CN103468065A - Natural inorganic purple paint - Google Patents
Natural inorganic purple paint Download PDFInfo
- Publication number
- CN103468065A CN103468065A CN2013103948571A CN201310394857A CN103468065A CN 103468065 A CN103468065 A CN 103468065A CN 2013103948571 A CN2013103948571 A CN 2013103948571A CN 201310394857 A CN201310394857 A CN 201310394857A CN 103468065 A CN103468065 A CN 103468065A
- Authority
- CN
- China
- Prior art keywords
- parts
- natural inorganic
- paint
- peach gum
- gum powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention provides a natural inorganic purple paint. The paint is prepared by uniformly mixing and stirring the following components in parts by weight: 75-90 parts of peach gum powder water, 55-70 parts of white filler, 22.5-27.5 parts of barium sulfate, 2.5-5.5 parts of ultrafine aluminum silicate, 0.6-1.5 parts of permanent bordeaux F4R, and 0.6-0.9 part of light red lake. The natural inorganic purple paint selects natural raw materials, does not contain organic additives, is simple in manufacture process and stable in property, is applicable to surfaces of indoor parts, furniture and show-windows of buildings, and has an excellent coating effect and water endurance.
Description
Technical field
The present invention relates to a kind of coating composition, particularly a kind of natural inorganic paint composition with good coat effect and water tolerance.
Background technology
At present, the coating of selling on market has a plurality of kinds, and wherein great majority have all added organic additive, or formaldehyde and benzene exceeds standard, and environment and human body are produced to considerable influence.
Be added with the coating of organic additive, increased the performance of coating, make the correlated performances such as effect, water tolerance, weather resistance that whitewash of coating increase, also increased the cost of product simultaneously, complex manufacturing, and the part organic additive has certain influence to environment.
CN 1185465A relates to a kind of concentrated advertisement pigment.The technical scheme that this pigment adopts is, by red, potter's clay, barium sulfate, aluminium powder, peach factice water and formaldehyde by a certain percentage through enduring glue, mix and blend, gelatinization, the filling large red concentrated advertisement pigment that is made into.As can be seen here, this technical scheme not only operation is numerous and diverse, and has wherein added formaldehyde, irritant smell and larger to people's harm.
Summary of the invention
Goal of the invention: for above-mentioned deficiency, the purpose of this invention is to provide and a kind ofly both had fewer environmental impacts, possess again the natural inorganic paint of good coat effect and water tolerance.
Technical scheme: technical scheme of the present invention is: 75-90 part peach gum powder water, 55-70 part white filler, 22.5-27.5 part barium sulfate, 2.5-5.5 part superfine alumina silicate, 0.6-1.5 part permanent bordeaux F4R and the light red color lake of 0.6-0.9 part mixing and stirring are made to this coating.
As preferably, the weight percent of peach gum powder water peach gum powder is 10%-18%.
As preferably, white filler is one or more of extra white potter's clay, calcined kaolin, titanium dioxide.
As preferably, the mass ratio in permanent bordeaux F4R and light red color lake is 5:3-1:1.
Beneficial effect: comparatively simple by the technical solution of the present invention production technique, be not added with organic additive, the coating of making, nontoxic, environment and human body, without negative impact, but also are had to good water tolerance and coating result.
In addition, the invention provides painting color is a kind of natural purple.
Embodiment
In order further to understand the present invention, below in conjunction with embodiment, the preferred embodiment of the invention is described, but should be appreciated that these are described is for further illustrating the features and advantages of the present invention, rather than limiting to the claimed invention.
Embodiment 1
The 0.4kg peach gum powder is joined in the water of 2kg, the light red color lake that adds permanent bordeaux F4R and the 16g of 16g after stirring, continue to stir, add successively afterwards the calcined kaolin of 1.5kg, the barium sulfate of 0.6kg and the superfine alumina silicate of 0.067kg, mix and blend, after treating evenly to mix, this coating that can make.
Embodiment 2
The 0.4kg peach gum powder is joined in 2kg water, mix and blend, the light red color lake that adds permanent bordeaux F4R and the 18g of 48g after stirring, continue to stir, add successively afterwards the calcined kaolin of 2.2kg, the barium sulfate of 0.8kg and the superfine alumina silicate of 0.19kg, mix and blend, after treating evenly to mix, this coating that can make.
Embodiment 3
The 0.4kg peach gum powder is joined in the water of 2kg, the light red color lake that adds permanent bordeaux F4R and the 22g of 26g after stirring, continue to stir, the extra white potter's clay and the titanium dioxide of 0.9kg, the barium sulfate of 0.75kg and the superfine alumina silicate of 0.12kg that add successively afterwards 2.3kg, mix and blend, after treating evenly to mix, this coating that can make.
The coating of respectively above 3 embodiments being made is sampled, and carries out the mensuration of water-resistant coating test and color.
Tested according to national GB/T 1733-1993 paint film water tolerance assay method, adopt water immersion test method wherein, result is as shown in table 1:
Table 1 natural inorganic ink water tolerance is measured
| Test item | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Loss of gloss | No | No | No |
| Variable color | No | No | No |
| Wrinkling | No | No | No |
| Come off | No | No | No |
| Get rusty | No | No | No |
Above result demonstration, natural inorganic ink provided by the invention has good water tolerance.
According to GB/T 1722-1992 varnish, edible vegetable oil and thinner color measurenent method measurement result, show, the color of embodiment 1, embodiment 2 and embodiment 3 is purple.
To the above-mentioned explanation of the disclosed embodiments, make professional and technical personnel in the field can realize or use the present invention.Multiple modification to these embodiment will be apparent for those skilled in the art, and General Principle as defined herein can be in the situation that do not break away from the spirit or scope of the present invention, realization in other embodiments.Therefore, the present invention will can not be restricted to these embodiment shown in this article, but will meet the widest scope consistent with principle disclosed herein and features of novelty.
Claims (4)
1. a natural inorganic ink is characterized in that this coating consists of the following composition:
Peach gum powder water, 75-90 part;
White filler, 50-70 part;
Barium sulfate, 22.5-27.5 part;
Superfine alumina silicate, 2.5-5.5 part;
Permanent bordeaux F4R, 0.6-1.5 part;
Light red color lake, 0.6-0.9 part.
2. natural inorganic ink according to claim 1, the weight percent that it is characterized in that peach gum powder in peach gum powder water is 10%-18%.
3. natural inorganic ink according to claim 1, is characterized in that white filler is one or more of extra white potter's clay, calcined kaolin, titanium dioxide.
4. natural inorganic ink according to claim 1, is characterized in that both mass ratio in permanent bordeaux F4R and light red color lake is 5:3-1:1.