CN103372565A - Manufacturing method of 28 mm diameter specification of steel wire rods and through high-speed wire rod production line - Google Patents
Manufacturing method of 28 mm diameter specification of steel wire rods and through high-speed wire rod production line Download PDFInfo
- Publication number
- CN103372565A CN103372565A CN2012101293918A CN201210129391A CN103372565A CN 103372565 A CN103372565 A CN 103372565A CN 2012101293918 A CN2012101293918 A CN 2012101293918A CN 201210129391 A CN201210129391 A CN 201210129391A CN 103372565 A CN103372565 A CN 103372565A
- Authority
- CN
- China
- Prior art keywords
- pass
- speed
- unit
- reducing unit
- production line
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a manufacturing method of 28 mm diameter specification of steel wire rods and through a high-speed wire rod production line. The manufacturing method includes that a, rolled pieces enter into a reducing unit to be rolled after passing through a plurality of roughing rolling units and a plurality of front finishing rolling units; b, the rolled pieces overleap a sizing unit after rolling of the reducing unit in the step a; c, the rolled pieces are conveyed to a laying head to spin in circles though a pinch roll to form into products of the steel wire rods after the rolled pieces achieve the step b. In the process of spinning in circles, the raising speed rate of the reducing unit, the sizing unit, the pinch roll and the tail portion of the laying head is arranged to be 1.14 to 1.15 meters per square second, the advance coefficient of the laying head is arranged to be 0.990 to 1.005, and the rolling speed of the reducing unit is arranged to be at least 8.0 meters per second. The manufacturing method of the 28 mm diameter specification of steel wire rods and through the high-speed wire rod production line can achieve production of extra-large specification of steel wire rods.
Description
Technical field
The present invention relates to steel wire rod product manufacture, is a kind of method of utilizing high-speed wire production line to prepare 28 mm dia specification wire rods.
Background technology
At present, 28 mm dia specifications
Unique manufacture approach of gren rod be to adopt to coil greatly technique.That coils greatly technique mainly is equipped for bar mill and machine for coiling large bundle of wire.Technological process by middle milling train or pre-quiet milling train group or coil greatly reducing sizing mill group (comprise tube reducing unit appraise and decide footpath unit) and prepare finished product, then through appropriate temperature control, is batched moulding by coiling machine at first.But, for the enforcement of coiling greatly technique, need to upgrade the existing equipment of steel industry, and the new production line that is consisted of by bar mill and machine for coiling large bundle of wire of acquisition price costliness again, this need to expend several hundred million at least fund inputs.
Therefore, if can utilize existing equipment to carry out the preparation of 28mm diameter specifications wire rod, then can greatly save the production cost of enterprise.In iron and steel is produced, existing high-speed wire production line can be used for wire rod production, the horizontal Laying head that high-speed wire production line comprises high-speed rod-rolling mill and is positioned at this high-speed rod-rolling mill rear end, it at first carries out roughing and finish rolling by high-speed rod-rolling mill to product, and finally produce finished product by the reducing sizing mill group of mm finishing mill unit rearmost end, again through after the control of appropriate temperature, by the Laying head lopping of weaving silk.The high speed that high-speed wire production line can satisfy the wire rod product prepares requirement, and still, the conventional fertile limit gren rod specification of high-speed wire production line of using is at present
And utilize high-speed wire production line to prepare the 28mm diameter specifications, then there is many difficulties, so do not implement in the industry.These difficulties comprise:
(1) lacks the pass technique of 28mm diameter specifications.Although existing bar produces line or coils greatly and produces line and have ripe
The round steel pass parameters, but since its finished product and finished product forebay be the relatively large roll in roller footpath (
Deng) or collars (
Deng), and high-speed rod-rolling mill finished product and finished product forebay be pony roll footpath collars (
Deng), collars width and rolling centerline require to have limited this important pass parameters of pass width, thereby make the existing bar produce line or coil greatly and produce line
The pass parameters of round steel is not suitable for high-speed rod and produces line.
