CN103115845A - 测量铁水覆盖剂铺展性的方法 - Google Patents

测量铁水覆盖剂铺展性的方法 Download PDF

Info

Publication number
CN103115845A
CN103115845A CN2013100189199A CN201310018919A CN103115845A CN 103115845 A CN103115845 A CN 103115845A CN 2013100189199 A CN2013100189199 A CN 2013100189199A CN 201310018919 A CN201310018919 A CN 201310018919A CN 103115845 A CN103115845 A CN 103115845A
Authority
CN
China
Prior art keywords
molten iron
cone
covering agent
iron covering
spreadability
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013100189199A
Other languages
English (en)
Inventor
汪勤峰
王涛
申波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhan Iron and Steel Group Kunming Iron and Steel Co Ltd
Original Assignee
Wuhan Iron and Steel Group Kunming Iron and Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan Iron and Steel Group Kunming Iron and Steel Co Ltd filed Critical Wuhan Iron and Steel Group Kunming Iron and Steel Co Ltd
Priority to CN2013100189199A priority Critical patent/CN103115845A/zh
Publication of CN103115845A publication Critical patent/CN103115845A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种测量铁水覆盖剂铺展性的方法，在铁水表面投加覆盖剂，测量覆盖剂自然堆积的锥体高度和锥体底部半径，先求出自然休止角；在覆盖剂锥体周围以机械振动使覆盖剂锥体自由落下，再测量此时覆盖剂的锥体高度，然后求出震动休止角，按铺展性=自然休止角-震动休止角，得到铁水覆盖剂的铺展性。本发明的测量方法简便快捷，可定量测出铁水覆盖剂的铺展性，以便根据测量结果对不同种类的覆盖剂进行评估优选，减少质量纠纷，避免盲目使用铁水覆盖剂造成的直接和间接经济损失。本发明方法除了测定铁水覆盖剂铺展性外，还可以测量其它粉体的铺展性能。

