CN103072417A - Engraving method of metal foil painting - Google Patents
Engraving method of metal foil painting Download PDFInfo
- Publication number
- CN103072417A CN103072417A CN2013100311222A CN201310031122A CN103072417A CN 103072417 A CN103072417 A CN 103072417A CN 2013100311222 A CN2013100311222 A CN 2013100311222A CN 201310031122 A CN201310031122 A CN 201310031122A CN 103072417 A CN103072417 A CN 103072417A
- Authority
- CN
- China
- Prior art keywords
- metal forming
- engraving
- stencil plate
- metal foil
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the technical field of artware marking, in particular to an engraving method of a metal foil painting. The invention aims at providing the engraving method of the metal foil painting, which is simple and convenient to process and can allow an engraved pattern to be more stereoscopic. In order to solve the problem, the method adopts the technical scheme that the engraving method of the metal foil painting comprises the following steps that metal foil is placed horizontally on a wax block before engraving, and the wax block is bonded with a contact surface of the metal foil. The method has the benefits that with the adoption of the technical scheme, the engraved pattern is more stereoscopic, lively. visually, and lifelike; the method is simple and easy to use; and the making efficiency is improved greatly.
Description
Technical field
The present invention relates to the ornameutal handiwork technical field, be specifically related to the engraving process that a kind of metal forming is drawn.
Background technology
The metal forming such as gold, silver, aluminium foil is the important materials of carving handicraft article, yet, existing engraving technology
There is significant deficiency, specific as follows: when using engraving tool when metal forming depicts required pattern, existing
It is plane that pattern is arranged, and without any third dimension, also just image is dull, shortage is angry so that metal forming is drawn,
Artistic value and reserve value that metal forming is drawn have been had a strong impact on.In order to make existing pattern possess third dimension,
In the prior art, can only use various tool that the marginal portion of pattern is repaired, but this measure operation inconvenience,
Difficulty of processing is large and efficient is very low.
So the engraving process that provides a kind of metal forming that can address the aforementioned drawbacks to draw has been urgent need.
Summary of the invention
Problem to be solved by this invention provides a kind ofly processes easy and can make the pattern behind the engraving have more vertical
The engraving process that the metal forming of body sense is drawn.
In order to address the above problem, technical scheme provided by the present invention is:
The engraving process that a kind of metal forming is drawn said method comprising the steps of: before engraving, with metal forming
Lie on the stencil plate, the contact-making surface of described stencil plate and described metal forming is fitted mutually.
Optionally, described method is further comprising the steps of:
The drawing of A, design metal forming picture case;
B, drawing is fixed on the surface of metal forming.
Optionally, the density of described stencil plate is 800kg/m3-900kg/m3.
Optionally, described stencil plate remains under the room temperature state.
Optionally, place a piece of paper between described metal forming and the described stencil plate.
Optionally, the thickness of described metal forming is 0.07-0.12mm.
Optionally, described metal forming is aluminium foil.
Beneficial effect of the present invention is:
After adopting technical scheme of the present invention, not only the pattern behind the engraving has more third dimension, more lively shape
Resemble, life-like, and be simple and easy to greatly improve with, make efficiency.Because in technical solution of the present invention,
Metal forming is lain on the stencil plate, because stencil plate is neither too hard, nor too soft, plasticity is good, when engraving tool is scratched metal
Behind the paper tinsel, taking advantage of a situation immediately enters in the stencil plate, is presented bending, stereoeffect so that metal forming draws the edge simultaneously
Obviously, overcome in the prior art that metallic foil pattern is plane shortcoming behind the engraving.And, this solid
Effect and engraving step synchronous forming need not the secondary operations such as finishing, have greatly improved make efficiency, overcome
The shortcoming of large, the inefficiency of prior art operation inconvenience, difficulty of processing.
Further, in the technical solution of the present invention, design first the drawing of metal forming picture case, then with drawing
Be fixed on the surface of metal forming, this has overcome needs the shortcoming that traces designs in metal forming in advance in the prior art,
Reduce operation, be simple and easy to greatly improve with, make efficiency.
Further, in the technical solution of the present invention, the density of described stencil plate is 800kg/m3-900kg/m3, this
Guaranteed that stencil plate is neither too hard, nor too soft, plasticity is good, is convenient to engraving and makes.
Further, in the technical solution of the present invention, described stencil plate remains under the room temperature state.This had both overcome
Stencil plate excess Temperature of living in and cause the bits problem have guaranteed the cleaning of engraving tool and metal forming, also gram
The stencil plate problem really up to the mark that has taken stencil plate excessive temperature of living in and caused has guaranteed engraving quality and efficient.