As shown in Figure 1 and Figure 2, be respectively certain bar and produce line
Round steel finished hole K1 and leader pass K2 pass schematic diagram.Wherein K1 hole pass width B K1 is 30.6mm, and pass height HK2 is 28.6mm; K2 hole pass width B K2 is 52.0mm, and pass height HK2 is 23.8mm.As shown in Figure 3, be configured in for this leader pass K2
Schematic diagram behind the collars, wherein collars width B 3 is 72mm, rolling center line distance is 22.225mm from collars edge L3.As shown in Figure 3, BK3/2 (52/2=26mm)>L3 (22.225mm), obviously, this leader pass K2 can't be configured in
On the collars.If realize that leader pass exists
Configuration on the collars must be carried out to it redesign of pass parameters, yet, because
The size of collars is less, if therefore realize configuration, must reduce the axial ratio (being pass width and ratio highly, such as the BK2/HK2 among Fig. 2) of pass., be designed with particular requirement for the pass axial ratio in industry, when the design of oval-shaped leader pass, its axial ratio usually can not be less than 1.7, otherwise with influence of rolled stability.For
Collars will be realized the successful configuration of leader pass, and then axial ratio obviously can not satisfy this requirement.
(2) the Laying head ability remains to be tested.Up to now, horizontal Laying head can batch maximum gauge and is
Wire rod, and if in the production process parameter improper meeting be set the afterbody poor quality problems of cast of weaving silk occur.In addition, produce
Laying head afterbody raising speed slope has reached design limit during specification.
Can specification remain to be tested through the smooth lopping of Laying head.
Because above difficulty did not attempt in the industry existing high-speed wire production line is used for the preparation of 28mm diameter specifications specification wire rod.
Summary of the invention
Purpose of the present invention is to overcome existing high-speed wire production line and carries out the above-mentioned difficulties of 28mm diameter specifications wire rod when preparing, thereby provides a kind of high-speed wire production line that utilizes of innovation to prepare 28 mm dia specifications
The method of wire rod.
The invention provides a kind of high-speed wire production line preparation that utilizes
The method of wire rod, this high-speed wire production line comprises a plurality of roughing units, a plurality of mm finishing mill unit and Laying head, tube reducing unit and sizing unit that these a plurality of mm finishing mill unit comprise a plurality of front mm finishing mill unit that is positioned at front end and are positioned at the rear end, the rolled piece product by these a plurality of roughing units and this a plurality of mm finishing mill unit carry out respectively the rolling and finish rolling of roughing rolling after, enter the lopping of weaving silk of this Laying head through pinch roll, form final wire rod product, the method comprises the steps:
A, after rolled piece these a plurality of roughing units of process and these a plurality of front mm finishing mill unit, entering this tube reducing unit is rolled, wherein, this tube reducing unit comprises the front passage of finished product and final pass, and the leader pass type before this finished product in the passage is set to single false ellipse pass, wherein the pass radius of this leader pass type is set to 21.62~23.23mm, the pass width is set to 38.26~40.0mm, and pass height is set to 22.56~25.71mm, and roll gap is set to 1.60~2.20mm; And the last groove in this final pass is set to double radius expansion circular arc circular hole, wherein the radius of this last groove is set to 14.20~14.28mm, the pass width is set to 29.69~30.07mm, pass height is set to 28.20~28.56mm, and roll gap is set to 1.40~2.00mm;
B, rolled piece in step a through behind tube reducing unit rolling, empty this sizing unit of crossing;
C behind the rolled piece completing steps b, is conveyed into the lopping of weaving silk of this Laying head by this pinch roll, and to form the wire rod product, in this weaved silk knitting cycle, the raising speed speed of this tube reducing unit, this pinch roll and this Laying head afterbody was set to 1.14~1.15m/S
2, the leading coefficient of this Laying head is set to 0.990~1.005, and the mill speed of this tube reducing unit is set to be not less than 8.0m/s.
Preferably, described tube reducing unit is duo mill, and passage and final pass all adopt before the described finished product
The collars of specification.
The high-speed wire production line that utilizes of the present invention prepares
The method of wire rod, by to the redesign of tube reducing unit mesothyrid size in the high-speed wire production line and to the adjustment of rolling mill practice, not increasing or transforming under the prerequisite of main equipment, can realize the manufacture of super large-scale wire rod, the upper limit of range of product size is extended to
Thereby realized
The high-speed production of wire rod product has increased the profit of enterprise.
Description of drawings
Fig. 2 is that certain bar produces line among Fig. 1
The pass schematic diagram of size round steel leader pass;
Fig. 3 is configured in the high-speed wire production line for the pass with the leader pass among Fig. 2
Schematic diagram on the collars;
Fig. 4 is the high-speed wire production line preparation that utilizes of the present invention
The schematic flow sheet of the method for wire rod;
Fig. 5 is for arranging in the present invention the schematic flow sheet of finished hole and each parameter of leader pass;
Fig. 6 is the schematic diagram of leader pass type in the front passage of finished product;
Fig. 7 is the schematic diagram of last groove in the final pass;
Fig. 8 is that the leader pass type is configured in the schematic diagram on the collars in the front passage of finished product;
Fig. 9 is that last groove is configured in the schematic diagram on the collars in the final pass.
