CN103243565A - 使莫代尔针织面料抗菌抗起毛起球的整理剂及其整理方法 - Google Patents

使莫代尔针织面料抗菌抗起毛起球的整理剂及其整理方法 Download PDF

Info

Publication number
CN103243565A
CN103243565A CN2013101948416A CN201310194841A CN103243565A CN 103243565 A CN103243565 A CN 103243565A CN 2013101948416 A CN2013101948416 A CN 2013101948416A CN 201310194841 A CN201310194841 A CN 201310194841A CN 103243565 A CN103243565 A CN 103243565A
Authority
CN
China
Prior art keywords
finishing agent
pilling
fabric
fluffing
finishing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013101948416A
Other languages
English (en)
Other versions
CN103243565B (zh
Inventor
王春梅
胡啸林
缪勤华
王海峰
蔡红芹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Jinying Textile Product Testing Center Co ltd
Original Assignee
Nantong University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong University filed Critical Nantong University
Priority to CN201310194841.6A priority Critical patent/CN103243565B/zh
Publication of CN103243565A publication Critical patent/CN103243565A/zh
Application granted granted Critical
Publication of CN103243565B publication Critical patent/CN103243565B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种使莫代尔针织面料抗菌抗起毛起球的整理剂及其整理方法，由占织物重量百分比为1-3％纤维素酶、占织物重量百分比为0.5～1％壳聚糖和占织物重量百分比为2-3％的柔软剂组成。本发明使莫代尔针织面料在具有抗菌性的同时，抗起毛起球等级达到3-4级。

