CN103233523A - 建筑用新型外墙保温材料 - Google Patents
建筑用新型外墙保温材料 Download PDFInfo
- Publication number
- CN103233523A CN103233523A CN2013101711364A CN201310171136A CN103233523A CN 103233523 A CN103233523 A CN 103233523A CN 2013101711364 A CN2013101711364 A CN 2013101711364A CN 201310171136 A CN201310171136 A CN 201310171136A CN 103233523 A CN103233523 A CN 103233523A
- Authority
- CN
- China
- Prior art keywords
- insulation material
- building
- external wall
- parts
- wall heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种建筑用新型外墙保温材料,将物料搅拌均匀后,经加热预发泡,再在模具中挤出成型,所述物料包括按重量份比组成的以下成分:聚苯乙烯树脂100份,发泡剂0.7-1.2份,成核剂0.4-0.8份,润滑剂0.1-0.3份,其他辅助剂10-15份。通过上述方式,本发明的保温材料强度更高,可以起到保温隔热、耐气候、保持室内温度稳定、防潮、避免外墙结霜等作用,从而延长建筑物的使用寿命。
Description
技术领域
本发明涉及建筑装饰材料领域,特别是涉及一种建筑用新型外墙保温材料。
背景技术
随着建筑业的飞速发展,建筑节能的推行和发展,保温隔热材料与制品越来越受到人们的重视。
目前,最常用的外墙保温材料为聚苯乙烯塑料泡沫板,其主要材料为聚苯乙烯树脂,由于普通的聚苯乙烯树脂无毒、无臭、无色,似玻璃状,其制品具有极高的透明度,透光率可达90%以上,电绝缘性能好,易着色,加工流动性好,刚性好及耐化学腐蚀性好等,因此受到人们的亲睐。但是,其性脆,冲击强度低,易出现应力开裂,耐热性差及不耐沸水,因此,使用寿命较短。
发明内容
本发明主要解决的技术问题是:针对现有技术的不足,提供一种建筑用新型外墙保温材料,强度更高,可以起到保温隔热、耐气候、保持室内温度稳定、防潮、避免外墙结霜等作用,从而延长建筑物的使用寿命。
为解决上述技术问题,本发明采用的一个技术方案是:提供一种建筑用新型外墙保温材料,将物料搅拌均匀后,经加热预发泡,再在模具中挤出成型,所述物料包括按重量份比组成的以下成分:
聚苯乙烯树脂 100份,
发泡剂 0.7-1.2份,
成核剂 0.4-0.8份,
润滑剂 0.1-0.3份,
其他辅助剂 10-15份。
在本发明一个较佳实施例中,所述成核剂包括柠檬酸和碳酸氢钠。
在本发明一个较佳实施例中,所述润滑剂为硬脂酸钙、硅油、液态石蜡中的一种或几种。
在本发明一个较佳实施例中,所述其他辅助剂包括改性剂和阻燃剂。
本发明的有益效果是:采用聚苯乙烯树脂作为原材料,通过各添加剂的作用,提高了聚苯乙烯树脂的强度,使其对建筑物外墙具有强有力的保护作用,可以起到保温隔热、耐气候、保持室内温度稳定、防潮、避免外墙结霜等作用,从而延长建筑物的使用寿命。
具体实施方式
下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
本发明实施例包括:
实施例一:
在100份聚苯乙烯树脂中加入发泡剂1份,成核剂0.6份,润滑剂0.1份,改性剂7份和阻燃剂8份,搅拌均匀后,经加热预发泡,再在模具中挤出成型。
其中,所述成核剂中包括柠檬酸0.3份和碳酸氢钠0.3份。
所述润滑剂为硬脂酸钙,可以提高聚苯乙烯树脂在挤出成型时的可加工性。
由此得到的建筑用新型外墙保温材料具有优良的保温隔热性能,强度提高了30%以上,耐候性能增强了1.5倍,使用寿命可达100年以上。
实施例二:
在100份聚苯乙烯树脂中加入发泡剂0.8份,成核剂0.8份,润滑剂0.2份,改性剂6份和阻燃剂6份,搅拌均匀后,经加热预发泡,再在模具中挤出成型。
其中,所述成核剂中包括柠檬酸0.4份和碳酸氢钠0.4份。
所述润滑剂为硅油0.1份和液态石蜡0.1份,可以提高聚苯乙烯树脂在挤出成型时的可加工性。
由此得到的建筑用新型外墙保温材料具有优良的保温隔热性能,强度提高了30%以上,耐候性能增强了1.5倍,使用寿命可达100年以上。
本发明揭示了一种建筑用新型外墙保温材料,采用聚苯乙烯树脂作为原材料,通过各添加剂的作用,提高了聚苯乙烯树脂的强度,使其对建筑物外墙具有强有力的保护作用,可以起到保温隔热、耐气候、保持室内温度稳定、防潮、避免外墙结霜等作用,从而延长建筑物的使用寿命。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其他相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (4)
1.一种建筑用新型外墙保温材料,其特征在于,将物料搅拌均匀后,经加热预发泡,再在模具中挤出成型,所述物料包括按重量份比组成的以下成分:
聚苯乙烯树脂 100份,
发泡剂 0.7-1.2份,
成核剂 0.4-0.8份,
润滑剂 0.1-0.3份,
其他辅助剂 10-15份。
2.根据权利要求1所述的建筑用新型外墙保温材料,其特征在于,所述成核剂包括柠檬酸和碳酸氢钠。
3.根据权利要求1所述的建筑用新型外墙保温材料,其特征在于,所述润滑剂为硬脂酸钙、硅油、液态石蜡中的一种或几种。
4.根据权利要求1所述的建筑用新型外墙保温材料,其特征在于,所述其他辅助剂包括改性剂和阻燃剂。