CN103161094A - Antistatic synthesis paper - Google Patents
Antistatic synthesis paper Download PDFInfo
- Publication number
- CN103161094A CN103161094A CN 201110406889 CN201110406889A CN103161094A CN 103161094 A CN103161094 A CN 103161094A CN 201110406889 CN201110406889 CN 201110406889 CN 201110406889 A CN201110406889 A CN 201110406889A CN 103161094 A CN103161094 A CN 103161094A
- Authority
- CN
- China
- Prior art keywords
- parts
- synthetic paper
- paper according
- antistatic
- antistatic synthetic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to antistatic synthesis paper, and belongs to the technical field of functional polymer materials. The antistatic synthesis paper comprises, by mass, 100-130 parts of a modified polymer resin, 20-30 parts of a starch filler, 10-20 parts of wood fibers, 5-15 parts of ultra-fine calcium carbonate, 2-5 parts of a phenolic antioxidant, 1-4 parts of a silane coupling agent, 0.5-3 parts of an acrylate toughening agent, and 1-2 parts of an aliphatic amide lubricant. The synthesis paper has characteristics of high tension resistance, water resistance and heat resistance, wherein static electricity generation can be effectively prevented during a printing process and a binding process.
Description
Technical field
The present invention relates to the antistatic synthetic paper, belong to the functional high molecule material technical field.
Background technology
Synthetic paper, it is emerging in recent years a kind of material, to utilize chemical raw material such as olefines to add again some additives to be made, have the quality softness, stretching resistance is strong, WATER RESISTANCE is high, fast light cold-hot, and can resist the corrosion of chemical substance, is widely used in the printing of the senior art work, map, picture album, high-grade books and periodicals etc.China's synthetic paper is started late, and market development is inadequate, and domestic only have several enterprises to produce, second-rate, also unstable, and present annual consumption is ten thousand tons of 3-4, is mainly import, and basic is the PP synthetic paper entirely.The history of external existing three more than ten years, development is very fast, and quality is better.Although synthetic paper has plurality of advantages, and development in recent years is swift and violent, and undeniable is the shortcoming that synthetic paper also has self, and wherein the most nerve-wracking is exactly electrostatic problem, the time printing process and the printing after all produce some problems.
Summary of the invention
Defective in view of prior art exists the purpose of this invention is to provide a kind of antistatic synthetic paper that can effectively prevent static.
for achieving the above object, the technology used in the present invention solution is: the antistatic synthetic paper, comprise the modified high-molecular resin, starch fillers, wood fibre, calcium carbonate superfine powder, phenol antioxidant, silane coupler, esters of acrylic acid flexibilizer, the aliphatic amide series lubricant agent, wherein each component is 100 ~ 130 parts of modified high-molecular resins by the quality proportioning, 20 ~ 30 parts of starch fillers, 10 ~ 20 parts of wood fibres, 5 ~ 15 parts of calcium carbonate superfine powders, 2 ~ 5 parts of phenol antioxidant, 1 ~ 4 part of silane coupler, 0.5 ~ 3 part of esters of acrylic acid flexibilizer, 1 ~ 2 part of aliphatic amide series lubricant agent.
A kind of in polyethylene, polypropylene, polystyrene, polyvinyl chloride and polyethylene terephthalate that described modified high-molecular resin is the carbon nano modification.
Described starch fillers is ultra-fine Oxidized Starch Filler.
Described wood fibre is bamboo and arbor fiber.
Described phenol antioxidant is a kind of in three grades of butyl of 2,6--4-methylphenol, two (three grades of butyl of 3,5--4-hydroxy phenyl) thioether.
Described silane coupler is APTES, γ-glycidyl ether oxygen propyl trimethoxy silicane, N-(β one aminoethyl)-a kind of in γ-aminopropyl front three (second) TMOS.
Described esters of acrylic acid flexibilizer is methyl methacrylate-ethyl acrylate high polymer.
Described aliphatic amide series lubricant agent is a kind of in dimethyl formamide and para Toluic Acid's acetamide.
The synthetic paper of gained of the present invention not only has higher stretching resistance, WATER RESISTANCE and heat resistance, has effectively prevented the generation of static simultaneously in printing process and forwarding.
