CN103351613A - Conductive nylon - Google Patents
Conductive nylon Download PDFInfo
- Publication number
- CN103351613A CN103351613A CN2013102871553A CN201310287155A CN103351613A CN 103351613 A CN103351613 A CN 103351613A CN 2013102871553 A CN2013102871553 A CN 2013102871553A CN 201310287155 A CN201310287155 A CN 201310287155A CN 103351613 A CN103351613 A CN 103351613A
- Authority
- CN
- China
- Prior art keywords
- weight parts
- parts
- conductive nylon
- ethylene
- tynex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to conductive nylon which comprises the following components in parts by weight: 40-70 parts of polyamide fibers, 3-8 parts of an interface coupling agent, 3-10 parts of a toughening agent, 0.5-1.0 part of a disperse lubricating agent, 5-10 parts of vanadium dioxide and 10-15 parts of tin dioxide. The conductive nylon is excellent in conductivity and can be widely used for manufacturing auto parts in the automobile industry, parts in the household appliance industry, parts in the building decoration industry, daily necessities such as safety helmets, motorcycle baffles, shoe heels, snow sports products, toys, clocks, sound box shells, suitcases, buttons and cosmetic boxes, and advertisement products such as nameplates and decorations.
Description
Technical field
The present invention relates to the nylon field, specifically, the present invention relates to a kind of conductive nylon.
Background technology
Tynex is commonly called as nylon, its purposes is very extensive, automotive industry is usually used in making automobile component such as dashboard, vehicle-body outer panel, inner trim panels, bearing circle, insulating board, door lock, collision bumper, vent-pipe etc., household electric appliances are usually used in making such as refrigerator, televisor, washing machine, vacuum cleaner, food mixer, the housing of telephone set etc., be usually used in making such as sanitary apparatus at architectural decoration, the swimming pool lining, tubing and pipe fitting etc. are in addition also for the manufacture of safety helmet, the motorcycle plate washer, heel, the snowfield sporting goods, toy, clock, casing of loudspeaker box, suitcase, button, daily necessities and the nameplates such as minaudiere, the advertising matters such as ornament.
Although tynex is widely used, because the characteristic of the molecular structure performance of tynex own, so that tynex is not enough aspect electroconductibility.
Summary of the invention
The object of the present invention is to provide a kind of conductive nylon.
In order to realize purpose of the present invention, the invention provides a kind of conductive nylon, comprise the component of following weight parts:
Tynex 40~70 weight parts;
Interface coupling agent 3~8 weight parts;
Toughner 3~10 weight parts;
Dispersed lubricant 0.5~1.0 weight part;
Vanadium dioxide 5~10 weight parts;
Tindioxide 10~15 weight parts.
Preferably, described interface coupling agent is γ-aminopropyl triethoxysilane (KH550), γ-glycidyl ether oxygen propyl trimethoxy silicane (KH560), γ-(methacryloxypropyl) propyl trimethoxy silicane (KH570), tynex grafting toxilic acid (tynex-g-MAH), styrene-maleic anhydride copolymer (SMA), Research of Grafting Malaic Anhydride Onto Polyethylene (LDPE-g-MAH), linear low density polyethylene grafted maleic anhydride (LLDPE-g-MAH), in the Racemic glycidol ether type epoxy one or more.
Preferably, described toughner is MBS (MBS), MBS, hydrogenated styrene/Butadiene/Styrene) in the segmented copolymer (SEBS) one or more.
Preferably, described dispersed lubricant is one or more in glyceryl monostearate, Tristearoylglycerol, ethylene bis stearamide, the bimonthly osmanthus of ethylene acid amides, the two amine hydroxybenzenes of ethylene, lower molecular weight ionomer, ethylene-acrylic acid copolymer, the ethylene-vinyl acetate copolymer.
More preferably, conductive nylon of the present invention comprises the component of following weight parts:
Tynex 60 weight parts;
γ-aminopropyl triethoxysilane 5 weight parts;
MBS 5 weight parts;
Glyceryl monostearate 0.8 weight part;
Vanadium dioxide 8 weight parts;
Tindioxide 13 weight parts.
