CN103289443B - Method for preparing medium-temperature-resistant iron oxide black granules - Google Patents
Method for preparing medium-temperature-resistant iron oxide black granules Download PDFInfo
- Publication number
- CN103289443B CN103289443B CN201310194677.9A CN201310194677A CN103289443B CN 103289443 B CN103289443 B CN 103289443B CN 201310194677 A CN201310194677 A CN 201310194677A CN 103289443 B CN103289443 B CN 103289443B
- Authority
- CN
- China
- Prior art keywords
- iron oxide
- oxide black
- viscous liquid
- iron
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a method for preparing medium-temperature-resistant iron oxide black granules. The method comprises the following specific steps of: dissolving sodium hexametahposphate, water-soluble sodium silicate and lauryl sodium sulfate into deionized water according to a certain weight ratio, so as to obtain viscous liquid; adding iron slag and graphite powder to the obtained viscous liquid so as to carry out modification; and adding iron oxide black to a granulator for granulation while uniformly spraying the modified viscous liquid to iron oxide black powder, so as to form small iron oxide black granules, drying and sieving, thereby obtaining finished products. The iron oxide black granules prepared by the method have the characteristics of excellent temperature resistance, good acid and alkali resistance, strong light absorption, high coloring power, good compatibility, good dispersion and the like and have huge market prospects.
Description
Technical field
The present invention relates to a kind of preparation method of iron oxide black, be specifically related to a kind of preparation method of resistance to middle temperature iron oxide black particle.
Background technology
Iron oxide black, molecular formula is Fe
3o
4, being black powder, is Fe
2o
3with the affixture of FeO, water insoluble, have magnetic, tinting strength and opacifying power are very high.Iron oxide black, as the one in iron pigment, due to its feature such as nontoxic, odorless, pollution-free, is widely used in phenolic antirust paint filler, heavy-duty coating priming paint etc. in building trade; For rubber, plastics painted time, have the effect that reinforcement is aging, simultaneously protect organism by the feature of ultraviolet degradation; In addition, also for artificial marble, pottery and cement flooring painted.But the phenomenons such as iron oxide black can fade at relatively high temperatures, variable color, heat-resistant stability is poor, thus limits the use range of iron oxide black.
Summary of the invention
The object of the present invention is to provide a kind of preparation method of resistance to middle temperature iron oxide black particle, improve the high-temperature stability of iron oxide black.
The technical solution used in the present invention is as follows:
A preparation method for resistance to middle temperature iron oxide black particle, comprises the following steps:
(1) taking Sodium hexametaphosphate 99, water-soluble metasilicate and sodium lauryl sulphate by weight 3-4:1-2:1 adds in 8-12 times of deionized water, and heating in water bath is to 55-65 DEG C, and ultrasonic disperse 20-30 minute, obtains viscous liquid;
(2) in above-mentioned obtained viscous liquid, add the Iron-ore Slag of 1-3% and the Graphite Powder 99 of 2-3%, 2000-3000rpm high speed shear dispersion 15-25 minute, obtains the viscous liquid of Iron-ore Slag and Graphite Powder 99 modification;
(3) get 115-130 part iron oxide black by weight to add in tablets press and carry out granulation, simultaneously by viscosity modifying uniform liquid ground spray obtained for 50-60 part step (2) on iron oxide black powder, form iron oxide black small-particle;
(4) the iron oxide black particle that step (3) is obtained is dried at 85-95 DEG C, then cross 50-60 mesh sieve, get product.
Ultrasonic power described in step (1) is 500-600W, and ultrasonic frequency is 25-30KHz.
The rotating speed of the tablets press described in step (3) is 1500-2000rpm.
Beneficial effect of the present invention:
Iron oxide black powder is manufactured surface coverage by the present invention granular pigment containing components such as Iron-ore Slag, graphite, Sodium hexametaphosphate 99s, the thermotolerance of the raising black iron oxide pigment of iron oxide black can be significantly improved, also improve mobility and the dispersiveness of black iron oxide pigment simultaneously; The iron oxide black that the present invention produces has superior heat resistance, and good acidproof, the feature such as alkaline resistance properties and light absorptive is strong, tinting strength is high, consistency is good, good dispersity, have huge market outlook.
Embodiment
A preparation method for resistance to middle temperature iron oxide black particle, comprises the following steps:
(1) taking Sodium hexametaphosphate 99, water-soluble metasilicate and sodium lauryl sulphate by weight 2:1.5:1 adds in 8 times of deionized waters, heating in water bath to 60 DEG C, and ultrasonic disperse 25 minutes, obtains viscous liquid;
(2) in above-mentioned obtained viscous liquid, add the Iron-ore Slag of 1.5% and the Graphite Powder 99 of 2%, 2000rpm high speed shear disperses 25 minutes, obtains the viscous liquid of Iron-ore Slag and Graphite Powder 99 modification;
(3) get 120 parts of iron oxide blacks by weight to add in tablets press and carry out granulation, simultaneously by viscosity modifying uniform liquid ground spray obtained for 55 parts of steps (2) on iron oxide black powder, form iron oxide black small-particle;
(4) the iron oxide black particle that step (3) is obtained is dried at 95 DEG C, then cross 60 mesh sieves, get product.
Ultrasonic power described in step (1) is 600W, and ultrasonic frequency is 25KHz.
The rotating speed of the tablets press described in step (3) is 2000rpm.
The iron oxide black product performance analysis data that the present embodiment is produced is as following table:
Project | Index | Detected result |
The water solubles (%) | ≤1.0 | ?0.68 |
105 DEG C of volatile matters (%) | ≤1.0 | 0.73 |
Oil number (%) | 15-25 | 22.1 |
Tinctorial strength (%) | 95-105 | 98.9 |
Resistance to 200 DEG C/30min (△ E) | ≤1.0 | 0.76 |
Claims (2)
1. a preparation method for resistance to middle temperature iron oxide black particle, is characterized in that comprising the following steps:
(1) taking Sodium hexametaphosphate 99, water-soluble metasilicate and sodium lauryl sulphate by weight 3-4:1-2:1 adds in 8-12 times of deionized water, and heating in water bath is to 55-65 DEG C, and ultrasonic disperse 20-30 minute, obtains viscous liquid;
(2) in above-mentioned obtained viscous liquid, add the Iron-ore Slag of 1-3% and the Graphite Powder 99 of 2-3%, 2000-3000rpm high speed shear dispersion 15-25 minute, obtains the viscous liquid of Iron-ore Slag and Graphite Powder 99 modification;
(3) get 115-130 part iron oxide black by weight to add in tablets press and carry out granulation, simultaneously by viscosity modifying uniform liquid ground spray obtained for 50-60 part step (2) on iron oxide black powder, form iron oxide black small-particle;
(4) the iron oxide black particle that step (3) is obtained is dried at 85-95 DEG C, then cross 50-60 mesh sieve, get product;
Ultrasonic power described in step (1) is 500-600W, and ultrasonic frequency is 25-30KHz.
2. the preparation method of a kind of resistance to middle temperature iron oxide black particle according to claim 1, it is characterized in that, the rotating speed of the tablets press described in step (3) is 1500-2000rpm.