CN103433991B - A kind of production method of composite floor for heating - Google Patents

A kind of production method of composite floor for heating Download PDF

Info

Publication number
CN103433991B
CN103433991B CN201310375402.5A CN201310375402A CN103433991B CN 103433991 B CN103433991 B CN 103433991B CN 201310375402 A CN201310375402 A CN 201310375402A CN 103433991 B CN103433991 B CN 103433991B
Authority
CN
China
Prior art keywords
heating
floor
production method
juggle
composite floor
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310375402.5A
Other languages
Chinese (zh)
Other versions
CN103433991A (en
Inventor
张勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHEJIANG FUMA FLOOR HEATING TECHNOLOGY Co Ltd
Original Assignee
ZHEJIANG FUMA FLOOR HEATING TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG FUMA FLOOR HEATING TECHNOLOGY Co Ltd filed Critical ZHEJIANG FUMA FLOOR HEATING TECHNOLOGY Co Ltd
Priority to CN201310375402.5A priority Critical patent/CN103433991B/en
Publication of CN103433991A publication Critical patent/CN103433991A/en
Application granted granted Critical
Publication of CN103433991B publication Critical patent/CN103433991B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of production method of composite floor for heating, the method comprises the steps: a, log is blocked into juggle, and juggle becomes veneer by rotary-cut or slicing; B, several veneers are made blank substrate, blank substrate overlays the panel through boiling process, obtain A plate; C, sawing after the cutting edge of A plate is become desirably board size, fluting japanning obtains finished product.The present invention can enhance productivity and the stability on floor, not yielding and cracking.

Description

A kind of production method of composite floor for heating
Technical field
The present invention relates to a kind of production method of heating floor, the production method of the wood composite floor heating floorboard of particularly a kind of stable performance.
Background technology
Heating floor is a kind of by being embedded in underfloor thermal source, floor heating to surface temperature 30-40 degree Celsius, reaches the floor of heating effect equably to indoor radiations heat energy.This floor adopts low-temp radiation heating device, and surface temperature is high, meets air flowing law.Because head temperature is low, temperature spreads all over whole body from underfooting, gives pin and warms up a cool comfort.Therefore heating floor also meets the theory " warm sufficient Liang Ding " of the traditional Chinese medical science.And compared with traditional heating system, geothermal heating system eliminates caliduct in room and radiator, be easier to the layout in room and attractive in appearance, more science and save the energy, its service life, maintenance maintenance expense are all lower than traditional heating mode, economical and practical.Therefore this heating system is admitted and is accepted by increasing people.
The thermal source be embedded in below floor is generally the water pipe being connected with hot water, in recent years, and the heating floor that also to have occurred with heating cable or Electric radiant Heating Film be thermal source.But the construction cost of these traditional underground heat is high, difficulty of construction is large.Due to the particularity of geothermal heating, heating floor must possess the requirement that heat-conductive characteristic is good, thermal stability is good, good environmental protection, anti-deformation are good.Wherein, solid wooden compound floor is through high-temperature process, and interior moisture content less (generally at 9-11%), so can not produce distortion because of scattering and disappearing of moisture, is the first-selection of heating floor.But due to the difference of technique, there is product stability difference in composite floor for heating commercially available at present, mutability and the surface problem such as easy to crack.
Summary of the invention
The object of the invention is to, a kind of production method of composite floor for heating is provided.The present invention can enhance productivity and the stability on floor, not yielding and cracking.
Technical scheme of the present invention: a kind of production method of composite floor for heating, is characterized in that, the method comprises the steps:
A, log is blocked into juggle, juggle becomes veneer by rotary-cut or slicing;
B, several veneers are made blank substrate, blank substrate overlays the panel through boiling process, obtain A plate;
C, sawing after the cutting edge of A plate is become desirably board size, fluting japanning obtains finished product.
In the production method of aforesaid composite floor for heating, described temperature when overlaying controls at 110-130 DEG C.
In the production method of aforesaid composite floor for heating, the boiling processing procedure of described panel is: be slowly warmed up to 60-80 DEG C from normal temperature, keeps 6-8 days.
In the production method of aforesaid composite floor for heating, the time of described slow intensification is 24 hours.
In the production method of aforesaid composite floor for heating, the described boiling retention time is 7 days.
In the production method of aforesaid composite floor for heating, the moisture control of described veneer is being 6%-8%.
In the production method of aforesaid composite floor for heating, the moisture control of described veneer is being 6%.
Compared with prior art, the present invention directly overlays whole panel on blank substrate, and then cutting edge, sawing become blank floor, substantially increase production efficiency; The mode counter plate slowly heated up by 24 hours carries out boiling process, also keep the high cooking of about 7 days, panel is made to be in solution Warm status for a long time, panel timber there occurs complicated chemical change in the boiling processing procedure of this pure physics, greatly reduce the quantity of free hydroxyl group in timber, reduce the water imbibition of timber, make timber hydrophobization, degree of crystallinity is also made to improve, improve the stability of heating floor, make to suppress mushroom amount reproduction in wood simultaneously, improve corrosion resistance and the wearability of heating floor.The combination of the blank substrate made at the veneer of 6%-8% by the panel of this boiling process and moisture control, greatly can improve the stability of size, the dry environment on ground can be born for a long time and not easily produce distortion and cracking, reducing the repair rate on floor, economical and practical.
The present invention also has the following advantages:
1, entirety is not yielding, good stability, wooden feel are strong;
2, floor surface hardness is large, and wearability is good;
3, only counter plate carries out boiling process, and production cost is lower, and cost performance is high;
4, whole panel carries out overlaying specification needed for rear sawing, and planarization is good, and production efficiency is high.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is further illustrated, but not as the foundation limited the present invention.
Embodiment.A production method for composite floor for heating, the method comprises the steps:
A, log is blocked into juggle, juggle becomes veneer by rotary-cut or slicing;
B, several veneers are made blank substrate, blank substrate overlays the panel through boiling process, obtain A plate;
C, sawing after the cutting edge of A plate is become desirably board size, fluting japanning obtains finished product.
Described temperature when overlaying controls at 110-130 DEG C.
The boiling processing procedure of described panel is: be slowly warmed up to 60-80 DEG C (can be 70 DEG C, 75 DEG C or 65 DEG C) from normal temperature, and keep 6-8 days, the time of described slow intensification is 24 hours.
Reasonable, the described boiling retention time is 7 days.
The moisture control of described veneer is being 6%-8%.Reasonable, the moisture control of described veneer is being 6%, better can improve the stability of heating floor.

Claims (1)

1. a production method for composite floor for heating, is characterized in that, the method comprises the steps:
A, log is blocked into juggle, juggle becomes veneer by rotary-cut or slicing;
B, several veneers are made blank substrate, blank substrate overlays the panel through boiling process, obtain A plate, described temperature when overlaying controls at 110-130 DEG C, the boiling processing procedure of described panel is: be slowly warmed up to 60-80 DEG C from normal temperature, keep 7 days, the time of described slow intensification is 24 hours, and the moisture control of described veneer is being 6%;
C, sawing after the cutting edge of A plate is become desirably board size, fluting japanning obtains finished product.
CN201310375402.5A 2013-08-26 2013-08-26 A kind of production method of composite floor for heating Expired - Fee Related CN103433991B (en)