CN103432626A - 纤维蛋白原静电纺丝膜片及制备工艺 - Google Patents

纤维蛋白原静电纺丝膜片及制备工艺 Download PDF

Info

Publication number
CN103432626A
CN103432626A CN2013103641493A CN201310364149A CN103432626A CN 103432626 A CN103432626 A CN 103432626A CN 2013103641493 A CN2013103641493 A CN 2013103641493A CN 201310364149 A CN201310364149 A CN 201310364149A CN 103432626 A CN103432626 A CN 103432626A
Authority
CN
China
Prior art keywords
fibrinogen
solution
electrostatic spinning
electrostatic
mixed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013103641493A
Other languages
English (en)
Inventor
倪迪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUJIANG YINGLIDA PLASTIC PACKAGING CO Ltd
Original Assignee
WUJIANG YINGLIDA PLASTIC PACKAGING CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUJIANG YINGLIDA PLASTIC PACKAGING CO Ltd filed Critical WUJIANG YINGLIDA PLASTIC PACKAGING CO Ltd
Priority to CN2013103641493A priority Critical patent/CN103432626A/zh
Publication of CN103432626A publication Critical patent/CN103432626A/zh
Pending legal-status Critical Current

Abstract

本发明公开了纤维蛋白原静电纺丝膜片及制备方法，以六氟异丙醇为溶剂，配制8-10%（w/v）牛纤维蛋白原的溶液；将六氟异丙醇与生理盐水以体积比9：1混合，配制成混合溶剂，将纤维蛋白原溶于混合溶剂中配制成浓度为100-200mg/ml的纤维蛋白原溶液，将牛纤维蛋白原溶液与纤维蛋白原溶液以体积比2：1混合，得静电纺丝溶液。将静电纺丝溶液以的2-4ml/h流速通过静电纺丝装置注射泵的22号钝性针头，静电纺丝纤维收集旋转圆轴（直径6cm，长20cm）上，转速为500-700r/min，从圆轴上取下膜片，真空干燥48h后，即得。本发明有显著的细胞外基质特征，较好的组织相容性。

Description

纤维蛋白原静电纺丝膜片及制备工艺
 
技术领域：本发明属于仿生材料领域。
 
技术背景：
采用应用工程学和生命科学的方法开发是新型的生物替代品是现阶段组织工程的重要课题。以聚氨酯类人工合成高分子材料具备良好的力学特性低弹性模量以及高顺应性等特点，在血管组织工程方面有巨大的应用潜力。但人工合成材料由于缺乏细胞识别信号，生物相容性往往较差。
 
发明内容：
本发明的目的设计一种纤维蛋白原静电纺丝膜片及制备方法，开放细胞识别信号好，生物相容性好的生物仿生材料。
本发明的设计方案是以牛纤维蛋白原，六氟异丙醇为原料，（1）以六氟异丙醇为溶剂，配制8-10%（w/v）牛纤维蛋白原的溶液；将六氟异丙醇与生理盐水以体积比9：1 混合，配制成混合溶剂，将纤维蛋白原溶于混合溶剂中配制成浓度为100-200mg/ml的纤维蛋白原溶液，将牛纤维蛋白原溶液与纤维蛋白原溶液以体积比2：1 混合，得静电纺丝溶液。（2）将静电纺丝溶液以 的2-4ml/h流速通过静电纺丝装置注射泵的22号钝性针头，静电纺丝纤维收集旋转圆轴（直径6cm，长20cm）上，转速为500-700r/min ，从圆轴上取下膜片，真空干燥48h后，即得。
本发明的的原理：纤维蛋白原是一种由肝脏合成并在血流中自由循环的糖蛋白类物质，对血管内皮生长因子碱性成纤维细胞生长因子以及其它细胞因子具有高亲和能力，故可用于改善组织工程血管的生物相容性。
 
本发明的有益效果为：本发明制造的静电纺丝膜片平均纤维直径为50-500nm，有显著的细胞外基质特征，较好的组织相容性。
 
具体实施方式：
实施例1：以六氟异丙醇为溶剂，配制8%（w/v）牛纤维蛋白原的溶液；将六氟异丙醇与生理盐水以体积比9：1 混合，配制成混合溶剂，将纤维蛋白原溶于混合溶剂中配制成浓度为100mg/ml的纤维蛋白原溶液，将牛纤维蛋白原溶液与纤维蛋白原溶液以体积比2：1 混合，得静电纺丝溶液。（2）将静电纺丝溶液以 的2-4ml/h流速通过静电纺丝装置注射泵的22号钝性针头，静电纺丝纤维收集旋转圆轴（直径6cm，长20cm）上，转速为500r/min ，从圆轴上取下膜片，真空干燥48h后，即得。
实施例2：以六氟异丙醇为溶剂，配制10%（w/v）牛纤维蛋白原的溶液；将六氟异丙醇与生理盐水以体积比9：1 混合，配制成混合溶剂，将纤维蛋白原溶于混合溶剂中配制成浓度为200mg/ml的纤维蛋白原溶液，将牛纤维蛋白原溶液与纤维蛋白原溶液以体积比2：1 混合，得静电纺丝溶液。（2）将静电纺丝溶液以 的4ml/h流速通过静电纺丝装置注射泵的22号钝性针头，静电纺丝纤维收集旋转圆轴（直径6cm，长20cm）上，转速为700r/min ，从圆轴上取下膜片，真空干燥48h后，即得。

Claims (2)

1.一种纤维蛋白原静电纺丝膜片，其特征在于：以牛纤维蛋白原，六氟异丙醇为原料。
2.一种纤维蛋白原静电纺丝膜片的制备工艺，其特征在于：步骤包括（1）以六氟异丙醇为溶剂，配制8-10%（w/v）牛纤维蛋白原的溶液；将六氟异丙醇与生理盐水以体积比9：1 混合，配制成混合溶剂，将纤维蛋白原溶于混合溶剂中配制成浓度为100-200mg/ml的纤维蛋白原溶液，将牛纤维蛋白原溶液与纤维蛋白原溶液以体积比2：1 混合，得静电纺丝溶液；
（2）将静电纺丝溶液以 的2-4ml/h流速通过静电纺丝装置注射泵的22号钝性针头，静电纺丝纤维收集旋转圆轴（直径6cm，长20cm）上，转速为500-700r/min ，从圆轴上取下膜片，真空干燥48h后，即得。
CN2013103641493A 2013-08-21 2013-08-21 纤维蛋白原静电纺丝膜片及制备工艺 Pending CN103432626A (zh)