CN103420667A - Strengthened low-bone china porcelain and production method thereof - Google Patents
Strengthened low-bone china porcelain and production method thereof Download PDFInfo
- Publication number
- CN103420667A CN103420667A CN2013103417619A CN201310341761A CN103420667A CN 103420667 A CN103420667 A CN 103420667A CN 2013103417619 A CN2013103417619 A CN 2013103417619A CN 201310341761 A CN201310341761 A CN 201310341761A CN 103420667 A CN103420667 A CN 103420667A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- soil
- raw material
- glazing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to strengthened low-bone china porcelain and a production method thereof, and mainly overcomes technical difficulties that the conventional bone chain is low in strength, is easily scratched by a knife and fork and difficult to clean. The invention adopts the technical scheme as follows: the strengthened low-bone china porcelain is prepared from a blank material and a glaze material, wherein the blank material is prepared from the following components in parts by weight: 25-33 parts of quartz, 20-25 parts of Datong soil, 3-5 parts of talc, 10-15 parts of Fujian soil, 5-10 parts of Hunan soil, 2-5 parts of alumina, 4-10 parts of bone powder, 8-10 parts of feldspar and 3-5 parts of Inner Mongolia soil; and the glaze material is prepared from the following components in parts by weight: 8-10 parts of quartz, 35-40 parts of feldspar, 4-6 parts of talc, 4-6 parts of Inner Mongolia soil, 10-13 parts of calcite, 3-5 parts of zinc oxide, 2-4 parts of barium oxide and 15-20 parts of porcelain powder. The production method comprises the following steps: 1) preparing the blank material; 2) preparing the glaze material; 3) preparing a blank; 4) glazing; and 5) firing.
Description
Technical field
The present invention relates to the low china porcelain of a kind of strengthening and production method thereof, it belongs to a kind of daily necessities porcelain tool and production method thereof.
Background technology
At present, china is the high-grade porcelain kind that generally acknowledge in high-grade household china market.But because the intensity of china is low, its glaze layer is easy fired, and in life-time service, glaze is easily marked scar by knife and fork simultaneously, easy residual tea stain, spot are difficult to clean.In addition, china adopts the processing step burnt till for twice in process of production.Complex process, production cost are high, and product price is also very high.
Summary of the invention
The objective of the invention is to solve the intensity that existing china exists low, easily by knife and fork, marked scar and difficult technological difficulties of cleaning, provide that a kind of intensity is high, easy cleaning and the difficult low china porcelain of strengthening and production method thereof of hindering glaze.
The present invention solves the problems of the technologies described above the technical scheme adopted to be: the low china porcelain of strengthening, blank and glaze that it is made by the raw material of following weight proportion make, the raw material weight proportioning of described blank is: quartzy 25～33 parts, and 20～25 parts, Datong District's soil, 3～5 parts, talcum, 10～15 parts, Fujian soil, 5～10 parts, Hunan soil, 2～5 parts, aluminum oxide, 4～10 parts of bone meal, 8～10 parts of feldspars, 3～5 parts, Inner Mongol soil; The raw material weight proportioning of described glaze is: quartzy 8～10 parts, and 35～40 parts of feldspars, 4～6 parts, talcum, 4～6 parts, Inner Mongol soil, 10～13 parts, calcite, 3～5 parts, zinc oxide, 2～4 parts, barium oxide, 15～20 parts, porcelain powder.
The raw material optimum weight proportioning of described blank is: quartzy 30 parts, and 23 parts, Datong District's soil, 5 parts, talcum, 12 parts, Fujian soil, 10 parts, Hunan soil, 3 parts, aluminum oxide, 5 parts of bone meal, 9 parts of feldspars, 3 parts, Inner Mongol soil.
The raw material optimum weight proportioning of described glaze is: quartzy 10 parts, and 38 parts of feldspars, 5 parts, talcum, 6 parts, Inner Mongol soil, 11 parts, calcite, 5 parts, zinc oxide, 3 parts, barium oxide, 20 parts, porcelain powder.
