CN103433048A - Visible-light-responsive photocatalyst Cu3Nb2O8 and preparation method thereof - Google Patents
Visible-light-responsive photocatalyst Cu3Nb2O8 and preparation method thereof Download PDFInfo
- Publication number
- CN103433048A CN103433048A CN201310406132XA CN201310406132A CN103433048A CN 103433048 A CN103433048 A CN 103433048A CN 201310406132X A CN201310406132X A CN 201310406132XA CN 201310406132 A CN201310406132 A CN 201310406132A CN 103433048 A CN103433048 A CN 103433048A
- Authority
- CN
- China
- Prior art keywords
- preparation
- ball
- photochemical catalyst
- raw material
- visible light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a visible-light-responsive photocatalyst Cu3Nb2O8 and a preparation method thereof. The chemical composition formula of the photocatalyst is Cu3Nb2O8. The invention also discloses a preparation method of the material. The preparation method disclosed by the invention is simple and low in cost; and the prepared photocatalyst has the advantages of excellent catalytic property and high stability, has the function of decomposing harmful chemical substances under visible light irradiation, and thus, has favorable application prospects.
Description
Technical field
The present invention relates to a kind of visible light-responded photochemical catalyst Cu
3nb
2o
8and preparation method thereof, belong to inorganic field of photocatalytic material.
Background technology
Along with socioeconomic development, people more and more pay close attention to for the energy and ecological environment, solve energy shortage and problem of environmental pollution and be realize sustainable development, improve people's living standard and safeguard national security in the urgent need to.
From phase late 1970s, people proposed to utilize in the photochemical catalyst decomposition water and atmosphere in agricultural chemicals and the organic matter such as odorant, and application examples such as self-cleaning that scribble the surface of solids of photochemical catalyst.The principle of light-catalyzed reaction is that photochemical catalyst is after the photon absorbed higher than its band-gap energy, hole and electronics have been generated, these holes and electronics carry out respectively oxidation reaction and reduction reaction, reach the purpose of decomposing harmful chemical, organic-biological matter and sterilization.Photochemical catalyst has many kinds, and wherein most representative is titanium dioxide (TiO
2), utilized titanium dioxide in water and the agricultural chemicals in atmosphere and the organic matters such as odorant decomposed, yet the band gap of titanium dioxide is 3.2eV, only under the ultraviolet irradiation shorter than 400nm, just can show activity, can only be indoor or the local work of uviol lamp arranged, almost can not utilize visible ray, this has limited the use of titanium dioxide optical catalyst greatly.
Consider the practicality of photochemical catalyst in decomposing harmful substances, utilizing sunshine is indispensable as light source.Irradiation is near sunshine medium wavelength visible light intensity maximum 500nm on earth's surface, the energy of the visible region that wavelength is 400nm ~ 750nm is approximately 43% of sunshine gross energy, so for efficient utilization, the R and D of bismuth series photocatalyst have obtained a series of great achievements, and bismuthous compound is as BiVO
4, Bi
2moO
6, Bi
2mo
2o
9, Bi
2mo
3o
12and Bi
2wO
4be reported under visible ray and there is good absorption.A series of niobiums (tantalum) hydrochlorate photochemical catalyst is widely studied owing to having higher photocatalytic activity.For example, niobate photocatalyst Pb
3nb
4o
13, BiNbO
4and Bi
2mNbO
7(M=Al, Ga, In, Y, rare earth element or Fe) etc. with niobium potassium compound oxide photocatalyst as KNbO
3, KNb
3o
8, K
4nb
6o
17and K
6nb
10.6o
30deng all thering is photocatalysis performance preferably.
Although photocatalysis research has been carried out the several years, but at present report to have visible light-responded photochemical catalyst kind still very limited, still exist that light conversion efficiency is low, poor stability and the problem such as the spectrum respective range is narrow, so research and develop the new visible light-responded high efficiency photocatalyst that has, be very necessary.We are to Cu
3nb
2o
8, Zn
3nb
2o
8and Ca
3nb
2o
8carry out Photocatalytic Performance Study Deng niobates, found that Cu
3nb
2o
8there is excellent visible light-responded photocatalysis performance, but Zn
3nb
2o
8and Ca
3nb
2o
8but do not there is visible light-responded photocatalysis performance.
Summary of the invention
The purpose of this invention is to provide a kind of visible light-responded photochemical catalyst Cu that has
3nb
2o
8and preparation method thereof.
The chemical constitution formula with visible light-responded photochemical catalyst the present invention relates to is: Cu
3nb
2o
8.
Preparation method's concrete steps of above-mentioned visible light-responded photochemical catalyst are:
(1) by 99.9% analytically pure chemical raw material CuO and Nb
2o
5, press Cu
3nb
2o
8the chemical formula weigh batching.
(2) raw material step (1) prepared mixes, and puts into ball grinder, adds zirconia ball and absolute ethyl alcohol, and ball milling 8 hours, be mixed and finely ground, and takes out and dries, and crosses 200 mesh sieves.
