CN103289217A - 一种丁基橡胶系高性能材料 - Google Patents

一种丁基橡胶系高性能材料 Download PDF

Info

Publication number
CN103289217A
CN103289217A CN2013102586287A CN201310258628A CN103289217A CN 103289217 A CN103289217 A CN 103289217A CN 2013102586287 A CN2013102586287 A CN 2013102586287A CN 201310258628 A CN201310258628 A CN 201310258628A CN 103289217 A CN103289217 A CN 103289217A
Authority
CN
China
Prior art keywords
isoprene
isobutylene rubber
performance material
butyl rubber
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102586287A
Other languages
English (en)
Inventor
严火标
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GERON RUBBER (HAIMEN) CO Ltd
Original Assignee
GERON RUBBER (HAIMEN) CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GERON RUBBER (HAIMEN) CO Ltd filed Critical GERON RUBBER (HAIMEN) CO Ltd
Priority to CN2013102586287A priority Critical patent/CN103289217A/zh
Publication of CN103289217A publication Critical patent/CN103289217A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种丁基橡胶系高性能材料，它以丁基橡胶为基体，包括以下重量份的组份：丁基橡胶14-20份；增粘树脂10-25份；胶黏赋予剂 5-10份；无机填充剂20-25份；脂肪族烃类稀释剂3-6份。本发明所采用的增粘树脂可以显著改善丁基橡胶的阻尼性能，同时胶黏赋予剂使材料具有高的剥离强度和剪切强度。本发明所获得的丁基橡胶系高性能材料是一种使用温度范围较宽的阻尼材料；力学性能好，且耐热、耐水、耐潮湿，在温度较高和潮湿环境下，仍然可以保持较好剥离强度和剪切强度好等力学性能。

Description

一种丁基橡胶系高性能材料
技术领域
本发明涉及一种丁基橡胶系高性能材料，属于高性能材料领域。
背景技术
高聚物阻尼材料是一种减震降噪的功能材料。由于具有优异的阻尼效果，被广泛应用于宇航事业、交通运输、机械设备、建筑工程及日常生活等领域。
一般均聚物的玻璃化转变的温度范围比较窄，产生有效阻尼的温度范围大致为玻璃化温度附近的±10~15℃，材料的使用温度范围有限。橡胶类材料的玻璃化转变区大多发生在室温以下，不能很好的满足实际使用的需要。因此，研制使用温度范围较宽且可控的阻尼材料成为本领域迫切需要解决的技术问题。
发明内容
本发明的目的是提供一种具有宽使用温度范围的丁基橡胶系高性能材料。
为实现上述目的，本发明采用的技术方案是：
一种丁基橡胶系高性能材料，它以丁基橡胶为基体，包括以下重量份的组份：
丁基橡胶           14-20份；
增粘树脂           10-25份；
胶黏赋予剂          5-10份；
无机填充剂         20-25份；
脂肪族烃类稀释剂     3-6份。
所述增粘树脂为石油树脂、酚醛树脂、松香树脂中的一种或几种。
所述石油树脂、酚醛树脂、松香树脂的软化温度为60-105℃。
所述胶黏赋予剂为聚丁烯，数均分子量2000-3000。
所述无机填充剂为云母、炭黑、二氧化硅中的一种或几种。
所述脂肪族烃类稀释剂为戊烷或己烷。
     本发明的优点：本发明所采用的增粘树脂可以显著改善丁基橡胶的阻尼性能，同时胶黏赋予剂使材料具有高的剥离强度和剪切强度。
本发明所获得的丁基橡胶系高性能材料是一种使用温度范围较宽的阻尼材料；力学性能好，且耐热、耐水、耐潮湿，在温度较高和潮湿环境下，仍然可以保持较好剥离强度和剪切强度好等力学性能。
具体实施方式
以下实施例旨在说明本发明而不是对本方明的进一步限定。
实施例1
一种丁基橡胶系高性能材料，它以丁基橡胶为基体，包括以下组份：
丁基橡胶             14㎏；
增粘树脂             10㎏；
胶黏赋予剂            5㎏；
无机填充剂           20㎏；
脂肪族烃类稀释剂      3㎏。
增粘树脂为石油树脂，石油树脂的软化温度为60℃，胶黏赋予剂为聚丁烯，数均分子量2000，无机填充剂为云母，脂肪族烃类稀释剂为戊烷。
实施例2
一种丁基橡胶系高性能材料，它以丁基橡胶为基体，包括以下组份：
丁基橡胶             17㎏；
增粘树脂             15㎏；
胶黏赋予剂            7㎏；
无机填充剂           22㎏；
脂肪族烃类稀释剂      4㎏。
增粘树脂为酚醛树脂，酚醛树脂的软化温度为80℃，胶黏赋予剂为聚丁烯，数均分子量2500，无机填充剂为炭黑，脂肪族烃类稀释剂为己烷。
实施例3
一种丁基橡胶系高性能材料，它以丁基橡胶为基体，包括以下组份：
丁基橡胶              20㎏；
增粘树脂              25㎏；
胶黏赋予剂            10㎏；
无机填充剂            25㎏；
脂肪族烃类稀释剂       6㎏。
增粘树脂为松香树脂，松香树脂的软化温度为105℃，胶黏赋予剂为聚丁烯，数均分子量3000，无机填充剂为二氧化硅，脂肪族烃类稀释剂为己烷。
本发明是在高分子量化合物中添加极性有机低分子量化合物，形成一种均匀分散的分子复合体，利用高分子与低分子的相互作用呈现出高阻尼特性，同时拓宽阻尼材料的使用温度范围且使阻尼材料具有压敏胶性能。
本发明所采用的增粘树脂可以显著改善丁基橡胶的阻尼性能，同时胶黏赋予剂使材料具有高的剥离强度和剪切强度。
本发明所获得的丁基橡胶系高性能材料是一种使用温度范围较宽的阻尼材料；力学性能好，且耐热、耐水、耐潮湿，在温度较高和潮湿环境下，仍然可以保持较好剥离强度和剪切强度好等力学性能。

Claims (6)

1.一种丁基橡胶系高性能材料，其特征在于，它以丁基橡胶为基体，包括以下重量份的组份：
丁基橡胶           14-20份；
增粘树脂           10-25份；
胶黏赋予剂          5-10份；
无机填充剂         20-25份；
脂肪族烃类稀释剂     3-6份。
2.根据权利要求1所述的一种丁基橡胶系高性能材料，其特征在于：所述增粘树脂为石油树脂、酚醛树脂、松香树脂中的一种或几种。
3.根据权利要求2所述的一种丁基橡胶系高性能材料，其特征在于：所述石油树脂、酚醛树脂、松香树脂的软化温度为60-105℃。
4.根据权利要求1所述的一种丁基橡胶系高性能材料，其特征在于：所述胶黏赋予剂为聚丁烯，数均分子量2000-3000。
5.根据权利要求1所述的一种丁基橡胶系高性能材料，其特征在于：所述无机填充剂为云母、炭黑、二氧化硅中的一种或几种。
6.根据权利要求1所述的一种丁基橡胶系高性能材料，其特征在于：所述脂肪族烃类稀释剂为戊烷或己烷。
CN2013102586287A 2013-06-26 2013-06-26 一种丁基橡胶系高性能材料 Pending CN103289217A (zh)