CN103254698B - Sound-insulation and vibration-absorption damping slurry and production method - Google Patents
Sound-insulation and vibration-absorption damping slurry and production method Download PDFInfo
- Publication number
- CN103254698B CN103254698B CN201310228688.4A CN201310228688A CN103254698B CN 103254698 B CN103254698 B CN 103254698B CN 201310228688 A CN201310228688 A CN 201310228688A CN 103254698 B CN103254698 B CN 103254698B
- Authority
- CN
- China
- Prior art keywords
- parts
- damping slurry
- sound insulation
- absorbing damping
- vibration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses sound-insulation and vibration-absorption damping slurry which comprises the following raw materials in parts by weight: 20-30 parts of water, 0.1-0.5 parts of cellulose, 0.1-0.2 parts of AMP-95 (2-amino-2-methyl-1-propanol), 0.5-2 parts of dispersing agent, 0.05-0.2 parts of wetting agent, 0.1-0.5 parts of defoaming agent, 5-10 parts of titanium dioxide, 10-20 parts of calcium carbonate, 10-20 parts of mica powder, 5-10 parts of vermiculite powder, 1-2 parts of film formation aid, 1-2 parts of glycol, 30-40 parts of styrene-acrylic emulsion, 0.05-0.2 parts of preserving agent, and 0.5-1 part of alkali swelling thickener. The sound-insulation and vibration-absorption damping slurry is lower in production cost, better in vibration-reduction effect and better in noise-reduction effect.
Description
Technical field
The present invention relates to a kind of damping slurry and production method, particularly a kind of sound insulation absorbing damping slurry and production method.
Background technology
In recent decades, along with the development of modern industry, vibration tool and at a high speed and automated mechanical equipment increasing, the vibration thereupon caused, noise and FATIGUE FRACTURE PROBLEMS are also more and more outstanding.In daily life, the health of this kind of vibration & noise meeting harmful to human, severe patient is disablement even; In engineering, the response of vibration & noise exciting resonance peak also directly can affect the normal work of electron device, instrument and instrument, can cause catastrophic effect time serious.
Therefore, a lot of employing damping slurry is coated in metal plate structure surface and carries out vibration and noise reducing to this, and damping slurry coating is different from sound-absorbing material, and its principle vibration mechanical energy is converted into heat energy dissipate.Conventional damping slurry coating is made up of vinylformic acid IPN emulsion, damping color stuffing, fire retardant and auxiliary agent, and raw materials cost is higher, and production cost is improved, and vibration and noise reducing performance is general.
Summary of the invention
The object of the invention is to, a kind of sound insulation absorbing damping slurry and production method are provided.Production cost of the present invention is lower, and effect of vibration and noise reduction is better.
Technical scheme of the present invention: sound insulation absorbing damping slurry, it is characterized in that, it is made up of the raw material of following weight part: 20 ~ 30 parts of water, 0.1 ~ 0.5 part of Mierocrystalline cellulose, 0.1 ~ 0.2 part of AMP-95,0.5 ~ 2 part of dispersion agent, 0.05 ~ 0.2 part of wetting agent, 0.1 ~ 0.5 part of defoamer, 5 ~ 10 parts of titanium dioxides, 10 ~ 20 parts of coarse whitings, 10 ~ 20 parts of mica powders, 5 ~ 10 parts of vermiculite powers, 1 ~ 2 part of film coalescence aid, 1 ~ 2 part of ethylene glycol, 30 ~ 40 parts of benzene emulsions, 0.05 ~ 0.2 part of sanitas, 0.5 ~ 1 part of alkali swollen thickener.
In aforesaid sound insulation absorbing damping slurry, it is made up of the raw material of following weight part: 25 parts of water, 0.3 part of Mierocrystalline cellulose, 0.15 part of AMP-95,1.25 parts of dispersion agents, 0.125 part of wetting agent, 0.3 part of defoamer, 7.5 parts of titanium dioxides, 15 parts of coarse whitings, 15 parts of mica powders, 7.5 parts of vermiculite powers, 1.5 parts of film coalescence aid, 1.5 parts of ethylene glycol, 35 parts of benzene emulsions, 0.125 part of sanitas, 0.75 part of alkali swollen thickener.
