CN103042163A - 改性水玻璃砂及其制作方法 - Google Patents

改性水玻璃砂及其制作方法 Download PDF

Info

Publication number
CN103042163A
CN103042163A CN 201110313648 CN201110313648A CN103042163A CN 103042163 A CN103042163 A CN 103042163A CN 201110313648 CN201110313648 CN 201110313648 CN 201110313648 A CN201110313648 A CN 201110313648A CN 103042163 A CN103042163 A CN 103042163A
Authority
CN
China
Prior art keywords
water glass
sand
modified water
making method
modified
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201110313648
Other languages
English (en)
Inventor
陈雨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201110313648 priority Critical patent/CN103042163A/zh
Publication of CN103042163A publication Critical patent/CN103042163A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种改性水玻璃砂及其制作方法，属于化工领域。一种改性水玻璃砂及其制作方法，其特征是：在波美度50-52°的水玻璃中加入水玻璃重量的6-8％，浓度为25％的聚丙烯酸钠溶液，搅拌后制成改性水玻璃，搅匀后得到高强度的砂型。本发明的优点在于通过在普通水玻璃中加入添加剂，在成本少量增加的情况下，使其砂型强度提高，提高砂型溃散性，减轻清理劳动强度，节约清理费用。

Description

改性水玻璃砂及其制作方法
技术领域
本发明涉及一种改性水玻璃砂及其制作方法，属于化工领域。
背景技术
铸造用砂有粘土砂、水玻璃砂、树脂砂等几种，其中水玻璃砂具有易紧实、流动性好、无毒无味的特点，因此是铸钢生产常用的砂型，但水玻璃砂存在着强度低、易产生裂纹、落砂清理困难等不足。
发明内容
本发明的目的：提供一种改性水玻璃砂的制作方法，以提高普通水玻璃砂的强度，从而提高铸件质量。
技术方案：一种改性水玻璃砂及其制作方法，其特征是：在波美度50-52°的水玻璃中加入水玻璃重量的6-8％，浓度为25％的聚丙烯酸钠溶液，搅拌后制成改性水玻璃，搅匀后得到高强度的砂型。
本发明的优点：通过在普通水玻璃中加入添加剂，在成本少量增加的情况下，使其砂型强度提高，提高砂型溃散性，减轻清理劳动强度，节约清理费用。
本发明的实施例
实施例1
在波美度为50°的水玻璃中加入水玻璃重量的6％，浓度为25％的聚丙烯酸钠溶液，搅拌后制成改性水玻璃，搅匀后得到高强度的砂型。
实施例2
在波美度为52°的水玻璃中加入水玻璃重量的8％，浓度为25％的聚丙烯酸钠溶液，搅拌后制成改性水玻璃，搅匀后得到高强度的砂型。

Claims (1)

1.一种改性水玻璃砂及其制作方法，其特征是：在波美度50-52°的水玻璃中加入水玻璃重量的6-8％，浓度为25％的聚丙烯酸钠溶液，搅拌后制成改性水玻璃，搅匀后得到高强度的砂型。
CN 201110313648 2011-10-17 2011-10-17 改性水玻璃砂及其制作方法 Pending CN103042163A (zh)