CN103254698A - Sound-insulation and vibration-absorption damping slurry and production method - Google Patents
Sound-insulation and vibration-absorption damping slurry and production method Download PDFInfo
- Publication number
- CN103254698A CN103254698A CN2013102286884A CN201310228688A CN103254698A CN 103254698 A CN103254698 A CN 103254698A CN 2013102286884 A CN2013102286884 A CN 2013102286884A CN 201310228688 A CN201310228688 A CN 201310228688A CN 103254698 A CN103254698 A CN 103254698A
- Authority
- CN
- China
- Prior art keywords
- parts
- damping slurry
- sound insulation
- film coalescence
- coalescence aid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses sound-insulation and vibration-absorption damping slurry which comprises the following raw materials in parts by weight: 20-30 parts of water, 0.1-0.5 parts of cellulose, 0.1-0.2 parts of AMP-95 (2-amino-2-methyl-1-propanol), 0.5-2 parts of dispersing agent, 0.05-0.2 parts of wetting agent, 0.1-0.5 parts of defoaming agent, 5-10 parts of titanium dioxide, 10-20 parts of calcium carbonate, 10-20 parts of mica powder, 5-10 parts of vermiculite powder, 1-2 parts of film formation aid, 1-2 parts of glycol, 30-40 parts of styrene-acrylic emulsion, 0.05-0.2 parts of preserving agent, and 0.5-1 part of alkali swelling thickener. The sound-insulation and vibration-absorption damping slurry is lower in production cost, better in vibration-reduction effect and better in noise-reduction effect.
Description
Technical field
The present invention relates to a kind of damping slurry and production method, particularly a kind of sound insulation absorbing damping slurry and production method.
Background technology
In recent decades, along with development of modern industry, vibration tool and high speed and automated mechanical equipment are increasing, and the vibration that thereupon causes, noise and FATIGUE FRACTURE PROBLEMS are also more and more outstanding.In daily life, the health of this class vibration and noise meeting harmful to human, severe patient even disablement; In engineering, vibration and the response of noise exciting resonance peak also can directly influence the works better of electron device, instrument and instrument, can cause catastrophic effect when serious.
Therefore, much adopt damping slurry to be coated in the metal plate structure surface and this is carried out vibration and noise reducing, damping slurry coating is different with sound-absorbing material, and its principle is vibration mechanical energy to be converted into heat energy dissipate.Conventional damping slurry coating is made by vinylformic acid IPN emulsion, damping color stuffing, fire retardant and auxiliary agent, and raw materials cost is higher, make production cost improve, and the vibration and noise reducing performance is general.
Summary of the invention
The objective of the invention is to, a kind of sound insulation absorbing damping slurry and production method are provided.Production cost of the present invention is lower, and effect of vibration and noise reduction is better.
Technical scheme of the present invention: sound insulation absorbing damping slurry, it is characterized in that it is made up of the raw material of following weight part: 20～30 parts of water, 0.1～0.5 part of Mierocrystalline cellulose, 0.1～0.2 part of AMP-95,0.5～2 part of dispersion agent, 0.05～0.2 part of wetting agent, 0.1～0.5 part of defoamer, 5～10 parts of titanium dioxides, 10～20 parts of coarse whitings, 10～20 parts of mica powders, 5～10 parts of vermiculite powers, 1～2 part of film coalescence aid, 1～2 part of ethylene glycol, 30～40 parts of benzene emulsions, 0.05～0.2 portion of sanitas, 0.5～1 part of alkali swelling thickening material.
In the aforesaid sound insulation absorbing damping slurry, it is made up of the raw material of following weight part: 25 parts of water, 0.3 part of Mierocrystalline cellulose, 0.15 part of AMP-95,1.25 parts of dispersion agents, 0.125 part of wetting agent, 0.3 part of defoamer, 7.5 parts of titanium dioxides, 15 parts of coarse whitings, 15 parts of mica powders, 7.5 parts of vermiculite powers, 1.5 parts of film coalescence aid, 1.5 parts of ethylene glycol, 35 parts of benzene emulsions, 0.125 portion of sanitas, 0.75 part of alkali swelling thickening material.
In the aforesaid sound insulation absorbing damping slurry, described coarse whiting is 800 purpose coarse whitings.
