CN103449800A - 一种高强度陶瓷用电石渣复配氧化铁红 - Google Patents
一种高强度陶瓷用电石渣复配氧化铁红 Download PDFInfo
- Publication number
- CN103449800A CN103449800A CN2013103612857A CN201310361285A CN103449800A CN 103449800 A CN103449800 A CN 103449800A CN 2013103612857 A CN2013103612857 A CN 2013103612857A CN 201310361285 A CN201310361285 A CN 201310361285A CN 103449800 A CN103449800 A CN 103449800A
- Authority
- CN
- China
- Prior art keywords
- carbide slag
- iron oxide
- slag
- carbide
- red iron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种高强度陶瓷用电石渣复配氧化铁红，其是由下述重量份的原料制得：改性电石渣10-20，纳米碳1-2，氧化铁红100-110，硅烷偶联剂KH530 1-2，羊毛脂0.2-0.4。
Description
技术领域
本发明涉及氧化铁红领域，确切地说是一种高强度陶瓷用电石渣复配氧化铁红。
背景技术
氧化铁红（Iron Oxide Red）又称铁氧红、铁丹、锈红，有天然的和人造的两种。天然的称西红，是基本上纯粹的氧化铁，为红色粉末。由于生产方法和操作条件的不同，它们的晶体结构和物理性状都有很大的差别，色泽变动于橙光到蓝光至紫光之间。遮盖力和着色力都很大。密度5-5.25。有优越的耐光、耐高温性能，并耐大气影响、耐污浊气体、耐一切碱类。只有在浓酸中加热的情况下才会逐渐溶解。
发明内容
本发明的目的在于提供一种高强度陶瓷用电石渣复配氧化铁红
上述目的通过以下方案实现：
一种高强度陶瓷用电石渣复配氧化铁红，其特征在于：其是由下述重量份的原料制得：改性电石渣10-20，纳米碳1-2，氧化铁红100-110，硅烷偶联剂KH530 1-2，羊毛脂0.2-0.4；
所述的改性电石渣由下述重量份的原料制得：电石渣100-110，氧化锌0.3-0.5,衣康酸酯0.1-0.2、氯化石蜡0.3-0.5，聚磷酸铵0.1-0.2。
所述的一种高强度陶瓷用电石渣复配氧化铁红，其特征在于：制备方法为：
（1）将氧化锌、衣康酸酯、氯化石蜡按重量份混匀，再加入适量去离子水，于30-40℃下搅拌10-20分钟，再按重量份加入聚磷酸铵，于100-200转/分下搅拌10-20分钟，得改性液备用；
（2）将电石渣于浓度为8-10%的盐酸溶液中浸泡5-8小时后，取出，去离子水洗涤，烘干，再研磨，过100-200目筛，得电石渣粉备用；
（3）将电石渣粉与改性液混匀后，高速剪切10-20分钟后，取出，60-70℃下烘干，所得粉末与其余原料混匀后，再加适量水，于30-40℃下搅拌反应5-12分钟后，即得。
本发明的有益效果为：本发明应用于陶瓷中，强度高，改性电石渣节约资源，变废为宝，制得陶瓷强度高。耐用。
具体实施方式
一种高强度陶瓷用电石渣复配氧化铁红，其是由下述重量份（kg)的原料制得：改性电石渣10，纳米碳2，氧化铁红110，硅烷偶联剂KH530 2，羊毛脂0.4；
所述的改性电石渣由下述重量份的原料制得：电石渣110，氧化锌0.5,衣康酸酯0.2、氯化石蜡0.5，聚磷酸铵0.2。
所述的一种高强度陶瓷用电石渣复配氧化铁红，制备方法为：
（1）将氧化锌、衣康酸酯、氯化石蜡按重量份混匀，再加入适量去离子水，于35℃下搅拌20分钟，再按重量份加入聚磷酸铵，于200转/分下搅拌20分钟，得改性液备用；
（2）将电石渣于浓度为10%的盐酸溶液中浸泡8小时后，取出，去离子水洗涤，烘干，再研磨，过200目筛，得电石渣粉备用；
（3）将电石渣粉与改性液混匀后，高速剪切20分钟后，取出，70℃下烘干，所得粉末与其余原料混匀后，再加适量水，于40℃下搅拌反应12分钟后，即得。
实施例生产出来的氧化铁红产品性能分析数据如下表：
| 项目 | 指标 | 检测结果 |
| 105℃挥发物（%） | ≤1.0 | 0.72 |
| 吸油量（%） | 15-25 | 22.9 |
| 着色强度（%） | 95-105 | 98.2 |
| 耐200℃/30min （△E） | ≤1.0 | 0.78 |
Claims (2)
1.一种高强度陶瓷用电石渣复配氧化铁红，其特征在于：其是由下述重量份的原料制得：改性电石渣10-20，纳米碳1-2，氧化铁红100-110，硅烷偶联剂KH530 1-2，羊毛脂0.2-0.4；
所述的改性电石渣由下述重量份的原料制得：电石渣100-110，氧化锌0.3-0.5,衣康酸酯0.1-0.2、氯化石蜡0.3-0.5，聚磷酸铵0.1-0.2。
2.根据权利要求1所述的一种高强度陶瓷用电石渣复配氧化铁红，其特征在于：制备方法为：
（1）将氧化锌、衣康酸酯、氯化石蜡按重量份混匀，再加入适量去离子水，于30-40℃下搅拌10-20分钟，再按重量份加入聚磷酸铵，于100-200转/分下搅拌10-20分钟，得改性液备用；
（2）将电石渣于浓度为8-10%的盐酸溶液中浸泡5-8小时后，取出，去离子水洗涤，烘干，再研磨，过100-200目筛，得电石渣粉备用；
（3）将电石渣粉与改性液混匀后，高速剪切10-20分钟后，取出，60-70℃下烘干，所得粉末与其余原料混匀后，再加适量水，于30-40℃下搅拌反应5-12分钟后，即得。