CN103146101A - Preparation method of high-crystallinity polyvinylidene fluoride (PVDF) - Google Patents

Preparation method of high-crystallinity polyvinylidene fluoride (PVDF) Download PDF

Info

Publication number
CN103146101A
CN103146101A CN2013100603127A CN201310060312A CN103146101A CN 103146101 A CN103146101 A CN 103146101A CN 2013100603127 A CN2013100603127 A CN 2013100603127A CN 201310060312 A CN201310060312 A CN 201310060312A CN 103146101 A CN103146101 A CN 103146101A
Authority
CN
China
Prior art keywords
pvdf
crystallinity
preparation
room temperature
microsphere
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013100603127A
Other languages
Chinese (zh)
Other versions
CN103146101B (en
Inventor
张光祖
姜胜林
易金桥
喻研
魏本杰
刘思思
付明
黎步银
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huazhong University of Science and Technology
Original Assignee
Huazhong University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Huazhong University of Science and Technology filed Critical Huazhong University of Science and Technology
Priority to CN201310060312.7A priority Critical patent/CN103146101B/en
Publication of CN103146101A publication Critical patent/CN103146101A/en
Application granted granted Critical
Publication of CN103146101B publication Critical patent/CN103146101B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a preparation method of high-crystallinity polyvinylidene fluoride (PVDF), which comprises the following steps: adding a microsphere expanding agent of which the thermal expansion coefficient is far higher than that of PVDF in the preparation of the PVDF material, wherein when the temperature rises from room temperature to the melting temperature of the PVDF, the microsphere sharply expands, and the volume of the microsphere is increased by about 10-20 times in comparison with the situation at room temperature; and then, cooling the PVDF from the melting temperature to room temperature to ensure that the PVDF is gradually solidified and crystallized, wherein in the cooling process, the microsphere sharply shrinks, so that uniform tensile stress can be formed in the PVDF in the solidification process, and the tensile stress can improve the crystallinity of a beta phase in the PVDF. For the PVDF prepared by the method, the crystallinity of the beta phase is obviously improved; and the pyroelectric property of the material is superior to that of the PVDF material prepared by a common method. The PVDF organic ferroelectric material prepared by the invention has high beta-phase crystallinity and spontaneous polarization rate and favorable pyroelectric property, and conforms to the use requirements of ferroelectric organic materials.

