CN103409069A - Preparation method of nano emulsified shoe polish - Google Patents
Preparation method of nano emulsified shoe polish Download PDFInfo
- Publication number
- CN103409069A CN103409069A CN201310312073XA CN201310312073A CN103409069A CN 103409069 A CN103409069 A CN 103409069A CN 201310312073X A CN201310312073X A CN 201310312073XA CN 201310312073 A CN201310312073 A CN 201310312073A CN 103409069 A CN103409069 A CN 103409069A
- Authority
- CN
- China
- Prior art keywords
- shoe polish
- preparation
- yelkin tts
- nano emulsified
- emulsified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation method of a nano emulsified shoe polish. The preparation method comprises following steps: (1) 20 to 40g of lecithin is dissolved in 100ml of water so as to obtain a saturated solution; (2) paraffin and lecithin are mixed at a ratio of 1:2-1:3, and the mixture is subjected to magnetic stirring at a speed of 1000/min for 3 to 5h, and then the nano emulsified shoe polishis obtained, wherein the pH value of the mixture is 8 to 10, and the temperature of the mixture is 55 to 65 DEG C. The nano emulsified shoe polish is stable, and polishing is easy.
Description
Technical field:
The present invention relates to a kind of shoe polish preparation field, be specifically related to a kind of nanometer emulsified shoe polish preparation field.
Background technology:
The shoe polish nanotechnology can be converted into liquid shoe polish nano level homogeneous emulsifiable paste, greatly improve shoe polish stability, be easy to glazing.
Yelkin TTS and derivative thereof are the compounds that a class has the particular molecule cavity structure; can be combined into the host-guest inclusion thing with many organic and inorganic and biomolecules; characteristic with protection, stable, solubilising guest molecule and selectivity oriented molecule; be a kind of desirable nano material, thereby all be widely used at aspects such as environment, medicine, food, makeup, chemical separations.
Nearly 2 years domestic has successively and usings Yelkin TTS and derivative thereof as the research of food nano material aspect, but rarely has the report prepared for shoe polish.
Summary of the invention:
Patent purpose of the present invention is the deficiency for present stage shoe polish preparation method, and the preparation method of nanometer emulsified shoe polish is provided, and can improve the stability of shoe polish, is easy to glazing.
The technical scheme of patent of the present invention is a kind of preparation method of nanometer emulsified shoe polish, and step comprises: (1) takes the Yelkin TTS of 20-40g, is dissolved in 100ml water, is made into saturated solution; (2) making paraffin and Yelkin TTS proportioning is that 1:2～1:3 mixes, Ph8～10, and temperature is 55～65 ℃, the 1000/min magnetic agitation continues to stir 3～5 h, obtains.
The principle of the invention: Yelkin TTS and derivative thereof, as nano material, carry out the inclusion of oil soluble paraffin, form micro-capsule, make paraffin change into emulsifiable paste, so, can improve the stability of shoe polish, are easy to glazing.
Beneficial effect is:
The present invention improves the stability of shoe polish, is easy to glazing.
Embodiment:
Embodiment 1. (1) takes the Yelkin TTS of 20g, is dissolved in 100ml water, is made into saturated solution; (2) making paraffin and Yelkin TTS proportioning is that 1:2 mixes, Ph8, and temperature is 55～65 ℃, the 1000/min magnetic agitation continues to stir 3 h, obtains.
Embodiment 2. (1) takes the Yelkin TTS of 20g, is dissolved in 100ml water, is made into saturated solution; (2) making paraffin and Yelkin TTS proportioning is that 1:3 mixes, Ph10, and temperature is 55～65 ℃, the 1000/min magnetic agitation continues to stir 5 h, obtains.
Claims (2)
1. the preparation method of a nanometer emulsified shoe polish, it is characterized in that: (1) takes the Yelkin TTS of 20g-40, is dissolved in 100ml water, is made into saturated solution; (2) making paraffin and Yelkin TTS proportioning is that 1:2～1:3 mixes, Ph8～10, and temperature is 55～65 ℃, the 1000/min magnetic agitation continues to stir 3～5 h, obtains.
2. the preparation method of a kind of nanometer emulsified shoe polish according to claim 1, is characterized in that (1) takes the Yelkin TTS of 20g, is dissolved in 100ml water, is made into saturated solution; (2) making paraffin and Yelkin TTS proportioning is that 1:2 mixes, Ph8, and temperature is 55～65 ℃, the 1000/min magnetic agitation continues to stir 3 h, obtains.