CN103436223A - Alumina zirconia grinding material and processing method thereof - Google Patents
Alumina zirconia grinding material and processing method thereof Download PDFInfo
- Publication number
- CN103436223A CN103436223A CN2013103686935A CN201310368693A CN103436223A CN 103436223 A CN103436223 A CN 103436223A CN 2013103686935 A CN2013103686935 A CN 2013103686935A CN 201310368693 A CN201310368693 A CN 201310368693A CN 103436223 A CN103436223 A CN 103436223A
- Authority
- CN
- China
- Prior art keywords
- alumina zirconia
- grinding material
- abrasive material
- processing method
- zircon corundum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an alumina zirconia grinding material and a processing method thereof. The processing method comprises the following steps: mixing 95-96% of 3200-6000-mesh nano fine-grain alumina zirconia micropowder with 3-4% of adhesive and 1-2% of plasticizer to obtain sludge, carrying out extrusion molding, drying for 22-26 hours, and sintering at 1200-1600 DEG C for 4-6 hours to obtain the finished product. The high-quality nano alumina zirconia micropowder used as the main raw material are mixed with right amounts of adhesive and plasticizer, and the mixture is subjected to extrusion molding and sintered at a certain temperature to implement secondary combination of the grinding material molecules, thereby obtaining a pencil-core-type special alumina zirconia grinding material TZA. The grinding material has the advantages of high strength, high toughness, favorable grinding efficiency, long service life of the grinding wheel, and high economic benefit.
Description
Technical field
The present invention relates to a kind of high-abrasive material, specifically a kind of zircon corundum abrasive material and working method.
Background technology
Existing zircon corundum abrasive material intensity, toughness are higher, are specially adapted to heavy load grinding, corase grind, snagging stainless steel, and grinding, the polishing of the high rigidity products such as special steel, pottery, silicon chip; But its intensity and toughness have much room for improvement, so emery wheel is not long work-ing life.
Summary of the invention
The present invention is in order to improve zircon corundum abrasive material intensity and toughness, and the spy proposes a kind of zircon corundum abrasive material and working method.
Technical scheme of the present invention is for this reason, and a kind of zircon corundum abrasive material is characterized in that: the formula in described abrasive material is zircon corundum micro mist 95 ~ 96%, binding agent 3 ~ 4%, fluidizer 1 ~ 2%.
Improvement to such scheme is: the zircon corundum micro mist is used the nano level fine granularity of 3200-6000 order.
The working method of zircon corundum abrasive material is: above-mentioned formula is mixed into to the pug extrusion moulding, and after dry 22-26 hour, sintering 4-6 hour both finished product at the temperature of 1200-1600 ℃.
beneficial effect:
It is main raw material that high-quality nano level zircon corundum micro mist is take in the present invention, add appropriate binding agent, fluidizer, mix and extrusion moulding, by the certain temperature sintering, thereby the secondary bond of realizing the abrasive material scintilla obtains a kind of pencil core pattern, special zircon corundum abrasive material is TZA, and this abrasive material intensity is large, toughness is high, and grinding efficiency is good, the emery wheel long service life, economic benefit is high.The emery wheel that uses TZA to manufacture and Large Diameter Slicing sheet are by use test, and its grinding efficiency is two times of common zircon corundum abrasive material, extends 80% left and right work-ing life.
Embodiment
In the present invention, use nano level 95 ~ 96% nano level fine granularity zircon corundum micro mists of 3200-6000 order and 3 ~ 4% binding agents, 1 ~ 2% fluidizer to be mixed into the pug extrusion moulding, after dry 22-26 hour, sintering 4-6 hour both finished product at the temperature of 1200-1600 ℃.
The high-quality nano level zircon corundum micro mist of take is main raw material, add appropriate binding agent, fluidizer, mix and extrusion moulding, by the certain temperature sintering, thereby the secondary bond of realizing the abrasive material scintilla obtains a kind of pencil core pattern, special zircon corundum abrasive material is TZA, and this abrasive material intensity is large, toughness is high, and grinding efficiency is good, the emery wheel long service life, economic benefit is high.The emery wheel that uses TZA to manufacture and Large Diameter Slicing sheet are by use test, and its grinding efficiency is two times of common zircon corundum abrasive material, extends 80% left and right work-ing life.
Claims (3)
1. a zircon corundum abrasive material, it is characterized in that: the formula in described abrasive material is zircon corundum micro mist 95 ~ 96%, binding agent 3 ~ 4%, fluidizer 1 ~ 2%.
2. zircon corundum abrasive material according to claim 1, is characterized in that: the nano level fine granularity of zircon corundum micro mist use 3200-6000 order.
3. the working method of zircon corundum abrasive material is characterized in that: above-mentioned formula is mixed into to the pug extrusion moulding, and after dry 22-26 hour, sintering 4-6 hour both finished product at the temperature of 1200-1600 ℃.