CN103214862A - Formula of wear-resistant and environment-friendly plastic pallet and production process - Google Patents
Formula of wear-resistant and environment-friendly plastic pallet and production process Download PDFInfo
- Publication number
- CN103214862A CN103214862A CN 201310094026 CN201310094026A CN103214862A CN 103214862 A CN103214862 A CN 103214862A CN 201310094026 CN201310094026 CN 201310094026 CN 201310094026 A CN201310094026 A CN 201310094026A CN 103214862 A CN103214862 A CN 103214862A
- Authority
- CN
- China
- Prior art keywords
- plastic pallet
- environment protection
- pallet
- protection plastic
- wearable environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a wear-resistant and environment-friendly plastic pallet, which is composed of the following components by weight: 15-28% of blue-green algae fibers, 20-32% of plant powder, 3-6% of plasticized starch, 3-6% of nano-calcium carbonate, 2-4% of sorbitol, 15-17% of polypropylene (PP), 5-7% of polyethylene (PE), 9-13% of a coupling agent, 4-7% of glycerol, and 3-5% of a degradation promoting agent. The production process of the plastic pallet includes: mixing the materials fully, conducting mixing at 120-150DEG C, injecting the well mixed material into a mold, and performing heat preservation at 30DEG C for 2h, and carrying out shaping, thus obtaining the product. The plastic pallet provided in the invention is wear resistant, and easily biodegradable, and has a simple production process and a low cost, thus having high market competitiveness.
Description
Technical field
The present invention relates to a kind of PP pallet, be specifically related to a kind of plastic pallet of wearable environment protection.
Background technology
By the pallet that the PP plastics are made, light weight, inexpensive is liked by the human consumer deeply, but plastics should not degrade, and easily causes environmental pollution, and uses the rear surface easily to be worn, and cut occurs, influences attractive in appearance.The easy degradative plastics goods of environmental protection are also arranged in the market, but price is higher relatively, to increase cost.
Summary of the invention
The objective of the invention is at the deficiencies in the prior art, a kind of plastic pallet of wearable environment protection is provided.
For achieving the above object, the technical solution used in the present invention is as follows: a kind of prescription of wearable environment protection plastic pallet, raw material is made up of following component in percentage by weight: blue-green algae fiber 15-28%, plant powder 20-32%, plasticized starch 3-6%, nano-calcium carbonate 3-6%, sorbyl alcohol 2-4%, polypropylene (PP) 15-17%, polyethylene (PE) 5-7%, coupling agent 9-13%, glycerine 4-7%, short degradation agents 3-5%.
Its production technique may further comprise the steps:
(a) blue-green algae fiber 15-20%, plant powder 20-25%, plasticized starch 3-6%, nano-calcium carbonate 3-6%, short degradation agents 3-5% are merged between 110-170 ℃;
(b) in (a), add sorbyl alcohol 2-4%, polypropylene (PP) 15-17%, polyethylene (PE) 5-7%, coupling agent 9-13%, glycerine 4-7%, mixing behind the thorough mixing at 120-150 ℃, the material that mixes is injected 30 ℃ of mould insulations, typing in 2 hours product.
Described plant powder is that drying made after the back hydrochloric acid soln by 2% of Pericarppium arachidis hypogaeae or soybean peel pulverizing soaked 1 hour.
Described plasticized starch is that sweet potato starch passes through the ethylene glycol plasticization and modification.
Described short degradation agents is an oil-containing shell fiber.
Beneficial effect of the present invention: plastic pallet of the present invention is wear-resisting, readily biodegradable, production technique is simple, cost is low, the market competitiveness is high.
Embodiment
The present invention is further illustrated below in conjunction with specific embodiment.
Embodiment 1
A kind of prescription of wearable environment protection plastic pallet, raw material is made up of following component in percentage by weight: blue-green algae fiber 15%, peanut hull meal 20%, plasticized starch 6%, nano-calcium carbonate 6%, sorbyl alcohol 4%, polypropylene (PP) 17%, polyethylene (PE) 7%, coupling agent 13%, glycerine 7%, oil-containing shell fiber 5%.
