CN103214892A - Corrosion-resistant antirusting paint - Google Patents
Corrosion-resistant antirusting paint Download PDFInfo
- Publication number
- CN103214892A CN103214892A CN 201310114633 CN201310114633A CN103214892A CN 103214892 A CN103214892 A CN 103214892A CN 201310114633 CN201310114633 CN 201310114633 CN 201310114633 A CN201310114633 A CN 201310114633A CN 103214892 A CN103214892 A CN 103214892A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- powder
- lacquer
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a corrosion-resistant antirusting paint. The paint is characterized by consisting of paint powder, maleic anhydride, zeolite powder, rosin phenolic resin, mica powder, a filler, pigment and a solvent. The paint has the beneficial effects that the paint powder is coated on metal, so that the metal and paint corrosion and oxidization due to rain seasons or long-term exposure can be effectively avoided, and the paint is suitable for severe environments; and the main raw materials of the paint are common materials in the market, are easily available and low in cost.
Description
Technical field
The present invention relates to a kind of antiseptic and rustproof paint.
Background technology
The general composition of paint comprises: filmogen, pigment, solvent, auxiliary agent.Paint is a kind ofly can firmly cover body surface, plays protection, decorates, the chemical mixture coating of sign and other special purposes.China's coating circle relatively authority's coating process one book is definition like this: coating is a kind of material, and this material can be coated in article surface with different implementing process, forms to adhere to firmly, have certain intensity, continuous solid-state film.The film common name that forms is like this filmed, and claims paint film or coating again.Belong to organic chemical industry's macromolecular material, formed filming belongs to the macromolecular compound type.According to the classification of current Chemicals of modern times, coating belongs to fine chemical product.The whitewashing of modern paint not only can spread out of one pungent taste later, and can be not easy to do in the regular hour, and very poor in viscosity, whitewashes on metal, and understanding react with metal gets rusty burning.
Summary of the invention
It is good that the technical problem to be solved in the present invention provides a kind of viscosity, long service life and whitewash have antiseptic and rustproof paint on metal.
For addressing the above problem, the present invention adopts following technical scheme:
A kind of antiseptic and rustproof paint, this paint is by lacquer powder, MALEIC ANHYDRIDE, zeolite powder, rosin phenolic resin, mica powder, filler, pigment and solvent composition.
As optimized technical scheme, described paint and each components contents are respectively:
As optimized technical scheme, the preparation process of described paint is as follows:
A) extract respectively by the deal of each content: 20 parts in lacquer powder, 7 parts of MALEIC ANHYDRIDE, 8 parts of zeolite powders, 15 parts of rosin phenolic resins, 8 parts of mica powders, 26 parts of fillers, 12 parts of 4 parts of pigment and solvents;
B) will coat with lacquer 20 parts in powder, 7 parts of MALEIC ANHYDRIDE, 8 parts of mica powders, 8 parts of zeolite powders, 26 parts of 12 parts of solvents and fillers are put into processing units and are carried out, and temperature is controlled at 30 ℃-80 ℃, then stirs 30-45 minute, makes it even, forms paint;
C) in paint, add 15 parts of rosin phenolic resins then, evenly stir and add 4 parts of pigment after 15 minutes again, be processed into coloured paint at the equipment of putting into solidification;
D) paint at last by specific equipment and be installed in the lacquer tube.
The invention has the beneficial effects as follows: 1, whitewashing of the present invention is on metal, and metal and paint corrosion and the oxidation that can effectively avoid because of rainy season or be exposed to the sun for a long time and caused are fit in the rugged environment; 2, raw material is mainly material common on some markets, obtain easily, and cost is low.
Embodiment
A kind of antiseptic and rustproof paint, this paint is by lacquer powder, MALEIC ANHYDRIDE, zeolite powder, rosin phenolic resin, mica powder, filler, pigment and solvent composition.
