CN103274750A - Mica compound type foaming agent - Google Patents
Mica compound type foaming agent Download PDFInfo
- Publication number
- CN103274750A CN103274750A CN2013102304863A CN201310230486A CN103274750A CN 103274750 A CN103274750 A CN 103274750A CN 2013102304863 A CN2013102304863 A CN 2013102304863A CN 201310230486 A CN201310230486 A CN 201310230486A CN 103274750 A CN103274750 A CN 103274750A
- Authority
- CN
- China
- Prior art keywords
- foaming agent
- mica compound
- compound foaming
- powder
- compound type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a mica compound type foaming agent. The technical scheme is characterized in that the mica compound type foaming agent comprises sericite powder, attapulgite potter clay powder provided with an air purifying function, hydrogen peroxide, N, N-dimethyldodecylamine-N-oxide, coconut diethanolamide, MPS, polyether-modified silicone oil and water. Paste ingredients of the mica compound type foaming agent are stirred into the paste, and stirred into a finished product of the mica compound type foaming agent. The mica compound type foaming agent has the characteristics of strong foaming capacity, high expansion rate, large foam generation quantity per unit volume, fine and uniform bubble diameter and low possibility of breaking, high product demoulding speed, good surface smoothness and high product later strength. A product produced by using the mica compound type foaming agent has the heat preservation, thermal insulation and soundproof effects, as well as the air purifying function; and the mica compound type foaming agent is suitable for producing a light board, a light wall body and noise damping and reduction products.
Description
Technical field
The present invention relates to whipping agent, be specifically related to a kind of mica compound foaming agent.
Background technology
Whipping agent can be divided into chemical foaming agent, pneumatogen and tensio-active agent three major types, and the many whipping agents of purposes have cement blowing agent, concrete foamer, plastics blowing agent, polyurethane foams, rubber pange agent, glass whipping agent etc.
Though the whipping agent kind is many, use also extensivelyr, exist performance comprehensive inadequately, can not satisfy the drawback of actual production and environmental protection needs, the function that existing whipping agent does not also purify air.
Summary of the invention
The objective of the invention is to overcome weak point in the prior art, a kind of mica compound foaming agent is provided.
The mica compound foaming agent is made up of sericite in powder, the Attapulgite potter's clay powder with air purification function, hydrogen peroxide, dimethyl dodecyl amine oxide, cocounut oil acyl diethanolamine, silicone resin polyethers emulsion, polyether modified silicon oil and water.
The production method of mica compound foaming agent: be paste with stirring in the mica compound foaming agent paste batching input low-speed mixer earlier, be the finished product of mica compound foaming agent with stirring in the mica compound foaming agent batching input homogenizer again.
Mica has characteristics such as good elasticity, toughness, insulativity, high temperature resistant, acid and alkali-resistance, corrosion-resistant, strong adhesion and satin luster, sericite has high resistance, be excellent insulating material and fire-retardant filler, sericite can significantly change a series of physics modulus of material, form or change the visco-elasticity of material, this class material absorbs vibrational energy expeditiously, weakens shock wave and sound wave, is used to prepare noise elimination, sound insulation, damping coating, and the present invention selects sericite for use.
Attapulgite potter's clay powder with air purification function is made up of the sticking attapulgite clay of height, attapulite constant humidity amendment, natural-minerals adsorptive filter medium, Leafy twigs of Oriental Arborvitae, aluminium silicate fiber peacekeeping polyacrylamide; have cohesiveness, plasticity-, thixotropy, resistivity against fire and thermostability preferably; effectively objectionable impuritiess such as formaldehyde, ammonia and benzene in the absorbed air are protected environment and are promoted the healthy of people.
High sticking attapulgite clay is the attapulgite clay that adopts the complete processing production that improves viscosity of attapulgite clay, attapulgite clay soil property exquisiteness, oily soapy is arranged, light weight, property are crisp, fracture is conchoidal or irregular shape, and water-absorbent is strong, tool viscosity and plasticity-when wet, its viscosity can reach more than the 3000mPas, is conducive to the bonding between the raw material.