A kind of method of producing the low china porcelain of described strengthening, it comprises the following steps:
1) prepare blank: the raw material weight proportioning by described blank takes raw material and mixes, and then the ratio of ball milling compound ， Liao ︰ Qiu ︰ water is 1 ︰ 1.5-1.7 ︰ 1.2; It is 250 purpose mud that compound is milled to fineness, and tailing over is 0.05%～0.15%; Mud is crossed respectively 160 orders, 180 orders, 200 mesh sieves, and three deironing of sieving are standby;
2) prepare glaze: the raw material weight proportioning by described glaze takes raw material and mixes, and then the ratio of ball milling compound ， Liao ︰ Qiu ︰ water is 1 ︰ 1.5-1.7 ︰ 0.5; It is 250 purpose glaze slips that compound is milled to fineness, and tailing over is 0.01%～0.03%; Glaze slip is crossed respectively 160 orders, 200 orders, 250 mesh sieves, and three deironing of sieving are standby;
3) prepare base substrate: use the blank of preparation to prepare base substrate;
4) glazing: use the glaze of preparation to the base substrate glazing; Glazing base substrate moisture control is 1.5%～2%; Adopt machinery or soak the glazing of glaze mode, mechanical glazing glaze concentration is controlled at the 1.75(Beaumé scale), soak the glaze glazing, soak glaze concentration and be controlled at 1.40～1.42(Beaumé scale);
5) fire: the glazing base substrate is placed in the cooled coal gas tunnel furnace and fires with the gasification flame, and the firing time is 16 hours, and temperature is 1270 ℃～1320 ℃.
The present invention adopts technique scheme, produces the new porcelain of a kind of boundary between china and strengthening porcelain.This porcelain adopts the processing step of high temperature once-firing, and the strong light transmission of existing china has again the high strength advantage of strengthening porcelain.
After testing, product of the present invention has following properties:
Embodiment
Embodiment 1
The low china porcelain of strengthening, blank and glaze that it is made by the raw material of following weight proportion make, and the raw material weight proportioning of described blank is: quartzy 25 parts, 20 parts, Datong District's soil, 3 parts, talcum, 10 parts, Fujian soil, 5 parts, Hunan soil, 2 parts, aluminum oxide, 4 parts of bone meal, 8 parts of feldspars, 3 parts, Inner Mongol soil; The raw material weight proportioning of described glaze is: quartzy 8 parts, and 35 parts of feldspars, 4 parts, talcum, 4 parts, Inner Mongol soil, 10 parts, calcite, 3 parts, zinc oxide, 2 parts, barium oxide, 15 parts, porcelain powder.
Produce the method for the low china porcelain of above-mentioned strengthening, it comprises the following steps:
1) prepare blank: the raw material weight proportioning by described blank takes raw material and mixes, and then the ratio of ball milling compound ， Liao ︰ Qiu ︰ water is 1 ︰ 1.5 ︰ 1.2; It is 250 purpose mud that compound is milled to fineness, and tailing over is 0.05%～0.15%; Mud is crossed respectively 160 orders, 180 orders, 200 mesh sieves, and three deironing of sieving are standby;
2) prepare glaze: the raw material weight proportioning by described glaze takes raw material and mixes, and then the ratio of ball milling compound ， Liao ︰ Qiu ︰ water is 1 ︰ 1.5 ︰ 0.5; It is 250 purpose glaze slips that compound is milled to fineness, and tailing over is 0.01%～0.03%; Glaze slip is crossed respectively 160 orders, 200 orders, 250 mesh sieves, and three deironing of sieving are standby;
3) prepare base substrate: use the blank of preparation to prepare base substrate;
4) glazing: use the glaze of preparation to the base substrate glazing; Glazing base substrate moisture control is 1.5%～2%; Adopt machinery or soak the glazing of glaze mode, mechanical glazing glaze concentration is controlled at the 1.75(Beaumé scale), soak the glaze glazing, soak glaze concentration and be controlled at 1.40～1.42(Beaumé scale);
5) fire: the glazing base substrate is placed in the cooled coal gas tunnel furnace and fires with the gasification flame, and the firing time is 16 hours, and temperature is 1270 ℃.
