CN103144316A - Surface treatment method of glasses leg - Google Patents
Surface treatment method of glasses leg Download PDFInfo
- Publication number
- CN103144316A CN103144316A CN2013100782269A CN201310078226A CN103144316A CN 103144316 A CN103144316 A CN 103144316A CN 2013100782269 A CN2013100782269 A CN 2013100782269A CN 201310078226 A CN201310078226 A CN 201310078226A CN 103144316 A CN103144316 A CN 103144316A
- Authority
- CN
- China
- Prior art keywords
- surface treatment
- treatment method
- pin body
- earpiece
- carbon fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a surface treatment method of a glasses leg, and belongs to the technical field of glasses manufacture. The method is used for solving the problems that the existing glasses leg is low in aesthetic measure and not fashionable enough after being subjected to surface treatment, and the like. The method comprises the following steps: A, surface coating; B, packing compact; and C, compaction. The method ensures that the treated glasses leg has an artistic structure and is exquisite and fashionable.
Description
Technical field
The invention belongs to glasses manufacturing technology field, relate to a kind of surface treatment method of earpiece.
Background technology
Glasses are comprised of spectacle-frame, lens and the earpiece with nose support; has the effect of correcting defects of vision or protecting eyes; popular along with the rising of near-sighted number, various decorative glasses; glasses more and more become the necessity of people life, and people require also more and more higher to the aesthetic property of glasses and fashion etc.
Existing glasses, earpiece are generally that the employing metal material is made or plastic material is made.The earpiece that metal material is made, the color of earpiece is single, lacks variation, and aesthetic measure is inadequate, and there is the possibility of getting rusty in metal; And the earpiece that plastic material is made is all generally that injection moulding forms, and the pin body easily weares and teares, and easily fractures, and firmly degree is not high.Also having a kind of is that the acetate fiber material is made, and for example the Chinese patent literature data discloses the preparation method [patent No. 200710067922.4 of memory sheet glasses frame; Publication number: CN101284424A], its earpiece adopts acetate fiber sheet material, and the material by two or more different colours carries out amalgamation, specifically 1, raw material are sawed material; 2, carry out amalgamation after the plate use solvent processing with two or more different colours; 3, the material of amalgamation being completed rushes material or mills material according to profile, is processed into blank; 4, adopt lock pin technique that metal connecting piece is squeezed into blank; 5, blank is carried out surface topography processing; 5, blank being carried out the light decorations processes.
After the pin chaeta base of above three kinds of earpieces completes, all can polish to the pin body, modification etc., but it is still keeping the appearance characteristics that original pin system is made material, aesthetic measure is not high, not fashion.
Summary of the invention
The objective of the invention is for the above-mentioned problems in the prior art, a kind of surface treatment method of earpiece is provided, make the earpiece structure attractive in appearance, exquisite fashion.
Purpose of the present invention can realize by following technical proposal: a kind of surface treatment method of earpiece, and the method comprises the following steps:
A, top layer coat: carbon fiber decorative pattern cloth is coated on the pin body of earpiece;
B, dress mould: the pin body that will be coated with carbon fiber decorative pattern cloth is put in the mould of 100-300 ℃, then mould is fastened;
C, compacting: the mould to above-mentioned fastening carries out hot pressing, makes above-mentioned carbon fiber decorative pattern cloth firmly stick to the pin surface.
add man-hour, first produce according to demand the earpiece pin body of required form, the pin body can be by metal, the material such as plastics or carbon fiber is made, then evenly smear epoxide-resin glue on carbon fiber decorative pattern cloth, cut again the carbon fiber decorative pattern cloth of required form according to the shape of earpiece pin body, carbon fiber decorative pattern cloth is coated on the outside of pin body, again the pin body is placed on and carries out hot pressing in specific mould, make carbon fiber decorative pattern cloth firmly stick to the surface of pin body, the good looking appearance of pin body, fashion is exquisite, and carbon fiber decorative pattern cloth is to be made by carbon fibre material, have lightweight, intensity is high, good springiness, the advantages such as good corrosion resistance, covered the inadequate shortcoming with getting rusty of pin body aesthetic measure that metal material is made, the wearability of the pin body that plastic material makes and firm degree have been improved.
In the surface treatment method of above-mentioned a kind of earpiece, in described steps A, carbon fiber decorative pattern cloth is coated on the place, four sides of pin body.The mode of this kind coating is fit to the thicker earpiece pin body of thickness, and larger side, four surfaces of pin body is all coated, and makes the overall structure of earpiece pin body attractive in appearance, and fashion is exquisite.
In the surface treatment method of above-mentioned a kind of earpiece, in described steps A, carbon fiber decorative pattern cloth is coated on place, two sides symmetrical on the pin body.The mode of this kind coating is fit to the earpiece pin body of thinner thickness, and two sides, pin body up and down are because the surface is less, and carbon coated fiber decorative pattern cloth does not affect the overall appearance of pin body yet.