Conductive nylon of the present invention has excellent electroconductibility, can be widely used for automotive industry and be usually used in making daily necessities and the advertising matters such as nameplate, ornament such as automobile component, household electric appliances, architectural decoration, safety helmet, motorcycle plate washer, heel, snowfield sporting goods, toy, clock, casing of loudspeaker box, suitcase, button, minaudiere.
Embodiment
Below the invention will be further described for the description by embodiment, but this is not to be limitation of the present invention, those skilled in the art are according to basic thought of the present invention, can make various modifications or improvement, but only otherwise break away from basic thought of the present invention, all within the scope of the present invention.
Embodiment 1
It is lower dry 4 hours in 90 ℃ to take by weighing 600 tynexs that restrain, then with vanadium dioxide 80 grams, tindioxide 130 grams, γ-aminopropyl triethoxysilane 50 grams, MBS 50 grams and glyceryl monostearate 8 grams, in homogenizer, stirred 5 minutes with 1100 rev/mins, after evenly, emit.To add length-to-diameter ratio (L/D) be in 40 the twin screw extruder mixing equal materials of spoon, the processing temperature of twin screw extruder: 180 ℃ of district's temperature, two district's temperature are 185 ℃, three district's temperature are 195 ℃, and four district's temperature are 210 ℃, and five district's temperature are 215 ℃, six district's temperature are 225 ℃, seven district's temperature are 235 ℃, and eight district's temperature are 240 ℃, and engine speed is 320 to turn/min; Cool off check rod, air-dry pelletizing through after extruding, namely prepare conductive nylon of the present invention.
Embodiment 2
According to preparing conductive nylon with embodiment 1 identical mode, difference is not use vanadium dioxide.
Embodiment 3
According to preparing conductive nylon with embodiment 1 identical mode, difference is not use tindioxide.
Experimental example
Carry out test surfaces resistivity by the IEC60093 requirement, the result is as follows: the surface resistivity of the conductive nylon of embodiment 1 (Ω) is 1.5 * 10
4, the surface resistivity of the conductive nylon of embodiment 2 (Ω) is 4.3 * 10
6, the surface resistivity of the conductive nylon of embodiment 3 (Ω) is 3.6 * 10
6Surface resistivity is larger, illustrates that electroconductibility is lower.This shows, add vanadium dioxide and tindioxide and produced unexpectedly synergy.
Claims (5)
1. a conductive nylon is characterized in that, comprises the component of following weight parts:
Tynex 40~70 weight parts;
Interface coupling agent 3~8 weight parts;
Toughner 3~10 weight parts;
Dispersed lubricant 0.5~1.0 weight part;
Vanadium dioxide 5~10 weight parts;
Tindioxide 10~15 weight parts.
2. conductive nylon according to claim 1, it is characterized in that described interface coupling agent is γ-aminopropyl triethoxysilane (KH550), γ-glycidyl ether oxygen propyl trimethoxy silicane (KH560), γ-(methacryloxypropyl) propyl trimethoxy silicane (KH570), tynex grafting toxilic acid (tynex-g-MAH), styrene-maleic anhydride copolymer (SMA), Research of Grafting Malaic Anhydride Onto Polyethylene (LDPE-g-MAH), linear low density polyethylene grafted maleic anhydride (LLDPE-g-MAH), in the Racemic glycidol ether type epoxy one or more.
3. conductive nylon according to claim 1, it is characterized in that described toughner is MBS (MBS), MBS, hydrogenated styrene/Butadiene/Styrene) in the segmented copolymer (SEBS) one or more.
4. conductive nylon according to claim 1, it is characterized in that described dispersed lubricant is one or more in glyceryl monostearate, Tristearoylglycerol, ethylene bis stearamide, the bimonthly osmanthus of ethylene acid amides, the two amine hydroxybenzenes of ethylene, lower molecular weight ionomer, ethylene-acrylic acid copolymer, the ethylene-vinyl acetate copolymer.
5. each described conductive nylon in 4 according to claim 1 is characterized in that, comprises the component of following weight parts:
Tynex 60 weight parts;
γ-aminopropyl triethoxysilane 5 weight parts;
MBS 5 weight parts;
Glyceryl monostearate 0.8 weight part;
Vanadium dioxide 8 weight parts;
Tindioxide 13 weight parts.