Embodiment 2
The low china porcelain of strengthening, blank and glaze that it is made by the raw material of following weight proportion make, and the raw material weight proportioning of described blank is: quartzy 33 parts, 25 parts, Datong District's soil, 5 parts, talcum, 15 parts, Fujian soil, 10 parts, Hunan soil, 5 parts, aluminum oxide, 10 parts of bone meal, 10 parts of feldspars, 5 parts, Inner Mongol soil; The raw material weight proportioning of described glaze is: quartzy 10 parts, and 40 parts of feldspars, 6 parts, talcum, 6 parts, Inner Mongol soil, 13 parts, calcite, 5 parts, zinc oxide, 4 parts, barium oxide, 20 parts, porcelain powder.
Produce the method for the low china porcelain of above-mentioned strengthening, it comprises the following steps:
1) prepare blank: the raw material weight proportioning by described blank takes raw material and mixes, and then the ratio of ball milling compound ， Liao ︰ Qiu ︰ water is 1 ︰ 1.7 ︰ 1.2; It is 250 purpose mud that compound is milled to fineness, and tailing over is 0.05%～0.15%; Mud is crossed respectively 160 orders, 180 orders, 200 mesh sieves, and three deironing of sieving are standby;
2) prepare glaze: the raw material weight proportioning by described glaze takes raw material and mixes, and then the ratio of ball milling compound ， Liao ︰ Qiu ︰ water is 1 ︰ 1.7 ︰ 0.5; It is 250 purpose glaze slips that compound is milled to fineness, and tailing over is 0.01%～0.03%; Glaze slip is crossed respectively 160 orders, 200 orders, 250 mesh sieves, and three deironing of sieving are standby;
3) prepare base substrate: use the blank of preparation to prepare base substrate;
4) glazing: use the glaze of preparation to the base substrate glazing; Glazing base substrate moisture control is 1.5%～2%; Adopt machinery or soak the glazing of glaze mode, mechanical glazing glaze concentration is controlled at the 1.75(Beaumé scale), soak the glaze glazing, soak glaze concentration and be controlled at 1.40～1.42(Beaumé scale);
5) fire: the glazing base substrate is placed in the cooled coal gas tunnel furnace and fires with the gasification flame, and the firing time is 16 hours, and temperature is 1320 ℃.
Embodiment 3
The low china porcelain of strengthening, blank and glaze that it is made by the raw material of following weight proportion make, and the raw material weight proportioning of described blank is: quartzy 29 parts, 23 parts, Datong District's soil, 4 parts, talcum, 13 parts, Fujian soil, 7 parts, Hunan soil, 4 parts, aluminum oxide, 7 parts of bone meal, 9 parts of feldspars, 4 parts, Inner Mongol soil; The raw material weight proportioning of described glaze is: quartzy 9 parts, and 37 parts of feldspars, 5 parts, talcum, 5 parts, Inner Mongol soil, 12 parts, calcite, 4 parts, zinc oxide, 3 parts, barium oxide, 18 parts, porcelain powder.
Produce the method for the low china porcelain of above-mentioned strengthening, it comprises the following steps:
1) prepare blank: the raw material weight proportioning by described blank takes raw material and mixes, and then the ratio of ball milling compound ， Liao ︰ Qiu ︰ water is 1 ︰ 1.6 ︰ 1.2; It is 250 purpose mud that compound is milled to fineness, and tailing over is 0.05%～0.15%; Mud is crossed respectively 160 orders, 180 orders, 200 mesh sieves, and three deironing of sieving are standby;
2) prepare glaze: the raw material weight proportioning by described glaze takes raw material and mixes, and then the ratio of ball milling compound ， Liao ︰ Qiu ︰ water is 1 ︰ 1.6 ︰ 0.5; It is 250 purpose glaze slips that compound is milled to fineness, and tailing over is 0.01%～0.03%; Glaze slip is crossed respectively 160 orders, 200 orders, 250 mesh sieves, and three deironing of sieving are standby;
3) prepare base substrate: use the blank of preparation to prepare base substrate;
4) glazing: use the glaze of preparation to the base substrate glazing; Glazing base substrate moisture control is 1.5%～2%; Adopt machinery or soak the glazing of glaze mode, mechanical glazing glaze concentration is controlled at the 1.75(Beaumé scale), soak the glaze glazing, soak glaze concentration and be controlled at 1.40～1.42(Beaumé scale);
5) fire: the glazing base substrate is placed in the cooled coal gas tunnel furnace and fires with the gasification flame, and the firing time is 16 hours, and temperature is 1290 ℃.