Wherein, described paint and each components contents are respectively:
The preparation process of described paint is as follows:
The preparation process of described paint is as follows:
A) extract respectively by the deal of each content: 20 parts in lacquer powder, 7 parts of MALEIC ANHYDRIDE, 8 parts of zeolite powders, 15 parts of rosin phenolic resins, 8 parts of mica powders, 26 parts of fillers, 12 parts of 4 parts of pigment and solvents;
B) will coat with lacquer 20 parts in powder, 7 parts of MALEIC ANHYDRIDE, 8 parts of mica powders, 8 parts of zeolite powders, 26 parts of 12 parts of solvents and fillers are put into processing units and are carried out, and temperature is controlled at 30 ℃-80 ℃, then stirs 30-45 minute, makes it even, forms paint;
C) in paint, add 15 parts of rosin phenolic resins then, evenly stir and add 4 parts of pigment after 15 minutes again, be processed into coloured paint at the equipment of putting into solidification;
D) paint at last by specific equipment and be installed in the lacquer tube.
The invention has the beneficial effects as follows: 1, whitewashing of the present invention is on metal, and metal and paint corrosion and the oxidation that can effectively avoid because of rainy season or be exposed to the sun for a long time and caused are fit in the rugged environment; 2, raw material is mainly material common on some markets, obtain easily, and cost is low.
Concrete enforcement 1
Described paint and each components contents are respectively:
Get the material of following mass fraction: 20 parts in lacquer powder, 7 parts of MALEIC ANHYDRIDE, 8 parts of zeolite powders, 15 parts of rosin phenolic resins, 8 parts of mica powders, 26 parts of fillers, 12 parts of 4 parts of pigment and solvents after the system of processing prepares, are placed two weeks in the lacquer tube, take out use again.The present invention finds that whitewashing has antiseptic and rustproof effect on metal in enforcement, is fit to use in the severe environment.
Concrete enforcement 2
Described paint and each components contents are respectively:
Get the material of following mass fraction: 20 parts in lacquer powder, 7 parts of MALEIC ANHYDRIDE, 8 parts of mica powders, 8 parts of zeolite powders, 26 parts of 12 parts of solvents and fillers, batching processing back is adding 4 parts of 15 parts of rosin phenolic resins and pigment, through obtaining coloured paint after the processing, place two weeks in the lacquer tube then, take out use again.The present invention finds that whitewashing not only has antiseptic and rustproof effect on metal in enforcement, and appearance is more attractive in appearance, is fit to use in the severe environment.
The above only is the specific embodiment of the present invention, but protection scope of the present invention is not limited thereto, and any variation or replacement of expecting without creative work all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claims were limited.
Claims (3)
1. antiseptic and rustproof paint is characterized in that: this paint is by lacquer powder, MALEIC ANHYDRIDE, zeolite powder, rosin phenolic resin, mica powder, filler, pigment and solvent composition.
2. antiseptic and rustproof paint according to claim 1 is characterized in that: described paint and each components contents are respectively:
3. according to claim 1 and 2 described antiseptic and rustproof paint and preparation method thereof, it is characterized in that: the preparation process of described paint is as follows:
A) extract respectively by the deal of each content: 20 parts in lacquer powder, 7 parts of MALEIC ANHYDRIDE, 8 parts of zeolite powders, 15 parts of rosin phenolic resins, 8 parts of mica powders, 26 parts of fillers, 12 parts of 4 parts of pigment and solvents;
B) will coat with lacquer 20 parts in powder, 7 parts of MALEIC ANHYDRIDE, 8 parts of mica powders, 8 parts of zeolite powders, 26 parts of 12 parts of solvents and fillers are put into processing units and are carried out, and temperature is controlled at 30 ℃-80 ℃, then stirs 30-45 minute, makes it even, forms paint;
C) in paint, add 15 parts of rosin phenolic resins then, evenly stir and add 4 parts of pigment after 15 minutes again, be processed into coloured paint at the equipment of putting into solidification;
D) paint at last by specific equipment and be installed in the lacquer tube.