In aforesaid sound insulation absorbing damping slurry, described coarse whiting is 800 object coarse whitings.
In aforesaid sound insulation absorbing damping slurry, described mica powder is 600 object mica powders.
In aforesaid sound insulation absorbing damping slurry, described vermiculite power is 300 object vermiculite powers.
In aforesaid sound insulation absorbing damping slurry, described film coalescence aid is C-12 film coalescence aid.
The production method of aforesaid sound insulation absorbing damping slurry, is characterized in that, carries out after above-mentioned each raw material dosage according to the following steps:
1. first speed stirring water, Mierocrystalline cellulose, dispersion agent, wetting agent and defoamer mixed with 800 revs/min makes it be uniformly dispersed;
2. add titanium dioxide, coarse whiting, mica powder and the vermiculite power speed of 1200 revs/min to stir;
3. add C-12 film coalescence aid, ethylene glycol and the benzene emulsion speed of 800 revs/min to stir;
4. finally add sanitas, AMP-95 and alkali swelling type thickening material, mix to obtain finished product.
Compared with prior art, the present invention, by rational proportion component, makes each component mutually mate, makes to have the following advantages: production cost is lower; Viscosity is low, easy construction, can be painted on the plate construction surfaces such as color steel and carry out vibration and noise reducing, workmen not easily be contacted, hygienic environment-protecting; Strong adhesion, difficult drop-off; Application property is good, can improve operating efficiency.Production method of the present invention is simple, and use equipment few, production cost is low, and quality is good.The present invention adopts environmental protection raw material, and mixes fully, and make the dispersed mixing of each component, the smell be not harmful to health completely, guarantees use safety.Not only viscosity is low in the present invention, strong adhesion, can spray, convenient construction, improves operating efficiency; And good leveling property, result of use is better.
The present invention draws by experiment: the long 180mm of metallic substance that experiment adopts, wide 9.1mm, plate thickness 0.86mm, metallic substance density 7800kg/m
3, spillage of material factor is 0.18, and be the damping layer (damping slurry of the present invention) of 1.94mm at metal material surface coating thickness, damping material loss factor can reach 0.479.The damping layer of coating is not only thinner, and effect of vibration and noise reduction is more satisfactory, also reduces use cost.
Embodiment
Below in conjunction with embodiment, the present invention is further illustrated, but not as the foundation limited the present invention.
Embodiment 1.Sound insulation absorbing damping slurry, it is characterized in that, it is made up of the raw material of following weight part: 20 ~ 30 parts of water, 0.1 ~ 0.5 part of Mierocrystalline cellulose, 0.1 ~ 0.2 part of AMP-95,0.5 ~ 2 part of dispersion agent, 0.05 ~ 0.2 part of wetting agent, 0.1 ~ 0.5 part of defoamer, 5 ~ 10 parts of titanium dioxides, 10 ~ 20 parts of coarse whitings, 10 ~ 20 parts of mica powders, 5 ~ 10 parts of vermiculite powers, 1 ~ 2 part of film coalescence aid, 1 ~ 2 part of ethylene glycol, 30 ~ 40 parts of benzene emulsions, 0.05 ~ 0.2 part of sanitas, 0.5 ~ 1 part of alkali swollen thickener.
Reasonable, it is made up of the raw material of following weight part: 25 parts of water, 0.3 part of Mierocrystalline cellulose, 0.15 part of AMP-95,1.25 parts of dispersion agents, 0.125 part of wetting agent, 0.3 part of defoamer, 7.5 parts of titanium dioxides, 15 parts of coarse whitings, 15 parts of mica powders, 7.5 parts of vermiculite powers, 1.5 parts of film coalescence aid, 1.5 parts of ethylene glycol, 35 parts of benzene emulsions, 0.125 part of sanitas, 0.75 part of alkali swollen thickener.
