CN103317870A - Method of printing high-resistance glossy-matte metal - Google Patents
Method of printing high-resistance glossy-matte metal Download PDFInfo
- Publication number
- CN103317870A CN103317870A CN2013102848190A CN201310284819A CN103317870A CN 103317870 A CN103317870 A CN 103317870A CN 2013102848190 A CN2013102848190 A CN 2013102848190A CN 201310284819 A CN201310284819 A CN 201310284819A CN 103317870 A CN103317870 A CN 103317870A
- Authority
- CN
- China
- Prior art keywords
- printing
- oil reservoir
- light
- light oil
- dumb
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a method of printing high-resistance glossy-matte metal. The method includes: coating the outer surface of metal, printing, and coating a glossy oil layer. The method is characterized in that a step of printing the glossy oil layer and a step of printing a matte oil layer are used after the step of coating the glossy oil layer, printing plates which are the same need to be independently made for the step of printing the glossy oil layer and the step of printing the matte oil layer, glossy oil and matte oil are transferred to the surface of a product through rubber cloth, the glossy oil and the matte oil are respectively independently solidified and dried by heating at 140-160 DEG C, glossiness of the glossy surface of the finished product is partially larger than or equal to 80 DEG, and glossiness of the matte surface of the finished product is smaller than or equal to 40 DEG. The method has the advantages that metal print with the whole surface which is both glossy and matte can be made by the method and the printed surface is well adhesive, scratch-resistant, good in printing stereoscopic impression and good in texture.
Description
Technical field
The present invention relates to the printing process on a kind of mental package surface, specifically the method for a kind of high patience light and dumb light hybrid metal printing.
Background technology
Demand along with market personal printing and Diversity of Product Design route, special print effects is that market is expected always, mental package is because the particularity of its production equipment and technique, the independent supporting polisher in printing equipment unit rear end, polisher adopts rubber roll roller coating mode to carry out the oil polish operation, the production technology of printing ink and gloss oil need be solidified by 140-180 ℃ of mode of heating dry, although can use polisher coating polish oil and dumb paint, but need separately coating and the whole space of a whole page all to cover, can't realize that printing surface has light and dumb light large tracts of land mixed effect simultaneously, has certain limitation.
The patent No. is 200480034303.X, patent name is for disclosing a kind of method in the Chinese patent of " for generation of the printing process of matte and glossy surfaces ": the offset press by comprising a plurality of hectographic printings unit and japanning unit, a downstream at first utilizes oil base hectographic printing printing ink that printing material is printed at least one of this hectographic printing unit once in service, in hectographic printing unit, a downstream, apply at the part surface that is printed with hectographic printing printing ink subsequently and contain delustering agent and organosilyl transparent oil base dumb light lacquer, then, in the japanning unit, apply transparent polish lacquer at the whole print surface that comprises the surface that is coated with the dumb light lacquer.Aforesaid way needs can realize on printing and glazing multicomputer equipment linkage, be fit to nonmetal stock printing, and metal effect is only for using metal ink to produce simulated effect, general multicomputer printing ink that interlocking equipment uses and gloss oil need use the UV curing process could realize producing, and have first the dumb light effect to have the light effect not reversible again.
The patent No. is 200910052856.2, patent name discloses a kind of technique in the Chinese patent of " the local UV typography on a kind of metal ink surface ", may further comprise the steps: (1) adds styrene-propene acid polymer, improved silica-Tissuemat E copolymer and self-crossing emulsion in oil at the bottom of the UV, under subzero 10 ℃-30 ℃, react, obtain oil at the bottom of the modification UV, be dumb light gloss; (2) behind brushing layer of metal printing ink on the thing to be printed, apply again oil at the bottom of the above-mentioned modification UV, dry through infrared radiation, then pass through screen printing mode, carry out the coating of local UV gloss oil, the irradiation through UV light is drying to obtain product again, and the product alternative presents light gloss and dumb light gloss.Aforesaid way only is fit to screen printing mode, generally is fit to nonmetal stock printing, and requires simultaneously as raw material use UV coating and metal ink, and resinous type is narrow and the process conditions requirement is high, has the light effect not reversible for the dumb light effect is arranged first again.
Summary of the invention
Technical problem to be solved by this invention is to overcome deficiency of the prior art and provide a kind of justifying mask of making to have light and dumb light mixed effect, print surface to have the method for the good high patience light of good adhesion and marresistance, printed three-dimensional sense and texture and the printing of dumb light hybrid metal.