Further, in the technical solution of the present invention, place a piece of paper between described metal forming and the described stencil plate.
This has been avoided metal forming directly to contact with described stencil plate, thereby avoids metal foil surface to be infected with the chip of stencil plate,
Also just guaranteed the cleaning of metal forming.
Further, in the technical solution of the present invention, the thickness of described metal forming is 0.07-0.12mm.This overcomes
The shortcoming that aluminium foil easily ruptures during metal foil thickness＜0.07mm, yield rate is low, guaranteed yield rate; Also restrain
Taken metal foil thickness〉the larger shortcoming of engraving difficulty of pattern during 0.12mm, guaranteed engraving quality and effect
Rate.
Further, in the technical solution of the present invention, described metal forming is aluminium foil.Comprehensively right with other metal formings
Ratio, aluminium foil not only have the advantages such as protection against the tide, airtight, shading, erosion resistant, guarantor be fragrant, nonpoisonous and tasteless, and
Quality is light, have graceful silvery white gloss, is easy to process the beautiful pattern of various beauty of colors and decorative pattern.
The specific embodiment
The below will be clearly and completely described the technical scheme in the embodiment of the invention, and obviously, institute retouches
The embodiment that states only is the present invention's part embodiment, rather than whole embodiment.In the present invention
Embodiment, those of ordinary skills do not make obtain under the creative work prerequisite all its
His embodiment belongs to the scope of protection of the invention.
Embodiment one:
The engraving process that a kind of metal forming is drawn said method comprising the steps of: before engraving, with metal forming
Lie on the stencil plate, the contact-making surface of described stencil plate and described metal forming is fitted mutually.
Described stencil plate needs neither too hard, nor too soft, and plasticity is good, such as: when the density of stencil plate is 800kg/m3-900kg/m3,
Can reach above-mentioned effect.
The function of described stencil plate is: utilize the characteristics that stencil plate is neither too hard, nor too soft, plasticity is good, work as engraving tool
After scratching metal forming, taking advantage of a situation immediately enters in the stencil plate, is presented bending so that metal forming draws the edge simultaneously,
Stereoeffect is obvious, has overcome in the prior art that metallic foil pattern is plane shortcoming behind the engraving.So,
Every stencil plate of above-mentioned functions of can realizing all falls into protection scope of the present invention.In addition, except using stencil plate
Outside, other possess material neither too hard, nor too soft, the good feature of plasticity and all can be used as stencil plate such as plasticine etc.
Substitute.
In addition, metal forming is lain on the stencil plate, the contact-making surface of described stencil plate and described metal forming is fitted mutually,
Function is: because the contact-making surface of described stencil plate and described metal forming fits mutually, and described stencil plate and described then
The space is minimum between the metal forming, so after engraving tool is scratched metal forming, can take advantage of a situation immediately and enter stencil plate
In, so that being drawn the edge, metal forming presents bending simultaneously.
Embodiment two:
On the basis of the engraving process that the described a kind of metal forming of embodiment one is drawn, described method also comprise with
The drawing of lower step: A, design metal forming picture case; B, drawing is fixed on the surface of metal forming;
Then carve in metal forming with engraving tool according to drawing.The function of above step is: overcome existing
Having needs the shortcoming that traces designs in metal forming in advance in the technology, reduce operation, be simple and easy to, make efficiency large
The large raising.
Embodiment three:
On the basis of the engraving process of embodiment one or two described a kind of metal landscapes, the density of described stencil plate
Be 800kg/m3 or 820kg/m3 or 840kg/m3 or 860kg/m3 or 880kg/m3 or 900kg/m3.
When the density of described stencil plate was above-mentioned numerical value, function was: this has guaranteed that stencil plate is neither too hard, nor too soft, can
Plasticity is good, is convenient to engraving and makes.If described stencil plate density＜800kg/m3, stencil plate is excessively soft, causes the carver
Tool easily is infected with the stencil plate chip, and then causes the stencil plate chip to be infected with in metal foil surface, has increased the cleaning burden;
If described stencil plate density〉900kg/m3, then stencil plate is really up to the mark, causes engraving tool to be difficult to go deep into smoothly in the stencil plate,
Thereby the effect and quality of impact engraving.
So, the density of described stencil plate can be 800kg/m3 or 820kg/m3 or 840kg/m3 or 860kg/m3 or
All meet the density of above-mentioned beneficial effect 880kg/m3 or 900kg/m3 etc.
