CN103043744B - 一种煤渣灰处理工业废水的方法 - Google Patents
一种煤渣灰处理工业废水的方法 Download PDFInfo
- Publication number
- CN103043744B CN103043744B CN201210595453.4A CN201210595453A CN103043744B CN 103043744 B CN103043744 B CN 103043744B CN 201210595453 A CN201210595453 A CN 201210595453A CN 103043744 B CN103043744 B CN 103043744B
- Authority
- CN
- China
- Prior art keywords
- ash
- water
- cinder
- cinder ash
- conducted
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种煤渣灰处理工业废水的方法;其方法为:取工业锅炉煤渣粉碎;把秸秆燃烧成灰,在灰里面掺和环丙基甲酸乙酯和羟基而乙叉二膦酸盐,搅拌混合均匀;加入适量水,进行搅拌均匀,并在105℃下烘干;烘干后的混合物与水泥按着质量比为10∶1~5∶1混合,拌入适量水;搅拌均匀后造粒,在高温下煅烧,得到煤渣灰吸附材料。把上述制备得到的煤渣灰吸附材料颗粒填充到吸附塔内,每层填料的厚度为30~40cm,让废水从上往下流过,出水即为处理后的水,处理效率可达99.99%,本发明操作简单,原料易得,成本比较低;既可实现资源的循环利用,还具有良好的经济效益。
Description
技术领域
本发明公开一种煤渣灰处理工业废水的方法,属于废水处理领域。
背景技术
目前的高浓度废水都是采用生化处理有机溶剂,但是这种处理方式一般只能处理COD、DOD含量在5万以下的废水,对于20万以上COD、DOD含量的废水则无法用生法化处理,因为其中有机溶剂的沸点比较高,采用加入药剂方式的处理方法,不仅成本高,而且无法有效去除。
废水的水解酸化处理工艺作为生物预处理技术在国内外已多有研究和应用。它可提高污水生化性能,降低后续生物处理负荷。因此,如何结合现有技术,设计高效低成本处理含高比例工业废水的污水系统和方法,一直是技术人员的关注的目标。
发明内容
本发明针对现有技术的不足,提供了一种煤渣灰处理工业废水的方法。
本发明采用的技术方案为:采用煤渣灰吸附的方法,吸附去除水中的污染物,并再进一步化学处理、过滤、水质达到可作循环水的补充水标准。吸附污染物的炭煤灰烧制成建筑用砖,达到以废治废综合利用的目的。
其吸附材料的具体制备方法为:
(1)取工业锅炉煤渣,粉碎成80~100目颗粒物质;
(2)把秸秆燃烧成灰,在灰里面掺和1~5ppm的环丙基甲酸乙酯和5~10ppm的羟基乙叉二膦酸盐,搅拌混合均匀;
(3)在上述两种物质里面加入适量水,进行搅拌均匀,并在105℃下烘干;
(4)烘干后的混合物与水泥按照质量比为10:1~5:1混合,拌入适量水;
(5)搅拌均匀后造粒,在高温下煅烧,得到煤渣灰吸附材料。
本发明的优点及有益效果:
(1)本发明操作简单,原料易得,成本比较低;
(2)既可实现资源的循环利用,还具有良好的经济效益。
具体实施方式
(1)取工业锅炉煤渣,粉碎成80~100目颗粒物质;
(2)把秸秆燃烧成灰,在灰里面掺和1~5ppm的环丙基甲酸乙酯和5~10ppm的羟基乙叉二膦酸盐,搅拌混合均匀;
(3)在上述两种物质里面加入适量水,进行搅拌均匀,并在105℃下烘干;
(4)烘干后的混合物与水泥按照质量比为10:1~5:1混合,拌入适量水;
(5)搅拌均匀后造粒,在高温下煅烧,得到煤渣灰吸附材料。
把上述制备得到的煤渣灰吸附材料颗粒填充到吸附塔内,每层填料的厚度为30~40cm,让废水从上往下流过,出水即为处理后的水。
实例1:
取工业锅炉煤渣,粉碎成80目颗粒物质;把秸秆燃烧成灰,在灰里面掺和1ppm的环丙基甲酸乙酯和5ppm的羟基乙叉二膦酸盐,搅拌混合均匀;在上述两种物质里面加入适量水,进行搅拌均匀,并在105℃下烘干;烘干后的混合物与水泥按照质量比为10:1混合,拌入适量水;搅拌均匀后造粒,在高温下煅烧,得到煤渣灰吸附材料。把上述制备得到的煤渣灰吸附材料颗粒填充到吸附塔内,每层填料的厚度为30cm,让废水从上往下流过,出水即为处理后的水,废水中COD处理效率达99.5%。
实例2:
取工业锅炉煤渣,粉碎成80目颗粒物质;把秸秆燃烧成灰,在灰里面掺和3ppm的环丙基甲酸乙酯和8ppm的羟基乙叉二膦酸盐,搅拌混合均匀;在上述两种物质里面加入适量水,进行搅拌均匀,并在105℃下烘干;烘干后的混合物与水泥按照质量比为5:1混合,拌入适量水;搅拌均匀后造粒,在高温下煅烧,得到煤渣灰吸附材料。把上述制备得到的煤渣灰吸附材料颗粒填充到吸附塔内,每层填料的厚度为35cm,让废水从上往下流过,出水即为处理后的水,废水中COD处理效率达99.9%。
实例3:
取工业锅炉煤渣,粉碎成100目颗粒物质;把秸秆燃烧成灰,在灰里面掺和5ppm的环丙基甲酸乙酯和10ppm的羟基乙叉二膦酸盐,搅拌混合均匀;在上述两种物质里面加入适量水,进行搅拌均匀,并在105℃下烘干;烘干后的混合物与水泥按照质量比为5:1混合,拌入适量水;搅拌均匀后造粒,在高温下煅烧,得到煤渣灰吸附材料。把上述制备得到的煤渣灰吸附材料颗粒填充到吸附塔内,每层填料的厚度为40cm,让废水从上往下流过,出水即为处理后的水,废水中COD处理效率达99.99%。
Claims (2)
1.一种煤渣灰处理工业废水的方法,其特征在于煤渣灰吸附材料的制备方法为:
(1)取工业锅炉煤渣,粉碎成80~100目颗粒物质;
(2)把秸秆燃烧成灰,在灰里面掺和1~5ppm的环丙基甲酸乙酯和5~10ppm的羟基乙叉二膦酸盐,搅拌混合均匀;
(3)在上述两种物质里面加入适量水,进行搅拌均匀,并在105℃下烘干;
(4)烘干后的混合物与水泥按照质量比为10:1~5:1混合,拌入适量水;
(5)搅拌均匀后造粒,在高温下煅烧,得到煤渣灰吸附材料。
2.根据权利要求1所述的一种煤渣灰处理工业废水的方法,其特征在于煤渣灰吸附材料处理工业废水的应用方法是:把上述制备得到的煤渣灰吸附材料颗粒填充到吸附塔内,每层填料的厚度为30~40cm,让废水从上往下流过,出水即为处理后的水。