Description

A kind of preparation method of high-crystallinity polyvinylidene difluoride (PVDF)
Technical field
The invention belongs to the technology of preparing of high-performance organic functional material, specifically, relate to the preparation method of high-crystallinity polyvinylidene difluoride (PVDF).
Background technology
In various materials, ferroelectric material is widely used in preparing large value capacitor, electric energy storing device, energy harvester, pressure transmitter and non-refrigerated infrared detector etc. because having good dielectric, piezoelectricity and pyroelectric property.
Ferroelectric material can be divided into inorganic iron electric material and the large class of Organic Iron electric material two.Inorganic iron electric material (as pottery and monocrystalline such as barium titanate, Pb-based lanthanumdoped zirconate titanatess) ferroelectricity is good, widely applies.But the shortcoming of inorganic iron electric material is that preparation cost is high, complicated process of preparation, material brittle, does not have snappiness, opaque and follow-up use processing difficulties.In addition, the ferroelectric material of larger area or volume be prepared, also special main equipment and technique must be adopted.Compare with the inorganic iron electric material, the Organic Iron electric material has softness, transparent, low cost of manufacture, technique is simple and be easy to the characteristics such as processing.The Organic Iron electric material of larger area or volume also can be by common equipment and technique manufacturing.
In numerous organism materials, polyvinylidene difluoride (PVDF) (PVDF) is the most noticeable.The degree of crystallinity of PVDF is high, its unique molecular chain structure makes in its body can form the β phase crystallization with higher spontaneous polarizability, and spontaneous polarizability is to weigh the ferroelectric important indicator of material, therefore the ferroelectricity of PVDF is better than other organic materialss, and the size of material spontaneous polarizability also becomes the important indicator of weighing its β phase degree of crystallinity.Yet except having good ferroelectric β phase crystal formation, PVDF also can follow in preparation process does not have ferroelectric alpha-crystal form growth (spontaneous polarizability of α phase is 0) generally.Therefore the degree of crystallinity that how to improve β phase crystal formation is the key of preparation high-performance PVDF Organic Iron electric material.
For improving the content of β phase crystal formation in PVDF, a lot of methods are used.Adopt crystal pulling method, in the process of setting of PVDF, it is applied tension stress, can effectively improve β phase degree of crystallinity, but the method requires high, complex process to Preparation equipment, is not suitable for a large amount of productions; Add three fluorine ethylenes (TrFE) in PVDF, form polyvinylidene difluoride (PVDF)-three fluorine ethylene (P (VDF-TrFE)) Ferroelectric Copolymers, also can improve the degree of crystallinity of material beta phase, but (P (VDF-TrFE)) multipolymer is expensive; Adding muriate in PVDF, as bismuth chloride etc., is also the method for conventional raising material beta phase content, and the method is simple to operation, but undesirable to the raising effect of β phase degree of crystallinity.
Although PVDF has the unrivaled softness of inorganic iron electric material, transparent, low cost of manufacture, technique is simple and be easy to the characteristics such as processing, and ferroelectricity is better than other organic materialss, and PVDF is used widely, the further raising that awaits of its ferroelectricity.Therefore, the method for the raising PVDF material beta phase degree of crystallinity that research and development is simple effective and with low cost has stronger realistic meaning, is to make PVDF obtain the key of further widespread use.
Summary of the invention
The object of the present invention is to provide a kind of preparation method of simple and effective high-crystallinity polyvinylidene difluoride (PVDF), the method can improve PVDF material beta phase degree of crystallinity.
The preparation method of a kind of polyvinylidene difluoride (PVDF) provided by the invention, its step comprises:
(1) PVDF was mixed with acrylic resin microballoon swelling agent in 99: 1 in mass ratio~80: 20, ball milling makes its even mixing;
(2) oven dry obtains mixed powder;
(3) powder is heated to 175 ℃~200 ℃, makes the PVDF melting, simultaneously at the pressure that axially applies 2MPa~8MPa;
(4) insulation is 10~60 minutes, then cooling;
(5) when temperature is down to 100 ℃~80 ℃, shed pressure, be cooled to room temperature.
The method of raising PVDF material beta phase degree of crystallinity provided by the invention is by adding thermal expansivity much larger than the microballoon swelling agent of PVDF in the preparation of PVDF material, when temperature rises to the melt temperature (approximately 185 ℃) of PVDF from room temperature, microballoon sharply expands, and the volume of microballoon is than increasing approximately 10~20 times in the room temperature situation.After this PVDF is lowered the temperature, be cooled to the process of room temperature from melt temperature, PVDF is solidification and crystallization gradually.In this course, microballoon sharply shrinks, and makes PVDF form uniform tension stress in body in process of setting, and tension stress can improve the degree of crystallinity of β phase in PVDF.Utilize the PVDF of the method preparation, its β phase degree of crystallinity obviously improves, and material pyroelectric property (pyroelectric coefficient) is better than the PVDF material of usual way preparation.
