CN103356082A - Production process of pink glass liner - Google Patents
Production process of pink glass liner Download PDFInfo
- Publication number
- CN103356082A CN103356082A CN2013103297369A CN201310329736A CN103356082A CN 103356082 A CN103356082 A CN 103356082A CN 2013103297369 A CN2013103297369 A CN 2013103297369A CN 201310329736 A CN201310329736 A CN 201310329736A CN 103356082 A CN103356082 A CN 103356082A
- Authority
- CN
- China
- Prior art keywords
- glass liner
- glass
- pink
- raw material
- blank
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the process of a glass liner, in particular to a production process of a pink glass liner, which is characterized by comprising the steps of first selecting raw materials for preprocessing the raw materials; then placing the preprocessed raw materials into a smelting furnace for fusing; continuously heating until solution is clear enough for blowing a glass liner; blowing two glass liners by a blowing machine; sealing the bottoms and the mouths of the two glass liners together by a sealing machine, and connecting a vacuumized tail to the bottom of a blank; filling silver plating solution between the glass liners through the tail, rotating the blank to enable the sliver plating to be uniform, and then cleaning and drying; vacuuming the blank on a vacuumizing table, scorifying the vacuum tail and stretching a tip to be cut off; carrying out heat treatment to change the state of the internal structure of the glass liner; and finally checking whether the pink glass liner is qualified or not. The production process has the advantages that the phenomenon of piece dropping inside the glass liner is avoided; the glass liner is low in expansion factor, thereby being nonbreakable; a health care effect is realized; the glass liner is pink, so that the attractive effect is realized; and the market requirements are met.
Description
Technical field
The present invention relates to glass liner technique, be specifically related to a kind of production technology of pink glass liner.
Background technology
Glass liner is double-deck, in vacuumize, make the inside heat be not easy to be passed out.The nexine periphery of courage also scribbles argent, is reflected also by silver mirror and can play heat insulation effect thereby hot water has again most in glass liner interior heat amount in the process that outwards runs off.The glass liner undercoating generally is silver-plated (silver mirror), utilizes silver mirror reaction to plate.(aluminium mirror) or ion vacuum plated film (tungsten mirror or the titanium mirror) glass liner of also aluminizing now.
Traditional explained hereafter glass liner, the inner flake of the easy glass liner of meeting, the coefficient of expansion is high, and easily fragmentation, and traditional glass liner just just is used for being filled with water, insulation effect, some special-shaped glass liners play certain artistic effect, and are still not with health role.
Summary of the invention
In order to address the above problem, the present invention proposes a kind of production technology of pink glass liner, glass liner is with health role, and the coefficient of expansion reduces, and inside occurs without flake.
In order to reach the foregoing invention purpose, the present invention proposes following technical scheme:
The production technology of pink glass liner specifically is following steps:
A, at first choose the glass liner raw material that need, carry out the raw material preprocessing and process, raw material are pulverized dry, the iron content raw material are carried out deironing process;
After B, the pre-treatment of raw material, put into smelting furnace and carry out heat fused, raw material begin fusion reaction, generate gaseous volatilization;
C, continuation heat up, and solution viscosity diminishes, and residual bubble is got rid of in the solution, and solution begins to clarify the state that can blow glass liner that reaches;
D, dip solution with mechanical blow-and-blow machine, be blow molded into two kinds of glass liners, small one and large one;
E, two kinds of glass liners are nested together, use sealing machine that two glass liners bottoms and oral area are sealed, burn warm pull-uply in the time of sealing while rotating, connect a tail that vacuumizes in the bottom of blank;
F, inject silver-plated molten material in the middle of the glass liner by tail, the blank rotation so that silver-plated evenly, then clean, dry;
G, then blank is put on the vacuum pumping stations, vacuumizes, and scorification vacuum tail, the point that stretches cuts off;
Stress, phase-splitting or the crystallization of glass liner inside eliminated or produced to H, heat treatment by annealing, quenching technical,, and change glass liner internal structure state;
I, check pink glass liner whether qualified at last.
Glass liner raw material described in the A step are borax powder, selenium powder, quartz sand, soda ash, feldspar and lime stone.
Smelting furnace described in the B step is electric smelting furnace.
Furnace heats temperature described in the B step is 900-1000 ℃, and raw material begin fusion reaction.
