CN103219107A - 一种电力电缆用聚四氟乙烯膜 - Google Patents
一种电力电缆用聚四氟乙烯膜 Download PDFInfo
- Publication number
- CN103219107A CN103219107A CN2012102707272A CN201210270727A CN103219107A CN 103219107 A CN103219107 A CN 103219107A CN 2012102707272 A CN2012102707272 A CN 2012102707272A CN 201210270727 A CN201210270727 A CN 201210270727A CN 103219107 A CN103219107 A CN 103219107A
- Authority
- CN
- China
- Prior art keywords
- power cable
- electric power
- polytetrafluoroethylene film
- poly tetrafluoroethylene
- tensile strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种电力电缆用聚四氟乙烯膜。其特征在于所述的电力电缆用聚四氟乙烯膜的卷长为50m－3000m，厚度为0.03mm－0.3mm，密度为1.5－1.6g/cm3,抗拉强度径向至少为15MPa，纬向至少为2.5MPa。本发明的电力电缆用聚四氟乙烯膜可有效提高电力电缆的综合性能，尤其是长度长，厚度均匀，缠绕导体上既可以避免重复缠绕而使电流传输过程中重复缠绕部位散热效率降低，温度升高，增加电力电缆阻抗，又可解决现有的电力电缆绝缘层和护套层同心度差的问题，并提高电流传输效率，降低能耗。本发明的电力电缆用聚四氟乙烯膜适宜于电力电缆的应用。
Description
技术领域
本发明涉及一种电力电缆，特别是涉及一种电力电缆用聚四氟乙烯膜。
背景技术
目前所使用的电力电缆绝缘层外径大，且安装使用时易被拉断或裂开，严重影响电力电缆使用的安全性，并且所使用的电力电缆绝缘层大多不耐高温，当天气炎热或电缆使用环境温度较高以及电力电缆导体传输电流过程中所产生大量的热量容易使绝缘层软化甚至引起火灾，另外所使用的电力电缆绝缘层和护套层同心度差，影响电流的传输效率，总而言之，所使用的电力电缆绝缘层存在种种不足之处，由此影响所用电力电缆的使用寿命。
发明内容
本发明的目的是要提供一种电力电缆用聚四氟乙烯膜，它不但能有效地提高电力电缆的综合性能，而且缠绕导体上既可以避免重复缠绕而使电流传输过程中重复缠绕部位散热效率降低，温度升高，增加电力电缆阻抗，又可解决现有的电力电缆绝缘层和护套层同心度差的问题，并提高电流传输效率，降低能耗。
为了达到上述的目的本发明是这样实现的: 本发明的电力电缆用聚四氟乙烯膜的卷长为50m－3000m，厚度为0.03mm－0.3mm，密度为1.5－1.6g/cm3，抗拉强度径向至少为15MPa，纬向至少为2.5MPa。
所述的电力电缆用聚四氟乙烯膜卷长为50m－1000m的厚度公差为±0.003mm。
所述的电力电缆用聚四氟乙烯膜卷长为1000m－2000m的厚度公差为±0.004mm。
所述的电力电缆用聚四氟乙烯膜卷长为2000m－3000m的厚度公差为±0.005mm。
所述的电力电缆用聚四氟乙烯膜的密度公差为±0.03g/cm3。
本发明提供了一种电力电缆用聚四氟乙烯膜，且将聚四氟乙烯分散树脂添加助剂混合成糊状，然后将糊状树脂经过模具挤出制成膜片，再将膜片加热脱油、高温烧结、一次定型、二次定型等工序制成电缆膜，最后分切成卷。
本发明的电力电缆用聚四氟乙烯膜的卷长为50m－3000m，厚度为0.03mm－0.3mm，密度为1.5－1.6g/cm3，抗拉强度径向至少为15MPa，纬向至少为2.5MPa。