In the surface treatment method of above-mentioned a kind of earpiece, in described steps A, carbon fiber decorative pattern cloth is coated on lateral surface and the up and down place, two sides of pin body.After wearing, the medial surface of pin body is difficult for observing inwardly due to glasses, and this kind coating mode does not affect the overall appearance of earpiece, and is conducive to save carbon fiber decorative pattern cloth, and is good in economic efficiency.
In the surface treatment method of above-mentioned a kind of earpiece, in described step B, mould comprises upper die body and lower mold body, is formed into die cavity between upper die body and lower mold body, and above-mentioned mould is positioned over and carries out hot pressing on hot press.The shape of the shape of forming cavity and earpiece pin body is complementary, and produces corresponding upper die body and lower mold body according to the difference of pin shape, during hot pressing, uses the mould of difformity forming cavity for difform pin body, replaces simply, and dismounting is simple.
In the surface treatment method of above-mentioned a kind of earpiece, adopt the pressure of 5-8 ton that upper die body is pressed together on lower mold body in described step B on common hot press.Pressure is set according to actual needs, and working (machining) efficiency is provided when guaranteeing product quality.
In the surface treatment method of above-mentioned a kind of earpiece, described upper die body and lower mold body are silica gel material.Silica gel is silica gel, be soft material, during hot pressing, silica gel can produce certain deformation, and namely mould produces certain deformation, the upper die body of deformation, lower mold body can be to forming cavity place's extruding, make on the carbon fiber decorative pattern cloth side that is fitted in the pin body tightly, the hot pressing through certain hour makes carbon fiber decorative pattern cloth be coated on the external side of pin, the coating process is simple, clad structure is ingenious, and upper die body and lower mold body are all to be made by silica gel material, and suitable coating has certain radian, pin body in irregular shape.
In the surface treatment method of above-mentioned a kind of earpiece, described upper die body is metal material, and described lower mold body is silica gel material.This kind mould is fit to coat inboard or the smooth pin body in the outside, also is applicable to not coat simultaneously the pin body of four sides.
In the surface treatment method of above-mentioned a kind of earpiece, after described step C, the pin body is polished, eliminate the burr, burr of pin surface etc., then at the even spray paint of the outer surface of pin body.To the pin surface modifying, remove burr, glue etc., make the pin surface clean, smooth, spray paint makes the pin body profile attractive in appearance.
In the surface treatment method of above-mentioned a kind of earpiece, described paint thickness is the 15-30 micron.The thickness of paint sprays according to actual needs, guarantees attractive in appearance the getting final product of earpiece pin body.
Compared with prior art, the surface treatment method of earpiece provided by the invention has advantages of following:
1, the outside of this earpiece pin body is coated with carbon fiber decorative pattern cloth, make the structure of earpiece pin body attractive in appearance, fashion is exquisite, and carbon fiber decorative pattern cloth is to be made by carbon fibre material, has lightweight, the advantage such as intensity is high, good springiness and good corrosion resistance, cover pin body aesthetic measure that metal material makes not and the shortcoming that may get rusty, improved the wearability of the pin body that plastic material makes and firm degree.
2, this earpiece pin body can select carbon fiber decorative pattern cloth to coat two sides, three sides or four sides according to different situations, and range of choice is wide, meets different demands.
3, the mould that uses of the surface treatment method of this earpiece is to be made by silica gel material, can be towards the characteristics of mould molding chamber place's extruding during according to silica gel material hot pressing, and make carbon fiber decorative pattern cloth stick to firmly the outside of pin body, design ingeniously, coat simply.
Description of drawings
Fig. 1 coats earpiece pin body.
Fig. 2 is that the master of earpiece mold and bed die looks cutaway view.
Fig. 3 is the earpiece pin body after machining.
In figure, 1, carbon fiber decorative pattern cloth; 2, pin body; 3, upper die body; 4, lower mold body; 5, forming cavity.
The specific embodiment
Be below specific embodiments of the invention and by reference to the accompanying drawings, technical scheme of the present invention is further described, but the present invention be not limited to these embodiment.
