CN103387357A - Thermal insulation fireproof veneer and manufacturing method thereof - Google Patents
Thermal insulation fireproof veneer and manufacturing method thereof Download PDFInfo
- Publication number
- CN103387357A CN103387357A CN2013103309116A CN201310330911A CN103387357A CN 103387357 A CN103387357 A CN 103387357A CN 2013103309116 A CN2013103309116 A CN 2013103309116A CN 201310330911 A CN201310330911 A CN 201310330911A CN 103387357 A CN103387357 A CN 103387357A
- Authority
- CN
- China
- Prior art keywords
- parts
- thermal insulation
- foaming
- veneer
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a thermal insulation fireproof veneer and a manufacturing method thereof. The thermal insulation fireproof veneer comprises the following components in parts by weight: 80-90 parts of cement, 50-60 parts of coal ash, 1-3 parts of calcium stearate, 3-6 parts of a styrene-acrylic emulsion, 3-8 parts of hydrogen peroxide, 4-8 parts of quick lime, 1-3 parts of aluminum sulfate and 1-3 parts of a foaming agent. The thermal insulation fireproof veneer is formed by foaming an inorganic material, has an environment-friendly effect, is fireproof and high-temperature resistant and belongs to an incombustible material, the fire-resistant temperature can be over 1000 DEG C, the combustion performance is up to the level A1, the fireproof safety performance is excellent, the water absorption rate is low, the veneer is prevented from being mildewed in a humid environment, the thermal insulation performance is not influenced, and the safety and durability of the veneer are guaranteed.
Description
Technical field:
The present invention relates to a kind of insulated fire decoration panel and preparation method thereof, belong to the construction material technical field.
Background technology:
Due to the generation of a lot of building heat preservation event of fire in recent years, caused the thinking of each bound pair insulated fire, the fire resistance of lagging material is beyond example has caused the great attention of all circles in the industry.Yet much lagging material is on fire all produces in construction process, as: electric welding, naked light, bad construction are accustomed to.Thing and toxic smoke are dripped in these materials constantly produce in combustion processes melt, and the gases such as the Chlorofluorocarbons (CFCs) that discharges simultaneously, HFC compound, freonll-11 are also very important to the harm of environment.Present lagging material generally adopts organic polymer to form; high insulating effect; but fire resistance is poor; how to improve the fire resistance of external thermal insulation system; should limit and use the organic lagging material, the compound lagging material of careful use organic-inorganic, develop and promote the use of the mineral-type lagging material; fireproof construction without cavity, fireproof partition and flameproof protection surface layer is set, the variety of issue such as that present inorganic heat insulation material remains is few in kind, heat-insulating property is not good.
Summary of the invention:
The objective of the invention is provides a kind of insulated fire decoration panel and preparation method thereof for the problem of above-mentioned existence, and fire resistance is good, good heat insulating.
Above-mentioned purpose realizes by following technical scheme:
The insulated fire decoration panel comprises by weight: cement 80-90 part, flyash 50-60 part, calcium stearate 1-3 part, benzene emulsion 3-6 part, hydrogen peroxide 3-8 part, unslaked lime 4-8 part, Tai-Ace S 150 1-3 part, whipping agent 1-3 part.
Described insulated fire decoration panel, described whipping agent comprise sodium bicarbonate and the water glass of equivalent.
The making method of insulated fire decoration panel, the method comprises the steps:
(1) material loading, mixing: by weight with cement 80-90 part, flyash 50-60 part, calcium stearate 1-3 part, benzene emulsion 3-6 part, hydrogen peroxide 3-8 part, unslaked lime 4-8 part, Tai-Ace S 150 1-3 part adds stirrer, is dry mixed 1-3 minute;
(2) stir: by weight the water of the 30-45 of 70-80 part ℃ is added stirrer, the wet stirring 2 minutes; Add stirrer to stir 8-15 second 1-3 part whipping agent;
(3) injection molding, foaming: slurry is injected in mould and foams, and foaming process is 2-4 minute approximately;
(4) initial curing: carried out initial curing after injection molding is completed in standing 3-24 hour;
(5) demoulding: treat that the foaming cement thermal insulation plate completes initial set, carry out the demoulding;
(6) cutting: can cut after the demoulding, cut form is adjusted as required cutting blade and is carried out;
(7) finished product maintenance: foaming cement thermal insulation plate curing age should be not less than 4 days.