Embodiment 4
The low china porcelain of strengthening, blank and glaze that it is made by the raw material of following weight proportion make, and the raw material weight proportioning of described blank is: quartzy 30 parts, 23 parts, Datong District's soil, 5 parts, talcum, 12 parts, Fujian soil, 10 parts, Hunan soil, 3 parts, aluminum oxide, 5 parts of bone meal, 9 parts of feldspars, 3 parts, Inner Mongol soil; The raw material weight proportioning of described glaze is: quartzy 10 parts, and 38 parts of feldspars, 5 parts, talcum, 6 parts, Inner Mongol soil, 11 parts, calcite, 5 parts, zinc oxide, 3 parts, barium oxide, 20 parts, porcelain powder.
Produce the method for the low china porcelain of above-mentioned strengthening, it comprises the following steps:
1) prepare blank: the raw material weight proportioning by described blank takes raw material and mixes, and then the ratio of ball milling compound ， Liao ︰ Qiu ︰ water is 1 ︰ 1.6 ︰ 1.2; It is 250 purpose mud that compound is milled to fineness, and tailing over is 0.05%～0.15%; Mud is crossed respectively 160 orders, 180 orders, 200 mesh sieves, and three deironing of sieving are standby;
2) prepare glaze: the raw material weight proportioning by described glaze takes raw material and mixes, and then the ratio of ball milling compound ， Liao ︰ Qiu ︰ water is 1 ︰ 1.6 ︰ 0.5; It is 250 purpose glaze slips that compound is milled to fineness, and tailing over is 0.01%～0.03%; Glaze slip is crossed respectively 160 orders, 200 orders, 250 mesh sieves, and three deironing of sieving are standby;
3) prepare base substrate: use the blank of preparation to prepare base substrate;
4) glazing: use the glaze of preparation to the base substrate glazing; Glazing base substrate moisture control is 1.5%～2%; Adopt machinery or soak the glazing of glaze mode, mechanical glazing glaze concentration is controlled at the 1.75(Beaumé scale), soak the glaze glazing, soak glaze concentration and be controlled at 1.40～1.42(Beaumé scale);
5) fire: the glazing base substrate is placed in the cooled coal gas tunnel furnace and fires with the gasification flame, and the firing time is 16 hours, and temperature is 1300 ℃.
The raw material of blank described in above-described embodiment can also be selected arbitrarily in the following weight proportioning: quartzy 25～33 parts, and 20～25 parts, Datong District's soil, 3～5 parts, talcum, 10～15 parts, Fujian soil, 5～10 parts, Hunan soil, 2～5 parts, aluminum oxide, 4～10 parts of bone meal, 8～10 parts of feldspars, 3～5 parts, Inner Mongol soil.
The raw material of glaze described in above-described embodiment can also be selected arbitrarily in the following weight proportioning: quartzy 8～10 parts, and 35～40 parts of feldspars, 4～6 parts, talcum, 4～6 parts, Inner Mongol soil, 10～13 parts, calcite, 3～5 parts, zinc oxide, 2～4 parts, barium oxide, 15～20 parts, porcelain powder.
