Summary of the invention
In view of this, be necessary to provide a kind of lower-cost glass cover-plate and preparation method thereof.
A method for making for glass cover-plate, comprising: make white tiles, described white tiles comprises glass substrate and photoimaging material layer, and described glass substrate has first surface, and described photoimaging material layer is covered with whole described first surface; One egative film is covered on described photoimaging material layer, described egative film has the first pattern, by described egative film, exposure imaging is carried out to be transferred to by described first pattern on described photoimaging material layer thus to obtain having the glass cover-plate of the second pattern to described white tiles.
A kind of glass cover-plate adopting said method to be made.
Compared with prior art, the making of the glass cover-plate of the present embodiment adopts egative film to expose white tiles, develop, photoimaging material layer in white tiles is with the difference of egative film, different colors and structure can be shown, to obtain different glass cover-plates, the making of egative film is compared with half tone, and not only structure is simple, easy to make, and cost is lower.
Accompanying drawing explanation
Fig. 1 is the schematic diagram making white tiles in the method for making of embodiment of the present invention glass cover-plate.
Fig. 2 is the schematic cross-section of white tiles in Fig. 1.
Fig. 3 is the schematic diagram making egative film in the method for making of embodiment of the present invention glass cover-plate.
Fig. 4 is the schematic cross-section of Fig. 3 mediella.
Fig. 5 is to the schematic diagram that white tiles exposes in the method for making of embodiment of the present invention glass cover-plate.
Fig. 6 is the schematic diagram developing to obtain glass cover-plate in the method for making of embodiment of the present invention glass cover-plate to white tiles.
Main element symbol description
White tiles |
10 |
Glass substrate |
11 |
First surface |
111 |
Second surface |
112 |
Photoimaging material layer |
12 |
Ruddiness photoimaging material layer |
121 |
Green glow photoimaging material layer |
122 |
Blue light sensitive imaging material |
123 |
White layer |
13 |
Egative film |
20 |
Substrate |
21 |
Coating |
22 |
Pattern |
200,400 |
Light |
30 |
Glass cover-plate |
40 |
Following embodiment will further illustrate the present invention in conjunction with above-mentioned accompanying drawing.
Embodiment
As shown in Figures 1 and 2, white tiles 10 is made.White tiles 10 comprises glass substrate 11, photoimaging material layer 12 and white layer 13.
Glass substrate 11 has relative first surface 111 and second surface 112, and photoimaging material layer 12 is covered with on whole first surface 111, and white layer 13 is arranged on the marginal portion of second surface 112 and is the hollow closed.Photoimaging material layer 12 comprises the ruddiness photoimaging material layer 121, green glow photoimaging material layer 122 and the blue light sensitive imaging material 123 that arrange away from glass substrate 11 gradually.White layer 13 can for being used for the white ink of reflection ray or the decorative film of other whites.
In other embodiments, the lamination order of ruddiness photoimaging material layer 121, green glow photoimaging material layer 122 and blue light sensitive imaging material 123 also can adjust according to demand.
Ruddiness photoimaging material layer 121, green glow photoimaging material layer 122 and blue light sensitive imaging material 123 can adopt the mode such as roll extrusion mode or rotary coating mode to be arranged on glass substrate 11.
As shown in Figures 3 and 4, egative film 20 comprises substrate 21, be arranged on coating 22 in substrate 21 and the first pattern 200, and substrate 21 can be made up of poly-acetic acid fat material, the size of substrate 21 and the measure-alike of white tiles 10.Coating 22 is covered with part substrate 21 not being arranged pattern 200, and the material of coating 22 can be silver halide, such as silver chloride or silver bromide.
When coating 22 is one deck, when there being illumination to be mapped in coating 22, silver halide changes the silver of black into, becomes the egative film 20 of black and white; When coating 22 is three layers, then it is colored egative film 20.
In the present embodiment, pattern 200 is positioned at the marginal portion of egative film 20.In other embodiments, the design of pattern 200 contact panel as required can be arranged on other positions, such as, and the centre of egative film 20 or corner.
As shown in Figure 5, egative film 20 to be covered in white tiles 10 and to make light 30 be radiated on egative film 20, namely exposing to be transferred in white tiles 10 by pattern 200 by egative film 20 pairs of white tiles 10.
When egative film 20 is black and white, when light 30 is radiated on egative film 20, coating 22 is reduced into black under the effect of light 30, thus stop that light 30 is irradiated to the photoimaging material layer 12 in white tiles 10 through egative film 20, pattern 200 part then allows light 30 to be irradiated on the photoimaging material layer 12 in white tiles 10 through egative film 20, so, the part of photoimaging material layer 12 corresponding pattern 200 is exposed other parts in the effect of light 30 and is not then exposed.
And when egative film 20 is colored, light 30 is radiated on egative film 20, blue light sensitive imaging material 123 the sensing blue light at photosensitive rear stained yellow of photoimaging material layer 12, green glow photoimaging material layer 122 is only photosensitive to green light and dye pink, ruddiness photoimaging material layer 121 is only photosensitive to ruddiness and be dyed to cyan, thus makes photoimaging material layer 12 present colour.
In the present embodiment, adopt the exposure that light 30 pairs of white tiles 10 are carried out about 30 seconds.
As shown in Figure 6, development treatment is carried out to the white tiles 10 after exposure, so obtains the glass cover-plate 40 with pattern 400.
According to the character of egative film 20, the white tiles 10 after development is glass cover-plate 40 or the stained glass cover plate 40 of black and white.
In the method for making of glass cover-plate 40, egative film 20 pairs of white tiles 10 are adopted to expose, develop, photoimaging material layer 12 in white tiles 10 is with the difference of egative film 20, different colors and structure can be shown, to obtain different glass cover-plates 40, the making of egative film 20 is compared with half tone, and not only structure is simple, easy to make, and cost is lower.
Be understandable that, those skilled in the art also can do other change etc. and be used in design of the present invention, as long as it does not depart from technique effect of the present invention in spirit of the present invention.These changes done according to the present invention's spirit, all should be included within the present invention's scope required for protection.