CN103107310B - 蓄电池生极板的制作方法 - Google Patents

蓄电池生极板的制作方法 Download PDF

Info

Publication number
CN103107310B
CN103107310B CN201210446757.4A CN201210446757A CN103107310B CN 103107310 B CN103107310 B CN 103107310B CN 201210446757 A CN201210446757 A CN 201210446757A CN 103107310 B CN103107310 B CN 103107310B
Authority
CN
China
Prior art keywords
plate
grid
storage battery
lead
lead alloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201210446757.4A
Other languages
English (en)
Other versions
CN103107310A (zh
Inventor
邓海超
吴盛祺
李革
李晓峰
易少芝
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGXI SWAN STORAGE BATTERY CO Ltd
Original Assignee
GUANGXI SWAN STORAGE BATTERY CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGXI SWAN STORAGE BATTERY CO Ltd filed Critical GUANGXI SWAN STORAGE BATTERY CO Ltd
Priority to CN201210446757.4A priority Critical patent/CN103107310B/zh
Publication of CN103107310A publication Critical patent/CN103107310A/zh
Application granted granted Critical
Publication of CN103107310B publication Critical patent/CN103107310B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种蓄电池生极板的制作方法，采用板栅铅合金制成，板栅铅合金由钙，锡，铝，铁，铋，锌，锑，银，铜，砷，铅熔化制得；包括以下步骤：将上述的板栅铅合金放入冶炼锅熔化；然后将铅合金熔液注入连铸板栅模具中，制成长条的板栅带卷成筒，待用；将铸造好的板栅输入涂板机的入口，把铅膏投入涂板机的铅膏斗中，将铅膏均匀的涂在所述连板栅带上；将连板栅带分成单片的蓄电池湿极板；将所述蓄电池湿极板排列进入干燥窑进行表面去湿，干燥窑温度为180℃-200℃，干燥时间为15秒；把干燥后的所述蓄电池湿极板送入固化房固化，固化时间为38小时；从固化房取出即可。较之现有技术，用该蓄电池生极板装配的蓄电池，内阻小、重量轻。

Description

蓄电池生极板的制作方法
技术领域
本发明涉及铅酸蓄电池制造技术领域，尤其是一种用于生产铅酸蓄电池的生极板的制造工艺方法。
背景技术
生极板是指未进行充电的极板，生极板制作是铅酸蓄电池制造过程中的第一道工序，也是至关重要的一道工序；生极板质量的好坏直接影响着蓄电池的整体质量。目前，生极板是由单片板栅连续涂板生产出来，而且生极板存在内阻大和重量较重及生产成本高的问题。造成这些问题的原因是由于生极板的质量与其制作方法有关外还与生极板铅合金的配方有关。因此，人们进行了大量的试验，一直在寻找一种适合生极板的专用铅合金配方和与之相匹配的制造工艺方法。
发明内容
本发明要解决的技术问题是提供一种蓄电池生极板的制作方法，这种蓄电池生极板的制作方法可解决现有的蓄电池生极板内阻大和成本高的问题。
本发明解决技术问题所采用的技术方案为：这种蓄电池生极板的制作方法，采用板栅铅合金制成，所述板栅铅合金由下列重量百分比的材料熔化制得：钙0.18%，锡1.5%，铝0.06%，铁0.002%，铋0.005%，锌0.001%，锑0.001%，银0.001%，铜0.0015%，砷0.001%，其余为铅；
包括以下步骤：
A、将所述的板栅铅合金放入冶炼锅熔化；然后将熔化的板栅铅合金熔液注入连铸板栅模具中，制成长条的板栅带卷成筒，待用；
B、将所述连板栅带输入涂板机的入口；
C、把铅膏投入涂板机的铅膏斗中，将铅膏均匀的涂在所述连板栅带上；
D、将所述连板栅带分成单片的蓄电池湿极板；
E、将所述蓄电池湿极板排列进入干燥窑进行表面去湿，干燥窑温度为180℃-200℃，干燥时间为15秒；
F、把干燥后的所述蓄电池湿极板送入固化房固化，固化时间为38小时；
G、从固化房取出，即得本蓄电池生极板。
由于采用了上述技术方案，本发明与现有技术相比，具有的有益效果是：1、在板栅铅合金中加入稳定合金的钙的比例，从而减小了板栅的电阻，增强了板栅的导电性，使得用该蓄电池生极板装配的蓄电池，内阻小、重量轻；2、 板栅由单块改为连铸，减少了涂板过程中的铅膏的浪费，同时也节约了单位产品所需板栅的铅合金的用量，降低了成本。
具体实施方式
制作蓄电池生极板采用下列操作步骤：配制100千克的板栅铅合金，板栅铅合金由下列重量百分比的材料熔化制得：钙0.18克，锡1.5千克，铝0.06千克，铁0.002千克，铋0.005千克，锌0.001千克，锑0.001千克，银0.001千克，铜0.0015千克，砷0.001千克，其余为铅。将这些原料放入冶炼锅熔化；将熔化的板栅铅合金熔液注入连铸板栅模具中，制成长条的板栅带卷成筒，待用；将连板栅带输入涂板机的入口，把铅膏投入涂板机的铅膏斗中，将铅膏均匀的涂在连板栅带上；把连板栅带分成单片的蓄电池湿极板；将蓄电池湿极板排列进入干燥窑进行表面去湿，干燥窑温度为180℃-200℃，干燥时间为15秒；把干燥后的所述蓄电池湿极板送入固化房固化，固化时间为38小时；从固化房取出，即得本蓄电池生极板。本发明在板栅铅合金中加入稳定合金的钙的比例，从而减小了板栅的电阻，增强了板栅的导电性，使得用该蓄电池生极板装配的蓄电池，内阻小、重量轻；板栅由单块改为连铸，减少了涂板过程中的铅膏的浪费，同时也节约了单位产品所需板栅的铅合金的用量，降低了成本。

Claims (1)

1.一种蓄电池生极板的制作方法，其特征在于：
采用板栅铅合金制成，所述板栅铅合金由下列重量百分比的材料熔化制得：钙0.18%，锡1.5%，铝0.06%，铁0.002%，铋0.005%，锌0.001%，锑0.001%，银0.001%，铜0.0015%，砷0.001%，其余为铅；
包括以下步骤：
A、将所述的板栅铅合金放入冶炼锅熔化；然后将熔化的板栅铅合金熔液注入连铸板栅模具中，制成长条的连板栅带卷成筒，待用；
B、将所述连板栅带输入涂板机的入口；
C、把铅膏投入涂板机的铅膏斗中，将铅膏均匀的涂在所述连板栅带上；
D、将所述连板栅带分成单片的蓄电池湿极板；
E、将所述蓄电池湿极板排列进入干燥窑进行表面去湿，干燥窑温度为180℃-200℃，干燥时间为15秒；
F、把干燥后的所述蓄电池湿极板送入固化房固化，固化时间为38小时；
G、从固化房取出，即得本蓄电池生极板。
CN201210446757.4A 2012-11-11 2012-11-11 蓄电池生极板的制作方法 Expired - Fee Related CN103107310B (zh)