The specific embodiment
Below in conjunction with the drawings and specific embodiments, the high-speed wire production line that utilizes of the present invention is prepared
The method of wire rod is elaborated.
Generally, the present invention is by improving existing high-speed wire production line, and auxiliary technological parameter with necessity, thereby has realized high-speed wire production line successfully is applied to
The manufacture of wire rod has overcome to achievement and has thought in the industry that this production line can not be used for
The technology prejudice that wire rod is produced.
For this high-speed wire production line, it comprises a plurality of roughing units, a plurality of mm finishing mill unit and Laying head, tube reducing unit and sizing unit that these a plurality of mm finishing mill unit comprise a plurality of front mm finishing mill unit that is positioned at front end and are positioned at the rear end, the rolled piece product by these a plurality of roughing units and this a plurality of mm finishing mill unit carry out respectively the rolling and finish rolling of roughing rolling after, enter the lopping of weaving silk of this Laying head through pinch roll, form final wire rod product.
Further, in conjunction with Fig. 4, the high-speed wire production line that utilizes of the present invention prepares
The method of wire rod comprises step S100-S300, in step S100, after rolled piece process roughing and front finish rolling are processed, enter the tube reducing unit and be rolled, and, pass in the tube reducing unit is through after the customized configuration, so that the product that is transferred out by the tube reducing unit meets the predetermined dimension requirement; In step S200, behind the rolled piece process tube reducing unit, the empty sizing unit of crossing; In step S300, rolled piece is conveyed into the Laying head processing of weaving silk, to finish the final processing of coiling under specific setting parameter.Below in conjunction with accompanying drawing, the technological process in the above step and setting parameter are described in more detail.
Step S100
Particularly, in conjunction with Fig. 6, Fig. 7, in this step, after rolled piece these a plurality of roughing units of process and these a plurality of front mm finishing mill unit, entering this tube reducing unit is rolled, wherein, this tube reducing unit comprises the front passage of finished product and final pass, leader pass type before this finished product in the passage is set to single false ellipse pass, wherein, and as shown in Figure 6, the pass radius R 4 of this leader pass type is set to 21.62~23.23mm, pass width B K4 is set to 38.26~40.0mm, and pass height HK4 is set to 22.56~25.71mm, and roll gap S4 is set to 1.60~2.20mm; And the last groove in this final pass is set to double radius expansion circular arc circular hole, wherein the radius R 5 of this last groove is set to 14.20~14.28mm, pass width B K5 is set to 29.69~30.07mm, pass height HK5 is set to 28.20~28.56mm, and roll gap S5 is set to 1.40~2.00mm.
As shown in Figure 5, be the flow chart that the last groove in this step and leader pass type are designed.In the design of last groove and leader pass type, need to consider that the ability, collars width of equipment are to the conditions such as configuration requirement of pass.Particularly, as shown in Figure 5, when carrying out two kinds of pass designs, can utilize the flow process shown in step S1 to S11, finally determine the pass design parameter of last groove and leader pass type.
As previously mentioned, it has been generally acknowledged that in the industry and the Traditional Textbooks that for the leader pass type, the pass axial ratio can not be too little, with the normal operation that guarantees each equipment and final compact dimensions.
For example, Zhao Songjun, Tang Wenlin " Pass design " (Beijing: metallurgical industry publishing house,, the 321st page in 2005) of writing is mentioned:
" the non-axial section pass design universal process that waits.After axis hole type design finishes, non-pass such as axial section such as grade in the middle of next will design.Method for designing adopts known two passes such as axial section such as grade to ask the middle non-method that waits the axial section pass, hereinafter to be referred as the design of flat hole.The design of flat hole has again two kinds of situations, and one is flat hole of folder between two types such as axis hole such as grade, and namely twice shut out one and wait axial section; Another is two flat holes such as folder such as two axial sections such as grade, and namely three roads shut out one and wait axial section.
The target of flat hole design is: obtain a flat rolled piece, make it rolling in next pass after, obtain waiting the axial section rolled piece; To the fixed rotating speed tandem mill, also require each frame heap of assurance to establish unprincipled connection, should guarantee workpiece measurement, guarantee again to pile and establish unprincipled connection, the target of pursuit is not unique.Sometimes also to consider the axial ratio in flat hole, when flat hole axial ratio greater than 2.8 the time, reduce axial ratio as far as possible.And when axial ratio less than 2 the time, then should strengthen axial ratio as far as possible.”
