CN103469193A - Formula of forming pickling passivation solution for surface oxide film of stainless steel casting - Google Patents
Formula of forming pickling passivation solution for surface oxide film of stainless steel casting Download PDFInfo
- Publication number
- CN103469193A CN103469193A CN2013103720705A CN201310372070A CN103469193A CN 103469193 A CN103469193 A CN 103469193A CN 2013103720705 A CN2013103720705 A CN 2013103720705A CN 201310372070 A CN201310372070 A CN 201310372070A CN 103469193 A CN103469193 A CN 103469193A
- Authority
- CN
- China
- Prior art keywords
- cast steel
- steel part
- acid
- stainless cast
- stainless steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a formula of forming pickling passivation solution for a surface oxide film of a stainless steel casting. The forming pickling passivation solution is prepared at a temperature of 40 to 46 DEG C from the following ingredients in part by weight (per litre): 40ml of nitric acid with concentration of 70 percent, 200ml of hydrochloric acid with concentration of 30 percent, 200ml of hydrofluoric acid with concentration of 30 percent and 200ml of water. The formula of the forming pickling passivation solution for the surface oxide film of the stainless steel casting, which is disclosed by the invention, has strong corrosion removal performance, enables a layer of compact oxide film to be formed on the surface of the stainless steel casting and improves corrosion resistance of the stainless steel casting.
Description
Technical field
The present invention relates to the stainless cast steel part field of surface treatment, specifically a kind of stainless cast steel part surface film oxide shaping acid wash passivation liquid formula.
Background technology
Under the condition of market economy, customer need is constantly to change and improve, concerning present valve industry,, the requirement of user to valve, the internal soundness that not only will have, the corrosion resistance on surface requires also very high, and the passive film of stainless steel surface is to its corrosion-resistant having a significant impact.Stainless cast steel part in use, in order to reduce and to delay rust corrosion speed, need to form a kind of fine and close oxide protective layer at cast(ing) surface, thereby reach the effect of protection.For guaranteeing the effect of Passivation Treatment, before passivation, first to being passivated surface, carry out cleanup acid treatment.Whole treating processes just is called acid wash passivation to be processed, and cylinder claims acid wash passivation.When general stainless valve foundry goods is heat-treated, all in oxidizing atmosphere, carry out, make the poor chromium of upper layer reduce its solidity to corrosion, so will carry out pickling, remove this poor chromium layer.The quality of precision castings pickling quality is relevant with the erosion resistance of alloying element, also depends in addition the corrosion removing ability of pickle solution to foundry goods oxide skin.Existing acid wash passivation liquid, it is general that performance is removed in its corrosion, can not get user's demand.
Summary of the invention
In order to solve the above-mentioned technical problem existed in prior art, the invention provides a kind of stainless cast steel part surface film oxide shaping acid wash passivation liquid formula, one-tenth assignment system (in every liter) by following parts by weight: 70% nitric acid of 400 milliliters, 30% hydrochloric acid of 200 milliliters, 30% hydrofluoric acid of 200 milliliters and the water of 200 milliliters, obtain in a temperature 40-46 ℃ preparation.
The present invention also provides a kind of stainless cast steel part surface film oxide forming technology, comprises the steps:
One. water cleans stainless cast steel part;
Two. with the described stainless cast steel part of above-mentioned acid wash passivation liquid cleanup acid treatment;
Three. water cleans described stainless cast steel part;
Four. with the described stainless cast steel part of above-mentioned acid wash passivation liquid acid Passivation Treatment;
Five. water cleans described stainless cast steel part.
It is strong that performance is removed in stainless cast steel part surface film oxide shaping acid wash passivation liquid formula corrosion of the present invention, makes the oxide film of stainless cast steel part surface formation one deck densification, improves the resistance to corrosion of stainless cast steel part.
Embodiment
Below the invention will be further described.
Stainless cast steel part surface film oxide shaping acid wash passivation liquid formula of the present invention, one-tenth assignment system (in every liter) by following parts by weight: 70% nitric acid of 400 milliliters, 30% hydrochloric acid of 200 milliliters, 30% hydrofluoric acid of 200 milliliters and the water of 200 milliliters, obtain in a temperature 40-46 ℃ preparation.
Stainless cast steel part surface film oxide forming technology flow process of the present invention is as follows:
Six. water cleans stainless cast steel part;
Seven. by above-mentioned acid wash passivation liquid cleanup acid treatment;
Eight. water cleans stainless cast steel part;
Nine. by above-mentioned acid wash passivation liquid Passivation Treatment;
Ten. water cleans stainless cast steel part.
The above is only the preferred embodiment of the present invention.It should be pointed out that for the person of ordinary skill of the art, under the prerequisite that does not break away from principle of the present invention, can also make some modification and improvement, these also should be considered as belonging to protection scope of the present invention.
Claims (2)
1. a stainless cast steel part surface film oxide shaping acid wash passivation liquid formula, one-tenth assignment system (in every liter) by following parts by weight: 70% nitric acid of 400 milliliters, 30% hydrochloric acid of 200 milliliters, 30% hydrofluoric acid of 200 milliliters and the water of 200 milliliters, obtain in a temperature 40-46 ℃ preparation.
2. a stainless cast steel part surface film oxide forming technology, comprise the steps:
One. water cleans stainless cast steel part;
Two. with the described stainless cast steel part of acid wash passivation liquid cleanup acid treatment claimed in claim 1;
Three. water cleans described stainless cast steel part;
Four. with the described stainless cast steel part of acid wash passivation liquid acid Passivation Treatment claimed in claim 1;
Five. water cleans described stainless cast steel part.