CN103232564A - 一种透明弹性腻子用弹性乳液及其制备方法 - Google Patents
一种透明弹性腻子用弹性乳液及其制备方法 Download PDFInfo
- Publication number
- CN103232564A CN103232564A CN 201310134652 CN201310134652A CN103232564A CN 103232564 A CN103232564 A CN 103232564A CN 201310134652 CN201310134652 CN 201310134652 CN 201310134652 A CN201310134652 A CN 201310134652A CN 103232564 A CN103232564 A CN 103232564A
- Authority
- CN
- China
- Prior art keywords
- elastic
- putty
- transparent
- add
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及了一种透明弹性腻子用弹性乳液及其制备方法,该透明弹性腻子用弹性乳液主要由:甲基丙烯酸甲脂、丙烯酸丁酯、甲基丙烯酸、乳化剂、过硫酸铵、醋酸钠、氨水、去离子水、消泡剂等组成。该弹性乳液制成透明弹性腻子后,其施工后无需打磨,表面光滑平整、抗拉强度极强,可实现对基材的无接缝处理等特点。
Description
技术领域
本发明涉及一种透明弹性腻子用弹性乳液及其制备方法,属建筑材料领域。
背景技术
建筑墙体由于地基的不均匀沉降、基材随高、低温变化的热胀冷缩、振动源振动等原因而产生基材裂纹。这些裂纹有的出现在基材表面,有的则深及整个墙体,这些裂纹使基材表面涂刷的乳胶漆漆膜遭到破坏,从而失去装饰作用和对墙体的保护作用。
在现代装修过程中,对接缝的处理常采用粘贴胶带的方法,但这种粘贴胶带容易产生“空鼓”、“开裂”,还会使乳胶漆漆膜遭到破坏,从而失去装饰作用。
发明内容
本发明的目的就是要提供一种弹性乳液配制成透明弹性腻子,这种用弹性乳液配制成透明弹性腻子,施工后无需打磨,表面光滑平整、抗拉强度极强,无需涂刷抗碱封闭底漆可实现对基材的无接缝处理,
本发明是通过以下技术方案来实现的:其特征在于该透明弹性腻子用弹性乳液主要由:一种透明弹性腻子用弹性乳液及其制备方法,其特征在于该透明弹性腻子用弹性乳液主要由:甲基丙烯酸甲脂、丙烯酸丁酯、甲基丙烯酸、乳化剂、过硫酸铵、醋酸钠、氨水、去离子水、消泡 剂等组成。
按其重量份为:甲基丙烯酸甲脂100~140;丙烯酸丁酯200~250;甲基丙烯酸2~6;乳化剂5~25;过硫酸铵0.4~1.2;醋酸钠0.2~0.6;氨水0.2~0.4;去离子水320~380;消泡剂适量组成。
其氨水的含量为25%。
其制备方法为:
在装有冷凝器、搅拌器等的器皿中加入部分去离子水、乳化剂及醋酸钠搅拌升温,溶解成透明澄清液,升温至90℃±1℃,加入5%乳化液,1min后加入甲基丙烯酸甲脂、丙烯酸丁酯、甲基丙烯酸,加完后,保温反应1h,消除残余单体,冷却至50℃以下,加入氨水调整至PH7~8,搅拌2min,加入消泡剂搅拌10min以上,冷却至40℃,过滤、出料、包装。
具体实施方式
按重量比称取甲基丙烯酸甲脂110份;丙烯酸丁酯220份;甲基丙烯酸5份;乳化剂15份;过硫酸铵1.0份;醋酸钠0.5份;氨水0.3份;去离子水360份;消泡剂适量。
在装有冷凝器、搅拌器等的器皿中加入部分去离子水、乳化剂及醋酸钠搅拌升温,溶解成透明澄清液,升温至90℃±1℃,加入5%乳化液,1min后加入甲基丙烯酸甲脂、丙烯酸丁酯、甲基丙烯酸,加完后,保温反应1h,消除残余单体,冷却至50℃以下,加入氨水调整至PH7~8,搅拌2min,加入消泡剂搅拌10min以上,冷却至40℃,过滤、出料、包装。
Claims (4)
1.一种透明弹性腻子用弹性乳液及其制备方法,其特征在于该透明弹性腻子用弹性乳液主要由:甲基丙烯酸甲脂、丙烯酸丁酯、甲基丙烯酸、乳化剂、过硫酸铵、醋酸钠、氨水、去离子水、消泡剂等组成。
2.根据权利1所述的一种透明弹性腻子用弹性乳液,按其重量份为:甲基丙烯酸甲脂100~140;丙烯酸丁酯200~250;甲基丙烯酸2~6;乳化剂5~25;过硫酸铵0.4~1.2;醋酸钠0.2~0.6;氨水0.2~0.4;去离子水320~380;消泡剂适量组成。
3.根据权利1、2所述的一种透明弹性腻子用弹性乳液,其氨水的含量为25%。
4.根据权利1、2所述的一种透明弹性腻子用弹性乳液,其制备方法为:
在装有冷凝器、搅拌器等的器皿中加入部分去离子水、乳化剂及醋酸钠搅拌升温,溶解成透明澄清液,升温至90℃±1℃,加入5%乳化液,1min后加入甲基丙烯酸甲脂、丙烯酸丁酯、甲基丙烯酸,加完后,保温反应1h,消除残余单体,冷却至50℃以下,加入氨水调整至PH7~8,搅拌2min,加入消泡剂搅拌10min以上,冷却至40℃,过滤、出料、包装。