(the 107th page) further mentioned in this book:
" the design of B leading oval pass
The formation parameter of oval groove is referring to table 4-7, the height H of its pass
KTo determine its width dimensions B by minimum round steel diameter d
KDetermine its B by maximum round steel diameter D
KAnd H
KWith the relation of D and d shown in table 4-7.When just design, preferably make H
KBe worth less so that adjust and necessary modification.
Its H of the 4-7 oval groove size that declines
KAnd B
KRelation with D and d
”
And among the present invention for
The specification wire rod is not considered the sharing nature of oval groove, therefore, and D=d=28mm.According to above-mentioned instruction, with the table in the empirical equation recommended parameter bring into after, the scope that can get the axial ratio of leader pass type is: 1.73~1.98, specifically be calculated as follows shown in the table 1:
Table 1: the leader pass profile shaft that utilizes the textbook training centre to calculate compares scope
BK4(28mm) | 1.38 | 1.78 |
HK4(28mm) | 0.80 | 0.9 |
BK4/HK4 | 1.73 | 1.98 |
For the leader pass type among the present invention, its pass width B K4 is 38.26~40.0mm, and pass height HK4 arranges 22.56~25.71mm, and therefore, the scope of pass axial ratio BK4/HK4 is 1.56~1.70.According to the instruction of textbook, this is less than axial ratio scope of usually considering in the industry, and still, the axial ratio scope of utilizing the present invention to design but can realize stable rollingly, and has guaranteed the requirement of dimensional accuracy.And just because of instruction and the usage of trade of textbook, do not attempt in the industry being suitable for limiting value and be
The high-speed wire production line of specification wire rod is applied to
On the manufacture of specification wire rod.The present invention is to the axial ratio design of leader pass type, and it is conventional to have broken through industry, has overcome industry prejudice, and has obtained beyond thought effect.
In embodiments of the present invention, preferably, described tube reducing unit is traditional duo mill, and namely passage and final pass are comprised of one group of roller-way respectively before the finished product in the tube reducing unit, and passage and final pass all adopt before the described finished product
The collars of specification.As shown in Figure 8, be configured in before the finished product schematic diagram on the collars in the passage for the leader pass type; Be illustrated in figure 9 as last groove and be configured in the schematic diagram on the collars in the final pass.As seen from Figure 8, because adopted the design of less axial ratio, the therefore configuration in Fig. 3, the leader pass type among the present invention can successfully be configured in
On the collars of specification.
In addition, in this step, taken into full account the sharing nature of roughing unit pass in the rough rolling process, therefore, the pass in the roughing unit still adopts original parameter.
Step S200
In this step, rolled piece in step S100 through behind tube reducing unit rolling, empty this sizing unit of crossing.
In step S100, rolling by in passage and the final pass before the finished product in the tube reducing unit transfers out dimensional accuracy and is
Therefore the product of specification, when product passes through the sizing unit, only needs empty this sizing unit of crossing, and namely the sizing unit is not rolled processing to product.In production practices, the accident that quick-fried collars occurs the sizing unit is much higher than the tube reducing unit, especially for leading oval pass design of the present invention, the Edge Distance ellipse pass edge of collars that disposes this oval groove is very little, therefore, if when being configured in the sizing unit, then be easy to cause the risk of collars cracking or explosion.So the empty mistake of sizing unit is not rolled processing to product, the purpose of doing like this is to eliminate the risk of sizing unit generation collars cracking or explosion.Therefore, in the present invention, selected to carry out last groove and the adjustment of leader pass type in the tube reducing unit, so that product is when sending from the tube reducing unit, its specification meets the requirements, and by sizing unit space-time mistake, carries out with the safety that guarantees production process.
Step S300
In this step, rolled piece is conveyed into the lopping of weaving silk of this Laying head by this pinch roll, to form final wire rod product behind completing steps S200, in this weaved silk knitting cycle, the raising speed speed of this tube reducing unit, this pinch roll and this Laying head afterbody was set to 1.14~1.15m/S
2, the leading coefficient of this Laying head (be the ratio of Laying head speed and mill speed, this value is set the whether reasonable and direct cast that affects wire rod) is set to 0.990~1.005, and the mill speed of this tube reducing unit is set to be not less than 8.0m/s.