Continuing described in the C step is warmed up to 1400-1500 ℃, the beginning settled solution.
Described glass liner pinkiness.
Advantage of the present invention is to use special production technology to produce glass liner, and glass liner inside does not have flake; The glass liner coefficient of expansion is low, is difficult for broken; In raw material, add a certain amount of selenium element, so that glass liner can have health-care effect to human body, can improve body immunity; Anti-oxidant, delay senility; The protection repair cell; Participate in the treatment of diabetes; Cancer-resisting; The protection eyes; Improve erythrocytic oxygen carrying capacity; The control cardiovascular and cerebrovascular disease; Detoxifcation, gas defence, antipollution; The protection liver; Glass liner outward appearance pinkiness has aesthetic; Meet the need of market.
The specific embodiment
For the present invention is described in detail, implementation is as follows:
A, at first choose glass liner raw material borax powder, selenium powder, quartz sand, soda ash, feldspar and the lime stone that needs, carry out the raw material preprocessing and process, raw material are pulverized dry, the iron content raw material are carried out deironing process;
After B, the pre-treatment of raw material, put into the electric smelting furnace stove and be heated to 900-1000 ℃ of fusion, raw material begin fusion reaction, generate gaseous volatilization;
1400-1500 ℃ of C, continuation intensification, solution viscosity diminishes, and residual bubble is got rid of in the solution, and solution begins to clarify the state that can blow glass liner that reaches;
D, dip solution with mechanical blow-and-blow machine, be blow molded into two kinds of glass liners, small one and large one;
E, two kinds of glass liners are nested together, use sealing machine that two glass liners bottoms and oral area are sealed, burn warm pull-uply in the time of sealing while rotating, connect a tail that vacuumizes in the bottom of blank;
F, inject silver-plated molten material in the middle of the glass liner by tail, the blank rotation so that silver-plated evenly, then clean, dry;
G, then blank is put on the vacuum pumping stations, vacuumizes, and scorification vacuum tail, the point that stretches cuts off;
Stress, phase-splitting or the crystallization of glass liner inside eliminated or produced to H, heat treatment by annealing, quenching technical,, and change glass liner internal structure state;
I, check pink glass liner whether qualified at last.
Claims (6)
1. the production technology of pink glass liner is characterized in that following steps:
A, at first choose the glass liner raw material that need, carry out the raw material preprocessing and process, raw material are pulverized dry, the iron content raw material are carried out deironing process;
After B, the pre-treatment of raw material, put into smelting furnace and carry out heat fused, raw material begin fusion reaction, generate gaseous volatilization;
C, continuation heat up, and solution viscosity diminishes, and residual bubble is got rid of in the solution, and solution begins to clarify the state that can blow glass liner that reaches;
D, dip solution with mechanical blow-and-blow machine, be blow molded into two kinds of glass liners, small one and large one;
E, two kinds of glass liners are nested together, use sealing machine that two glass liners bottoms and oral area are sealed, burn warm pull-uply in the time of sealing while rotating, connect a tail that vacuumizes in the bottom of blank;
F, inject silver-plated molten material in the middle of the glass liner by tail, the blank rotation so that silver-plated evenly, then clean, dry;
G, then blank is put on the vacuum pumping stations, vacuumizes, and scorification vacuum tail, the point that stretches cuts off;
Stress, phase-splitting or the crystallization of glass liner inside eliminated or produced to H, heat treatment by annealing, quenching technical,, and change glass liner internal structure state;
I, check pink glass liner whether qualified at last.
2. the production technology of pink glass liner according to claim 1 is characterized in that the glass liner raw material described in the A step are borax powder, selenium powder, quartz sand, soda ash, feldspar and lime stone.
3. the production technology of pink glass liner according to claim 1 is characterized in that the smelting furnace described in the B step is electric smelting furnace.
4. the production technology of pink glass liner according to claim 1 is characterized in that the furnace heats temperature described in the B step is 900-1000 ℃, and raw material begin fusion reaction.
5. the production technology of pink glass liner according to claim 1 is characterized in that continuing described in the C step is warmed up to 1400-1500 ℃, the beginning settled solution.
6. the production technology of pink glass liner according to claim 1 is characterized in that described glass liner pinkiness.