本发明的电力电缆用聚四氟乙烯膜具有如下特点：
1、柔韧性：本发明的电力电缆用聚四氟乙烯膜借助自身柔韧性，且提高抗拉强度径向至少为15MPa，纬向至少为2.5MPa，由此，缠绕在导体上，大大提高了电力电缆的安全性及使用寿命。
2、绝缘性：本发明的电力电缆用聚四氟乙烯膜在很宽的频率范围内都具有良好的介电性能及电学稳定性，在达到10MHz频率之前介质损耗角正切值在0.0004以下，介电常数为2.1。
3、耐寒热性：本发明的电力电缆用聚四氟乙烯膜的介电常数和介质损耗角正切值在-40℃－240℃温度范围内基本保持恒定，达到c级绝缘材料标准，即耐温180℃以上。
4、耐化学性：本发明的电力电缆用聚四氟乙烯膜另具有极好的耐大气老化性，老化寿命是所有塑料中时间最长的材料，对大多数化学药品和溶剂，表现出惰性。除氟气和熔融状态下的金属钠对其有一定腐蚀性外，几乎所有的强酸、强碱、强氧化剂和有机溶剂对它都不起作用。
5、阻燃性：本发明的电力电缆用聚四氟乙烯膜耐高温至260℃，熔点温度在330℃以上，且不易燃烧，可以有效避免电力电缆使用过程中因发热起火的现象，限氧指数在90以下。
6、厚度均匀：本发明的电力电缆用聚四氟乙烯膜厚度为0.03mm－0.3mm，厚度公差为±0.005mm，密度为1.5－1.6g/cm3，密度公差为±0.03g/cm3，且缠绕导体上既可以解决现有的电缆绝缘层和护套层同心度差的问题，并提高电流传输效率，降低能耗，又可以有效保证电线电流传输过程中所产生的热量在各个方位散热效率基本相同，从而也保证整个电力电缆各位置温度基本相同，从而减少温差所产生阻抗。
7、长度长：本发明的电力电缆用聚四氟乙烯膜的卷长为50m－3000m，将有利于减少缠绕长度不够而产生接头，有效避免重复缠绕而使电流传输过程中重复缠绕部位散热效率降低，温度升高，增加电缆阻抗。
简而言之，本发明的电力电缆用聚四氟乙烯膜既拥用聚四氟乙烯的特性又加工制作成符合电力电缆用的膜，且可有效提高电力电缆的综合性能。本发明的电力电缆用聚四氟乙烯膜适宜于电力电缆的应用。
附图说明
本发明的具体结构由以下的实施例及其附图给出。
图１是本发明的电力电缆用聚四氟乙烯膜的示意图。
具体实施方式
以下将结合附图对本发明的电力电缆用聚四氟乙烯膜作进一步的详细描述。
参照图1，该发明的电力电缆用聚四氟乙烯膜1的卷长为50m－3000m，厚度为0.03mm－0.3mm，所述的电力电缆用聚四氟乙烯膜1卷长为50m－1000m的厚度公差为±0.003mm，所述的电力电缆用聚四氟乙烯膜1卷长为1000m-2000m的厚度公差为±0.004mm。所述的电力电缆用聚四氟乙烯膜1卷长为2000m－3000m的厚度公差为±0.005mm。
所述的电力电缆用聚四氟乙烯膜1的密度为1.5－1.6g/cm3，密度公差为±0.03g/cm3。
所述的电力电缆用聚四氟乙烯膜1的抗拉强度径向至少为15MPa，纬向至少为2.5MPa。
Claims (5)
1.一种电力电缆用聚四氟乙烯膜，其特征在于所述的电力电缆用聚四氟乙烯膜（1）的卷长为50m－3000m，厚度为0.03mm－0.3mm，密度为1.5－1.6g/cm3, 抗拉强度径向至少为15MPa，纬向至少为2.5MPa。
2.根据权利要求1所述的电力电缆用聚四氟乙烯膜，其特征在于所述的电力电缆用聚四氟乙烯膜（1）卷长为50m－1000m的厚度公差为±0.003mm。
3.根据权利要求1所述的电力电缆用聚四氟乙烯膜，其特征在于所述的电力电缆用聚四氟乙烯膜（1）卷长为1000m-2000m的厚度公差为±0.004mm。
4.根据权利要求1所述的电力电缆用聚四氟乙烯膜，其特征在于所述的电力电缆用聚四氟乙烯膜（1）卷长为2000m－3000m的厚度公差为±0.005mm。
5.根据权利要求1所述的电力电缆用聚四氟乙烯膜，其特征在于所述的电力电缆用聚四氟乙烯膜（1）的密度公差为±0.03g/cm3。