Embodiment one
As Fig. 1, Fig. 2, shown in Figure 3, the surface treatment method of this earpiece comprises the following steps:
A, top layer coat: use the hot pressing of carbon fiber cloth to become earpiece pin body 2, evenly smear epoxide-resin glue in a side of carbon fiber decorative pattern cloth 1, cut rectangular carbon fiber decorative pattern cloth 1, then carbon fiber decorative pattern cloth 1 is coated on four sides of pin body 2;
B, dress mould: the temperature setting of mould is set to 150 ℃, it comprises upper die body 3 and lower mold body 4, upper die body 3 and lower mold body 4 in the present embodiment are made by silica gel material, in actual production, upper die body 3 can be made by metal material, lower mold body 4 is made by silica gel material, changes according to actual needs different moulds.Have elongated forming cavity 5 on the position of upper die body 3 and lower mold body 4 correspondences, the pin body 2 that is coated with carbon fiber decorative pattern cloth 1 is put in this forming cavity 5;
C, compacting: then upper die body 3 is fastened on lower mold body 4 and is put on hot press, use the pressure of 6 tons to carry out hot pressing to mould, upper die body 3 and lower mold body 4 produce deformation, towards forming cavity 5 places extruding, make on carbon fiber decorative pattern cloth 1 four sides that are fitted in pin body 2 tightly, epoxide-resin glue makes carbon fiber decorative pattern cloth 1 firmly stick to the surface of pin body 2, can not come off.
After step C completes, take out and coat good earpiece pin body 2, pin body 2 is polished, eliminate burr, burr and the glue on pin body 2 surfaces, make pin body 2 surface clean, smooth, then be the paint of 15 microns at the coating thickness of the surface uniform of pin body 2, make the color and luster on pin body 2 surfaces bright.
Embodiment two
The present embodiment is basic identical with the scheme of embodiment one, different place is that the pin body 2 in steps A is to be made by metal material, and only coat pin body 2 areas larger inside and outside two sides, the temperature of the mould setting in step B is 300 ℃, use the pressure of 8 tons to carry out hot pressing to pin body 2 in step C, the thickness of paint spraying is 20 microns.
Embodiment three
The present embodiment is basic identical with the scheme of embodiment one, different place is that the pin body 2 in steps A is to be made by plastic material, and coat two sides of lateral surface and up and down of pin body 2, the temperature of the mould setting in step B is 100 ℃, use the pressure of 5 tons to carry out hot pressing to pin body 2 in step C, the thickness of paint spraying is 30 microns.
Specific embodiment described herein is only to the explanation for example of the present invention's spirit.Those skilled in the art can make various modifications or replenish or adopt similar mode to substitute described specific embodiment, but can't depart from spirit of the present invention or surmount the defined scope of appended claims.
Although this paper has more used the terms such as carbon fiber decorative pattern cloth 1, pin body 2, upper die body 3, lower mold body 4, forming cavity 5, do not get rid of the possibility of using other term.Using these terms is only in order to describe more easily and explain essence of the present invention; They are construed to any additional restriction is all contrary with spirit of the present invention.
Claims (10)
1. the surface treatment method of an earpiece, the method comprises the following steps:
A, top layer coat: carbon fiber decorative pattern cloth (1) is coated on the pin body (2) of earpiece;
B, dress mould: the pin body (2) that will be coated with carbon fiber decorative pattern cloth (1) is put in the mould of 100-300 ℃, then mould is fastened;
C, compacting: the mould to above-mentioned fastening carries out hot pressing, makes above-mentioned carbon fiber decorative pattern cloth (1) firmly stick to pin body (2) surface.
2. the surface treatment method of earpiece according to claim 1, is characterized in that, in described steps A, carbon fiber decorative pattern cloth (1) is coated on the place, four sides of pin body (2).
3. the surface treatment method of earpiece according to claim 1, is characterized in that, in described steps A, carbon fiber decorative pattern cloth (1) is coated on place, the upper symmetrical two sides of pin body (2).
4. the surface treatment method of earpiece according to claim 1, is characterized in that, in described steps A, carbon fiber decorative pattern cloth (1) is coated on lateral surface and the up and down place, two sides of pin body (2).
5. the surface treatment method of according to claim 1 and 2 or 3 or 4 described earpieces, it is characterized in that, in described step B, mould comprises upper die body (3) and lower mold body (4), be formed into die cavity (5) between upper die body (3) and lower mold body (4), above-mentioned mould is positioned over and carries out hot pressing on hot press.
6. the surface treatment method of earpiece according to claim 5, is characterized in that, adopting the pressure of 5-8 ton that upper die body (3) is pressed together on lower mold body (4) on common hot press in described step B.
7. the surface treatment method of earpiece according to claim 5, is characterized in that, described upper die body (3) and lower mold body (4) are silica gel material.
8. the surface treatment method of earpiece according to claim 5, is characterized in that, described upper die body (3) is metal material, and described lower mold body (4) is silica gel material.
9. the surface treatment method of earpiece according to claim 1, it is characterized in that, after described step C, pin body (2) is polished, eliminate the burr, burr on pin body (2) surface etc., then at the even spray paint of outer surface of pin body (2).
10. the surface treatment method of earpiece according to claim 9, is characterized in that, described paint thickness is the 15-30 micron.