CN103147242A - Method for immersing silk threads in molten paraffin - Google Patents
Method for immersing silk threads in molten paraffin Download PDFInfo
- Publication number
- CN103147242A CN103147242A CN2013100665871A CN201310066587A CN103147242A CN 103147242 A CN103147242 A CN 103147242A CN 2013100665871 A CN2013100665871 A CN 2013100665871A CN 201310066587 A CN201310066587 A CN 201310066587A CN 103147242 A CN103147242 A CN 103147242A
- Authority
- CN
- China
- Prior art keywords
- silk thread
- silk threads
- molten paraffin
- cured
- immersing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a method for immersing silk threads in molten paraffin, which includes the following steps: melting the middle part of a paraffin block through an electric iron; and immersing one ends of silk threads in molten paraffin through a thread pressing plate sequentially, and then drawing the silk threads out of the molten paraffin. Compared with the conventional technology for immersing silk threads in molten paraffin, the method has the advantages that the purchasing cost for equipment such as electric furnaces is avoided, the speed of immersing the silk threads in molten paraffin is improved by two times, the labor cost is saved, and the silk threads after being immersed in molten paraffin are evenly coated with molten paraffin, and the quality of immersing the silk threads in molten paraffin is excellent.
Description
Technical field
The invention belongs to the circuit assembly field, be specifically related to a kind of silk thread and soak cured method.
Background technology
An electronic equipment often has many wires, and they are undertaking between internal circuit element, the various connection between element and outside.Because wire is a lot, make machine routing attractive in appearance in order to improve the making quality, be convenient to again installation, the line inspection, Wiring technique is to be particular about.It is an important ring of machine routing technique that wire is shaped.After online beam shaping, must carry out colligation to wire harness, otherwise wire harness will be dispersed within casing as a branch of tangled skein of jute.Degree of tightness appropriateness is wanted in the colligation of wire harness, and tension easily destroys wire insulation, cross pine wire harness be difficult for straight and uprightly, affect attractive in appearance.
The silk thread colligation is often adopted in the wire harness colligation, the silk thread of colligation wire harness has cotton thread, bright and beautiful silk thread, linen thread, nylon wire, nylon yarn, to be placed on them in the not high paraffin liquid of temperature before the silk thread colligation and soak, to increase the adstringency of silk thread, silk thread be buckled be difficult for getting loose.
It is that paraffin mass is put into a basin electric furnace heating and melting that traditional silk thread soaks cured technique, then silk thread is immersed in cured liquid, and the silk thread that will soak at last wax takes out standby from basin.During the operation of this process, wax liquid needs to melt fully, and wax liquid temperature is high, it is slow to soak cured speed, and needs to be equipped with special-purpose electric furnace, complex operation.
Summary of the invention
The object of the present invention is to provide a kind of silk thread to soak cured method.
For achieving the above object, the present invention has adopted following technical scheme:
1) with electric iron, the wax stone mid portion is melted into wax liquid;
2) use tension disc to make silk thread immerse successively wax liquid since an end, then extract out from wax liquid.
One end of described tension disc offers for silk thread being fixed in the wire casing of wax liquid.
Described tension disc adopts the making of epoxy resin bonded fiber, plank or bamboo chopsticks.
The speed that described silk thread is extracted out is 5-15 m/min.
Soak cured technique with existing silk thread and compare, the method for the invention has been saved the original equipment cost of electric furnace etc., and silk thread soaks cured speed and improved twice, has saved labour cost, and soak cured silk thread hang cured evenly, to soak cured quality good.
Description of drawings
Fig. 1 is the structural representation of tension disc of the present invention;
In figure: 1 is tension disc, and 2 is groove.
The specific embodiment
The present invention will be further described below in conjunction with drawings and Examples.
Silk thread of the present invention soaks cured method, comprises the following steps:
1) with electric iron, the wax stone mid portion is melted into wax liquid; 2) use tension disc to make silk thread immerse successively wax liquid since an end, then extract out from wax liquid.The speed that described silk thread is extracted out is 5-15 m/min.One end of described tension disc offers for silk thread being fixed in the wire casing of wax liquid.Described tension disc adopts the making of epoxy resin bonded fiber, plank or bamboo chopsticks.
Embodiment
A kind of silk thread soaks cured process, comprises the following steps:
1) prepare instrument and the materials such as electric iron, porcelain dish, nipper pliers, bright and beautiful silk thread, paraffin wax piece, cotton;
2) with epoxy resin bonded fiber (or other nonflammable material, if there is no the also replacements such as available bamboo chopsticks, little plank of suitable material) by tension disc of making shown in Figure 1, tension disc 1 one ends are opened a groove 2;
3) porcelain dish is placed on workbench, paraffin mass is placed in porcelain dish;
4) open the electric iron switch, the electric iron that burns heat is placed on the paraffin mass mid portion makes the paraffin mass partial melting;
5) need are soaked the groove that cured bright and beautiful silk thread passes tension disc, and immerse in the cured liquid that melts;
6) bright and beautiful silk thread is fixed in the cured groove of thawing with tension disc, guarantees that bright and beautiful silk thread is soaked by wax liquid;
7) the hand-held electric iron of operator and tension disc; Electric iron is the fixed point heating, and slower owing to conducting heat, hand-held electric iron also moves at any time always, to continue to provide thermal source.
8) another operator clamps bright and beautiful silk thread head with cotton of nipper pliers pad, will soak cured bright and beautiful silk thread and at the uniform velocity extract out with speed faster, completes the whole cured process of soaking, and the speed that bright and beautiful silk thread is extracted out is generally 10 m/mins.Purpose with the wired line of nipper pliers pad cotton is to prevent that wax liquid from adhering on hand, and the protection silk thread.
The present invention has following advantages:
1, equipment used in the present invention (electric iron, porcelain dish, tension disc, nipper pliers, cotton) is all daily necessary article in circuit assembly, need not use other equipment such as electric furnace;
2, method of operating is simple, and operating process is easily implemented;
3, method of operating is with low cost; Saved cost of labor;
4, it is fast that employing this method is soaked cured speed, can complete the cured work of soaking of 100 meters silk threads in ten minutes;
5, adopt this method to soak cured silk thread extension cured evenly, non-slip during the colligation wire harness.
Claims (4)
1. a silk thread soaks cured method, it is characterized in that, comprises the following steps:
1) with electric iron, the wax stone mid portion is melted into wax liquid;
2) use tension disc to make silk thread immerse successively wax liquid since an end, then extract out from wax liquid.
2. a kind of silk thread soaks cured method according to claim 1, it is characterized in that: an end of described tension disc offers for silk thread being fixed in the wire casing of wax liquid.
3. a kind of silk thread soaks cured method according to claim 1, it is characterized in that: described tension disc adopts the making of epoxy resin bonded fiber, plank or bamboo chopsticks.
4. a kind of silk thread soaks cured method according to claim 1, it is characterized in that: the speed that described silk thread is extracted out is 5-15 m/min.