The technical scheme that the present invention solves the problems of the technologies described above employing is: the method for this high patience light and the printing of dumb light hybrid metal, first the metal surface is coated with outer being coated with, then printing, be coated with again the light oil reservoir, it is characterized in that: also comprise printing light oil reservoir and printing dumb light oil reservoir two-step after the coating light oil reservoir, printing light oil reservoir and printing dumb light oil reservoir two-step need separately making forme and forme identical, make polish oil and dumb paint transfer to product surface by blanket, solidify separately respectively dry by 140-160 ℃ of mode of heating, light effect part glossiness is more than or equal to 80 ° behind the finished product, and dumb light effect part glossiness is less than or equal to 40 °.Printing first printing dumb light oil reservoir behind the light oil reservoir is convenient to increase the adhesive force of printing dumb light oil reservoir and reaches the properties of product requirement, be fit to printing light oil reservoir identical with printing dumb light oil reservoir two-step needs independent making forme and forme, make polish oil and dumb paint transfer to product surface by blanket, solidify separately respectively dry by 140-160 ℃ of mode of heating, be convenient to print the light oil reservoir good with the chromatography of printing dumb light oil reservoir, local generation dumb light effect and adhesion property are good.
Printing light oil reservoir of the present invention adopts alkyd resins, and printing dumb light oil reservoir adopts alkyd resins, and to contain mass percent be 10% ~ 20% delustering agent.Printing light oil reservoir is selected alkyd resins, and it act as improvement because of different resins coating polish oil surface tension, increases printing dumb light oil reservoir and the tack that is coated with the light oil reservoir.
Solid content is 90% ~ 100%(mass percent in printing light oil reservoir of the present invention and the printing dumb light oil reservoir operation), the China ink amount is controlled between 0.3CC ~ 0.6CC, be convenient to make printing surface not track down and recover stolen goods and pollute, be convenient to solidify, printing light oil reservoir and the ply adhesion of printing dumb paint are good, dumb light successful and clear.
Printing light oil reservoir of the present invention and the stacked seal error of printing dumb paint are convenient to make printing dumb light oil reservoir and coating light oil reservoir good gap to be arranged, space of a whole page Product mix visual effect less than or equal to 0.2mm.
The surface tension of printing light oil reservoir of the present invention is controlled at 36 ~ 42 dynes per centimeter, is convenient to make printing varnish and printing polish oil interlayer that good adhesion is arranged.
Between printing light oil reservoir of the present invention and the coating light oil reservoir, printing dumb light oil reservoir with print between the light oil reservoir adhesive force more than or equal to the I level.The printed article surface has good tack, the preservation of the product that is conducive to transport for long-distance.
Coating light oil reservoir of the present invention, printing dumb light oil reservoir case hardness are more than or equal to 2H, and coating light oil reservoir, printing dumb light oil reservoir surface anti scuffing are more than or equal to 1200g.The printed article surface has good marresistance, for directly the contact performance performance is better between the long-distance transport product.
Coating of the present invention is coated with and is coated with light oil reservoir two-step outward and all adopts justifying face rubber roll roller coating mode, continues to use traditional metal printing coating process, utilizes existing equipment not increase product cost, for product dumb light effect is established the ground quality base.
Coating light oil reservoir of the present invention adopts mylar or acrylic resin or epoxy resin, and solid content is 35% ~ 40%(mass percent), coating thickness is 5-8g/m
2, make product have good processing characteristics and surface quality.
The present invention compared with prior art has the following advantages: realize that 1, printing surface while justifying mask has light and dumb light mixed effect; 2, realize that adjacent light and dumb light surface have high-contrast, and have the special-effects such as third dimension and texture; 3, the mixed effect surface has good adhesion and marresistance, for directly the contact performance performance is better between the long-distance transport product; 4, the method also is fit to the realization of local light and dumb light mixed effect.
Description of drawings
Fig. 1 is process chart of the present invention.
The specific embodiment
Referring to Fig. 1, technological process of the present invention comprises that coating is outer and is coated with printing, coating light oil reservoir, printing light oil reservoir and printing dumb light oil reservoir.Be coated with and be coated with light oil reservoir two-step outside the coating and all adopt justifying face rubber roll roller coating mode, coating light oil reservoir adopts mylar or acrylic resin or epoxy resin, and solid content is 35% ~ 40%(mass percent), coating thickness is 5-8g/m
2Being coated with, printing and be coated with polish oil three operations outside the coating is the mental package common process, part is described in detail in detail belongs to prior art, finishes above-mentioned three operations such as needs light effect and is finished product.
Also comprise printing light oil reservoir and printing dumb light oil reservoir two-step in the method for the invention after the coating light oil reservoir.It is identical that printing light oil reservoir and printing dumb light oil reservoir two-step need to make separately forme and forme, makes polish oil and dumb paint transfer to product surface by blanket, solidifies drying by 140-160 ℃ of mode of heating separately respectively.