Be more preferably, described coarse whiting is 800 object coarse whitings.Described mica powder is 600 object mica powders.Described vermiculite power is 300 object vermiculite powers.Described film coalescence aid is C-12 film coalescence aid.
The production method of above-mentioned sound insulation absorbing damping slurry, carry out after above-mentioned each raw material dosage according to the following steps:
1. first speed stirring water, Mierocrystalline cellulose, dispersion agent, wetting agent and defoamer mixed with 800 revs/min makes it be uniformly dispersed;
2. add titanium dioxide, coarse whiting, mica powder and the vermiculite power speed of 1200 revs/min to stir;
3. add C-12 film coalescence aid, ethylene glycol and the benzene emulsion speed of 800 revs/min to stir;
4. finally add sanitas, AMP-95 and alkali swelling type thickening material, mix to obtain finished product.
Embodiment 2.Sound insulation absorbing damping slurry, it also can be made up of the raw material of following weight part: 20 parts of water, 0.5 part of Mierocrystalline cellulose, 0.1 part of AMP-95,2 parts of dispersion agents, 0.05 part of wetting agent, 0.5 part of defoamer, 5 parts of titanium dioxides, 20 parts of coarse whitings, 10 parts of mica powders, 10 parts of vermiculite powers, 1 part of film coalescence aid, 2 parts of ethylene glycol, 30 parts of benzene emulsions, 0.2 part of sanitas, 0.5 part of alkali swollen thickener.Be prepared by the production method in embodiment 1.
Embodiment 3.Sound insulation absorbing damping slurry, it can also be made up of the raw material of following weight part: 30 parts of water, 0.1 part of Mierocrystalline cellulose, 0.2 part of AMP-95,0.5 part of dispersion agent, 0.2 part of wetting agent, 0.1 part of defoamer, 10 parts of titanium dioxides, 10 parts of coarse whitings, 20 parts of mica powders, 5 parts of vermiculite powers, 2 parts of film coalescence aid, 1 part of ethylene glycol, 40 parts of benzene emulsions, 0.05 part of sanitas, 1 part of alkali swollen thickener.Be prepared by the production method in embodiment 1.
Claims (6)
1. insulate against sound absorbing damping slurry, it is characterized in that, it is made up of the raw material of following weight part: 25 parts of water, 0.3 part of Mierocrystalline cellulose, 0.15 part of AMP-95,1.25 parts of dispersion agents, 0.125 part of wetting agent, 0.3 part of defoamer, 7.5 parts of titanium dioxides, 15 parts of coarse whitings, 15 parts of mica powders, 7.5 parts of vermiculite powers, 1.5 parts of film coalescence aid, 1.5 parts of ethylene glycol, 35 parts of benzene emulsions, 0.125 part of sanitas, 0.75 part of alkali swollen thickener.
2. sound insulation absorbing damping slurry according to claim 1, is characterized in that: described coarse whiting is 800 object coarse whitings.
3. sound insulation absorbing damping slurry according to claim 1, is characterized in that: described mica powder is 600 object mica powders.
4. sound insulation absorbing damping slurry according to claim 1, is characterized in that: described vermiculite power is 300 object vermiculite powers.
5. sound insulation absorbing damping slurry according to claim 1, is characterized in that: described film coalescence aid is C-12 film coalescence aid.
6. the production method of the sound insulation absorbing damping slurry according to the arbitrary claim of claim 1-5, is characterized in that, carries out after above-mentioned each raw material dosage according to the following steps:
1. first speed stirring water, Mierocrystalline cellulose, dispersion agent, wetting agent and defoamer mixed with 800 revs/min makes it be uniformly dispersed;
2. add titanium dioxide, coarse whiting, mica powder and the vermiculite power speed of 1200 revs/min to stir;
3. add C-12 film coalescence aid, ethylene glycol and the benzene emulsion speed of 800 revs/min to stir;
4. finally add sanitas, AMP-95 and alkali swelling type thickening material, mix to obtain finished product.