CN103304896A - Plastic for automobile steering wheel and preparation method thereof - Google Patents
Plastic for automobile steering wheel and preparation method thereof Download PDFInfo
- Publication number
- CN103304896A CN103304896A CN2013102514698A CN201310251469A CN103304896A CN 103304896 A CN103304896 A CN 103304896A CN 2013102514698 A CN2013102514698 A CN 2013102514698A CN 201310251469 A CN201310251469 A CN 201310251469A CN 103304896 A CN103304896 A CN 103304896A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastics
- vehicle steering
- polypropylene
- polyethylene wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention relates to a plastic for an automobile steering wheel and a preparation method thereof. The plastic is prepared from the following ingredients in parts by weight: 75-90 parts of polypropylene, 15-25 parts of glass fiber, 10-28 parts of ethylene propylene terpolymer, 5-12 parts of butadiene styrene rubber, 1.2-4 parts of butylated hydroxytoluene, 0.8-1.2 parts of dilauryl thiodipropionate, 0.5-2.5 parts of antioxidant 168, 0.4-1 part of chlorinated paraffin, 0.15-0.4 part of polyethylene wax, 0.3-0.7 part of nanometer copper oxide, and 8-15 parts of white oil.The plastic for the automobile steering wheel provided by the invention has light weight, and anti-aging, antibacterial and anti-skidding effects.
Description
Technical field
The present invention relates to a kind of plastics and preparation method thereof, relate in particular to a kind of vehicle steering plastics and preparation method thereof.
Background technology
Polypropylene is the polymkeric substance of nontoxic, odorless, the tasteless high crystallization of oyster white, and its degree of crystallinity is high, and compound with regular structure has good mechanical property.Polyacrylic chemical stability is fine, and is outside decapacitation is corroded by the vitriol oil, concentrated nitric acid, all more stable to other various chemical reagent.But polypropylene is very sensitive to ultraviolet ray, needs to add antiaging agent and strengthens its aging-resistant performance.
In the daily life, the vehicle steering that people use often is under the irradiation of sunlight, if ageing resistance is not good, is easy to fade aging.Bearing circle also must have anti-skidding effect, guarantee people's traffic safety.For the modern, almost every household has car, and basically all can drive every day, and on hand sweat can be stayed on the bearing circle in heat, and easily breed bacteria is very unhygienic.
Summary of the invention
The technical problem that solves:Easily wear out, understand the shortcomings such as breed bacteria for above-mentioned vehicle steering, the invention provides a kind of vehicle steering plastics and preparation method thereof.
Technical scheme:The vehicle steering plastics, contain following composition in mass parts:
75～90 parts of polypropylene
15～25 parts in glass fibre
10～28 parts of terpolymer EP rubbers
5～12 parts in styrene-butadiene rubber(SBR)
1.2～4 parts of butylated hydroxytoluenes
0.8～1.2 part of Tyox B
0.5～2.5 part of irgasfos 168
0.4～1 part of clorafin
0.15～0.4 part of polyethylene wax
0.3～0.7 part of nano cupric oxide
8～15 parts of white oils.
Vehicle steering plastics described above, contain following composition in mass parts:
80～88 parts of polypropylene
18～23 parts in glass fibre
17～25 parts of terpolymer EP rubbers
6～10 parts in styrene-butadiene rubber(SBR)
2～3.5 parts of butylated hydroxytoluenes
0.8～1.2 part of Tyox B
1～1.5 part of irgasfos 168
0.5～0.7 part of clorafin
0.2～0.33 part of polyethylene wax
0.5～0.7 part of nano cupric oxide
10～14 parts of white oils.
Vehicle steering described above is as follows with the preparation process of plastics:
The first step: polypropylene, glass fibre, terpolymer EP rubber, styrene-butadiene rubber(SBR), irgasfos 168, clorafin and polyethylene wax are added in the agitator, are that 350～400rpm, temperature are 100～120 ℃ of lower 5～10min of stirring at rotating speed;
Second step: then add butylated hydroxytoluene, Tyox B, nano cupric oxide and white oil, mixing and stirring;
The 3rd step: be to carry out extruding pelletization under 170～190 ℃ in temperature then, cooling forming obtains the vehicle steering plastics again.
Beneficial effect:Vehicle steering provided by the invention plastics and preparation method thereof, these plastics have used the very little polypropylene of density, quality is light, and the adding of butylated hydroxytoluene and Tyox B is so that plastics have had resistance to deterioration, and aging speed slows down under the irradiation of sunlight; The adding of nano cupric oxide is avoided breed bacteria so that plastics have antibiotic effect; Simultaneously, these plastics also have anti-skidding effect, guarantee people's traffic safety.
Embodiment
Embodiment 1
The present embodiment provides a kind of vehicle steering plastics, contains following composition in mass parts:
75 parts of polypropylene
15 parts in glass fibre
10 parts of terpolymer EP rubbers
5 parts in styrene-butadiene rubber(SBR)
1.2 parts of butylated hydroxytoluenes
0.8 part of Tyox B
0.5 part of irgasfos 168
0.4 part of clorafin
0.15 part of polyethylene wax
0.3 part of nano cupric oxide
8 parts of white oils.
Vehicle steering is as follows with the preparation process of plastics:
The first step: polypropylene, glass fibre, terpolymer EP rubber, styrene-butadiene rubber(SBR), irgasfos 168, clorafin and polyethylene wax are added in the agitator, are that 350～400rpm, temperature are 100～120 ℃ of lower 5～10min of stirring at rotating speed;
Second step: then add butylated hydroxytoluene, Tyox B, nano cupric oxide and white oil, mixing and stirring;
The 3rd step: be to carry out extruding pelletization under 170～190 ℃ in temperature then, cooling forming obtains the vehicle steering plastics again.