Description

使莫代尔针织面料抗菌抗起毛起球的整理剂及其整理方法
技术领域
本发明涉及一种整理剂及其整理工艺，具体涉及一种专用于莫代尔针织面料，能够使其抗菌抗起毛起球的整理剂及其整理方法。
背景技术
莫代尔(Modal)纤维是一种新型高湿模量纤维素纤维，具有十分优良的性能，是一种集棉的柔软、粘胶的吸湿能力、真丝的光泽为一体的生物降解纤维。由于莫代尔纤维比棉纤维细，纤维横截面为均匀圆形，纵向没有跟棉纤维相似的三维卷曲，随着纱线横截面数量的增加，加上纤维表面光滑，在湿整理加工过程中更多的纤维端从纱线中游离出来，产生表面起毛起球的倾向。莫代尔针织物结构疏松手感柔软，纤维间的抱合力小，受到摩擦时，纤维从织物内滑出，因而导致了莫代尔针织物起毛起球现象严重。
现有技术中，为了解决这一技术难题，通常采用酶的生物抛光处理、树脂整理、H2O2/紫外辐射、抗起毛起球剂整理等方法来提高织物的抗起毛起球效果。公开号为CN102808331A，发明名称为《一种具有抗起球效果的莫代尔面料生产方法》公开了一种具有抗起毛起球效果的莫代尔面料的生产方法，包括酶的预处理工艺和多元羧酸及催化剂的抗起毛起球整理工艺，这种工艺流程较长，对织物有一定的损伤。
发明内容
发明目的：本发明的目的是为了弥补现有技术的不足，提供一种使莫代尔针织面料抗菌抗起毛起球的整理剂，同时，本发明还提供了整理剂用于莫代尔织物的整理方法。
技术方案：一种使莫代尔针织面料抗菌抗起毛起球的整理剂，由占织物重量百分比为1-3％纤维素酶、占织物重量百分比为0.5～1％壳聚糖和占织物重量百分比为2-3％的柔软剂组成。
作为优选，所用纤维素酶为中性纤维素酶cellusoft CR即纤柔酶CR。
作为优选，壳聚糖分子量5万左右，脱乙酰度90％。
作为优选，柔软剂为TWSOFT HPS即亲水性柔油精。
为了实现本发明的另外一个目的，还提供了一种使莫代尔针织面料抗菌抗起毛起球的整理剂的整理方法，用上述整理剂，按照浴比为10-20∶1加入，在60℃处理40-50min，脱水之后，于90℃烘干后，再在140℃的温度下焙烘2min，即完成整理过程。
有益效果：本发明的整理剂由纤维素酶、壳聚糖和柔软剂组成，专用于容易起毛起球的莫代尔针织面料，纤维素酶能弱化微纤末端，去除从纱线表面的伸出的微细纤维，同时纤维素酶对壳聚糖具有水解作用，壳聚糖分子和纤维素分子相似，两者之间具有良好的亲和力。分子量较大的壳聚糖在纤维表面成膜，较小的壳聚糖分子或大分子的一端可以进入纤维内部，填充了纤维内的空隙并与纤维分子发生氢键、范德华力结合，阻止了纤维分子间在外力作用下的相对滑移。另外，带有-NH3 +的壳聚糖与纤维结合使纤维具有离子导电功能，使摩擦产生的静电荷迅速泄露，从而间接地提高了纤维的抗静电能力，摩擦时不易起球。同时壳聚糖分子上的-NH3 +通过结合负电子具有抑菌作用。柔软剂可降低织物纤维的定向摩擦效应，改善手感。这种整理方法，不仅工艺流程短，操作简单，节能节水，而且整理织物在具有抗起毛起球的同时还具有抗菌性能。
具体实施方式
在本申请中，中性纤维素酶cellusoft CR(纤柔酶CR)，由诺维信(Novozymes)公司生产；壳聚糖由南通生物工程研究所有限公司生产；柔软剂为TWSOFT HPS(亲水性柔油精)，由珠海华大浩宏化工有限公司生产。
实施例1
一种使莫代尔针织面料抗菌抗起毛起球的整理剂，由占织物重量百分比为1％纤维素酶、占织物重量百分比为0.5％壳聚糖和占织物重量百分比为2％的柔软剂组成。在本发明中，所用纤维素酶为cellusoft CR，壳聚糖分子量5万左右，脱乙酰度90％。柔软剂用的是为TWSOFTHPS。整理方法为：将上述整理剂，按照浴比(即整理液与织物重量之比)为10∶1加入，在60℃处理40min，脱水之后，于90℃烘干后，再在140℃的温度下焙烘2min，即完成整理过程。
用本发明所制的整理剂和整理方法得到的织物，参照GB/T4802.1-2008《纺织品织物起毛起球性能的测定第1部分：圆轨迹法》测试，抗起球起毛等级为3-4级。参照GB/T20944.1-2007《纺织品抗菌性能评价第1部分：琼脂平皿扩散法》标准，选用自然界和人体皮肤黏膜中较为常见的2种菌：金黄色匍萄球菌和大肠杆菌，测得抑菌圈宽度分别为1mm和2mm。
实施例2
一种使莫代尔针织面料抗菌抗起毛起球的整理剂，由占织物重量百分比为3％纤维素酶、占织物重量百分比为1％壳聚糖和占织物重量百分比为3％的柔软剂组成。在本发明中，所用纤维素酶为cellusoft CR，壳聚糖分子量5万左右，脱乙酰度90％。柔软剂用的是为TWSOFTHPS。整理方法为：将上述整理剂，按照浴比(即整理液与织物重量之比)为20∶1加入，在60℃处理50min，脱水之后，于90℃烘干后，再在140℃的温度下焙烘2min，即完成整理过程。
用本发明所制的整理剂和整理方法得到的织物，参照GB/T4802.1-2008《纺织品织物起毛起球性能的测定第1部分：圆轨迹法》测试，抗起球起毛等级为4级。参照GB/T20944.1-2007《纺织品抗菌性能评价第1部分：琼脂平皿扩散法》标准，选用自然界和人体皮肤黏膜中较为常见的2种菌：金黄色葡萄球菌和大肠杆菌，测得抑菌圈宽度分别为2mm和3mm。
实施例3：
一种使莫代尔针织面料抗菌抗起毛起球的整理剂，由占织物重量百分比为2％纤维素酶、占织物重量百分比为0.8％壳聚糖和占织物重量百分比为2.5％的柔软剂组成。在本发明中，所用纤维素酶为cellusoft CR，壳聚糖分子量5万左右，脱乙酰度90％。柔软剂用的是为TWSOFT HPS。整理方法为：将上述整理剂，按照浴比(即整理液与织物重量之比)为15∶1加入，在60℃处理45min，脱水之后，于90℃烘干后，再在140℃的温度下焙烘2min，即完成整理过程。
用本发明所制的整理剂和整理方法得到的织物，参照GB/T4802.1-2008《纺织品织物起毛起球性能的测定第1部分：圆轨迹法》测试，抗菌抗起球起毛等级为3-4级。参照GB/T20944.1-2007《纺织品抗菌性能评价第1部分：琼脂平皿扩散法》标准，选用自然界和人体皮肤黏膜中较为常见的2种菌：金黄色葡萄球菌和大肠杆菌，测得抑菌圈宽度分别为1.5mm和2.5mm。
实施例4：
一种使莫代尔针织面料抗菌抗起毛起球的整理剂，由占织物重量百分比为2.5％纤维素酶、占织物重量百分比为0.7％壳聚糖和占织物重量百分比为2.8％的柔软剂组成。在本发明中，所用纤维素酶为cellusoft CR，壳聚糖分子量5万左右，脱乙酰度90％。柔软剂用的是为TWSOFT HPS。整理方法为：将上述整理剂，按照浴比(即整理液与织物重量之比)为15∶1加入，在60℃处理45min，脱水之后，于90℃烘干后，再在140℃的温度下焙烘2min，即完成整理过程。
用本发明所制的整理剂和整理方法得到的织物，参照GB/T4802.1-2008《纺织品织物起毛起球性能的测定第1部分：圆轨迹法》测试，抗菌抗起球起毛等级为3-4级。参照GB/T20944.1-2007《纺织品抗菌性能评价第1部分：琼脂平皿扩散法》标准，选用自然界和人体皮肤黏膜中较为常见的2种菌：金黄色葡萄球菌和大肠杆菌，测得抑菌圈宽度分别为1.5mm和2.5mm。

Claims (5)

1.一种使莫代尔针织面料抗菌抗起毛起球的整理剂，其特征在于：由占织物重量百分比为1-3％纤维素酶、占织物重量百分比为0.5～1％壳聚糖和占织物重量百分比为2-3％的柔软剂组成。
2.如权利要求1所述的使莫代尔针织面料抗菌抗起毛起球的整理剂，其特征在于：所用纤维素酶为中性纤维素酶cellusoft CR即纤柔酶CR。
3.如权利要求1所述的使莫代尔针织面料抗菌抗起毛起球的整理剂，其特征在于：壳聚糖分子量5万左右，脱乙酰度约90％。
4.如权利要求1所述的使莫代尔针织面料抗菌抗起毛起球的整理剂，其特征在于：柔软剂为TWSOFT HPS即亲水性柔油精。
5.一种使莫代尔针织面料抗菌抗起毛起球的整理剂的整理方法，其特征在于：用权利要求1中所述的整理剂，按照浴比为10-20∶1加入，在60℃处理40-50min，脱水之后，于90℃烘干后，再在140℃的温度下焙烘2min，即完成整理过程。
CN201310194841.6A 2013-05-23 2013-05-23 使莫代尔针织面料抗菌抗起毛起球的整理剂及其整理方法 Active CN103243565B (zh)