CN103409030A - High-temperature-resistant amino resin impregnating varnish and preparation method thereof - Google Patents
High-temperature-resistant amino resin impregnating varnish and preparation method thereof Download PDFInfo
- Publication number
- CN103409030A CN103409030A CN2013102724465A CN201310272446A CN103409030A CN 103409030 A CN103409030 A CN 103409030A CN 2013102724465 A CN2013102724465 A CN 2013102724465A CN 201310272446 A CN201310272446 A CN 201310272446A CN 103409030 A CN103409030 A CN 103409030A
- Authority
- CN
- China
- Prior art keywords
- parts
- impregnating varnish
- preparation
- aminoresin
- hour
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides high-temperature-resistant amino resin impregnating varnish and a preparation method thereof. The impregnating varnish is prepared from the following raw materials in parts by weight: 32-35 parts of 583-2 amino resin, 3-4 parts of unsaturated polyester resin, 5-7 parts of organic silicon resin, 2-3 parts of calcium naphthenate, 20-24 parts of xylene, 4-5 parts of methyl ethyl ketone, 2-3 parts of tetraethylenepentamine, 4-6 parts of maleic anhydride, 1-2 parts of monobutyltin oxide, 1-2 parts of tert-Butyl peroxybenzoate, 6-9 parts of butadiene, 4-5 parts of poly(propylene glycol) acrylate, 9-10 parts of alkylphenol ethoxylate phosphate, and 4-5 parts of film forming agent. The impregnating varnish can be used for a long time without yellowing or bubbling in a high-temperature environment, can be widely applied to impregnating insulation of medium-small motor coils, transformers, rectifiers and other electrical appliance coils.
Description
Technical field
The invention belongs to the insulating material field, relate to a kind of impregnating varnish, especially a kind of high temperature resistant aminoresin impregnating varnish and preparation method thereof.
Background technology
Pressure impregnation technique is generally adopted in the productions such as motor, transformer, wire.Go tide rear cooling the workpiece preliminary drying, be placed in vacuum environment, get rid of inner air and volatile matter, rely in vacuum the effect of painting liquid gravity, applying certain pressure, make to paint the liquid rapid permeability and be full of the insulation system internal layer.This technique can obtain the paint film of continuous densification, free of pinholes.
Existing impregnating varnish is as matrix resin, acid anhydrides, to be solidifying agent by epoxy resin.But the temperature resistant grade of this system cured product and toughness deficiency, need to carry out modification to epoxy anhydride impregnating varnish system, is the requirement that impregnating varnish system cured article meets temperature resistant grade and mechanical property simultaneously.
Summary of the invention
The purpose of this invention is to provide a kind of high temperature resistant aminoresin impregnating varnish and preparation method thereof.
Technical scheme of the present invention is as follows:
A kind of high temperature resistant aminoresin impregnating varnish is characterized in that being made by the raw material of following weight part:
582-2 aminoresin 32-35, unsaturated polyester resin 3-4, silicone resin 5-7, calcium naphthenate 2-3, dimethylbenzene 20-24, methylethylketone 4-5, tetraethylene pentamine 2-3, MALEIC ANHYDRIDE 4-6, Mono-n-butyltin 1-2, peroxidized t-butyl perbenzoate 1-2, divinyl 6-9, polypropylene glycol acrylate 4-5, alkylphenol polyoxyethylene phosphoric acid ester 9-10, membrane-forming agent 4-5.
Described membrane-forming agent is made by the raw material of following weight part: phenyl triethoxysilane 1-2, anilinomethyl triethoxysilane 1-2, ferrocene 2-3, aluminium nitride 1-2, nano-attapulgite 1-2, epoxy soybean oil 4-5, morpholine 1-2, polyisobutene 3-4;
The preparation method is: by each mixing of materials, be heated to 105-110 ℃, and stirring reaction 2-3 hour, grinding removes slag obtains.
The preparation method of described high temperature resistant aminoresin impregnating varnish, it is characterized in that comprising the following steps: divinyl 6-9, polypropylene glycol acrylate 4-5, alkylphenol polyoxyethylene phosphoric acid ester, methylethylketone, tetraethylene pentamine, MALEIC ANHYDRIDE, dimethylbenzene are mixed, be heated to 100-105 ℃, drip peroxidized t-butyl perbenzoate, stirring reaction 1-2 hour, then, add other remaining component, continue stirring reaction 2-3 hour, obtain.