High sticking attapulgite clay powder refers to get 28.0g attapulgite clay powder sample, add in the suspension cup of homogenizer, add 372g water again, the suspension cup is placed on the homogenizer, under 11000 rev/mins rotating speed, stirred 20 minutes, to pour in the beaker of 250ml the viscosity of using NDJ-1 type rotational viscosimeter to test its suspension, tested viscosity value 〉=2200 again through the high-speed stirring sample suspension into
MPasThe attapulgite clay powder.
Hydrogen peroxide is commonly called as hydrogen peroxide, outward appearance is colourless transparent liquid, be a kind of strong oxidizer, the present invention selects massfraction 〉=35% of industrial hydrogen peroxide for use, can generate a large amount of bubbles with sericite in powder with after having the batch mixes such as Attapulgite potter's clay powder of air purification function.
Dimethyl dodecyl amine oxide is a kind of amphoterics, colourless transparent liquid, be the weak cation tensio-active agent, in acidic medium, be cationic, be nonionic in alkaline medium, have good thickening, antistatic, soft, foam enhancing and detergency ability, foam is abundant and stablize, the gentle pungency of character is low, has excellent antistatic and flexibility.
Cocounut oil acyl diethanolamine is water-soluble, has good decontamination, emulsification, foaming, steady bubble, dispersion, solubilising.
Silicone resin polyethers emulsion is a kind of novel high polymer suds-stabilizing agent, put in order by changing intramolecule, make between tensio-active agent bubble and the bubble and arrange closely neatly, thereby form fine and close inner layer film, make anti-pressure ability strong especially, can control the structural stability of air bubble liquid-membrane, make surfactant molecule in the Methodistic distribution of the liquid film of bubble, give elasticity and the self-reparing capability of have good lather, thereby reach desirable especially steady bubble effect.
Polyether modified silicon oil is the organosilicon nonionogenic tenside that adopts a kind of unique properties that polyethers and dimethyl siloxane graft copolymerization forms, and can reduce internal friction, the stress of its molecule for the present invention, thereby play levelling, froth breaking.
The present invention is achieved by following technical proposals:
1, mica compound foaming agent batching is made up of following component by weight percentage: mica compound foaming agent paste 25～80%, hydrogen peroxide 2～35%, polyether modified silicon oil 0.001～5% and water 1～45%.
The production method of described mica compound foaming agent: will stir in the mica compound foaming agent batching input homogenizer, the speed control of stirrer is at 1400～1800 rev/mins, churning time control was at 2～30 minutes, be the finished product of mica compound foaming agent after stirring, contain a large amount of stable intensive bubbles in the mica compound foaming agent.
Described mica compound foaming agent paste batching is made up of following component by weight percentage: sericite in powder 15～55%, the Attapulgite potter's clay powder 5～35% with air purification function, dimethyl dodecyl amine oxide 0.01～25%, cocounut oil acyl diethanolamine 0.01～20%, silicone resin polyethers emulsion 0.01～5% and water 5～55%.
The production method of described mica compound foaming agent paste: will stir in the mica compound foaming agent paste batching input low-speed mixer, the speed control of stirrer is at 600～800 rev/mins, churning time control was at 2～20 minutes, stir the back for mica compound foaming agent paste, produced the part bubble in the mica compound foaming agent paste.
Described sericite in powder production method is: 1. sericite is imported in the pulverizer and pulverized, particle fineness≤5 millimeter; 2. be processed as sericite in powder in sericite after will the pulverizing input pulverizing mill, the particle fineness of sericite in powder≤0.074 millimeter;
Described batching with Attapulgite potter's clay powder of air purification function is made up of following component by weight percentage: high sticking attapulgite clay 35～60%, attapulite constant humidity amendment 10～35%, natural-minerals adsorptive filter medium 5～20%, Leafy twigs of Oriental Arborvitae 2～15%, aluminum silicate fiber 1～5% and polyacrylamide 0.1～3%.
Described production method with Attapulgite potter's clay powder of air purification function is, and: ⑴ will have after the batch mixes of Attapulgite potter's clay powder of air purification function and pulverize in the input pulverizer, and the compound particles fineness after the pulverizing is less than 0.5 millimeter; ⑵ soak the old work in-process that are treated to water in the old pond of pulverulent mixture adding immersion, soaks old time control at 7～30 days; ⑶ import work in-process and be squeezed into cylindrical strip thing in the vacuum-extruder, and the diameter control of cylindrical strip thing is at 2～10 millimeters; ⑷ be input to the cement threshing ground with cylindrical strip thing and carry out airing, and the cylindrical strip thing water content after the airing is less than 15%; ⑸ carrying out abrasive dust in the cylindrical strip thing input grinding machine after with airing is meal, and the particle fineness of meal is less than 0.074 millimeter.