When rolled piece by behind the sizing unit, need to carry out above setting to the raising speed speed of tube reducing unit, this sizing unit and this Laying head afterbody, the leading coefficient of Laying head and the mill speed of tube reducing unit, with guarantee Laying head can be successfully with
The operation of weaving silk of the product of specification is coiled processing to finish smoothly.
Utilize the present invention, can successfully realize high-speed wire production line pair
The production of specification wire rod, and produce
The dimensional accuracy of specification wire rod and quality satisfy " deviation of GB/T14981-2004 gren rod size, profile, weight and permission " standard, meet user's instructions for use.
For example, in one embodiment, utilize production of the present invention
The low-alloy the cold heading steel of specification.Mill speed 8.0m/s; Finished hole is set roll gap 1.60mm, pass width 29.85mm, pass height 28.40mm; Leader pass intermesh determination 2.00mm, pass width 38.58mm, pass height 25.52mm.Rolled piece smooth excessively steel and the lopping of weaving silk, cast is good.The rolling line apparatus of load is at controlled area charactert.The wire rod diameter deviation of producing is-0.22~+ 0.20mm, out-of-roundness is 0.42mm, has reached C level dimensional accuracy standard among the GB/T 14981-2004.Wire rod surface quality, tissue, functional satisfy SAE J403 standard, meet user's instructions for use.
In another embodiment, produce
Specification carbon element the cold heading steel, 124 tons of rolling tonnages.Mill speed 8.0m/s; Finished hole is set roll gap 1.50mm, pass width 29.85mm, pass height 28.30mm; The leader pass intermesh determination is 2.20mm, pass width 38.58mm, pass height 25.72mm.Rolled piece smooth excessively steel and the lopping of weaving silk, cast is good.The rolling line apparatus of load is at controlled area charactert.The wire rod diameter deviation of producing is-0.35~+ 0.23mm, out-of-roundness is 0.58mm, has reached GB/T 14981-2004B level dimensional accuracy standard.Wire rod surface quality, tissue, functional satisfy Q/BQB 517 standards, meet user's instructions for use.
In sum, the high-speed wire production line that utilizes of the present invention prepares
The method of wire rod, overcome industry prejudice, by to the redesign of tube reducing unit mesothyrid size in the high-speed wire production line and to the adjustment of rolling mill practice, do not increasing or transforming under the prerequisite of main equipment, can realize the manufacture of super large-scale wire rod, the upper limit of range of product size is extended to
Thereby realized
The high-speed production of wire rod product has increased the profit of enterprise.
Claims (2)
1. method of utilizing high-speed wire production line to prepare 28 mm dia specification wire rods, this high-speed wire production line comprises a plurality of roughing units, a plurality of mm finishing mill unit and Laying head, tube reducing unit and sizing unit that these a plurality of mm finishing mill unit comprise a plurality of front mm finishing mill unit that is positioned at front end and are positioned at the rear end, the rolled piece product by these a plurality of roughing units and this a plurality of mm finishing mill unit carry out respectively the rolling and finish rolling of roughing rolling after, enter the lopping of weaving silk of this Laying head through pinch roll, form final wire rod product, it is characterized in that the method comprises the steps:
A, after rolled piece these a plurality of roughing units of process and these a plurality of front mm finishing mill unit, entering this tube reducing unit is rolled, wherein, this tube reducing unit comprises the front passage of finished product and final pass, and the leader pass type before this finished product in the passage is set to single false ellipse pass, wherein the pass radius of this leader pass type is set to 21.62~23.23mm, the pass width is set to 38.26~40.0mm, and pass height is set to 22.56~25.71mm, and roll gap is set to 1.60~2.20mm; And the last groove in this final pass is set to double radius expansion circular arc circular hole, wherein the radius of this last groove is set to 14.20~14.28mm, the pass width is set to 29.69~30.07mm, pass height is set to 28.20~28.56mm, and roll gap is set to 1.40~2.00mm;
B, rolled piece in step a through behind tube reducing unit rolling, empty this sizing unit of crossing;
C behind the rolled piece completing steps b, is conveyed into the lopping of weaving silk of this Laying head by this pinch roll, and to form the wire rod product, in this weaved silk knitting cycle, the raising speed speed of this tube reducing unit, this pinch roll and this Laying head afterbody was set to 1.14~1.15m/S
2, the leading coefficient of this Laying head is set to 0.990~1.005, and the mill speed of this tube reducing unit is set to be not less than 8.0m/s.