CN103467872A - Flame-retardant PS plastic - Google Patents
Flame-retardant PS plastic Download PDFInfo
- Publication number
- CN103467872A CN103467872A CN2013103712516A CN201310371251A CN103467872A CN 103467872 A CN103467872 A CN 103467872A CN 2013103712516 A CN2013103712516 A CN 2013103712516A CN 201310371251 A CN201310371251 A CN 201310371251A CN 103467872 A CN103467872 A CN 103467872A
- Authority
- CN
- China
- Prior art keywords
- parts
- mass parts
- plastic
- flame
- retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a flame-retardant PS plastic. The flame-retardant PS plastic comprises the following components in parts by weight: 120-135 parts of PS, 10 parts of zinc borate, 10-15 parts of nano silicon dioxide, 10-18 parts of azobisisobutyronitrile, 10-15 parts of melamine cyanurate, 10-15 parts of glass fiber, 10-12 parts of triethylene tetramine and 10-15 parts of ammonium polyphosphate. The flame-retardant PS plastic has a good flame-retardant function; an obvious flame-retardant function can be performed when a very small amount of flame-retardant PC plastic is used. The anti-bacterial PS plastic does not decompose or react with other materials during the processing of high-temperature fusing forming and thermal forming. The anti-bacterial PP plastic can be dispersed in a plastic product easily and uniformly, and is high in weatherability and durability, so that the plastic product has a long-term antibacterial property.
Description
Technical field
The invention belongs to polymeric material field, be specifically related to a kind of PS flame retardant plastics.
Technical background
Along with science and technology and economic development, by the daily living article of plastics-production, play in daily life more and more important effect.But the plastics easy firing, and combustionvelocity is fast, can produce a large amount of toxic gases according to statistics, according to statistics, in fire, because of the loss of life and personal injury of suffocating and smoke poisoning causes, accounts for 50~80% of the total casualties of fire.Along with the widespread use of plastics at aspects such as building, furniture, traffic, Aeronautics and Astronautics, electrical equipment, the fire caused due to plastic products also innumerable simultaneously, fire hazard situation allows of no optimist, some fire disaster accidents occur again and again, and be all much that the inflammable materials such as nylon wire, polyurethane foam burn rapidly, shine into the loss of people's casualties and property.Most plastics are all inflammable substances, but all need plastics not burn in the material of construction of plastics, communications and transportation material, home electric appliance material etc., and good flame retardant properties is arranged, and require the degree of being fuming of plastics in big fire little.For this reason, in plastic formula, select to add fire retardant and just become extremely important.Fire retardant is used in the U.S. at first, and after the sixties in 20th century, consumption increases severely, and consumption is only second to softening agent at present.Consuming the maximum plastics variety of fire retardant is polyvinyl chloride, polystyrene, urethane foam, unsaturated polyester, ABS resin and polypropylene.In people's life, at present now a lot of formula of flame-retardant plastics when the material pyrolysis, produce toxic gas cause fire in poison gas and flue gas to the human body side effect that suffocates, grievous injury people's physical and mental health, environmental-protecting performance is very undesirable.In recent years, the higher requirement of the fast development of electronic apparatus, building, aviation and automobile industry to the performance proposition of plastics.Wherein, the plastics of flame retardant type are nonflammable, and rate of flame propagation is little, and mass loss rate and heat release rate are lower, and have certain self-extinguishing.But the flame retardant plastics performance of using at present can not meet the demands, and adopts halogen flame more, combustion processes can be emitted hydrogen halide human body is caused to serious harm.So the selection of fire retardant in plastics, be a very complicated process, must consider above-mentioned every factor.In existing textbook, provided such as: protective membrane mechanism, not so mechanism such as gas mechanism, coolant mechanism and terminating chain lock reactor mechanism; these can select to provide a fuzzy direction to fire retardant, but but can't provide real, effectively help.
Summary of the invention
For above shortcomings in prior art, the object of the invention is to provide a kind of PS flame retardant plastics.
The objective of the invention is to be achieved through the following technical solutions: a kind of PS flame retardant plastics is comprised of the following weight parts component: 120-135 mass parts PS, 10 mass parts zinc borates, 10-15 mass parts nano silicon, 10-18 mass parts azo-bis-isobutyl cyanide, 10-15 mass parts melamine cyanurate, 10-15 mass parts glass fibre, 10-12 mass parts triethylene tetramine, 10-15 mass parts ammonium polyphosphate.
The beneficial effect that the present invention has: the PS flame retardant plastics that the present invention makes has good anti-flaming function, and consumption seldom just can obviously play fire retardation; In high-temperature fusion moulding and thermoforming process engineering, do not decompose, with other materials, do not react yet; In plastics, be easy to be uniformly dispersed, good weatherability, persistence is good, makes plastics have long-term flame retardant resistance.
Embodiment
Example of the present invention is can not limit the present invention to explanation of the present invention, in the implication suitable with the present invention and any change and the adjustment in scope, all should think within the scope of the invention.
embodiment 1
The preparation of PS flame retardant plastics: 120-135 mass parts PS, 10 mass parts zinc borates, 10-15 mass parts nano silicon, 10-18 mass parts azo-bis-isobutyl cyanide, 10-15 mass parts melamine cyanurate, 10-15 mass parts glass fibre, 10-12 mass parts triethylene tetramine, 10-15 mass parts ammonium polyphosphate are mixed and put into stirrer, put into the Banbury mixer banburying after stirring, the internally mix temperature is that 180-185 ℃, rotating speed are 1100-1200rpm; Then by the mixture after banburying through granulator granulation, obtain particle, particle is put into to tank cooling, then dry at normal temperatures; The salient features of the material that the present embodiment is prepared is as follows: tensile strength MPa(GB/T1040-2006): 39, and elongation at break %(GB/T 1040-2006): 8-11; Shock strength kJ/m
2(GB/T1043-2008): 3.0; Flexural strength MPa(GB/T9341-2000): 42; Oxygen index % (GB/T2406-1993): 36; Vertical combustion rank UL-94: V0.Thermotolerance and the flame retardant resistance of flame retardant plastics of the present invention are more excellent, and preparation technology is simple, and product cost is low, and the over-all properties of product is more excellent.
Claims (1)
1. a PS flame retardant plastics, is characterized in that being comprised of the following weight parts component: 120-135 mass parts PS, 10 mass parts zinc borates, 10-15 mass parts nano silicon, 10-18 mass parts azo-bis-isobutyl cyanide, 10-13 mass parts ferrocene, 5-8 part vinylbenzene, 6-9 part vinyl cyanide, 10-14 part benzene sulfonamide acid esters, 10-15 mass parts melamine cyanurate, 10-15 mass parts glass fibre, 10-12 mass parts triethylene tetramine, 10-15 mass parts ammonium polyphosphate.