CN103289145A - 一种含有二环戊二烯的抗冲击耐高温塑胶 - Google Patents
一种含有二环戊二烯的抗冲击耐高温塑胶 Download PDFInfo
- Publication number
- CN103289145A CN103289145A CN2013102525739A CN201310252573A CN103289145A CN 103289145 A CN103289145 A CN 103289145A CN 2013102525739 A CN2013102525739 A CN 2013102525739A CN 201310252573 A CN201310252573 A CN 201310252573A CN 103289145 A CN103289145 A CN 103289145A
- Authority
- CN
- China
- Prior art keywords
- parts
- shock resistance
- plastic cement
- dcpd
- temperature resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种含有二环戊二烯的抗冲击耐高温塑胶，由以下成分按照重量比组成：二环戊二烯30～40份、异戊橡胶40～50份、棕榈酸异辛酯20～30份、1-庚烯20～30份、聚对苯二甲酰对苯二胺纤维10～20份、四氢邻苯二甲酸二缩水甘油酯10～20份。制成的含有二环戊二烯的塑胶具有良好的抗冲击耐高温效果。
Description
技术领域
本发明涉及一种抗冲击耐高温塑胶，特别是涉及一种含有二环戊二烯的抗冲击耐高温塑胶。
背景技术
随着科技的迅速发展，塑胶塑料等相关行业也得到了迅猛发展。塑胶具有很多不同的性能，如耐酸碱、耐腐蚀、耐高温、良好延伸性等等。其中人们在涉及到抗冲击耐高温塑胶的专业领域，以及一些特殊领域，对抗冲击耐高温塑胶的要求也很高，目前市场上同时具有抗冲击和耐高温效果的塑胶种类非常少，因此开发一种同时具有良好抗冲击耐高温的塑胶非常的必要。
发明内容
要解决的技术问题：常规塑胶抗冲击和耐高温效果较差的问题。
技术方案：本发明为一种含有二环戊二烯的抗冲击耐高温塑胶，由以下成分按照重量比组成：二环戊二烯30～40份、异戊橡胶40～50份、棕榈酸异辛酯20～30份、1-庚烯20～30份、聚对苯二甲酰对苯二胺纤维10～20份、四氢邻苯二甲酸二缩水甘油酯10～20份。在70℃下，将各种成分投入反应容器调配，搅拌均匀，加热至160℃保持8h，冷却后即可获得具有良好抗冲击耐高温效果的塑胶。
有益效果：制备好含有二环戊二烯的抗冲击耐高温塑胶后，对其抗冲击性和耐高温进行了实验。采用ASTMD256标准对塑胶的抗冲击性进行了测试，结果表明本发明制成的含有二环戊二烯的抗冲击耐高温塑胶，抗冲击性为260～280J/M，具有良好的抗冲击性。另外塑胶在温度为700～800℃下保持20h，含有二环戊二烯的抗冲击耐高温塑胶没有任何异常现象产生，具有良好的抗冲击耐高温特性。
具体实施方式
实施例1
打开反应容器，温度调至70℃，取二环戊二烯30kg，投入反应釜中，搅拌，同时加入异戊橡胶40kg，再加入棕榈酸异辛酯20kg，加入1-庚烯20kg，再加入聚对苯二甲酰对苯二胺纤维10kg，再加入四氢邻苯二甲酸二缩水甘油酯10kg，待彻底搅拌均匀后加热至160℃保持8h，冷却后获得含有二环戊二烯的抗冲击耐高温塑胶。此塑胶抗冲击性结果为260J/M，具有良好的抗冲击性。另外塑胶在温度为700℃下保持20h，含有二环戊二烯的抗冲击耐高温塑胶没有任何异常现象产生，具有良好的抗冲击耐高温特性。
实施例2
产品制备方法同实施例1，区别在于配方由下述成分组成：二环戊二烯40kg、异戊橡胶50kg、棕榈酸异辛酯30kg、1-庚烯30kg、聚对苯二甲酰对苯二胺纤维20kg、四氢邻苯二甲酸二缩水甘油酯20kg。此塑胶抗冲击性结果为270J/M，具有良好的抗冲击性。另外塑胶在温度为750℃下保持20h，含有二环戊二烯的抗冲击耐高温塑胶没有任何异常现象产生，具有良好的抗冲击耐高温特性。
实施例3
产品制备方法同实施例1，区别在于配方由下述成分组成：二环戊二烯35kg、异戊橡胶45kg、棕榈酸异辛酯25kg、1-庚烯25kg、聚对苯二甲酰对苯二胺纤维15kg、四氢邻苯二甲酸二缩水甘油酯15kg。此塑胶抗冲击性结果为280J/M，具有良好的抗冲击性。另外塑胶在温度为800℃下保持20h，含有二环戊二烯的抗冲击耐高温塑胶没有任何异常现象产生，具有良好的抗冲击耐高温特性。
Claims (6)
1.一种含有二环戊二烯的抗冲击耐高温塑胶，其特征在于：由以下成分按照重量比组成：二环戊二烯30～40份、异戊橡胶40～50份、棕榈酸异辛酯20～30份、1-庚烯20～30份、聚对苯二甲酰对苯二胺纤维10～20份、四氢邻苯二甲酸二缩水甘油酯10～20份。
2.根据权利要求1所述的一种含有二环戊二烯的抗冲击耐高温塑胶，其特征在于：涂料组成中二环戊二烯为40份。
3.根据权利要求1所述的一种含有二环戊二烯的抗冲击耐高温塑胶，其特征在于：涂料组成中异戊橡胶为40份。
4.根据权利要求1所述的一种含有二环戊二烯的抗冲击耐高温塑胶，其特征在于：涂料组成中棕榈酸异辛酯为30份。
5.根据权利要求1所述的一种含有二环戊二烯的抗冲击耐高温塑胶，其特征在于：涂料组成中1-庚烯为30份。
6.根据权利要求1所述的一种含有二环戊二烯的抗冲击耐高温塑胶，其特征在于：涂料组成中聚对苯二甲酰对苯二胺纤维为10份。