The specific embodiment
Embodiment 1
The antistatic synthetic paper, comprise 5 parts of 100 parts of the polyvinyl resins of carbon nano modification, 20 parts of ultra-fine Oxidized Starch Fillers, 10 parts of willow fibers, calcium carbonate superfine powder, 2, three grades of butyl of 6--2 parts of 4-methylphenol antioxidants, 1 ~ 4 part of APTES coupling agent, methyl methacrylate-0.5 part of ethyl acrylate high polymer flexibilizer, 1 part of dimethyl formamide lubricant, this made synthetic paper toughness of filling a prescription is not too high, can be used for wall advertisement.
Embodiment 2
The antistatic synthetic paper, comprise 10 parts of 120 parts of the acrylic resins of carbon nano modification, 25 parts of ultra-fine Oxidized Starch Fillers, 15 parts of willow fibers, calcium carbonate superfine powder, two (3, three grades of butyl of 5--4-hydroxy phenyl) 4 parts of thioether antioxidants, γ-3 parts of glycidyl ether oxygen propyl trimethoxy silicane coupling agents, methyl methacrylate-1.5 parts of ethyl acrylate high polymer flexibilizer, para Toluic Acid's acetamide lubricant are 1.5 parts, this made synthetic paper toughness of filling a prescription is larger, intensity is also larger, is suitable for map, picture album and billboard.
Embodiment 3
The antistatic synthetic paper, comprise 15 parts of 130 parts of the polystyrene resins of carbon nano modification, 30 parts of ultra-fine Oxidized Starch Fillers, 20 parts of bamboo fibers, calcium carbonate superfine powder, 2, three grades of butyl of 6--5 parts of 4-methylphenols, N-(β one aminoethyl)-2 parts of γ-4 parts of aminopropyl front three (second) TMOS coupling agents, methyl methacrylate-2 parts of ethyl acrylate high polymer flexibilizer, para Toluic Acid's acetamide lubricant, this fills a prescription, and made synthetic paper toughness is large, intensity is high, can in all case use.
Claims (8)
1. antistatic synthetic paper, it is characterized in that comprising modified high-molecular resin, starch fillers, wood fibre, calcium carbonate superfine powder, phenol antioxidant, silane coupler, esters of acrylic acid flexibilizer, aliphatic amide series lubricant agent, wherein each component is 100 ~ 130 parts of modified high-molecular resins, 20 ~ 30 parts of starch fillers, 10 ~ 20 parts of wood fibres, 5 ~ 15 parts of calcium carbonate superfine powders, 2 ~ 5 parts of phenol antioxidant, 1 ~ 4 part of silane coupler, 0.5 ~ 3 part of esters of acrylic acid flexibilizer, 1 ~ 2 part of aliphatic amide series lubricant agent by the quality proportioning.
2. antistatic synthetic paper according to claim 1 is characterized in that described modified high-molecular resin is a kind of in the polyethylene of carbon nano modification, polypropylene, polystyrene, polyvinyl chloride and polyethylene terephthalate.
3. antistatic synthetic paper according to claim 1, is characterized in that described starch fillers is ultra-fine Oxidized Starch Filler.
4. antistatic synthetic paper according to claim 1, is characterized in that described wood fibre is bamboo and arbor fiber.
5. antistatic synthetic paper according to claim 1 is characterized in that described phenol antioxidant is a kind of in three grades of butyl of 2,6--4-methylphenol, two (three grades of butyl of 3,5--4-hydroxy phenyl) thioether.
6. antistatic synthetic paper according to claim 1, is characterized in that described silane coupler is APTES, γ-glycidyl ether oxygen propyl trimethoxy silicane, N-(β one aminoethyl)-a kind of in γ-aminopropyl front three (second) TMOS.
7. antistatic synthetic paper according to claim 1, is characterized in that described esters of acrylic acid flexibilizer is methyl methacrylate-ethyl acrylate high polymer.
8. antistatic synthetic paper according to claim 1 is characterized in that described aliphatic amide series lubricant agent is a kind of in dimethyl formamide and para Toluic Acid's acetamide.