CN103194035A - 一种改性的pom材料及其制备方法 - Google Patents
一种改性的pom材料及其制备方法 Download PDFInfo
- Publication number
- CN103194035A CN103194035A CN201310123684XA CN201310123684A CN103194035A CN 103194035 A CN103194035 A CN 103194035A CN 201310123684X A CN201310123684X A CN 201310123684XA CN 201310123684 A CN201310123684 A CN 201310123684A CN 103194035 A CN103194035 A CN 103194035A
- Authority
- CN
- China
- Prior art keywords
- pom
- modification
- pom material
- parts
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种改性的POM材料及其制备方法，包括以下组分且各组分的重量份数为：POM60-70份；共混剂10-20份；增溶剂5-7份；抗氧剂0.5-2份；其他助剂1-2份。通过在POM材料中加入线性低密度聚乙烯以及增溶剂，克服了POM因结构问题与其他试剂相容性差的缺陷，大大促进POM与线性低密度聚乙烯的融合，提高POM的韧性，使得制备的POM材料具有更加广泛的应用前景。
Description
技术领域
本发明涉及一种改性的POM材料及其制备方法，尤其是涉及一种增韧的POM材料及其制备方法，属于高分子材料技术领域。
背景技术
随着我国电子电器、汽车、航空航天工业的迅速发展，对高强度的工程塑料的需求日益增长。聚甲醛（POM）是一种综合性能优良的工程塑料，是工程塑料中力学性能最接近金属的材料，常被用来代替有色金属和合金广泛应用于汽车、电子电器工业、一般及精密机械和五金建材等行业。但POM的抗紫外光老化性差、缺口冲击强度低、耐候性差，为进一步拓宽其应用的领域，众多研发人员对其性能进行了改进。目前对POM的改性主要有3种方法：填充、增强、共混，其中以共混制备POM合金为主要手段。
发明内容
为解决现有技术的不足，本发明提供了一种改性的POM材料。同时，本发明还提供一种改性的POM材料的制备方法。
为了实现上述目标，本发明采用如下的技术方案：一种改性的POM材料，其特征在于，包括以下组分且各组分的重量份数为：
前述的一种改性的POM材料，其特征在于，所述共混剂为线性低密度聚乙烯。
前述的一种改性的POM材料，其特征在于，所述的增溶剂为OPE。
前述的一种改性的POM材料，其特征在于，所述抗氧剂为抗氧剂1010、抗氧剂168。
制备前述的一种改性的POM材料的方法，其特征在于，包括以下步骤：
（1）按照前述的一种改性的POM材料称取各组分。
（2）将步骤（1）中称取的各组分投入到辊温为175度的双棍塑炼机上混炼5分钟。
（3）将步骤（2）中的共混物从辊筒上取下，迅速放在平板硫化机上预热的模腔内，其条件为：模具温度142度，保压90秒。
（4）将模具冷却6分钟，打开模具并取出产品。
本发明的有益效果为：通过在POM材料中加入线性低密度聚乙烯以及增溶剂，克服了POM因结构问题与其他试剂相容性差的缺陷，大大促进POM与线性低密度聚乙烯的融合，提高POM的韧性，使得制备的POM材料具有更加广泛的应用前景。
具体实施方式：
下面结合具体实施例对本发明做进一步的说明。
表1为实施例1-3和对比例1、2的各组分的配比。
如表1所示：
表1实施例1-3和对比例1、2的各组分的配比
其中，实施例1-3中所用的共混剂分别为均为线性低密度聚乙烯，增溶剂均为OPE。
实施例1-3所用抗氧剂分别为抗氧剂1010、抗氧剂1010、抗氧剂168，对比例1、2所用的抗氧剂分别为抗氧剂1010、抗氧剂168。
将表1中各组分按照以下步骤进行处理，然后对所得POM材料进行性能测试：
（1）按照前述的一种改性的POM材料称取各组分。
（2）将步骤（1）中称取的各组分投入到辊温为175度的双棍塑炼机上混炼5分钟。
（3）将步骤（2）中的共混物从辊筒上取下，迅速放在平板硫化机上预热的模腔内，其条件为：模具温度142度，保压90秒。
（4）将模具冷却6分钟，打开模具并取出产品。
表2为各实施例和对比例的性能测试结果，如表2所示。
表2各实施例和对比例的性能测试结果
注：参考标准为：GB13525/T-92。
从表2可以看出，实施例1-3中加入了共混剂线性低密度聚乙烯和增溶剂OPE，对比例均未加入，实施例1-3的拉伸强度、弯曲模量、缺口抗冲击强度均优于对比例，其韧性得到进一步增强。
以上显示和描述了本发明的基本原理、主要特征和优点。本行业的技术人员应该了解，上述实施例不以任何形式限制本发明，凡采用等同替换或等效变换的方式所获得的技术方案，均落在本发明的保护范围内。
Claims (5)
1. 一种改性的POM材料，其特征在于，包括以下组分且各组分的重量份数为：
POM 60-70份；
共混剂 10-20份；
增溶剂 5-7份；
抗氧剂 0.5-2份；
其他助剂 1-2份。
2.根据权利要求1所述的一种改性的POM材料，其特征在于，所述共混剂为线性低密度聚乙烯。
3.根据权利要求1所述的一种改性的POM材料，其特征在于，所述的增溶剂为OPE。
4.根据权利要求1所述的一种改性的POM材料，其特征在于，所述抗氧剂为抗氧剂1010、抗氧剂168。
5.制备如权利要求1-4中任一所述的一种改性的POM材料的方法，其特征在于，包括以下步骤：
（1）按照权利要求1所述的一种改性的POM材料称取各组分；
（2）将步骤（1）中称取的各组分投入到辊温为175度的双棍塑炼机上混炼5分钟；
（3）将步骤（2）中的共混物从辊筒上取下，迅速放在平板硫化机上预热的模腔内，其条件为：模具温度142度，保压90秒；
（4）将模具冷却6分钟，打开模具并取出产品。