Beneficial effect:
1. the present invention adopts the inorganic materials foaming to form, environmental protection, fireproof high-temperature resistant, refractory temperature can reach more than 1000 degrees centigrade, combustionproperty is the A1 level, belongs to non-fire material, and the fire safety performance is superior, water-intake rate is low, guarantee that product can not go mouldy under wet environment, can not affect heat-insulating property, guaranteed security, the weather resistance of product.
2. production technique of the present invention is simple, and production cost is low, is applicable to mass industrialized production.
Embodiment:
Embodiment 1:
The insulated fire decoration panel comprises by weight: cement 80-90 part, flyash 50-60 part, calcium stearate 1-3 part, benzene emulsion 3-6 part, hydrogen peroxide 3-8 part, unslaked lime 4-8 part, Tai-Ace S 150 1-3 part, whipping agent 1-3 part.
Embodiment 2:
The described insulated fire decoration panel of embodiment 1, described whipping agent comprises sodium bicarbonate and the water glass of equivalent.
The making method of above-mentioned insulated fire decoration panel, the method comprises the steps:
(1) material loading, mixing: by weight with cement 80-90 part, flyash 50-60 part, calcium stearate 1-3 part, benzene emulsion 3-6 part, hydrogen peroxide 3-8 part, unslaked lime 4-8 part, Tai-Ace S 150 1-3 part adds stirrer, is dry mixed 1-3 minute;
(2) stir: by weight the water of the 30-45 of 70-80 part ℃ is added stirrer, the wet stirring 2 minutes; Add stirrer to stir 8-15 second 1-3 part whipping agent;
(3) injection molding, foaming: slurry is injected in mould and foams, and foaming process is 2-4 minute approximately;
(4) initial curing: carried out initial curing after injection molding is completed in standing 3-24 hour;
(5) demoulding: treat that the foaming cement thermal insulation plate completes initial set, carry out the demoulding;
(6) cutting: can cut after the demoulding, cut form is adjusted as required cutting blade and is carried out;
(7) finished product maintenance: foaming cement thermal insulation plate curing age should be not less than 4 days.
The disclosed technical scheme of the present invention program is not limited only to the disclosed technique means of above-mentioned technical characterictic, also comprises by above technical characterictic and is equal to the technical scheme that replacement forms.Unaccomplished matter of the present invention, belong to those skilled in the art's common practise.
Claims (3)
1. an insulated fire decoration panel, is characterized in that: comprise by weight: cement 80-90 part, flyash 50-60 part, calcium stearate 1-3 part, benzene emulsion 3-6 part, hydrogen peroxide 3-8 part, unslaked lime 4-8 part, Tai-Ace S 150 1-3 part, whipping agent 1-3 part.
2. insulated fire decoration panel according to claim 1, it is characterized in that: described whipping agent comprises sodium bicarbonate and the water glass of equivalent.
3. the making method of an insulated fire decoration panel, it is characterized in that: the method comprises the steps:
(1) material loading, mixing: by weight with cement 80-90 part, flyash 50-60 part, calcium stearate 1-3 part, benzene emulsion 3-6 part, hydrogen peroxide 3-8 part, unslaked lime 4-8 part, Tai-Ace S 150 1-3 part adds stirrer, is dry mixed 1-3 minute;
(2) stir: by weight the water of the 30-45 of 70-80 part ℃ is added stirrer, the wet stirring 2 minutes; Add stirrer to stir 8-15 second 1-3 part whipping agent;
(3) injection molding, foaming: slurry is injected in mould and foams, and foaming process is 2-4 minute approximately;
(4) initial curing: carried out initial curing after injection molding is completed in standing 3-24 hour;
(5) demoulding: treat that the foaming cement thermal insulation plate completes initial set, carry out the demoulding;
(6) cutting: can cut after the demoulding, cut form is adjusted as required cutting blade and is carried out;
(7) finished product maintenance: foaming cement thermal insulation plate curing age should be not less than 4 days.