The present invention is life-time service xanthochromia, non-foaming not under hot environment, and shock strength is greater than 50Kg/cm, and the insulation temperature classification is high, can be widely used in the varnished insulation of the electric apparatus coils such as middle and small motor coil, transformer, rectifier.
Embodiment
A kind of high temperature resistant aminoresin impregnating varnish, by the raw material (kilogram) of following weight part, made:
582-2 aminoresin 35, unsaturated polyester resin 4, silicone resin 7, calcium naphthenate 3, dimethylbenzene 20, methylethylketone 5, tetraethylene pentamine 3, MALEIC ANHYDRIDE 6, Mono-n-butyltin 2, peroxidized t-butyl perbenzoate 1, divinyl 9, polypropylene glycol acrylate 5, alkylphenol polyoxyethylene phosphoric acid ester 9, membrane-forming agent 4.
Described membrane-forming agent is made by the raw material of following weight part: phenyl triethoxysilane 2, anilinomethyl triethoxysilane 2, ferrocene 2, aluminium nitride 1, nano-attapulgite 2, epoxy soybean oil 5, morpholine 1, polyisobutene 4;
The preparation method is: by each mixing of materials, be heated to 105-110 ℃, and stirring reaction 2-3 hour, grinding removes slag obtains.
The preparation method of high temperature resistant aminoresin impregnating varnish, comprise the following steps: divinyl 6-9, polypropylene glycol acrylate 4-5, alkylphenol polyoxyethylene phosphoric acid ester, methylethylketone, tetraethylene pentamine, MALEIC ANHYDRIDE, dimethylbenzene are mixed, be heated to 100-105 ℃, drip peroxidized t-butyl perbenzoate, stirring reaction 1-2 hour, then, add other remaining component, continue stirring reaction 2-3 hour, obtain.
Curing process: smoke 3-5 hour under 110 ~ 150 ℃;
It solidifies rear cohesive strength and is greater than 25N, and temperature classification is the H level, and volume specific resistance is not less than 1 * 1014 Ω m, and surface resistivity is not less than 1 * 1014 Ω, and after immersion, volume specific resistance is not less than 1 * 1012 Ω m, and surface resistivity is not less than 1 * 1012 Ω.Impregnating varnish of the present invention can high temperature resistant, high humidity, and electrical insulation capability is good, and physical strength is high, has improved thermal conductivity, but 200 ℃ of long term operations, and 220 ℃ of short-terms, met design requirements.
Claims (2)
1. high temperature resistant aminoresin impregnating varnish is characterized in that being made by the raw material of following weight part:
582-2 aminoresin 32-35, unsaturated polyester resin 3-4, silicone resin 5-7, calcium naphthenate 2-3, dimethylbenzene 20-24, methylethylketone 4-5, tetraethylene pentamine 2-3, MALEIC ANHYDRIDE 4-6, Mono-n-butyltin 1-2, peroxidized t-butyl perbenzoate 1-2, divinyl 6-9, polypropylene glycol acrylate 4-5, alkylphenol polyoxyethylene phosphoric acid ester 9-10, membrane-forming agent 4-5;
Described membrane-forming agent is made by the raw material of following weight part: phenyl triethoxysilane 1-2, anilinomethyl triethoxysilane 1-2, ferrocene 2-3, aluminium nitride 1-2, nano-attapulgite 1-2, epoxy soybean oil 4-5, morpholine 1-2, polyisobutene 3-4;
The preparation method is: by each mixing of materials, be heated to 105-110 ℃, and stirring reaction 2-3 hour, grinding removes slag obtains.
2. the preparation method of high temperature resistant aminoresin impregnating varnish according to claim 1 is characterized in that comprising the following steps:
Divinyl, polypropylene glycol acrylate, alkylphenol polyoxyethylene phosphoric acid ester, methylethylketone, tetraethylene pentamine, MALEIC ANHYDRIDE, dimethylbenzene are mixed, be heated to 100-105 ℃, drip peroxidized t-butyl perbenzoate, stirring reaction 1-2 hour, then, add other remaining component, continue stirring reaction 2-3 hour, obtain.