(3) powder step (2) mixed is 800 ~ 850 ℃ of pre-burnings, and is incubated 6 hours, naturally cools to room temperature, then by ball mill pulverizing means, particle diameter diminished, and lower than 2 μ m, obtains Cu
3nb
2o
8powder.
Preparation method of the present invention is simple, cost is low, and the photochemical catalyst of preparation has good catalytic performance, has the effect of decomposing harmful chemical, organic-biological matter and sterilization under radiation of visible light.
The specific embodiment
Below will be specifically described the present invention:
1, the composite oxides in order to obtain using in the present invention, at first used solid-phase synthesis to prepare powder, the various oxides as raw material or carbonate measured than being mixed according to the target constitutional chemistry, more synthetic in air atmosphere under normal pressure.
2, in order effectively to utilize light, the size of the photochemical catalyst in the present invention is preferably in micron level, or even nano particle, and specific area is larger.The oxide powder prepared with solid-phase synthesis, its particle is large and surface area is less, but can particle diameter be diminished by pulverizing means such as ball mills.
3, photocatalysis experiment of the present invention is usingd methyl orange as the simulation organic pollution, and its concentration is 20mg/L; Photochemical catalyst Cu
3nb
2o
8addition be 1g/L; Light source is used the xenon lamp of 300W, and the vessel that reactive tank is used pyrex to make, obtain by wave filter the light that wavelength is greater than 420nm long wavelength, then irradiates photochemical catalyst; Catalysis time is set as 120 minutes.
Embodiment 1:
(1) by 99.9% analytically pure chemical raw material CuO and Nb
2o
5, press Cu
3nb
2o
8the chemical formula weigh batching.
(2) raw material step (1) prepared mixes, and puts into ball grinder, adds zirconia ball and absolute ethyl alcohol, and ball milling 8 hours, be mixed and finely ground, and takes out and dries, and crosses 200 mesh sieves.
(3) powder step (2) mixed is 800 ℃ of pre-burnings, and is incubated 6 hours, naturally cools to room temperature, then by ball mill pulverizing means, particle diameter diminished, and lower than 2 μ m, obtains Cu
3nb
2o
8powder.
Prepared photochemical catalyst, be greater than at wavelength under the radiation of visible light of 420nm, the methyl orange clearance reached to 98.9% in 120 minutes.
Embodiment 2:
(1) by 99.9% analytically pure chemical raw material CuO and Nb
2o
5, press Cu
3nb
2o
8the chemical formula weigh batching.
(2) raw material step (1) prepared mixes, and puts into ball grinder, adds zirconia ball and absolute ethyl alcohol, and ball milling 8 hours, be mixed and finely ground, and takes out and dries, and crosses 200 mesh sieves.
(3) powder step (2) mixed is 825 ℃ of pre-burnings, and is incubated 6 hours, naturally cools to room temperature, then by ball mill pulverizing means, particle diameter diminished, and lower than 2 μ m, obtains Cu
3nb
2o
8powder.
Prepared photochemical catalyst, be greater than at wavelength under the radiation of visible light of 420nm, the methyl orange clearance reached to 98.5% in 120 minutes.
Embodiment 3:
(1) by 99.9% analytically pure chemical raw material CuO and Nb
2o
5, press Cu
3nb
2o
8the chemical formula weigh batching.
(2) raw material step (1) prepared mixes, and puts into ball grinder, adds zirconia ball and absolute ethyl alcohol, and ball milling 8 hours, be mixed and finely ground, and takes out and dries, and crosses 200 mesh sieves.
(3) powder step (2) mixed is 850 ℃ of pre-burnings, and is incubated 6 hours, naturally cools to room temperature, then by ball mill pulverizing means, particle diameter diminished, and lower than 2 μ m, obtains Cu
3nb
2o
8powder.
Prepared photochemical catalyst, be greater than at wavelength under the radiation of visible light of 420nm, and 120min reaches 98.1% to the methyl orange clearance.
The present invention never is limited to above embodiment.The bound of each temperature, interval value can realize the present invention, at this, do not enumerate embodiment.
The made photocatalyst powder of above inventive embodiments can be carried on multiple matrix surface.Matrix can be glass, pottery, active carbon or quartz sand etc., and photochemical catalyst can be carried on matrix surface with the form of film.
Claims (1)
1. a niobates, as the application of visible light-responded photochemical catalyst, is characterized in that the chemical constitution formula of described niobates is: Cu
3nb
2o
8;
Preparation method's concrete steps of described niobates are:
(1) by 99.9% analytically pure chemical raw material CuO and Nb
2o
5, press Cu
3nb
2o
8the chemical formula weigh batching;
(2) raw material step (1) prepared mixes, and puts into ball grinder, adds zirconia ball and absolute ethyl alcohol, and ball milling 8 hours, be mixed and finely ground, and takes out and dries, and crosses 200 mesh sieves;
(3) powder step (2) mixed is 800 ~ 850 ℃ of pre-burnings, and is incubated 6 hours, naturally cools to room temperature, then by ball mill pulverizing means, particle diameter diminished, and lower than 2 μ m, obtains Cu
3nb
2o
8powder.