CN103289437A - Method for preparing high-dispersion black iron oxide particles - Google Patents
Method for preparing high-dispersion black iron oxide particles Download PDFInfo
- Publication number
- CN103289437A CN103289437A CN2013101945723A CN201310194572A CN103289437A CN 103289437 A CN103289437 A CN 103289437A CN 2013101945723 A CN2013101945723 A CN 2013101945723A CN 201310194572 A CN201310194572 A CN 201310194572A CN 103289437 A CN103289437 A CN 103289437A
- Authority
- CN
- China
- Prior art keywords
- iron oxide
- oxide black
- viscous liquid
- black iron
- polymolecularity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for preparing high-dispersion black iron oxide particles. The method comprises the following concrete steps of: dissolving polyethylene glycol, methylcellulose and span-80 into deionized water according to a certain weight ratio to obtain viscous liquid; adding nano silica and carbon black to the prepared viscous liquid to modify; feeding black iron oxide to a pelletizer to pelletize; evenly spraying the modified vicious liquid on black iron oxide powder to form black iron oxide granules; drying and screening to obtain the product, namely nano-silica and 1.5-2.5% of stearic acid monoglyceride.
Description
Technical field
The present invention relates to a kind of preparation method of iron oxide black, be specifically related to a kind of preparation method of polymolecularity iron oxide black particle.
Background technology
Iron oxide black, molecular formula are Fe
3O
4, be black powder, be Fe
2O
3With the affixture of FeO, water insoluble, have magnetic, tinting strength and opacifying power are very high.A kind of as in the iron pigment of iron oxide black because it is nontoxic, do not have characteristics such as smell, pollution-free, is widely used in phenolic antirust paint filler, heavy-duty coating priming paint etc. in the building trade; When being used for rubber, plastics painted, the aging effect of reinforcement is arranged, protect organism by the characteristics of ultraviolet degradation simultaneously; In addition, also be used for the painted of artificial marble, pottery and cement flooring.But phenomenons such as iron oxide black can fade under comparatively high temps, variable color, heat-resistant stability is poor, thereby has limited the use range of iron oxide black.
Summary of the invention
The object of the present invention is to provide a kind of preparation method of polymolecularity iron oxide black particle, improve the high-temperature stability of iron oxide black.
The technical solution used in the present invention is as follows:
A kind of preparation method of polymolecularity iron oxide black particle may further comprise the steps:
(1) take by weighing polyoxyethylene glycol, methylcellulose gum and Arlacel-80 by weight 3-5:2-3:1 and add in the 10-15 times of deionized water, heating in water bath ultra-sonic dispersion 20-30 minute, gets viscous liquid to 55-60 ℃;
(2) add the nano silicon of 2-3% and the hard ester acid direactive glyceride of 1.5-2.5% in the above-mentioned viscous liquid that makes, the 2000-2500rpm high speed shear was disperseed 15-20 minute, got nano silicon and carbon black modified viscous liquid;
(3) get 130-160 part iron oxide black by weight and add in the tablets press and carry out granulation, the modification viscous liquid that 60-80 part step (2) is made sprays on the iron oxide black powder equably simultaneously, forms the iron oxide black small-particle;
(4) the iron oxide black particle that step (3) is made is crossed the 50-60 mesh sieve then in 85-95 ℃ of oven dry down, gets product.
Ultrasonic power described in the step (1) is 600-800W, and ultrasonic frequency is 20-30KHz.
The rotating speed of the tablets press described in the step (3) is 2000-3000rpm.
Beneficial effect of the present invention:
The present invention manufactures surface coverage with the iron oxide black powder components such as the nano silicon of containing, hard ester acid direactive glyceride, can obviously improve the flowability of iron oxide black with dispersed, be conducive to mix with other raw material, improve the quality of products, the iron oxide black that the present invention produces has superior heat resistance, well acidproof, alkaline resistance properties and characteristics such as light absorptive is strong, tinting strength is high, consistency is good, good dispersity have huge market outlook.
Embodiment
A kind of preparation method of polymolecularity iron oxide black particle may further comprise the steps:
(1) take by weighing polyoxyethylene glycol, methylcellulose gum and Arlacel-80 adds in 15 times of deionized waters by weight 4:2:1, heating in water bath to 60 ℃, ultra-sonic dispersion 25 minutes gets viscous liquid;
(2) add 3% nano silicon and 2% hard ester acid direactive glyceride in the above-mentioned viscous liquid that makes, the 2500rpm high speed shear was disperseed 15 minutes, got nano silicon and carbon black modified viscous liquid;
(3) get 145 parts of iron oxide blacks by weight and add in the tablets presss and carry out granulation, the modification viscous liquid that 70 parts of steps (2) are made sprays on the iron oxide black powder equably simultaneously, forms the iron oxide black small-particle;
(4) the iron oxide black particle that step (3) is made is crossed 60 mesh sieves then in 90 ℃ of oven dry down, gets product.
Ultrasonic power described in the step (1) is 800W, and ultrasonic frequency is 20KHz.
The rotating speed of the tablets press described in the step (3) is 3000rpm.
Iron oxide black product performance analysis data such as following table that present embodiment is produced:
Project | Index | Detected result |
The water solubles (%) | ≤1.0 | ?0.68 |
105 ℃ of volatile matters (%) | ≤1.0 | 0.72 |
Oil number (%) | 15-25 | 22.9 |
Tinctorial strength (%) | 95-105 | 98.2 |
Anti-200 ℃/30min (△ E) | ≤1.0 | 0.78 |
Claims (3)
1. the preparation method of a polymolecularity iron oxide black particle is characterized in that may further comprise the steps:
(1) take by weighing polyoxyethylene glycol, methylcellulose gum and Arlacel-80 by weight 3-5:2-3:1 and add in the 10-15 times of deionized water, heating in water bath ultra-sonic dispersion 20-30 minute, gets viscous liquid to 55-60 ℃;
(2) add the nano silicon of 2-3% and the hard ester acid direactive glyceride of 1.5-2.5% in the above-mentioned viscous liquid that makes, the 2000-2500rpm high speed shear was disperseed 15-20 minute, got nano silicon and carbon black modified viscous liquid;
(3) get 130-160 part iron oxide black by weight and add in the tablets press and carry out granulation, the modification viscous liquid that 60-80 part step (2) is made sprays on the iron oxide black powder equably simultaneously, forms the iron oxide black small-particle;
(4) the iron oxide black particle that step (3) is made is crossed the 50-60 mesh sieve then in 85-95 ℃ of oven dry down, gets product.
2. the preparation method of a kind of polymolecularity iron oxide black particle according to claim 1 is characterized in that, the ultrasonic power described in the step (1) is 600-800W, and ultrasonic frequency is 20-30KHz.
3. the preparation method of a kind of polymolecularity iron oxide black particle according to claim 1 is characterized in that, the rotating speed of the tablets press described in the step (3) is 2000-3000rpm.