The chemical constitution of the blank raw material in above-described embodiment is:
| ? | SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | K2O | Na2O | P2O5 | IL | Total amount |
| Feldspar | 65.6 | 18.2 | 0.04 | 0.21 | 0.07 | 0.01 | 12.47 | 3.03 | 0 | 0.12 | 99.77 |
| Quartzy | 98.8 | 0.48 | 0.06 | 0 | 0.1 | 0.19 | 0 | 0 | 0 | 0.2 | 99.83 |
| Talcum | 64.43 | 0.28 | 0.05 | 0.09 | 4.97 | 29.7 | 0.04 | 0.09 | 0 | 0.3 | 99.95 |
| Fujian soil | 75.91 | 13.5 | 0.21 | 0.1 | 0.09 | 0.14 | 4.43 | 0.33 | 0 | 4.75 | 99.44 |
| Inner Mongol soil | 70.8 | 13.2 | 0.33 | 0.11 | 2.95 | 3.07 | 0.64 | 0.16 | 0 | 8.47 | 99.71 |
| Datong District's soil | 47.18 | 36.1 | 0.26 | 0.5 | 0.26 | 0.08 | 0.18 | 0.37 | 0 | 14.76 | 99.67 |
| Hunan soil | 67.38 | 21.6 | 0.83 | 0 | 0.43 | 0.3 | 1.95 | 2.75 | 0 | 0.59 | 95.82 |
| Aluminium powder | 0 | 99 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0.4 | 99.4 |
| Bone meal | 0 | 0 | 0 | 0 | 54.8 | 0 | 3.2 | 0 | 37.5 | 0.2 | 95.7 |
The chemical constitution of the glaze raw material in above-described embodiment is:
Protection scope of the present invention is not restricted to the described embodiments.
Claims (4)
1. the china porcelain is hanged down in a strengthening, it is characterized in that: blank and glaze that it is made by the raw material of following weight proportion make, the raw material weight proportioning of described blank is: quartzy 25～33 parts, and 20～25 parts, Datong District's soil, 3～5 parts, talcum, 10～15 parts, Fujian soil, 5～10 parts, Hunan soil, 2～5 parts, aluminum oxide, 4～10 parts of bone meal, 8～10 parts of feldspars, 3～5 parts, Inner Mongol soil; The raw material weight proportioning of described glaze is: quartzy 8～10 parts, and 35～40 parts of feldspars, 4～6 parts, talcum, 4～6 parts, Inner Mongol soil, 10～13 parts, calcite, 3～5 parts, zinc oxide, 2～4 parts, barium oxide, 15～20 parts, porcelain powder.
2. the china porcelain is hanged down in strengthening according to claim 1, and it is characterized in that: the raw material weight proportioning of described blank is: quartzy 30 parts, and 23 parts, Datong District's soil, 5 parts, talcum, 12 parts, Fujian soil, 10 parts, Hunan soil, 3 parts, aluminum oxide, 5 parts of bone meal, 9 parts of feldspars, 3 parts, Inner Mongol soil.
3. the china porcelain is hanged down in strengthening according to claim 1, and it is characterized in that: the raw material weight proportioning of described glaze is: quartzy 10 parts, and 38 parts of feldspars, 5 parts, talcum, 6 parts, Inner Mongol soil, 11 parts, calcite, 5 parts, zinc oxide, 3 parts, barium oxide, 20 parts, porcelain powder.
4. a method of producing the low china porcelain of claim 1,2 or 3 described strengthenings, it is characterized in that: it comprises the following steps:
1) prepare blank: the raw material weight proportioning by described blank takes raw material and mixes, and then the ratio of ball milling compound ， Liao ︰ Qiu ︰ water is 1 ︰ 1.5-1.7 ︰ 1.2; It is 250 purpose mud that compound is milled to fineness, and tailing over is 0.05%～0.15%; Mud is crossed respectively 160 orders, 180 orders, 200 mesh sieves, and three deironing of sieving are standby;
2) prepare glaze: the raw material weight proportioning by described glaze takes raw material and mixes, and then the ratio of ball milling compound ， Liao ︰ Qiu ︰ water is 1 ︰ 1.5-1.7 ︰ 0.5; It is 250 purpose glaze slips that compound is milled to fineness, and tailing over is 0.01%～0.03%; Glaze slip is crossed respectively 160 orders, 200 orders, 250 mesh sieves, and three deironing of sieving are standby;
3) prepare base substrate: use the blank of preparation to prepare base substrate;
4) glazing: use the glaze of preparation to the base substrate glazing; Glazing base substrate moisture control is 1.5%～2%; Adopt machinery or soak the glazing of glaze mode, mechanical glazing glaze concentration is controlled at the 1.75(Beaumé scale), soak the glaze glazing, soak glaze concentration and be controlled at 1.40～1.42(Beaumé scale);
5) fire: the glazing base substrate is placed in the cooled coal gas tunnel furnace and fires with the gasification flame, and the firing time is 16 hours, and temperature is 1270 ℃～1320 ℃.