Embodiment 2
The present embodiment provides a kind of vehicle steering plastics, contains following composition in mass parts:
80 parts of polypropylene
18 parts in glass fibre
17 parts of terpolymer EP rubbers
6 parts in styrene-butadiene rubber(SBR)
2 parts of butylated hydroxytoluenes
0.8 part of Tyox B
1 part of irgasfos 168
0.5 part of clorafin
0.2 part of polyethylene wax
0.5 part of nano cupric oxide
10 parts of white oils.
Vehicle steering is as follows with the preparation process of plastics:
The first step: polypropylene, glass fibre, terpolymer EP rubber, styrene-butadiene rubber(SBR), irgasfos 168, clorafin and polyethylene wax are added in the agitator, are that 350～400rpm, temperature are 100～120 ℃ of lower 5～10min of stirring at rotating speed;
Second step: then add butylated hydroxytoluene, Tyox B, nano cupric oxide and white oil, mixing and stirring;
The 3rd step: be to carry out extruding pelletization under 170～190 ℃ in temperature then, cooling forming obtains the vehicle steering plastics again.
Embodiment 3
The present embodiment provides a kind of vehicle steering plastics, contains following composition in mass parts:
88 parts of polypropylene
23 parts in glass fibre
25 parts of terpolymer EP rubbers
10 parts in styrene-butadiene rubber(SBR)
3.5 parts of butylated hydroxytoluenes
1.2 parts of Tyox Bs
1.5 parts of irgasfos 168s
0.7 part of clorafin
0.33 part of polyethylene wax
0.7 part of nano cupric oxide
14 parts of white oils.
Vehicle steering is as follows with the preparation process of plastics:
The first step: polypropylene, glass fibre, terpolymer EP rubber, styrene-butadiene rubber(SBR), irgasfos 168, clorafin and polyethylene wax are added in the agitator, are that 350～400rpm, temperature are 100～120 ℃ of lower 5～10min of stirring at rotating speed;
Second step: then add butylated hydroxytoluene, Tyox B, nano cupric oxide and white oil, mixing and stirring;
The 3rd step: be to carry out extruding pelletization under 170～190 ℃ in temperature then, cooling forming obtains the vehicle steering plastics again.
Embodiment 4
The present embodiment provides a kind of vehicle steering plastics, contains following composition in mass parts:
85 parts of polypropylene
20 parts in glass fibre
20 parts of terpolymer EP rubbers
8 parts in styrene-butadiene rubber(SBR)
2.9 parts of butylated hydroxytoluenes
1 part of Tyox B
1.2 parts of irgasfos 168s
0.6 part of clorafin
0.28 part of polyethylene wax
0.6 part of nano cupric oxide
12.5 parts of white oils.
Vehicle steering is as follows with the preparation process of plastics:
The first step: polypropylene, glass fibre, terpolymer EP rubber, styrene-butadiene rubber(SBR), irgasfos 168, clorafin and polyethylene wax are added in the agitator, are that 350～400rpm, temperature are 100～120 ℃ of lower 5～10min of stirring at rotating speed;
Second step: then add butylated hydroxytoluene, Tyox B, nano cupric oxide and white oil, mixing and stirring;
The 3rd step: be to carry out extruding pelletization under 170～190 ℃ in temperature then, cooling forming obtains the vehicle steering plastics again.
The above-mentioned vehicle steering of stating embodiment 1～embodiment 4 technical performance index of plastics, its detected result is as follows:
Detected result
The above vehicle steering that the embodiment of the invention is provided is described in detail with plastics and preparation method thereof, for one of ordinary skill in the art, thought according to the embodiment of the invention, all will change in specific embodiments and applications, in sum, this description should not be construed as limitation of the present invention.
Claims (3)
1. vehicle steering plastics is characterized in that containing following composition in mass parts:
75～90 parts of polypropylene
15～25 parts in glass fibre
10～28 parts of terpolymer EP rubbers
5～12 parts in styrene-butadiene rubber(SBR)
1.2～4 parts of butylated hydroxytoluenes
0.8～1.2 part of Tyox B
0.5～2.5 part of irgasfos 168
0.4～1 part of clorafin
0.15～0.4 part of polyethylene wax
0.3～0.7 part of nano cupric oxide
8～15 parts of white oils.
2. vehicle steering plastics according to claim 1 is characterized in that containing following composition in mass parts:
80～88 parts of polypropylene
18～23 parts in glass fibre
17～25 parts of terpolymer EP rubbers
6～10 parts in styrene-butadiene rubber(SBR)
2～3.5 parts of butylated hydroxytoluenes
0.8～1.2 part of Tyox B
1～1.5 part of irgasfos 168
0.5～0.7 part of clorafin
0.2～0.33 part of polyethylene wax
0.5～0.7 part of nano cupric oxide
10～14 parts of white oils.
3. vehicle steering as claimed in claim 1 is characterized in that the preparation process of the method is as follows with the preparation method of plastics:
The first step: polypropylene, glass fibre, terpolymer EP rubber, styrene-butadiene rubber(SBR), irgasfos 168, clorafin and polyethylene wax are added in the agitator, are that 350～400rpm, temperature are 100～120 ℃ of lower 5～10min of stirring at rotating speed;
Second step: then add butylated hydroxytoluene, Tyox B, nano cupric oxide and white oil, mixing and stirring;
The 3rd step: be to carry out extruding pelletization under 170～190 ℃ in temperature then, cooling forming obtains the vehicle steering plastics again.