Printing light oil reservoir adopts alkyd resins, and solid content is 90% ~ 100%(mass percent), the China ink amount is controlled between 0.3CC ~ 0.6CC.The surface tension of printing light oil reservoir is controlled at 36 ~ 42 dynes per centimeter.Printing dumb light oil reservoir adopts alkyd resins, and to contain mass percent be 10% ~ 20% delustering agent, and solid content is 90% ~ 100%(mass percent), the China ink amount is controlled between 0.3CC ~ 0.6CC.Printing light oil reservoir and the stacked seal error of printing dumb paint are less than or equal to 0.2mm.Light effect part glossiness is more than or equal to 80 ° in the finished product that makes, and dumb light effect part glossiness is less than or equal to 40 °.
Detection to end product quality comprises adhesive force test, case hardness test and the test of surperficial anti scuffing.
Adhesion test method: use 3M #610 tape-stripping on printing surface, compress with the forefinger translation, and reserve the long adhesive tape of 15mm～20mm in order to grip, adhesive tape is torn from filming fast with reference to figure below direction, the adhesive tape of tearing be not stained with printing ink then printing ink and primary coat adhere to be qualified.The present invention prints between light oil reservoir and the coating light oil reservoir, printing dumb light oil reservoir with print between the light oil reservoir adhesive force more than or equal to the I level.
Case hardness method of testing: use Chinese board pencil to carry out with reference to GB/T6739.The present invention is coated with light oil reservoir, printing dumb light oil reservoir case hardness more than or equal to 2H.
Surface anti scuffing method of testing: use the SHEEN hardness-testing device, with 150X100mm sheet sample coated surface up, the dull and stereotyped seat of putting into instrument is upper fixing, adds counterweight, make from left to right paddling at the uniform velocity of dull and stereotyped seat, the standard take not show-through counterweight weight grams as hardness of film.The present invention is coated with light oil reservoir, printing dumb light oil reservoir surface anti scuffing more than or equal to 1200g.
Although the present invention with embodiment openly as above; but it is not to limit protection scope of the present invention; any technical staff who is familiar with this technology not breaking away from change and the retouching of doing in the spirit and scope of the present invention, all should belong to protection scope of the present invention.
Claims (9)
1. the method for one kind high patience light and dumb light hybrid metal printing, first the metal surface is coated with outer being coated with, then printing, be coated with again the light oil reservoir, it is characterized in that: also comprise printing light oil reservoir and printing dumb light oil reservoir two-step after the coating light oil reservoir, printing light oil reservoir and printing dumb light oil reservoir two-step need separately making forme and forme identical, make polish oil and dumb paint transfer to product surface by blanket, solidify separately respectively dry by 140-160 ℃ of mode of heating, light effect part glossiness is more than or equal to 80 ° behind the finished product, and dumb light effect part glossiness is less than or equal to 40 °.
2. the method for high patience light according to claim 1 and dumb light hybrid metal printing, it is characterized in that: described printing light oil reservoir adopts alkyd resins, and printing dumb light oil reservoir adopts alkyd resins, and to contain mass percent be 10% ~ 20% delustering agent.
High patience light according to claim 1 and dumb light hybrid metal the printing method, it is characterized in that: solid content is 90% ~ 100%(mass percent in described printing light oil reservoir and the printing dumb light oil reservoir operation), the China ink amount is controlled between 0.3CC ~ 0.6CC.
4. the method for high patience light according to claim 1 and dumb light hybrid metal printing, it is characterized in that: described printing light oil reservoir and printing dumb paint stacked seal error are less than or equal to 0.2mm.
High patience light according to claim 1 and dumb light hybrid metal the printing method, it is characterized in that: the surface tension of described printing light oil reservoir is controlled at 36 ~ 42 dynes per centimeter.
6. the method for high patience light according to claim 1 and dumb light hybrid metal printing is characterized in that: between described printing light oil reservoir and the coating light oil reservoir, printing dumb light oil reservoir and print between the light oil reservoir adhesive force more than or equal to the I level.
High patience light according to claim 1 and dumb light hybrid metal the printing method, it is characterized in that: described coating light oil reservoir, printing dumb light oil reservoir case hardness are more than or equal to 2H, and coating light oil reservoir, printing dumb light oil reservoir surface anti scuffing are more than or equal to 1200g.
High patience light according to claim 1 and dumb light hybrid metal the printing method, it is characterized in that: described coating is coated with and is coated with light oil reservoir two-step outward and all adopts justifying face rubber roll roller coating mode.
High patience light according to claim 1 and dumb light hybrid metal the printing method, it is characterized in that: described coating light oil reservoir adopts mylar or acrylic resin or epoxy resin, solid content is 35% ~ 40%(mass percent), coating thickness is 5-8g/m
2