Embodiment four:
On the basis of the engraving process that the described a kind of metal forming of embodiment one to three any one is drawn, described
Stencil plate remains under the room temperature state.When described stencil plate temperature of living in is higher than room temperature, then stencil plate is excessively soft, causes carving
Quarter, instrument easily was infected with the stencil plate chip, and then caused the stencil plate chip to be infected with in metal foil surface, had increased cleaning negative
Load; When described stencil plate temperature of living in is lower than room temperature, then stencil plate is really up to the mark, causes engraving tool to be difficult to smoothly deeply
In the stencil plate, thus the effect and quality of impact engraving.
Embodiment five:
On the basis of the engraving process that the described a kind of metal forming of embodiment one to four any one is drawn, described
Place a piece of paper between metal forming and the described stencil plate.Described paper should be neither too hard, nor too soft, guarantees engraving tool such as icking tool
Can insert smoothly, such as: described paper is the papers in the office such as printing paper of 32～80g/ ㎡, can reach
State effect.The function of placing a piece of paper is: avoid metal forming directly to contact with described stencil plate, thereby avoid
Metal foil surface is infected with the chip of stencil plate, has also just guaranteed the cleaning of metal forming.So, every can the realization
The paper of above-mentioned functions all falls into protection scope of the present invention.
Embodiment six:
On the basis of the engraving process that the described a kind of metal forming of embodiment one to five any one is drawn, described
The thickness of aluminium foil is 0.07mm or 0.075mm or 0.08mm or 0.085mm or 0.09mm or 0.095mm or 0.1mm
Or 0.105mm or 0.11mm or 0.115mm or 0.12mm.
When the thickness of metal forming was above-mentioned numerical value, function was: 1, metal forming easy fracture not, metal forming is drawn
Yield rate is high; 2, metal foil thickness is moderate, and the engraving difficulty is little; 3, more be conducive to present the engraving edge
The third dimension at place is simultaneously also so that the global pattern behind the engraving is more true to nature, life-like.
If but metal foil thickness＜0.07mm, metal forming easily ruptures, and yield rate is low; If metal foil thickness
0.12mm, the engraving difficulty of pattern is larger.And, when metal foil thickness＜0.07mm or during 0.12mm, gold
Belong to paper tinsel engraving edge and all be difficult to present third dimension true to nature.
So, the thickness of described metal forming can be 0.07mm or 0.075mm or 0.08mm or 0.085mm or
0.09mm or 0.095mm or 0.1mm or 0.105mm or 0.11mm or 0.115mm or 0.12mm etc. all meet
State the thickness of beneficial effect.
Embodiment seven:
On the basis of the engraving process that the described a kind of metal forming of aforementioned one to six any one embodiment is drawn,
Described metal forming is aluminium foil.With other metal forming Comprehensive Correlations, aluminium foil not only have protection against the tide, airtight, shading,
Erosion resistant, protect the advantages such as fragrant, nonpoisonous and tasteless, and quality is light, silvery white gloss with gracefulness, is easy to
Process the beautiful pattern of various beauty of colors and decorative pattern.So aluminium foil is the clear lumber of engraving metal forming picture handicraf
Material.
To sum up, detailed Jie has been carried out in the engraving process of drawing of the above a kind of metal forming that the embodiment of the invention is provided
Continue, used specific case herein principle of the present invention and embodiment are set forth, above enforcement
The explanation of example just is used for helping to understand method of the present invention and core concept thereof; Simultaneously, for this area
Those skilled in the art according to thought of the present invention, all can change in specific embodiments and applications
Part, in summary, this description should not be construed as limitation of the present invention.
Claims (5)
1. the engraving process that metal forming is drawn is characterized in that, said method comprising the steps of: before engraving,
Metal forming is lain on the stencil plate, and the contact-making surface of described stencil plate and described metal forming is fitted mutually.
2. the according to claim 1 engraving process of described a kind of metal forming picture is characterized in that, described method also
May further comprise the steps:
The drawing of A, design metal forming picture case;
B, drawing is fixed on the surface of metal forming.
3. according to claim 1 or the engraving process of drawing of 2 described a kind of metal formings, it is characterized in that described wax
The density of plate is 800kg/m3-900kg/m3.
4. the according to claim 3 engraving process of described a kind of metal forming picture is characterized in that, described stencil plate is protected
Be held under the room temperature state.
5. the according to claim 4 engraving process of described a kind of metal forming picture is characterized in that described metal forming
And place a piece of paper between the described stencil plate.