Attapulgite potter's clay powder with air purification function is to adopt " the Attapulgite potter's clay powder with air purification function " in application on February 25th, 2011 by the inventor, the Chinese patent Granted publication number is: CN 102173743 B, Granted publication day: on July 25th, 2012.
The sticking attapulgite clay of described height is the attapulgite clay that adopts the complete processing production that improves viscosity of attapulgite clay, it is characterized in that, and from the attapulgite clay of mining area exploitation, need be through 30～120 days natural weathering; Modification processing method is: calculate by weight percentage, take from the attapulgite clay 94～98% after the right weathering, evenly add 2～6% yellow soda ash, import jointly in the fermentation vat, add clear water and soak ageing, soak time is 72～120 hours; Get the attapulgite clay after the immersion, stir in the input stirrer, and the attapulgite clay after will stirring, be extruded into thin slice through extrusion machine, its gauge control is at 0.5～2 millimeter, with the attapulgite clay thin slice, carry out airing, the attapulgite clay thin slice after the airing, its water content≤15%; Batching is calculated by weight percentage: the attapulgite clay 94～98% after the airing, High hydrophilous resin 0.5～5% and Mierocrystalline cellulose 0.5～3%, above-mentioned batching is stirred, and carry out abrasive dust in the back input grinding machine that stirs, particle fineness≤0.074 millimeter.
Above-mentioned production technique is to adopt " improving the complete processing of viscosity of attapulgite clay " in application on June 20th, 2005 by the inventor, and the Chinese patent Granted publication number is: CN 1317067C, Granted publication day: on May 23rd, 2007.
Described water content is weight percentage.
The present invention selects massfraction 〉=35% of industrial hydrogen peroxide for use, takes the production scene to add the batching per-cent that water is adjusted industrial hydrogen peroxide, is conducive to reduce trucking costs and production cost, improves the foaming quality of product.
When simple use hydrogen peroxide foams, the generation bubble is very fast, but it is also fast that the part bubble breaks and disappears, cause the less stable of foam, the present invention is a kind of compound foaming agent, mica compound foaming agent paste has produced the part bubble in process of production, the mica compound foaming agent is to foam again on mica compound foaming agent paste basis, has that foaming power is strong, foam expansion is high, unit volume produces that the bubble amount is big, abscess is fine and smooth evenly is difficult for the characteristics broken, that product stripping speed is fast, surface smoothness good and the product later strength is high.
Raw materials such as the wilkinite after the rice hulls of the Attapulgite potter's clay powder with air purification function after by the sticking attapulgite clay of height, quick dissolved sodium silicate, zeolite powder, acidifying, the zeolite after the acidifying, Concavo-convex excellent stone clay after the acidify, the acidifying, the mica after the acidifying, volcanics, alumine, Leafy twigs of Oriental Arborvitae, aluminium silicate fiber peacekeeping polyacrylamide are formed; Have cohesiveness, plasticity-, thixotropy, resistivity against fire and thermostability preferably, effectively objectionable impuritiess such as formaldehyde, ammonia and benzene in the absorbed air are protected environment and are promoted the healthy of people.
Adopt the Attapulgite potter's clay powder with air purification function for mainly being raw material among the present invention, produce the mica compound foaming agent, given full play to the effective efficiency of Attapulgite potter's clay powder.
Adopt polyether modified silicon oil can eliminate the partial invalidity air pocket that produces in the production process among the present invention, and can improve the speed of product stripping, to guarantee the quality of integral foam process.
The product that uses the mica compound foaming agent to produce not only has the effect of insulation, heat insulation, sound insulation, the function that purifies air in addition; These products are used for facilities such as motorway, viaduct, urban light rail, subway, factory, warehouse, public place.
The mica compound foaming agent is applicable to produces light weight board, lightweight body of wall and sound-deadening and noise-reducing product.
Embodiment
The invention will be further described below in conjunction with embodiment:
1, mica compound foaming agent batching is made up of following component by weight percentage: mica compound foaming agent paste 68%, hydrogen peroxide 22.95%, polyether modified silicon oil 0.05% and water 9%.
