CN1033789A - 一种无机水泥增强剂 - Google Patents
一种无机水泥增强剂 Download PDFInfo
- Publication number
- CN1033789A CN1033789A CN87101204A CN87101204A CN1033789A CN 1033789 A CN1033789 A CN 1033789A CN 87101204 A CN87101204 A CN 87101204A CN 87101204 A CN87101204 A CN 87101204A CN 1033789 A CN1033789 A CN 1033789A
- Authority
- CN
- China
- Prior art keywords
- cement
- slag
- dihydrate gypsum
- phosphogypsum
- flyash
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种无机水泥增强剂,它主要由活化剂、激化剂
组成,其中活化剂主要是指金属渣。激化剂是指硬石
膏或煅烧二水石膏、磷石膏、二水石膏,将本发明所提
供的增强剂加入到各种类型的水泥中可以在不增加
或减少熟料比的情况下,使其各项性能指标增加,尤
其是在高水泥早期强度,解决水泥安定性不良问题等
方面,效果最佳不仅如此,它还可提高水泥标号,降低
水泥成本,是一种迄今为止较为理想的水泥增强剂。
Description
本发明系属于建筑材料领域,既提供了一种用来提高水泥强度,标号的增强剂。
长期以来,国内外许多人士一直在致力于如何增强水泥标号和提高水泥质量的探索、研究工作,但大多数人都重视生料的配料和熟料的煅烧研究,很少有人在水泥配料中同时加入多种成份的活化剂和激发剂来提高水泥标号。本发明者曾于1985年、1986年分别递交两次专利申请。一份是通过加入活性Al2O3和活性SiO2来提高水泥强度,另一份是通过加入激发剂煅烧石膏来提高水泥强度。上述两份专利申请所提供的方法虽可提高水泥的强度,但确未能解决安定性问题。
本发明的目的是要提供一种既能解决水泥安定性不良问题又能提高水泥强度、标号的增强剂。
本发明合理的选择了活化剂,如铝渣、锰渣、锌渣、磷渣、矾泥、电石渣、赤泥、兰宝石、钡渣、粉煤灰和激发性很强的煅烧二水石膏或硬石膏、磷石膏、二水石膏,这些成分与水泥的熟料作用,发生如下反应:
1、无水硫酸钙与熟料进行水化:
2、硫酸钙、氟化钙与熟料作用:
3、活性SiO2、Al2O5(或P2O5、MnO)与Ca(OH)2作用:
本发明正是同时利用了上述激化、活化和水化反应原理,使加入的激化剂激发活化剂活化。活化后,形成许多可以提高水泥强度的铝酸钙硅酸钙、磷酸钙等。另外水泥熟料中C3S强度最高,是生产高标号水泥必不可少的成分,它水化时生成Ca(OH)2,又与SiO2、Al2O3、P2O5等活化剂作用也生成上述可提高水泥强度的生成物。
本发明所提供的水泥增强剂的成份如下:
1、活化剂:
铝渣 1~5.5% 锰渣 1~5%
锌渣 0.5~4% 磷渣 0.7~4.5%
粉煤灰 0.8~5% 电石渣 1~5%
赤泥 1~7% 兰宝石 0.3~2%
钡渣 0.6~4%
2、激化剂:
硬石膏或煅烧二水石膏 1~7%
磷石膏 1~7% 二水石膏 1~2%
上述各成分可以组成多组增强剂,其中较为理想的效果可由下述三组成分组成获得。(占水泥重量比)
1、磷渣1~4% 铝渣1~5% 矾泥1~6%
荧石1~3% 硬石膏(或烧石膏)1~6%
二水石膏1~2%
其中最佳成分为:
磷渣2.5% 铝渣3% 矾泥3.5%
荧石3% 硬石膏(或烧石膏)4.5%
二水石膏1%
2、磷石膏1~5% 钡渣1~5% 锰渣1~5%
粉煤灰1~5% 电石渣1~5% 赤泥0.5~7%
兰宝石0.3~2%
其中最佳成分为:
磷石膏4% 钡渣2% 锰渣2.5% 粉煤灰1%
电石膏1.5% 赤泥0.5% 兰宝石2%
3、锰渣1~6% 兰宝石1~7% 锌渣1~5%
粉煤灰1~6% 磷石膏1~7% 二水石膏1~2%
其中最佳成分为:
锰渣3% 兰宝石2.5% 锌渣3.5%
粉煤灰4% 磷石膏4% 二水石膏1%
下面给出本发明所提供的三个实施例
实施例1(指占水泥重量比)
一、配料:2.5%磷渣 3%铝渣 3.5%矾泥
3%荧石 4%硬石膏(或烧石膏)
1.5%二水石膏
二、工艺:除烧石膏外,其余均烘干→破碎→配料→湿磨
实施例2(指占水泥重量比)
一、配料:磷石膏4% 钡渣2% 锰渣2.5%
粉煤灰1% 电石膏1.5% 赤泥0.5%
兰宝石2%
二、工艺与实施例1相同
三、性能指标
实施例3(指占水泥重量比)
一、配料:锰渣3% 兰宝石2.5% 锌渣3.5%
粉煤灰4% 磷石膏4% 二水石膏1%
二、工艺与实施例1相同
三、性能指标:
项目 | 熟料用量% | 7天 | 28天 | ||
抗压 | 抗检 | 抗压 | 抗检 | ||
旧技术(常规配方) | 55 | 259 | 65 | 464 | 79 |
实施例3 | 45 | 297 | 64 | 470 | 88 |
由实施例1、2、3可见,采用本发明所提供的水泥增强剂,虽然减少了水平中的熟料比,但确提高了各项性能指标,解决了水泥安定性不良问题,提高了早期强度,凝结时间也较为理想,因此,它是一种既可提高水泥各项性能和水泥标号又可降低成本的新型水泥增强剂。
Claims (3)
1、一种无机水泥增强剂,其特征在于它由活化剂、激化剂组成,其中活化剂是指:
铝渣1~5.5% 锰渣1~5%
锌渣0.5~4% 磷渣0.7~4.5%
粉煤灰0.8~5% 电石渣1~5%
赤泥1~7% 兰宝石0.3~2%
钡渣0.6~4%(占水泥重量比)
激化剂是指:硬石膏或煅烧二水石膏 1~7%
磷石膏 1~7%
二水石膏1~2%(占水泥重量比)。
2、按权利要求1所述的水泥增强剂,其特征在于最佳组成如下:(占水泥重量比)
(1)磷渣1~4% 铝渣1~5%
矾泥1~6% 荧石1~3%
硬石膏(或烧石膏)1~7%
二水石膏1~2%
(2)磷石膏1~7% 钡渣1~5%
锰渣1~5% 粉煤灰1~5%
电石膏1~5% 赤泥0.5~7%
兰宝石0.3~2%
(3)锰渣1~6% 兰宝石1~7%
锌渣1~5% 粉煤灰1~6%
磷石膏1~7% 二水石膏1~2%
3、按权利要求2所述的水泥增强剂,其特征在于最佳成分为:(占水泥重量比)
(1)磷渣2.5% 铝渣3% 矾泥3.5% 荧石3%
硬石膏(或烧石膏)6% 二水石膏2%
(2)磷石膏6% 钡渣2% 锰渣2.5% 粉煤灰1%
电石渣1.5% 赤泥0.5% 兰宝石2%
(3)锰渣3% 兰宝石2.5% 锌渣3.5%
粉煤灰4% 磷石膏5% 二水石膏1%