CN103046397A - Coconut fiber elastomer material - Google Patents
Coconut fiber elastomer material Download PDFInfo
- Publication number
- CN103046397A CN103046397A CN2012105906687A CN201210590668A CN103046397A CN 103046397 A CN103046397 A CN 103046397A CN 2012105906687 A CN2012105906687 A CN 2012105906687A CN 201210590668 A CN201210590668 A CN 201210590668A CN 103046397 A CN103046397 A CN 103046397A
- Authority
- CN
- China
- Prior art keywords
- fiber
- pet
- coconut
- elastomer material
- melting point
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of an environmentally-friendly elastomer material, in particular to a coconut fiber elastomer material. The coconut fiber elastomer material comprises natural coconut fibers and polyethylene terephthalate (PET)/Propene Polymer (PP), wherein the percent of the natural coconut fibers is 50% to 90% and the percent of PET/PP is 10% to 50%. The coconut fiber elastomer material is more environmentally-friendly, has better performance and longer service life, and can be used as elastomer filling materials for mattresses, sofas, and upholstery soft rolls, and base materials of outdoor bulletin boards.
Description
Technical field
The present invention relates to Environmental-protecting elastic body material technology field, refer in particular to a kind of coconut fibre elastomeric material.
Background technology
The natural coconut palm fiber is gathered around very strong compressive property and elasticity, for a long time the coir fibre mattress made as raw material of coconut fibre as good packing material by a large amount of applying in the household goods such as mattress sofa, and the great majority of manufacturing in the process of coir fibre mattress of the prior art still use chemical adhesive to the bonding reinforcing of finalizing the design of natural coconut palm fiber, this technique has determined that resulting coir fibre mattress contains more content of formaldehyde, and the chemical adhesive rear snake that goes mouldy easily that makes moist, be used for using not environmental protection on the household, and lose easily cohesive force after chemical adhesive is aging, make the loose frangibility of material, thereby affect overall performance and the service life of coir fibre mattress.
Summary of the invention
The objective of the invention is for the deficiencies in the prior art, and provide a kind of coconut fibre elastomeric material, its material environment friendly is energy-conservation, after adopting mutually entanglement melt bonded, the coconut fibre elastomer material structure that forms is tightr, compressive property is stronger, flexible, pulling force strong, Anti-temperature difference is difficult for deformation, planarization is better, even thickness, soundproof effect are good, can be used for mattress, sofa, the elastomer-filled material of indoor decoration Soft Roll, outdoor billboard base material etc.
For achieving the above object, the present invention adopts following technical scheme, it comprises the natural coconut palm fiber, it is characterized in that: described coconut fibre elastomeric material composition comprises: any one mixture material in natural coconut palm fiber and modification low-melting point polyester staple fiber (PET) or the polypropene staple (PP), the per distribution ratio of natural coconut palm fiber is 50-90%, and modification low-melting point polyester staple fiber (PET) or polypropene staple (PP) per distribution ratio are 10-50%.
A kind of coconut fibre elastomeric material preparation method is: described coconut fibre elastomeric material is that the natural coconut palm fiber is by evenly mixing adding modification low-melting point polyester staple fiber (PET) or polypropene staple (PP) by the 100-300 ℃ of bonding formation of high-temperature fusion.
Beneficial effect of the present invention is: the natural coconut palm fiber has very strong compressive property, after melt bonded through the mutual entanglement of modification low-melting point polyester staple fiber (PET) or polypropene staple (PP), the coconut fibre elastomer material structure that forms is tightr, compressive property is stronger, flexible, pulling force strong, Anti-temperature difference is difficult for deformation, planarization is better, even thickness, soundproof effect are good; Described coconut fibre elastomeric material does not add any chemical adhesive, adopt modification low-melting point polyester staple fiber (PET) or polypropene staple (PP) as bonding reinforcement material, meet national requirements for environmental protection, bonding more firm, be difficult for wearing out longer service life.