Described peanut hull meal preparation method is: 2% hydrochloric acid soln immersion was passed through after 1 hour in Pericarppium arachidis hypogaeae pulverizing back, and drying makes.
Described plasticized starch is that sweet potato starch makes by the ethylene glycol plasticization and modification.
A kind of production technique of wearable environment protection plastic pallet may further comprise the steps:
(a) blue-green algae fiber 15%, peanut hull meal 20%, plasticized starch 6%, nano-calcium carbonate 6%, oil-containing shell fiber 5% are merged between 110-170 ℃;
(b) in (a), add sorbyl alcohol 4%, polypropylene (PP) 17%, polyethylene (PE) 7%, coupling agent 13%, glycerine 7%, behind the thorough mixing 120-150 ℃ mixing, the material that mixes is injected 30 ℃ of mould insulations, typing in 2 hours product.
Embodiment 2
A kind of prescription of wearable environment protection plastic pallet, raw material is made up of following component in percentage by weight: blue-green algae fiber 28%, soybean peel powder 32%, plasticized starch 3%, nano-calcium carbonate 3%, sorbyl alcohol 2%, polypropylene (PP) 15%, polyethylene (PE) 5%, coupling agent 9%, glycerine 4%, oil-containing shell fiber 3%.
Described soybean peel powder, preparation method thereof is: 2% hydrochloric acid soln immersion was passed through after 1 hour in Pericarppium arachidis hypogaeae pulverizing back, and drying makes.
Described plasticized starch is that sweet potato starch makes by the ethylene glycol plasticization and modification.
A kind of production technique of wearable environment protection plastic pallet may further comprise the steps:
(a) blue-green algae fiber 28%, peanut hull meal 32%, plasticized starch 3%, nano-calcium carbonate 3%, oil-containing shell fiber 3% are merged between 110-170 ℃;
(b) in (a), add sorbyl alcohol 2%, polypropylene (PP) 15%, polyethylene (PE) 5%, coupling agent 9%, glycerine 4%, behind the thorough mixing 120-150 ℃ mixing, the material that mixes is injected 30 ℃ of mould insulations, typing in 2 hours product.
Claims (5)
1. the prescription of a wearable environment protection plastic pallet, it is characterized in that: raw material is made up of following component in percentage by weight: blue-green algae fiber 15-28%, plant powder 20-32%, plasticized starch 3-6%, nano-calcium carbonate 3-6%, sorbyl alcohol 2-4%, polypropylene (PP) 15-17%, polyethylene (PE) 5-7%, coupling agent 9-13%, glycerine 4-7%, short degradation agents 3-5%.
2. the pallet of a kind of wearable environment protection plastic pallet according to claim 1 is characterized in that: described plant powder is that drying made after the back hydrochloric acid soln by 2% of Pericarppium arachidis hypogaeae or soybean peel pulverizing soaked 1 hour.
3. the pallet of a kind of wearable environment protection plastic pallet according to claim 1 is characterized in that: described plasticized starch is that sweet potato starch passes through the ethylene glycol plasticization and modification.
4. the pallet of a kind of wearable environment protection plastic pallet according to claim 1 is characterized in that: described short degradation agents is an oil-containing shell fiber.
5. the production technique of a wearable environment protection plastic pallet is characterized in that: may further comprise the steps:
(a) blue-green algae fiber 15-28%, plant powder 20-32%, plasticized starch 3-6%, nano-calcium carbonate 3-6%, short degradation agents 3-5% are merged between 110-170 ℃;
(b) in (a), add sorbyl alcohol 2-4%, polypropylene (PP) 15-17%, polyethylene (PE) 5-7%, coupling agent 9-13%, glycerine 4-7%, mixing behind the thorough mixing at 120-150 ℃, the material that mixes is injected 30 ℃ of mould insulations, typing in 2 hours product.