CN103122153A - Resin based composite - Google Patents
Resin based composite Download PDFInfo
- Publication number
- CN103122153A CN103122153A CN2013101017077A CN201310101707A CN103122153A CN 103122153 A CN103122153 A CN 103122153A CN 2013101017077 A CN2013101017077 A CN 2013101017077A CN 201310101707 A CN201310101707 A CN 201310101707A CN 103122153 A CN103122153 A CN 103122153A
- Authority
- CN
- China
- Prior art keywords
- reinforced plastic
- glass
- velvet
- thing
- glass fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a resin based composite and belongs to a glass fiber reinforced plastic composite. The resin based composite comprises unsaturated resin and glass powder and also comprises a glass fiber reinforced plastic velvet material, wherein the glass fiber reinforced plastic velvet material, the unsaturated resin and the unsaturated resin are mixed in proportion. The resin based composite product prepared by the invention is high in evenness and beautiful, the resin based composite product can be quickly and effectively prepared, a process is scientific and practical, and cost is low, so that the resin based composite is applicable to popularization and application in the glass fiber reinforced plastic industry.
Description
Technical field
The present invention relates to a kind of glass fiber reinforced plastics composite material, particularly a kind of matrix material that utilizes glass fiber reinforced plastic wastes to be made.
Background technology
The a large amount of thermoset frp product of the annual demand of China, have simultaneously a large amount of glass fiber reinforced plastic wastes, the processing of glass fiber reinforced plastic wastes is a global problem, and existing processing mode is burnt and buried, glass fiber reinforced plastic wastes is difficult to again degraded, so this dual mode has all caused very large pollution to environment.
Summary of the invention
Not enough for overcoming above-mentioned prior art, the invention discloses a kind of polymer matrix composites, solved glass fiber reinforced plastic wastes recycling problem, environmental pollution improves.
The technical solution adopted in the present invention is a kind of polymer matrix composites, comprises that insatiable hunger resin, glass powder form, and characterized by further comprising the velvet-like thing of glass reinforced plastic, and the velvet-like thing of glass reinforced plastic, insatiable hunger resin, glass powder are mixed in proportion.
The velvet-like thing of glass reinforced plastic is that glass fiber reinforced plastic wastes is pulverized as short glass fiber, is stained with the insatiable hunger resin on short glass fiber, and short glass fiber can form lint ball short glass fiber, broken wool shape short glass fiber and short glass fiber powder.
The production technique of described polymer matrix composites, glass fiber reinforced plastic wastes is ground into the velvet-like thing of glass reinforced plastic, the velvet-like thing of glass reinforced plastic, insatiable hunger resin, glass powder, catalyzer, solidifying agent are fully mixed by weight 1:2:0.2:0.01:0.01, mixture is inserted in mould solidify, 7-15 minutes set times, become finished product after the demoulding, what the production efficiency of this mode of production improved than the production efficiency of the traditional glass steel mode of production.After testing, the technical indicator of this product is up to state standards.
The production technique of described polymer matrix composites, glass fiber reinforced plastic wastes is ground into the velvet-like thing of glass reinforced plastic, the velvet-like thing of glass reinforced plastic, insatiable hunger resin, glass powder, catalyzer, solidifying agent are fully mixed by weight 1:2:0.2:0.01:0.01, mixture is inserted in mould solidify, 7-15 minutes set times, become finished product after the demoulding, make efficiency is high, same fibre glass product manufacture, traditional way is made one, and the present invention can make three.After testing, the technical indicator of this product is up to state standards.
The invention has the beneficial effects as follows the glass fiber reinforced plastic wastes recycling, environmental pollution is greatly improved, highly efficient in productivity, make same fibre glass product manufacture, traditional way can be made one, and mode of the present invention can be made three, energy-conserving and environment-protective, the present invention is a kind of brand-new matrix material mode of production, sticks with paste, is wound around all soon much than traditional hand, and the product planeness that the present invention produces is high and attractive in appearance.The present invention rapidly and efficiently, craft science is practical, with low cost, is adapted at applying in the glass reinforced plastic industry.
Embodiment
Embodiment 1, and a kind of polymer matrix composites are mixed in proportion and are made by the velvet-like thing of glass reinforced plastic, insatiable hunger resin, glass powder.
a kind of production technique of polymer matrix composites, manufacturing flange, elbow, reducing mold, glass fiber reinforced plastic wastes is ground into the velvet-like thing of glass reinforced plastic, with the velvet-like thing of glass reinforced plastic, 196 insatiable hunger resins, glass powder, catalyzer, solidifying agent fully mixes by weight 1:2:0.2:0.01:0.01, mixture is inserted flange, solidify in elbow or reducing mold, 7-15 minutes set times, simply repair after the demoulding, become flange, elbow or reducing finished product, the resistance to compression of this product reaches 1MPa after testing, stretching resistance reaches 25KN, the product planeness of making like this is higher than traditional fibre glass product manufacture.
Embodiment 2, and a kind of polymer matrix composites are mixed in proportion and are made by the velvet-like thing of glass reinforced plastic, insatiable hunger resin, glass powder.
a kind of production technique of polymer matrix composites, make sheet material, wall brick, floor brick die, glass fiber reinforced plastic wastes is ground into the velvet-like thing of glass reinforced plastic, with the velvet-like thing of glass reinforced plastic, 196 insatiable hunger resins, glass powder, catalyzer, solidifying agent fully mixes by weight 1:2:0.2:0.01:0.01, mixture is inserted sheet material, solidify in wall brick or floor brick die, 7-15 minutes set times, after the demoulding, repair noon, become sheet material, wall brick or floor tile finished product, the resistance to compression of this product reaches 10 kilograms after testing, stretching resistance reaches 10 kilograms, the product planeness of making like this is higher than traditional fibre glass product manufacture.
Claims (3)
1. polymer matrix composites, comprise that insatiable hunger resin, glass powder form, and characterized by further comprising the velvet-like thing of glass reinforced plastic, and the velvet-like thing of glass reinforced plastic, insatiable hunger resin, glass powder are mixed in proportion.
2. the production technique of 1 described polymer matrix composites as requested, it is characterized in that glass fiber reinforced plastic wastes is ground into the velvet-like thing of glass reinforced plastic, the velvet-like thing of glass reinforced plastic, insatiable hunger resin, glass powder, catalyzer, solidifying agent are fully mixed by weight 1:2:0.2:0.01:0.01, mixture is inserted in mould solidify, 7-15 minutes set times, become finished product after the demoulding.
3. the production technique of 1 described polymer matrix composites as requested, it is characterized in that glass fiber reinforced plastic wastes is ground into the velvet-like thing of glass reinforced plastic, the velvet-like thing of glass reinforced plastic, insatiable hunger resin, glass powder, catalyzer, solidifying agent are fully mixed by weight 1:1:0.2:0.01:0.01, mixture is inserted in mould solidify, 7-15 minutes set times, become finished product after the demoulding.