Description of drawings:
Fig. 1 is cross-sectional view of the present invention.
The specific embodiment:
As shown in Figure 1: the present invention includes the natural coconut palm fiber, described coconut fibre elastomeric material composition comprises: any one mixture material in natural coconut palm fiber 1 and modification low-melting point polyester staple fiber (PET) or the polypropene staple (PP) 2, the per distribution ratio of natural coconut palm fiber 1 is 50-90%, and modification low-melting point polyester staple fiber (PET) or polypropene staple (PP) 2 per distribution ratios are 10-50%.
A kind of coconut fibre elastomeric material preparation method is: described coconut fibre elastomeric material is that natural coconut palm fiber 1 is by evenly mixing adding modification low-melting point polyester staple fiber (PET) or polypropene staple (PP) 2 by the 100-300 ℃ of bonding formation of high-temperature fusion, because natural coconut palm fiber 1 has the characteristic of itself with modification low-melting point polyester staple fiber (PET) or polypropene staple (PP) 2, can mutually tangle melt bonded by high temperature.
This coconut fibre elastomeric material composition comprises: natural coconut palm fiber 1 and modification low-melting point polyester staple fiber (PET) or polypropene staple (PP) 2, natural coconut palm fiber 1 is by evenly mixing adding modification low-melting point polyester staple fiber (PET) or polypropene staple (PP) 2 by the bonding formation of high-temperature fusion, polyester staple fiber (PET) or polypropene staple (PP) can be selected wherein, and a kind of material gets final product, the natural coconut palm fiber itself has very strong compressive property, after melt bonded through the mutual entanglement of modification low-melting point polyester staple fiber (PET) or polypropene staple (PP), the coconut fibre elastomer material structure that forms is tightr, compressive property is stronger, flexible, pulling force is strong, Anti-temperature difference is difficult for deformation, planarization is better, even thickness, the new material that soundproof effect is good; And the coconut fibre elastomeric material does not add any chemical adhesive, adopt modification low-melting point polyester staple fiber (PET) or polypropene staple (PP) as bonding reinforcement material, fiber with certain-length can be described as staple fibre, such as cotton fiber, wool fibre etc., and polyester is the general designation of a large class, be commonly referred to as polyethylene terephthalate, claim again PET, such fiber is called terylene in China, is a kind of of chemical fibre; Polypropene staple claims defend and split fibre not only but also claim PP fiber, building materials fiber, building fiber.Polypropene staple is a kind of take polypropylene as raw material, makes the high strength pencil monfil that forms.Have the microcrack that factors such as preventing solid plastic shrinkage, drying shrinkage, variations in temperature causes, prevent and suppress formation and the development in crack, have anti-cracking impervious property, shock resistance and shock resistance, very environmental protection, bonding more firm, be difficult for wearing out longer service life.
Can be used for mattress, sofa, the elastomer-filled material of indoor decoration Soft Roll, outdoor billboard base material, soundproof wall etc.
The above only is preferred embodiment of the present invention, so all equivalences of doing according to the described structure of patent claim of the present invention, feature and principle change or modify, is included in the patent claim of the present invention.
Claims (2)
1. coconut fibre elastomeric material, it comprises the natural coconut palm fiber, it is characterized in that: described coconut fibre elastomeric material composition comprises: any one mixture material in natural coconut palm fiber (1) and modification low-melting point polyester staple fiber (PET) or the polypropene staple (PP) (2), the per distribution ratio of natural coconut palm fiber (1) is 50-90%, and modification low-melting point polyester staple fiber (PET) or polypropene staple (PP) (2) per distribution ratio are 10-50%.
2. a kind of coconut fibre elastomeric material preparation method according to claim 1 is: it is characterized in that: described coconut fibre elastomeric material is that natural coconut palm fiber (1) is by evenly mixing adding modification low-melting point polyester staple fiber (PET) or polypropene staple (PP) (2) by the 100-300 ℃ of bonding formation of high-temperature fusion.