CN103223410A - Method for cleaning beer or drink glass bottle by high-pressure water - Google Patents

Abstract

The invention discloses a method for cleaning a beer or drink glass bottle by high-pressure water. The method comprises the steps as follows: firstly, soaking the beer or drink glass bottle with clear water of normal temperature to 45 DEG C for 4-5 min; secondly, synchronously aligning a bottle opening and the outer surface of the glass bottle, and carrying out high-pressure washing on the bottle opening and the outer surface of the glass bottle for 2-5 s by the clear water with the pressure of 1.5-2.0 MPa; thirdly, soaking the glass bottle once by alkali liquor of 45-55 DEG C for 2-3 min; and lastly, after soaking, washing out the alkali liquor by the clear water with the pressure of 0.1-0.3 MPa. The method has the characteristics of energy saving, water saving, capabilities of reducing the equipment manufacturing cost, the usage amount of the alkali liquor and the environmental pollution, simplicity for operation and the like.

Description

A kind of method that is used for beer, the cleaning of beverage glass bottle water under high pressure

 

Technical field

The present invention relates to the matting on beer, the beverage filling production lines, specifically is a kind of method that is used for beer, the cleaning of beverage glass bottle water under high pressure.

Background technology

The present vial that uses of beer, beverage, the still new bottle of returnable bottle no matter, all be to adopt following cleaning method before use: clear water pre-soaking-85 ° C dipping by lye-75 ° C dipping by lye-65 ° C dipping by lye-clear water washes.

The shortcoming of this technology is:

1, energy consumes high: because the high about 85 ° of C of thermokalite temperature and total soak time were about 12-15 minute, on average clean 0.4 liter of each vial consume water, consume steam 0.028KG.

2, equipment investment height: because the bottle that domestic recovery is returned is very dirty, bottle end dirt is many, generally is difficult to the bottle inner surface is cleaned up with a bottle washing machine, often adopts 2 series connection to use, perhaps bottle washing machine is strengthened and use, perhaps before wash bottle, set up a hairbrush prewasher.。

4, the long-time heat alkali liquid immersion of vial can cause the outer surface blushing, influences the vial outward appearance, and bad to the Fouling Cleaning effect of returnable bottle bottom.

Summary of the invention

Technical problem to be solved by this invention provides a kind of water under high pressure cleaning method, and this method is not only simple to operate, energy-saving and water-saving, has reduced the alkali lye use amount, has reduced equipment manufacturing cost simultaneously, has also reduced the pollution of environment.

A kind of method that is used for beer, the cleaning of beverage glass bottle water under high pressure of the present invention, this cleaning method step is as follows:

A kind of method that is used for the cleaning of beer beverage glass bottle water under high pressure is characterized in that this cleaning method step is as follows:

1) at first, the clear water of beer beverage glass bottle with normal temperature～45 ℃ soaked 4-5 minute;

2) then, adopting pressure is the clear water of 1.5～2.0MPa, aims at vial bottleneck and appearance thereof synchronously and carries out 2-5 high pressure washing second;

3) adopt 45-55 ° of C alkali lye that vial is once soaked, soak time is 2-3 minute;

4) soaked after, be that the clear water of 0.1～0.3MPa is rinsed alkali lye well and got final product with pressure at last.

Compared with prior art, the invention has the advantages that:

1, conserve energy: because the temperature that alkali soaks has only 40-45 ° of C, the time only needs about 2 minutes, therefore saves heat energy 70-80%;

2, conserve water: soak owing to adopt direct hydro-peening to substitute, and the hydro-peening time is of short duration, water saving reaches 30-40%;

3, environmental protection: the dipping by lye time reduced to 2-3 minute by 12-15 minute, therefore saved alkali lye and consumed 60-70%; The alkali lye use amount reduces simultaneously, has also reduced discharge capacity, has protected environment.

4, reduce equipment manufacturing cost: owing to reduce the time of dipping by lye, also reduced by 3-4 alkali groove accordingly, can reduce equipment manufacturing cost about 20%.

The specific embodiment

A kind of method that the beer beverage glass bottle water under high pressure cleans that is used for of the present invention, this method step is as follows:

1) at first, the clear water of beer beverage glass bottle with normal temperature～45 ℃ soaked 4-5 minute;

2) then, adopting pressure is the clear water of 1.5～2.0MPa, aims at vial bottleneck and appearance thereof synchronously and carries out 2-5 high pressure washing second;

3) adopt 45-55 ° of C alkali lye that vial is once soaked again, soak time is 2-3 minute;

4) soaked after, be that the clear water of 0.1～0.3MPa is rinsed alkali lye well and got final product with pressure at last.

The invention provides a kind of method that the beer beverage glass bottle water under high pressure cleans that is used for; the above only is a preferred implementation method of the present invention; should be understood that; for those skilled in the art; under the prerequisite that does not break away from the principle of the invention; can also make some improvement, these improvement also should be considered as protection scope of the present invention.

Claims (1)

1. one kind is used for the method that the beer beverage glass bottle water under high pressure cleans, and it is characterized in that this cleaning method step is as follows:

1) at first, the clear water of beer beverage glass bottle with normal temperature～45 ℃ soaked 4～5 minutes;

2) then, adopting pressure is the clear water of 1.5～2.0MPa, aims at vial bottleneck and appearance thereof synchronously and carries out 2-5 high pressure washing in second;

3) adopt 45～55 ° of C alkali lye that vial is once soaked, soak time is 2～3 minutes;

4) soaked after, be that the clear water of 0.1～0.3MPa is rinsed alkali lye well and got final product with pressure at last.