In the aforesaid sound insulation absorbing damping slurry, described mica powder is 600 purpose mica powders.
In the aforesaid sound insulation absorbing damping slurry, described vermiculite power is 300 purpose vermiculite powers.
In the aforesaid sound insulation absorbing damping slurry, described film coalescence aid is the C-12 film coalescence aid.
The production method of aforesaid sound insulation absorbing damping slurry is characterized in that, will carry out according to the following steps after above-mentioned each raw material dosage:
1. the speed stirring that water, Mierocrystalline cellulose, dispersion agent, wetting agent and defoamer is mixed with 800 rev/mins earlier is uniformly dispersed it;
2. adding titanium dioxide, coarse whiting, mica powder and vermiculite power stirs with 1200 rev/mins speed;
3. adding C-12 film coalescence aid, ethylene glycol and benzene emulsion stirs with 800 rev/mins speed;
4. add sanitas, AMP-95 and alkali swelling type thickening material at last, mix finished product.
Compared with prior art, the present invention can mate each component by the rational proportion component mutually, and make to have the following advantages: production cost is lower; Viscosity is low, and easy construction can be painted on plate construction surface such as color steel and carry out vibration and noise reducing, makes the workmen be difficult for contact, hygienic environment-protecting; Strong adhesion, difficult drop-off; Application property is good, can improve operating efficiency.Production method of the present invention is simple, and use equipment is few, and production cost is low, and quality is good.The present invention adopts the environmental protection raw material, and mixes fully, makes the even dispersing and mixing of each component, and the smell that is not harmful to health fully exists, and guarantees to use safety.Not only viscosity is low in the present invention, strong adhesion, can spray, and convenient construction improves operating efficiency; And good leveling property, result of use is better.
The present invention draws by experiment: the long 180mm of metallic substance that experiment is adopted, wide 9.1mm, plate thickness 0.86mm, metallic substance density 7800kg/m
3, the spillage of material factor is the damping layer (damping slurry of the present invention) of 1.94mm 0.18 at the metal material surface coating thickness, the damping material loss factor can reach 0.479.The damping layer that applies is not only thinner, and effect of vibration and noise reduction is more satisfactory, has also reduced use cost.
Embodiment
The present invention is further illustrated below in conjunction with embodiment, but not as the foundation to the present invention's restriction.
Embodiment 1.Sound insulation absorbing damping slurry, it is characterized in that it is made up of the raw material of following weight part: 20～30 parts of water, 0.1～0.5 part of Mierocrystalline cellulose, 0.1～0.2 part of AMP-95,0.5～2 part of dispersion agent, 0.05～0.2 part of wetting agent, 0.1～0.5 part of defoamer, 5～10 parts of titanium dioxides, 10～20 parts of coarse whitings, 10～20 parts of mica powders, 5～10 parts of vermiculite powers, 1～2 part of film coalescence aid, 1～2 part of ethylene glycol, 30～40 parts of benzene emulsions, 0.05～0.2 portion of sanitas, 0.5～1 part of alkali swelling thickening material.
Reasonable is that it is made up of the raw material of following weight part: 25 parts of water, 0.3 part of Mierocrystalline cellulose, 0.15 part of AMP-95,1.25 parts of dispersion agents, 0.125 part of wetting agent, 0.3 part of defoamer, 7.5 parts of titanium dioxides, 15 parts of coarse whitings, 15 parts of mica powders, 7.5 parts of vermiculite powers, 1.5 parts of film coalescence aid, 1.5 parts of ethylene glycol, 35 parts of benzene emulsions, 0.125 portion of sanitas, 0.75 part of alkali swelling thickening material.
Be more preferably, described coarse whiting is 800 purpose coarse whitings.Described mica powder is 600 purpose mica powders.Described vermiculite power is 300 purpose vermiculite powers.Described film coalescence aid is the C-12 film coalescence aid.
The production method of above-mentioned sound insulation absorbing damping slurry, will carry out according to the following steps after above-mentioned each raw material dosage:
1. the speed stirring that water, Mierocrystalline cellulose, dispersion agent, wetting agent and defoamer is mixed with 800 rev/mins earlier is uniformly dispersed it;
2. adding titanium dioxide, coarse whiting, mica powder and vermiculite power stirs with 1200 rev/mins speed;
3. adding C-12 film coalescence aid, ethylene glycol and benzene emulsion stirs with 800 rev/mins speed;
4. add sanitas, AMP-95 and alkali swelling type thickening material at last, mix finished product.
