A kind of Disperse green dye composition
Technical field
The present invention relates to disperse dye composition preparation field, particularly relate to a kind of high fastness Disperse Green dye composition being applicable to terylene and spandex blended fabric dyeing.
Background technology
In recent years; every laws and regulations of environmental protection aspect have been put into effect in every country and area all in succession; China also determines the fundamental state policy economized on resources with protection of the environment; large to energy consumption; the dyeing and finishing industry that blowdown is large is had higher requirement; traditional high fastness dispersed dye are applied to pure dyeing terylene and must wash through reduction at least one times, and application terylene and spandex blended fabric at least need twice reduction to wash just can reach fastness requirement.
Common dispersion green is in the market mainly Disperse Green 9, or for Disperse Blue-60 and DISPERSE YELLOW blending form, this type of Conventional dye fastness on 100% ordinary polyester still can, but it is just completely not all right when ultra-fine fibre or terylene add spandex blended fabric, fastness is very poor, even if rely on repeatedly reduction to wash fastness also promote not quite that (the reduction mode of washing has two kinds of 1. alkali cleanings: take a policy powder and sheet alkali; 2. pickling: add acidic reduction detergent and acetic acid), can not meet the requirement of high-end order!
Summary of the invention
Technical problem to be solved by this invention is: provide a kind of dyeing behavior good, and at dacron ultrafine fiber and terylene spandex blended fabric, after dyeing, colour fastness can reach more than 4 grades, thus can meet the Disperse Green dye composition of high-end order requirements.
For solving the problems of the technologies described above, the technical solution used in the present invention: by mass fraction, it consists of: component A:28-31 part, B component: 43-47 part, component C:3-5 part, component D:18-25 part, component E:10-15 part;
Described component A is as the formula (1):
Described B component is as the formula (2):
Described component C is as the formula (3):
Described component D is as the formula (4):
Described component E is dispersion agent NNO.
Described dispersed deep blue dye composition, by mass fraction, it preferably consists of: component A:28 part, B component: 45 parts, component C:4 part, component D:20 part, component E:12 part.
Described dispersed deep blue dye composition, by mass fraction, it preferably consists of: component A:30 part, B component: 43 parts, component C:3 part, component D:20 part, component E:15 part.
Tool of the present invention has the following advantages and effect: Disperse Green dye composition provided by the invention, because its component selected is all high fastness product, so it is applied to super fine polyester and the dyeing of terylene spandex blended fabric, wash through reduction, colour fastness can reach more than 4 grades, and component is all environmentally friendly machine, not containing the banned substance contained in OEKO-TEXStandard100, high-end order requirements can be met.
Embodiment
Be described in further detail in conjunction with specific embodiments, make advantage of the present invention more obvious.Should be appreciated that, content wherein just with explaining, and is construed as limiting protection scope of the present invention absolutely not.The experimental technique of unreceipted actual conditions in the following example, usually conveniently condition, or carry out according to the condition that manufacturer advises.
Component A:28-31 part, B component: 43-47 part, component C:3-5 part, component D:18-25 part, component E:10-15 part;
Each component unit g.
Embodiment |
Component A |
B component |
Component C |
Component D |
Component E |
Embodiment 1 |
28 |
45 |
3 |
24 |
10 |
Embodiment 2 |
29 |
43 |
5 |
23 |
15 |
Embodiment 3 |
30 |
44 |
4 |
22 |
13 |
Embodiment 4 |
31 |
46 |
3 |
20 |
13 |
Embodiment 5 |
30 |
46 |
4 |
20 |
12 |
Embodiment 6 |
30 |
47 |
5 |
18 |
10 |
Embodiment 7 |
31 |
46 |
4 |
19 |
11 |
Embodiment 8 |
29 |
47 |
3 |
21 |
14 |
By above-mentioned quality proportioning, each component fully being ground stirs both obtains finished product; The dispersion green colouring material that above-mentioned enforcement is obtained carries out performance test, and testing method is as follows:
Get this finished product 0.5 gram, be scattered in 500 grams of cold water, mix with 32mL water get 8mL after fully stirring after, PH=4.0 is regulated with acetic acid, put into 2 grams of polyster fibres to dye, rise to 130 DEG C with the temperature rise rate of 3 DEG C/min, after insulation 30min, be cooled to 80 DEG C, cleaning sampling, obtain green dyeing and weaving thing, through reduction clearing, check its coloured light dynamics value, adopt GB/T3921-1997, GB/T5718-1997, GB/T8426-1998 method to carry out fastness test, test result is as shown in the table:
Embodiment title |
Color |
Washing fastness (60 DEG C) |
Sublimation fastness (180 DEG C) |
Light fastness |
Embodiment 1 |
Green |
4-5 level |
3-4 level |
4 grades |
Embodiment 2 |
Green |
4 grades |
3 grades |
4 grades |
Embodiment 3 |
Green |
4-5 level |
3-4 level |
4 grades |
Embodiment 4 |
Green |
4-5 level |
3-4 level |
3-4 level |
Embodiment 5 |
Green |
4-5 level |
3-4 level |
4 grades |
Embodiment 6 |
Green |
4 grades |
3 grades |
4 grades |
Embodiment 7 |
Green |
4-5 level |
3-4 level |
3-4 level |
Embodiment 8 |
Green |
4 grades |
3-4 level |
4 grades |
According to above-mentioned test result, consider the dye shade performance of different ratio, embodiment 5 is selected to be optimum proportioning: Disperse Green dye composition provided by the present invention, through reduction clearing on dacron ultrafine fiber, fastness performance is excellent, can reach more than 4 grades, and it is not containing the banned substance contained in OEKO-TEX Standard100, meets environmental requirement.