Description

测量铁水覆盖剂铺展性的方法
技术领域
本发明涉及一种测量铁水覆盖剂铺展性的方法，属于测量方法技术领域。
背景技术
在高炉生产过程中，向出炉铁水投加覆盖剂以达到保温的目的是一种常用的工艺。现场投加过程中，覆盖剂的铺展性十分重要，铁水覆盖剂铺展性表征的反映了覆盖剂加入铁水后覆盖铁水液面的能力。由于铁水覆盖剂投加在液面后，一般是形成堆状，再铺展开来，类似于粉体的流动，难以表征其铺展性。目前，用什么方法和标准评价覆盖剂的铺展性，还尚无统一的认识。
发明内容
为解决铁水覆盖剂（粉体）的铺展性尚无统一的评价，本发明的目的在于提供一种测量铁水覆盖剂铺展性的方法，对铁水覆盖剂（或粉体）的铺展性进行量化评估。
本发明通过下列技术方案实现：一种测量铁水覆盖剂铺展性的方法，其特征在于经过下列各步骤：
1）将铁水覆盖剂自设定高度，该设定高度是铁水覆盖剂锥底直径的1～5倍，自由下落到平面板上，并堆积成圆锥体，直至堆积高度不再增加时止，测量覆盖剂自然堆积的锥体高度h和锥底半径r，按下式求出自然休止角α：
α=arctg                                                
Figure 2013100189199100002DEST_PATH_IMAGE001
；
式中，h——锥体高度，mm；
r——锥体底部半径，mm；
2）用铁水覆盖剂总重量的5～10%的重物，自设定高度，依次落在步骤1）的堆积有铁水覆盖剂的平面板上1～4次，该设定高度是铁水覆盖剂锥底直径的1～5倍，测量覆盖剂振动后的锥体高度h1和锥底半径r1，按下式求出振动休止角α1：
α1=arctg
Figure 2013100189199100002DEST_PATH_IMAGE002
；
式中，h1——振动后的锥体高度，mm；
r1——振动后的锥底半径，mm；
3）按下列公式计算，即得到铁水覆盖剂的铺展性P：
P=α - α1
式中：P：铁水覆盖剂的铺展性，单位：度；
      α：自然休止角；
      α1：振动休止角。
所述步骤1）的平面板为圆形或者矩形板。
 本发明所述铁水覆盖剂的铺展性是指：覆盖剂在铁水表面流动展开的能力，通常以一定质量的覆盖剂覆盖在铁水液面的面积来衡量。自然休止角为物料自然堆积形成的圆锥状料堆表面与水平面的夹角，是衡量干燥物料流动性能的一个重要指标。震动休止角（下落角）为物料自然堆积后，在震动状态下，使物料堆受振动后，形成的圆锥状料堆表面与水平面的夹角。
为了量化评价铁水覆盖剂的铺展性能，本发明是根据粉状物体流动性原理，通过测量覆盖剂的自然堆积状态下形成的休止角，以及同一物料堆受振动后，形成的圆锥状料堆表面与水平面的振动休止角，求出它们之间的差角大小，来衡量铁水覆盖剂在铁水液面的铺展情况，定量地表达出铁水覆盖剂的铺展性，计算结果中，差角越大，表明铁水铺展性越好。
本发明具有如下优点和效果：采用上述方案，可简便、快捷地定量测出铁水覆盖剂铺展性；用户在使用铁水覆盖剂产品前，可根据测量结果对不同种类的覆盖剂进行评估优选，减少质量纠纷，避免盲目使用铁水覆盖剂造成的直接和间接经济损失；本发明除了测定铁水覆盖剂铺展性外，还可以测量其它粉体料的铺展性能或流动性。
具体实施方式
下面通过实施例对本发明做进一步说明。
实施例1
1）将2000克铁水覆盖剂自200mm高度，自由下落到圆形平面板上，并堆积成圆锥体，直至堆积高度不再增加时止，测量铁水覆盖剂自然堆积的锥体高度h和锥底半径r，如此重复三次，锥底半径r=100mm，锥体高度h分别为h1=67mm、h2=69mm、h3=68mm，按下式求出自然休止角α：
α=arctg
Figure 524121DEST_PATH_IMAGE001
；
分别为：
α1=arctg
Figure 2013100189199100002DEST_PATH_IMAGE003
=arctg
Figure 2013100189199100002DEST_PATH_IMAGE004
=34°，
α2=arctg
Figure DEST_PATH_IMAGE005
=arctg
Figure 2013100189199100002DEST_PATH_IMAGE006
=35°，
α3=arctg
Figure DEST_PATH_IMAGE007
=arctg
Figure 2013100189199100002DEST_PATH_IMAGE008
=34°；
则自然休止角平均值=（α1+α2+α3）/3=（34°+35°+34°）/3=34；
2）用铁水覆盖剂总重量的5%的重物100克，自200mm高度，依次落在步骤1）的堆积有铁水覆盖剂的平面板上4次，测量覆盖剂振动后的锥体高度h1和锥底半径r1，如此重复三次，锥底半径r=100mm，锥体高度h分别为h1=57mm、h2=59mm、h3=58mm，按下式求出振动休止角α1：
α1=arctg
Figure 690529DEST_PATH_IMAGE002
；
分别为：
α1=arctg
Figure 939107DEST_PATH_IMAGE003
=arctg
Figure DEST_PATH_IMAGE009
=30°、
α2=arctg
Figure 272000DEST_PATH_IMAGE005
=arctg
Figure 2013100189199100002DEST_PATH_IMAGE010
=31°、
α3=arctg
Figure 522590DEST_PATH_IMAGE007
=arctg=30°，
则震动休止角平均值=（α1+α2+α3）/3=（30°+31°+30°）=30°；
3）按公式P=α - α1计算，即得到铁水覆盖剂的铺展性P为4°。
实施例2
1）将2000克铁水覆盖剂自500mm高度，自由下落到圆形平面板上，并堆积成圆锥体，直至堆积高度不再增加时止，测量覆盖剂自然堆积的锥体高度h和锥底半径r，如此重复三次，锥底半径r=100mm，锥体高度h分别为h1=70mm、h2=68mm、h3=72mm，按下式求出自然休止角α：
α=arctg；
分别为：
α1=arctg
Figure 2013100189199100002DEST_PATH_IMAGE012
=arctg
Figure DEST_PATH_IMAGE013
=35°、
α2=arctg=arctg=34°、
α3=arctg
Figure 260291DEST_PATH_IMAGE007
=arctg=36°，
则自然休止角平均值=（α1+α2+α3）/3=（35°+34°+36°）/3=35；
2）用铁水覆盖剂总重量的10%的重物1000克，自500mm高度，依次落在步骤1）的堆积有铁水覆盖剂的平面板上1次，测量覆盖剂振动后的锥体高度h1和锥底半径r1，如此重复三次，锥底半径r=100mm，锥体高度h分别为h1=62mm、h2=63mm、h3=64mm，按下式求出振动休止角α1：
α1=arctg
Figure 191338DEST_PATH_IMAGE002
；
分别为：
α1=arctg
Figure 414509DEST_PATH_IMAGE003
=arctg
Figure DEST_PATH_IMAGE015
=32°、
α2=arctg=arctg
Figure 2013100189199100002DEST_PATH_IMAGE016
=32°、
α3=arctg
Figure 550272DEST_PATH_IMAGE007
=arctg
Figure DEST_PATH_IMAGE017
=33°，
则震动休止角平均值=（α1+α2+α3）/3=（32°+32°+33°）/3=32；
3）按公式P=α - α1计算，即得到铁水覆盖剂的铺展性P为3°。
实施例3
1）将2000克铁水覆盖剂自300mm高度，自由下落到圆形平面板上，并堆积成圆锥体，直至堆积高度不再增加时止，测量覆盖剂自然堆积的锥体高度h和锥底半径r，如此重复三次，锥底半径r=100mm，锥体高度h分别为h1=70mm、h2=68mm、h3=72mm，按下式求出自然休止角α：
α=arctg
Figure 885176DEST_PATH_IMAGE001
；
分别为：
α1=arctg
Figure 595643DEST_PATH_IMAGE012
=arctg
Figure 339608DEST_PATH_IMAGE013
=35°、
α2=arctg
Figure 451921DEST_PATH_IMAGE005
=arctg
Figure 255929DEST_PATH_IMAGE008
=34°、
α3=arctg
Figure 453692DEST_PATH_IMAGE007
=arctg
Figure 499883DEST_PATH_IMAGE014
=36°，
则自然休止角平均值=（α1+α2+α3）/3=（35°+34°+36°）/3=35；
2）用铁水覆盖剂总重量的10%的重物500克，自300mm高度，依次落在步骤1）的堆积有铁水覆盖剂的平面板上2次，测量覆盖剂振动后的锥体高度h1和锥底半径r1，如此重复三次，锥底半径r=100mm，锥体高度h分别为h1=62mm、h2=63mm、h3=64mm，按下式求出振动休止角α1：
α1=arctg
Figure 466702DEST_PATH_IMAGE002
；
分别为：
α1=arctg=arctg
Figure 126670DEST_PATH_IMAGE015
=32°、
α2=arctg
Figure 478017DEST_PATH_IMAGE005
=arctg
Figure 299343DEST_PATH_IMAGE016
=32°、
α3=arctg
Figure 710733DEST_PATH_IMAGE007
=arctg
Figure 617509DEST_PATH_IMAGE017
=33°，
则震动休止角平均值=（α1+α2+α3）/3=（32°+32°+33°）/3=32；
3）按公式P=α - α1计算，即得到铁水覆盖剂的铺展性P为3°。
由上述实施例1、2、3得知，实施例1的铁水覆盖剂的铺展性优于实施例2和3。