Embodiment 2.Sound insulation absorbing damping slurry, it also can be made up of the raw material of following weight part: 20 parts of water, 0.5 part of Mierocrystalline cellulose, 0.1 part of AMP-95,2 parts of dispersion agents, 0.05 part of wetting agent, 0.5 part of defoamer, 5 parts of titanium dioxides, 20 parts of coarse whitings, 10 parts of mica powders, 10 parts of vermiculite powers, 1 part of film coalescence aid, 2 parts of ethylene glycol, 30 parts of benzene emulsions, 0.2 portion of sanitas, 0.5 part of alkali swelling thickening material.Be prepared by the production method among the embodiment 1.
Embodiment 3.Sound insulation absorbing damping slurry, it can also be made up of the raw material of following weight part: 30 parts of water, 0.1 part of Mierocrystalline cellulose, 0.2 part of AMP-95,0.5 part of dispersion agent, 0.2 part of wetting agent, 0.1 part of defoamer, 10 parts of titanium dioxides, 10 parts of coarse whitings, 20 parts of mica powders, 5 parts of vermiculite powers, 2 parts of film coalescence aid, 1 part of ethylene glycol, 40 parts of benzene emulsions, 0.05 portion of sanitas, 1 part of alkali swelling thickening material.Be prepared by the production method among the embodiment 1.
Claims (7)
1. the absorbing damping slurry insulates against sound, it is characterized in that it is made up of the raw material of following weight part: 20～30 parts of water, 0.1～0.5 part of Mierocrystalline cellulose, 0.1～0.2 part of AMP-95,0.5～2 part of dispersion agent, 0.05～0.2 part of wetting agent, 0.1～0.5 part of defoamer, 5～10 parts of titanium dioxides, 10～20 parts of coarse whitings, 10～20 parts of mica powders, 5～10 parts of vermiculite powers, 1～2 part of film coalescence aid, 1～2 part of ethylene glycol, 30～40 parts of benzene emulsions, 0.05～0.2 portion of sanitas, 0.5～1 part of alkali swelling thickening material.
2. sound insulation absorbing damping slurry according to claim 1, it is characterized in that it is made up of the raw material of following weight part: 25 parts of water, 0.3 part of Mierocrystalline cellulose, 0.15 part of AMP-95,1.25 parts of dispersion agents, 0.125 part of wetting agent, 0.3 part of defoamer, 7.5 parts of titanium dioxides, 15 parts of coarse whitings, 15 parts of mica powders, 7.5 parts of vermiculite powers, 1.5 parts of film coalescence aid, 1.5 parts of ethylene glycol, 35 parts of benzene emulsions, 0.125 portion of sanitas, 0.75 part of alkali swelling thickening material.
3. sound insulation absorbing damping slurry according to claim 1 and 2, it is characterized in that: described coarse whiting is 800 purpose coarse whitings.
4. sound insulation absorbing damping slurry according to claim 1 and 2, it is characterized in that: described mica powder is 600 purpose mica powders.
5. sound insulation absorbing damping slurry according to claim 1 and 2, it is characterized in that: described vermiculite power is 300 purpose vermiculite powers.
6. sound insulation absorbing damping slurry according to claim 1 and 2, it is characterized in that: described film coalescence aid is the C-12 film coalescence aid.
7. according to the production method of the described sound insulation absorbing of the arbitrary claim of claim 1-6 damping slurry, it is characterized in that, will carry out according to the following steps after above-mentioned each raw material dosage:
1. the speed stirring that water, Mierocrystalline cellulose, dispersion agent, wetting agent and defoamer is mixed with 800 rev/mins earlier is uniformly dispersed it;
2. adding titanium dioxide, coarse whiting, mica powder and vermiculite power stirs with 1200 rev/mins speed;
3. adding C-12 film coalescence aid, ethylene glycol and benzene emulsion stirs with 800 rev/mins speed;
4. add sanitas, AMP-95 and alkali swelling type thickening material at last, mix finished product.