CN103456386A - Efficient ion resistance reducing agent and preparing method thereof - Google Patents
Efficient ion resistance reducing agent and preparing method thereof Download PDFInfo
- Publication number
- CN103456386A CN103456386A CN2013103801149A CN201310380114A CN103456386A CN 103456386 A CN103456386 A CN 103456386A CN 2013103801149 A CN2013103801149 A CN 2013103801149A CN 201310380114 A CN201310380114 A CN 201310380114A CN 103456386 A CN103456386 A CN 103456386A
- Authority
- CN
- China
- Prior art keywords
- reducing agent
- resistance reducing
- water
- strong
- absorbing resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an efficient ion resistance reducing agent and a preparing method thereof. The efficient ion resistance reducing agent is formed by the following components of 50-85 parts of strong electrolyte conducting salt, 15-49 parts of additives, 1 part-10 parts of strong water absorbent resin and 400-650 parts of water. The conducting salt raw material and all additives are mixed, then water is added to enable the conducting salt raw material and the additives to be dissolved, the strong water absorbent resin is slowly added when the conducting salt raw material and the additives are stirred, and the prepared resistance reducing agent is poured or pressed around a ground electrode. The efficient ion resistance reducing agent has the advantages of being quick in resistance reducing, high in efficiency, safe, free of pollution, wide in application range, convenient to use, small in harm to operators and the like.
Description
Technical field
The invention belongs to resistance reducing agent and preparing technical field thereof, be specifically related to the Ionic conductivity material of the non-rock type soil property of a kind of fast reducing resistivity.
Research background
Resistance reducing agent is a kind of composite material that rapidly and efficiently reduces non-rock type soil property resistivity function that has; it can rapid osmotic, around the diffusion earth electrode; thereby effectively increase the contact area of earth electrode and soil; reduce contact resistance between grounding electrode and soil, reduce the drift resistance of soil; be widely used in quick, the short-term ground protection of the facilities such as electric power system, communication, be specially adapted to move the high area of soil resistivity frequent, that need the fast reducing soil resistivity.Current earthing device mainly contains two kinds of horizontal and vertical earth electrodes, and the main using method of powdered form physical resistance reducing agent is to repave the mode of burying on every side after earthing device is digged pit or dug moat, although its fall the resistance long-lasting good, but this mode quantities is large, onset is slow, reaching stable state needs several months or half a year, is difficult to meet convenient, operating characteristic fast, can't be applicable to frequently change in the ground connection facility in place.Therefore, need the new resistance reducing agent of exploitation to adapt to the use needs rapid-action, that efficiency is high.
Summary of the invention
The purpose of this invention is to provide a kind of high-effect ionic type resistance reducing agent, it falls, and resistance is fast, efficiency is high, safe, pollution-free, applied widely, production, transportation and easy to use, the operator is injured little.
High-effect ionic resistance reducing agent of the present invention and preparation method thereof is characterized in that: following component, consist of:
Strong electrolyte conducting salt: 50-85 part;
Additive: 15-49 part;
Strong water-absorbing resin 1-10 part;
Water: 400 parts～650 parts;
Wherein: the mixture that additive is sodium sulphate, magnesium sulfate and ammonium chloride three.
Further optimize the strong electrolyte conducting salt: 70-85 part, additive: 10-28.5 part,
Strong water-absorbing resin: 1.5-4.5 part, water is 500～600 parts.
Additive is sodium sulphate, magnesium sulfate or ammonium chloride, and wherein sodium sulphate and magnesium sulfate are mainly the affinity interactions of reinforcement and soil, and ammonium chloride is used for regulating the Acidity of Aikalinity of resistance reducing agent.
Strong water-absorbing resin adopts the cast-type perfusion.
The ratio of the strong water-absorbing resin of cast-type is 1.5-10.
After getting in proportion various raw materials ready, after conducting salt raw material and various additive are mixed, after adding moisture content to dissolve, then add while stirring strong water-absorbing resin, wherein strong water-absorbing resin need slowly add, and then the resistance reducing agent cast or the pressure injection that prepare is got final product around earth electrode.
Resistance reducing agent in the present invention has following advantage:
1, preparation is simple, cost is low, convenient transport, easy to use, and it is with after suitable quantity of water is mixed, pours into a mould or pressure injection gets final product on every side at earth electrode; Need not carry out a large amount of constructions, if resistance reducing effect changes, only need continuation cast or pressure injection to get final product, easy to adjust;
2, resistance reducing effect is good, reaches that to stablize the required time short; Resistance-reducing efficiency reaches as high as 50%～84.63%, and after adding resistance reducing agent, 30 minutes can obviously take effect, and within 2～4 hours, resistance reducing effect reaches stable.
3, environmental pollution is little, operating personnel is injured little.
Embodiment
Embodiment 1
Sodium chloride, sodium sulphate, magnesium chloride, ammonium chloride are prepared by 80kg, 13.5kg, 4kg, 4kg, prepare eager to do well in everything water-absorbing resin 1.5kg simultaneously.
Using method: front four kinds of mixed materials are dissolved in 400kg water, then slowly add while stirring strong water-absorbing resin to get final product.
Embodiment 2
Sodium chloride, sodium sulphate, magnesium chloride, ammonium chloride are prepared by 80kg, 6kg, 5kg, 5kg, prepare eager to do well in everything water-absorbing resin 4kg simultaneously.
Using method: front four kinds of mixed materials are dissolved in 500kg water, then slowly add while stirring strong water-absorbing resin to get final product.
Embodiment 3
Potassium chloride, sodium sulphate, magnesium chloride, ammonium chloride are prepared by 75kg, 12kg, 9.5kg, 2kg, be ready to the strong water-absorbing resin 10kg of cast-type simultaneously.
Using method: front four kinds of mixed materials are dissolved in 600kg water, then slowly add while stirring the strong water-absorbing resin of cast-type to get final product.
Claims (6)
1. a high-effect ionic resistance reducing agent is characterized in that: following component, consist of:
Strong electrolyte conducting salt: 50-85 part;
Additive: 15-49 part;
Strong water-absorbing resin 1-10 part;
Water: 400～650 parts;
Wherein: the mixture that additive is sodium sulphate, magnesium sulfate and ammonium chloride three.
2. a kind of high-effect ionic resistance reducing agent according to claim 1 is characterized in that: the strong electrolyte conducting salt: 70-85 part, additive: 10-28.5 part, strong water-absorbing resin: 1.5-4.5 part, water is 500～600 parts.
3. a kind of high-effect ionic resistance reducing agent according to claim 1 and 2, it is characterized in that: the strong electrolyte conducting salt is sodium chloride or potassium chloride.
4. a kind of high-effect ionic resistance reducing agent according to claim 1, is characterized in that: the perfusion of strong water-absorbing resin employing cast-type.
5. a kind of high-effect ionic resistance reducing agent according to claim 5, it is characterized in that: the ratio of the strong water-absorbing resin of cast-type is 1.5-10.
6. the preparation method of a kind of high-effect ionic resistance reducing agent according to claim 1, it is characterized in that: after getting in proportion various raw materials ready, after strong electrolyte conducting salt and additive are mixed, after adding moisture content to dissolve, add while stirring stronger water-absorbing resin, wherein strong water-absorbing resin need slowly add, and then the resistance reducing agent cast or the pressure injection that prepare is got final product around earth electrode.