In a word, the PVDF Organic Iron electric material of the present invention's preparation has higher β phase degree of crystallinity, spontaneous polarizability and good pyroelectric property, meets ferroelectric organic materials service requirements.Its performance such as table 1.
Description of drawings
Fig. 1 is the section electron scanning micrograph that adds the PVDF material for preparing after the microballoon swelling agent.
Embodiment
The preparation method of a kind of high-crystallinity polyvinylidene difluoride (PVDF) provided by the invention, its step comprises:
(1) PVDF was mixed with acrylic resin microballoon swelling agent in 99: 1 in mass ratio~80: 20, after this take pure water as the medium ball milling, PVDF is evenly mixed with microballoon;
(2) oven drying at low temperature obtains the even mixed powder of PVDF and microspheres;
(3) powder is placed in hot pressing furnace and carries out hot pressing.Powder is heated to 175 ℃~200 ℃, makes PVDF melting (at this temperature, microballoon still is in globular solids).Simultaneously at the pressure that axially applies 2MPa~8MPa;
(4) to sample insulation 20 minutes, after this cooling naturally;
(5) when temperature is down to 100 ℃~80 ℃, shed pressure, after this make sample naturally be cooled to room temperature;
(6) polishing of the PVDF sample after preparing, clean.
As improvement of the technical scheme, (1) the middle microballoon swelling agent median size at room temperature of using is 6 μ m~20 μ m.
Below in conjunction with accompanying drawing, the specific embodiment of the present invention is described further.Need to prove at this, understand the present invention for the explanation of these embodiments for helping, but do not consist of limitation of the invention.In addition, below in each embodiment of described the present invention involved technical characterictic just can mutually not make up as long as consist of each other conflict.
Example 1:
Be the acrylic resin microballoon swelling agent of 10 μ m and PVDF according to the quality of 90: 10 than weighing with particle diameter under room temperature, after this take pure water as the medium ball milling, PVDF evenly mixed with microballoon.Even mixed slurry is dried under the environment of 50 ℃, obtain the even mixed powder of PVDF and microspheres.Powder is placed in hot pressing furnace carries out hot pressing.Powder is heated to 175 ℃, makes the PVDF melting, simultaneously at the pressure that axially applies 2MPa.To sample insulation 20 minutes, after this cooling naturally.When temperature is down to 100 ℃, shed pressure, after this make sample naturally be cooled to room temperature.With the polishing of the PVDF sample after preparation, cleaning.
Its performance sees Table 3.
Example 2-5:
Microspheres and PVDF compare weighing according to the quality of 99: 1,95: 5,85: 15 and 80: 20.All the other are with example 1.Processing parameter sees Table 2, and its performance sees Table 3.
Example 6-7
The hot pressing temperature of powder is respectively 190 ℃ and 200 ℃, and all the other are with example 1.Processing parameter sees Table 2, and its performance sees Table 3.
Example 8-9
The hot pressing pressure of material is distributed as 5MP and 8MP, and all the other are with example 1, and processing parameter sees Table 2.Its performance sees Table 3.
Example 10-12
The acrylic resin microballoon swelling agent that adds at room temperature particle diameter is 6 μ m, 15 μ m and 20 μ m, and all the other are with example 1, and processing parameter sees Table 2.Its performance sees Table 3.
Example 13
Temperature-fall period sheds pressure when sample temperature is down to 80 ℃, all the other are with example 1.Processing parameter sees Table 2, and its performance sees Table 3.
The above is preferred embodiment of the present invention, but the present invention should not be confined to the disclosed content of this embodiment and accompanying drawing.So everyly do not break away from the equivalence of completing under spirit disclosed in this invention or revise, all falling into the scope of protection of the invention.
The performance perameter of table 1 high-crystallinity PVDF
Degree of crystallinity (%) 65
Spontaneous polarizability (C/m 2) 0.035
Pyroelectric coefficient (nC/cm 2℃) ≥8.0
Table 2 different technical parameters table
The performance perameter of the PVDF material of table 3 Different Preparation
Figure BDA00002859882700052
Figure BDA00002859882700061

Claims (2)

1. the preparation method of a polyvinylidene difluoride (PVDF), its step comprises:
(1) PVDF was mixed with acrylic resin microballoon swelling agent in 99: 1 in mass ratio~80: 20, ball milling makes its even mixing;
(2) oven dry obtains mixed powder;
(3) powder is heated to 175 ℃~200 ℃, makes the PVDF melting, simultaneously at the pressure that axially applies 2MPa~8MPa;
(4) insulation is 10~60 minutes, then cooling;
(5) when temperature is down to 100 ℃~80 ℃, shed pressure, be cooled to room temperature.
2. the preparation method of polyvinylidene difluoride (PVDF) according to claim 1, in step (1), described acrylic resin microballoon swelling agent median size at room temperature is 6 μ m~20 μ m.
CN201310060312.7A 2013-02-26 2013-02-26 Preparation method of high-crystallinity polyvinylidene fluoride (PVDF) Expired - Fee Related CN103146101B (en)