Claims (2)

1.一种测量铁水覆盖剂铺展性的方法，其特征在于经过下列各步骤：
1）将铁水覆盖剂自设定高度，该设定高度是铁水覆盖剂锥底直径的1～5倍，自由下落到平面板上，并堆积成圆锥体，直至堆积高度不再增加时止，测量覆盖剂自然堆积的锥体高度h和锥底半径r，按下式求出自然休止角α：
α=arctg                                               
Figure 2013100189199100001DEST_PATH_IMAGE002
；
式中，h——锥体高度，mm；
r——锥体底部半径，mm；
2）用铁水覆盖剂总重量的5～10%的重物，自设定高度，依次落在步骤1）的堆积有铁水覆盖剂的平面板上1～4次，该设定高度是铁水覆盖剂锥底直径的1～5倍，测量覆盖剂振动后的锥体高度h1和锥底半径r1，按下式求出振动休止角α1：
α1=arctg
Figure 2013100189199100001DEST_PATH_IMAGE004
；
式中，h1——振动后的锥体高度，mm；
r1——振动后的锥底半径，mm；
3）按下列公式计算，即得到铁水覆盖剂的铺展性P：
P=α - α1
式中：P：铁水覆盖剂的铺展性，单位：度；
      α：自然休止角；
      α1：振动休止角。
2.根据权利要求1所述的测量铁水覆盖剂铺展性的方法，其特征在于：所述步骤1）的平面板为圆形或者矩形板。
CN2013100189199A 2013-01-18 2013-01-18 测量铁水覆盖剂铺展性的方法 Pending CN103115845A (zh)