CN103451529B - A kind of Aluminum-titanium-iralloy alloy material - Google Patents
A kind of Aluminum-titanium-iralloy alloy material Download PDFInfo
- Publication number
- CN103451529B CN103451529B CN201310370948.1A CN201310370948A CN103451529B CN 103451529 B CN103451529 B CN 103451529B CN 201310370948 A CN201310370948 A CN 201310370948A CN 103451529 B CN103451529 B CN 103451529B
- Authority
- CN
- China
- Prior art keywords
- aluminum
- iralloy
- titanium
- alloy material
- chain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a kind of Aluminum-titanium-iralloy alloy material, Aluminum-titanium-iralloy alloy material is made up of according to weight ratio following composition: Zn is 0.3wt% ~ 0.6wt%, Al be 2.4wt% ~ 2.5wt%, Ti be 1.7wt% ~ 1.9wt%, Si be 0.3wt% ~ 0.4wt%, Ca is 1.1wt% ~ 1.3wt%, surplus is Fe.The Aluminum-titanium-iralloy alloy material prepared has very high tensile strength.
Description
Technical field
The present invention relates to a kind of alloy material, particularly relate to a kind of Aluminum-titanium-iralloy alloy material.
Background technology
The range of application of steel is boundless, is seen everywhere in the middle of industrial production and life.In the middle of industrial production, especially in the application process of pumping unit chain, there is higher requirement to the quality of pumping unit chain, if the tensile strength of chain is lower, the use duration of chain can be constrained greatly, and then also can reduce the performance of steel.If a kind of chain that can strengthen tensile strength can be developed, then can the performance of lifting chain greatly, expand the professional skill field of its application.
Summary of the invention
The technical problem solved: the problem of chain alloy material tensile strength difference.
Technical scheme: the invention discloses a kind of Aluminum-titanium-iralloy alloy material, steel is made up of according to weight ratio following composition: Zn to be 0.3 wt% ~ 0.6wt%, Al be 2.4 wt% ~ 2.5wt%, Ti be 1.7 wt% ~ 1.9wt%, Si be 0.3 wt% ~ 0.4wt%, Ca is 1.1 wt% ~ 1.3wt%, surplus is Fe.Method prepared by Aluminum-titanium-iralloy alloy material is as follows: get required each chemical composition, drop in vacuum induction furnace according to above-mentioned mass ratio, carry out vacuum metling, Heating temperature to 1100 ~ 1200 DEG C, aluminum ferrotitanium plate is rolled into after heating, heat-treat again, Heating temperature is slowly reduced to room temperature, prepare chain Aluminum-titanium-iralloy alloy material.
Beneficial effect: the chain Aluminum-titanium-iralloy alloy material prepared has good tensile strength.Tensile strength bioassay standard is GB/T 228.1-2010, and the tensile strength of Aluminum-titanium-iralloy alloy material is 1850 ~ 1900Mpa.The Aluminum-titanium-iralloy alloy material prepared can be widely used in the middle of chain production process.
Embodiment
Embodiment 1
Get required each chemical composition, Zn to be 0.3wt%, Al be 2.4wt%, Ti be 1.9wt%, Si be 0.4wt%, Ca is 1.3wt%, surplus is Fe.Drop in vacuum induction furnace according to above-mentioned mass ratio, carry out vacuum metling, Heating temperature to 1100 DEG C, be rolled into aluminum ferrotitanium plate after heating, then heat-treat, Heating temperature is slowly reduced to room temperature, prepare chain Aluminum-titanium-iralloy alloy material.
Embodiment 2
Get required each chemical composition, Zn to be 0.4wt%, Al be 2.5wt%, Ti be 1.8wt%, Si be 0.3wt%, Ca is 1.2wt%, surplus is Fe.Drop in vacuum induction furnace according to above-mentioned mass ratio, carry out vacuum metling, Heating temperature to 1200 DEG C, be rolled into aluminum ferrotitanium plate after heating, then heat-treat, Heating temperature is slowly reduced to room temperature, prepare chain Aluminum-titanium-iralloy alloy material.
Embodiment 3
Get required each chemical composition, Zn to be 0.6wt%, Al be 2.4wt%, Ti be 1.7wt%, Si be 0.4wt%, Ca is 1.1wt%, surplus is Fe.Drop in vacuum induction furnace according to above-mentioned mass ratio, carry out vacuum metling, Heating temperature to 1100 DEG C, be rolled into aluminum ferrotitanium plate after heating, then heat-treat, Heating temperature is slowly reduced to room temperature, prepare chain Aluminum-titanium-iralloy alloy material.
Carried out Product checking to the chain Aluminum-titanium-iralloy alloy material that embodiment 1, embodiment 2, embodiment 3 prepare, determined tensile strength, tensile strength bioassay standard is GB/T 228.1-2010.The product tensile strength of embodiment 1, embodiment 2, embodiment 3 is respectively 1850Mpa, 1900Mpa, 1880Mpa.Measurement result shows, the said products has all possessed good tensile strength.Can be widely used in the middle of chain preparation.
Claims (5)
1. an Aluminum-titanium-iralloy alloy material, is characterized in that Aluminum-titanium-iralloy alloy material consists of the following composition: Zn to be 0.3 wt% ~ 0.6wt%, Al be 2.4 wt% ~ 2.5wt%, Ti be 1.7 wt% ~ 1.9wt%, Si be 0.3 wt% ~ 0.4wt%, Ca is 1.1 wt% ~ 1.3wt%, surplus is Fe.
2. a kind of Aluminum-titanium-iralloy alloy material according to claim 1, is characterized in that in Aluminum-titanium-iralloy alloy material composition, Zn is 0.3wt%.
3. a kind of Aluminum-titanium-iralloy alloy material according to claim 1, is characterized in that in Aluminum-titanium-iralloy alloy material composition, Al is 2.5wt%.
4. a kind of Aluminum-titanium-iralloy alloy material according to claim 1, is characterized in that in Aluminum-titanium-iralloy alloy material composition, Ti is 1.9wt%.
5. a kind of Aluminum-titanium-iralloy alloy material according to claim 1, is characterized in that in Aluminum-titanium-iralloy alloy material composition, Ca is 1.1wt%.