The production method of described mica compound foaming agent: will stir in the mica compound foaming agent batching input homogenizer, the speed control of stirrer is at 1500～1600 rev/mins, churning time control was at 10 minutes, and the back that stirs is the finished product of mica compound foaming agent.
Described mica compound foaming agent paste batching is made up of following component by weight percentage: sericite in powder 32%, the Attapulgite potter's clay powder 24% with air purification function, dimethyl dodecyl amine oxide 3%, cocounut oil acyl diethanolamine 2%, silicone resin polyethers emulsion 1% and water 38%.
The production method of described mica compound foaming agent paste: will stir in the mica compound foaming agent paste batching input low-speed mixer, the speed control of stirrer is at 650～750 rev/mins, churning time control was at 12 minutes, and the back that stirs is mica compound foaming agent paste.
Described sericite in powder production method is: 1. sericite is imported in the pulverizer and pulverized, particle fineness≤2 millimeter; 2. be processed as sericite in powder in sericite after will the pulverizing input pulverizing mill, the particle fineness of sericite in powder≤0.044 millimeter.
Claims (1)
1. mica compound foaming agent, it is characterized in that mica compound foaming agent batching is made up of following component by weight percentage: mica compound foaming agent paste 25～80%, hydrogen peroxide 2～35%, polyether modified silicon oil 0.001～5% and water 1～45%;
The production method of described mica compound foaming agent: will stir in the mica compound foaming agent batching input homogenizer, the speed control of stirrer is at 1400～1800 rev/mins, churning time control was at 2～30 minutes, and the back that stirs is the finished product of mica compound foaming agent;
Described mica compound foaming agent paste batching is made up of following component by weight percentage: sericite in powder 15～55%, the Attapulgite potter's clay powder 5～35% with air purification function, dimethyl dodecyl amine oxide 0.01～25%, cocounut oil acyl diethanolamine 0.01～20%, silicone resin polyethers emulsion 0.01～5% and water 5～55%;
The production method of described mica compound foaming agent paste: will stir in the mica compound foaming agent paste batching input low-speed mixer, the speed control of stirrer is at 600～800 rev/mins, churning time control was at 2～20 minutes, and the back that stirs is mica compound foaming agent paste;
Described sericite in powder production method is: 1. sericite is imported in the pulverizer and pulverized, particle fineness≤5 millimeter; 2. be processed as sericite in powder in sericite after will the pulverizing input pulverizing mill, the particle fineness of sericite in powder≤0.074 millimeter;
Described batching with Attapulgite potter's clay powder of air purification function is made up of following component by weight percentage: high sticking attapulgite clay 35～60%, attapulite constant humidity amendment 10～35%, natural-minerals adsorptive filter medium 5～20%, Leafy twigs of Oriental Arborvitae 2～15%, aluminum silicate fiber 1～5% and polyacrylamide 0.1～3%;
Described production method with Attapulgite potter's clay powder of air purification function is, and: ⑴ will have after the batch mixes of Attapulgite potter's clay powder of air purification function and pulverize in the input pulverizer, and the compound particles fineness after the pulverizing is less than 0.5 millimeter; ⑵ soak the old work in-process that are treated to water in the old pond of pulverulent mixture adding immersion, soaks old time control at 7～30 days; ⑶ import work in-process and be squeezed into cylindrical strip thing in the vacuum-extruder, and the diameter control of cylindrical strip thing is at 2～10 millimeters; ⑷ be input to the cement threshing ground with cylindrical strip thing and carry out airing, and the cylindrical strip thing water content after the airing is less than 15%; ⑸ carrying out abrasive dust in the cylindrical strip thing input grinding machine after with airing is meal, and the particle fineness of meal is less than 0.074 millimeter;
The sticking attapulgite clay powder of described height refers to get 28.0g attapulgite clay powder sample, add in the suspension cup of homogenizer, add 372g water again, the suspension cup is placed on the homogenizer, under 11000 rev/mins rotating speed, stirred 20 minutes, to pour in the beaker of 250ml the viscosity of using NDJ-1 type rotational viscosimeter to test its suspension, tested viscosity value 〉=2200 again through the high-speed stirring sample suspension into
MPasThe attapulgite clay powder.