0.1-0.3 part of benzoin, 2.1-3.2 parts of N-[3-(trimethoxysilyl)propyl]aniline, 10-13 parts of fluorite powder, 2-4 parts of zinc borate hydrate, 3-4 parts of rosin, 1-2 parts of sodium tripolyphosphate, 1-2 parts of tartaric acid, 2-3 parts of mannitol and 16-20 parts of composite filler. The acrylic transparent powder paint has high transparency, fine leveling property and excellent filamentation and crazing resistance, can be cured under low-temperature conditions, and is very suitable for spray coating of automobile aluminum wheels and automobile surfaces.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of vinylformic acid transparent powder paint.
Background technology
Heat curable powder coating refers to usings thermosetting resin as filmogen, has added the solidifying agent of crosslinking reaction can form insoluble not molten quality hard coat after heating.Temperature high this coating can be not softening as thermoplastic coating more yet, and can only decompose.The resin adopted due to thermosetting powder coating(s) is the prepolymer that the polymerization degree is lower, molecular weight is lower, so the levelling property of coating is better, have ornamental preferably, and low-molecular-weight prepolymer is after solidifying, can form the macromole of cross-linked network, thereby coating have better preservative property and mechanical property.Therefore thermosetting powder coating(s) development is particularly rapid, and in order to improve the overall performance of conventional powder, by adding new compounded mix etc. to improve its performance, be necessary.
Summary of the invention
The object of the invention is exactly for a kind of vinylformic acid transparent powder paint is provided.
The present invention is achieved by the following technical solutions:
A kind of vinylformic acid transparent powder paint is characterized in that what it was comprised of the raw material of following weight parts:
The acrylic resin 70-80 that oxirane value is 320-525, tetradecane diprotic acid 6-10, polyisobutene 2-3, st-yrax 0.1-0.3, N-phenyl-3-TSL 8330 2.1-3.2, Fluorspar Powder 10-13, hydration zinc borate 2-4, rosin 3-4, tripoly phosphate sodium STPP 1-2, tartrate 1-2, N.F,USP MANNITOL 2-3, compounded mix 16-20;
Described compounded mix is comprised of the raw material of following weight parts:
Laterite 50-60, bone meal 4-6, iron ore ground-slag 10-13, wollastonite powder 5-7, tripoly phosphate sodium STPP 1-2, Dodecyl trimethyl ammonium chloride 2-3, Oil of Eucalyptus 1-2;
Above-mentioned laterite, iron ore ground-slag, wollastonite powder are mixed to calcining 3-4 hour under 600-800 ℃, cooling discharging, add Oil of Eucalyptus, mix, obtain Preblend, tripoly phosphate sodium STPP is joined in 15-20 times of water, add Dodecyl trimethyl ammonium chloride after stirring, the rising temperature is 60-80 ℃, with above-mentioned Preblend mixed grinding, dries, cross the 80-100 mesh sieve, obtain described compounded mix.
A kind of preparation method of vinylformic acid transparent powder paint comprises the following steps:
Above-mentioned N-phenyl-3-TSL 8330 is mixed with Fluorspar Powder, hydration zinc borate, be heated to 55-60 ℃, 400-600 rev/min of dispersed with stirring 2-3 minute, with each raw material of residue, mix, put into high-speed mixer and mix fully, then the gained compound is put into to mixing extrusion in high-speed extruder, then after the compressing tablet fragmentation, pulverize, sieve through pulverising mill again, obtain described vinylformic acid transparent powder paint.
Advantage of the present invention is:
Vinylformic acid transparent powder paint of the present invention has heigh clarity and excellent levelling property, anti-thread splendid with crazing, and can under cold condition, solidify, very suitable aluminum wheels of automobiles and car surface spraying.
Embodiment
Embodiment 1,
A kind of vinylformic acid transparent powder paint, it is comprised of the raw material of following weight parts (kilogram):
The acrylic resin 80 that oxirane value is 320-525, tetradecane diprotic acid 10, polyisobutene 3, st-yrax 0.3, N-phenyl-3-TSL 8330 3.2, Fluorspar Powder 13, hydration zinc borate 2, rosin 4, tripoly phosphate sodium STPP 1-2, tartrate 1, N.F,USP MANNITOL 2, compounded mix 20;
Described compounded mix is comprised of the raw material of following weight parts:
Laterite 60, bone meal 6, iron ore ground-slag 13, wollastonite powder 7, tripoly phosphate sodium STPP 1, Dodecyl trimethyl ammonium chloride 2, Oil of Eucalyptus 2;
Above-mentioned laterite, iron ore ground-slag, wollastonite powder are mixed, and under 800 ℃, calcining is 4 hours, cooling discharging, add Oil of Eucalyptus, mix, obtain Preblend, tripoly phosphate sodium STPP is joined in 20 times of water, add Dodecyl trimethyl ammonium chloride after stirring, the rising temperature is 80 ℃, with above-mentioned Preblend mixed grinding, dries, cross the 80-100 mesh sieve, obtain described compounded mix.
A kind of preparation method of vinylformic acid transparent powder paint comprises the following steps:
Above-mentioned N-phenyl-3-TSL 8330 is mixed with Fluorspar Powder, hydration zinc borate, be heated to 60 ℃, 600 rev/mins of dispersed with stirring 3 minutes, with each raw material of residue, mix, put into high-speed mixer and mix fully, then the gained compound is put into to mixing extrusion in high-speed extruder, then after the compressing tablet fragmentation, pulverize, sieve through pulverising mill again, obtain described vinylformic acid transparent powder paint.
Performance test:
Shock resistance: >=50kg/cm;
Hardness: 2H.
Claims (2)
1. a vinylformic acid transparent powder paint is characterized in that what it was comprised of the raw material of following weight parts:
The acrylic resin 70-80 that oxirane value is 320-525, tetradecane diprotic acid 6-10, polyisobutene 2-3, st-yrax 0.1-0.3, N-phenyl-3-TSL 8330 2.1-3.2, Fluorspar Powder 10-13, hydration zinc borate 2-4, rosin 3-4, tripoly phosphate sodium STPP 1-2, tartrate 1-2, N.F,USP MANNITOL 2-3, compounded mix 16-20;
Described compounded mix is comprised of the raw material of following weight parts:
Laterite 50-60, bone meal 4-6, iron ore ground-slag 10-13, wollastonite powder 5-7, tripoly phosphate sodium STPP 1-2, Dodecyl trimethyl ammonium chloride 2-3, Oil of Eucalyptus 1-2;
Above-mentioned laterite, iron ore ground-slag, wollastonite powder are mixed to calcining 3-4 hour under 600-800 ℃, cooling discharging, add Oil of Eucalyptus, mix, obtain Preblend, tripoly phosphate sodium STPP is joined in 15-20 times of water, add Dodecyl trimethyl ammonium chloride after stirring, the rising temperature is 60-80 ℃, with above-mentioned Preblend mixed grinding, dries, cross the 80-100 mesh sieve, obtain described compounded mix.
2. the preparation method of a vinylformic acid transparent powder paint as claimed in claim 1 is characterized in that comprising the following steps:
Above-mentioned N-phenyl-3-TSL 8330 is mixed with Fluorspar Powder, hydration zinc borate, be heated to 55-60 ℃, 400-600 rev/min of dispersed with stirring 2-3 minute, with each raw material of residue, mix, put into high-speed mixer and mix fully, then the gained compound is put into to mixing extrusion in high-speed extruder, then after the compressing tablet fragmentation, pulverize, sieve through pulverising mill again, obtain described vinylformic acid transparent powder paint.